Abstract
The W-type hexagonal ferrites with the composition Sr1−x La x Co2Fe16O27 (0 ≤ x ≤ 0.35) magnetic powders were synthesized by the solid state method. The phase constituents, micro-morphology, and magnetic properties of the particles were investigated by x-ray diffraction (XRD), a scanning electron microscope, and a vibrating sample magnetometer. The single phase was observed in the W-type ferrites with different La content from XRD. The micro-morphology of the particles exhibits the hexagonal plate-like shape, and the particles are distributed homogeneously of W-type ferrites with different La content. The coercivity (H c) of the particles increases with the increase of La content (x), while the saturation magnetization (M s) of the particles first increases with x from 0 to 0.15, and then begins to decrease when x continues to increase.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
K. Huang, X.S. Liu, S.J. Feng, Z.J. Zhang, J.Y. Yu, X.F. Niu, F.R. Lv, and X. Huang, J. Magn. Magn. Mater. 379, 16 (2015).
M. Matsumoto and Y.J. Miyata, J. Appl. Phys. 79, 5486 (1996).
X.X. Liu, J.M. Bai, F.L. Wei, Z. Yang, A.M. Morisako, and M. Matsumoto, J. Magn. Magn. Mater. 212, 273 (2000).
J.D. Adam, L.E. Davis, G.F. Dionne, E.F. Schloemann, S.N. Stitzer, and I.E.E.E. Trans, Microw. Theor. Tech. 50, 721 (2002).
S.A. Oliver, P. Shi, W. Hu, H. How, S.W. McKnight, N.E. McGruer, P.M. Zavracky, C. Vittoria, and I.E.E.E. Trans, Microw. Theor. Tech. 49, 385 (2001).
J. Feng, N. Funabashi, N. Matsushita, S. Nakagawa, and M. Naoe, IEEE Trans. Magn. 36, 2930 (2005).
X. Liu, P. Hernández-Gómez, K. Huang, S. Zhou, Y. Wang, X. Cai, H. Sun, and B. Ma, J. Magn. Magn. Mater. 305, 524 (2006).
A. Morisako, T. Kubono, M. Matsumoto, and M. Naoe, IEEE Trans. Magn. 36, 2339 (2000).
C.S. Wang, X.W. Qi, L.T. Li, J. Zhou, X.H. Wang, and Z.X. Yue, Mater. Sci. Eng., B 99, 576 (2003).
P.S. Sawadh and D.K. Kulkarni, B. Mater. Sci 24, 47 (2001).
D. Lisjak, A. Znidarsic, A. Sztanislav, and M. Drofenik, J. Eur. Ceram. Soc. 28, 2057 (2008).
F. Lv, X. Liu, S.J. Feng, K. Huang, X.F. Niu, X. Huang, F. Huang, Y.Q. Ma, S. Jiang, and Y.C. Wu, Mater. Lett. 157, 277 (2015).
W. Jing, Z. Hong, B. Shuxin, C. Ke, and Z. Changrue, J. Magn. Magn. Mater. 312, 310 (2007).
M.A. Ahmed, N. Okasha, O. Maf, and R.M. Kershi, J. Magn. Magn. Mater. 320, 1146 (2008).
S. Ounnunkad, Solid State Commun. 138, 472 (2006).
L.S. You, L. Qiao, J.W. Zheng, M.Y. Jiang, L.Q. Jiang, and J.W. Sheng, J. Rare Earth. 26, 81 (2008).
F.Y. Guo, X.M. Wu, G.J. Ji, J.J. Xu, L.C. Zou, and S.C. Gan, J. Supercond. Nov. Magn. 27, 411 (2014).
X. Liu, W. Zhong, S. Yang, Z. Yu, B. Gu, and Y. Du, J. Magn. Magn. Mater. 238, 207 (2002).
F.K. Lotgering, P.H.G.M. Vromans, and M.A.H. Huyberts, J. Appl. Phys. 51, 5913 (1980).
M. Ahmad, I. Ali, R. Grössinger, M. Kriegisch, F. Kubel, and M.U. Ranaa, J. Alloy. Compd. 579, 57 (2013).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (Nos. 51072002 and 51272003), Dr. Start-up capital of Suzhou University (2016jb10), and the Natural Science Research Fund of Anhui Provincial Department of Education (KJ2016A775).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Niu, X., Liu, Y., Li, M. et al. The Study of Microstructure and Magnetic Properties of La3+ doped W-Type Hexagonal Ferrites Sr1−x La x Co2Fe16O27 . J. Electron. Mater. 46, 4299–4303 (2017). https://doi.org/10.1007/s11664-017-5387-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-017-5387-y