Abstract
The use of the pulse plasma sintering technique for CoSb3 thermoelectric material consolidation is reported in this work. The influence of sintering temperature on the microstructure and material properties such as the Seebeck coefficient, electrical resistivity, and thermal conductivity has been investigated. It is shown that, for samples fabricated at 923 K and 973 K, there were no significant differences in the average grain size or final phase composition. In both cases, a fine-grained polycrystalline structure of the compacts with density nearly equal to the theoretical value was achieved. Both samples were composed almost uniquely of CoSb3 phase. The measured thermoelectric parameters such as the Seebeck coefficient, electrical, and thermal conductivity showed similar dependence on temperature. For both samples, the Seebeck coefficient was negative at room temperature and showed a transition from n- to p-type conduction over the temperature range of 400 K to 460 K. The measured minimum thermal conductivity values, 4 W m−1 K−1 to 5 W m−1 K−1 at 723 K, are typical for undoped bulk CoSb3. A maximum ZT value of 0.08 at 623 K was obtained for the sample consolidated at 923 K for 5 min. The results of this work are very promising from the point of view of use of pulse plasma sintering as an alternative method for fabrication of a broad range of thermoelectric materials in the future.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J.R. Sootsman, D.Y. Chung, and M.G. Kanatzidis, Angew. Chem. Int. Ed. Engl. 48, 8616 (2009).
J.R. Salvador, J. Yang, H. Wang, and X. Shi, J. Appl. Phys. 107, 043705 (2010).
X. Shi, J. Yang, J.R. Salvador, M. Chi, J.Y. Cho, H. Wang, S. Bai, J. Yang, W. Zhang, and L. Chen, J. Am. Chem. Soc. 133, 7837 (2011).
G.S. Nolas, X. Lin, J. Martin, M. Beekman, and H. Wang, J. Electron. Mater. 38, 1052 (2009).
W. Zhao, P. Wei, Q. Zhang, H. Peng, W. Zhu, D. Tang, J. Yu, H. Zhou, Z. Liu, X. Mu, D. He, J. Li, C. Wang, X. Tang, and J. Yang, Nat. Commun. 6, 6197 (2015).
L. Yang, J.S. Wu, and L.T. Zhang, J. Alloys Compd. 375, 114 (2004).
K.T. Wojciechowski, J. Alloys Compd. 439, 18 (2007).
A. Khan, M. Saleemi, M. Johnsson, L. Han, N.V. Nong, M. Muhammed, and M.S. Toprak, J. Alloys Compd. 612, 293 (2014).
Z. He, C. Stiewe, D. Platzek, G. Karpinski, E. Müller, S. Li, M. Toprak, and M. Muhammed, J. Appl. Phys. 101, 053713 (2007).
W.-S. Liu, B.-P. Zhang, J.-F. Li, and L.-D. Zhao, J. Phys. D Appl. Phys. 40, 566 (2007).
J.L. Mi, T.J. Zhu, X.B. Zhao, and J. Ma, J. Appl. Phys. 101, 054314 (2007).
W.-S. Liu, B.-P. Zhang, J.-F. Li, and L.-D. Zhao, J. Phys. D Appl. Phys. 40, 6784 (2007).
P. Nieroda, R. Zybala, and K.T. Wojciechowski, in AIP Conference Proceedings (2012), pp. 199–202.
R. Zybala and K.T. Wojciechowski, in AIP Conference Proceedings (2012), pp. 393–396.
T. Liang, X. Su, Y. Yan, G. Zheng, Q. Zhang, H. Chi, X. Tang, and C. Uher, J. Mater. Chem. A 2, 17914 (2014).
X. Su, F. Fu, Y. Yan, G. Zheng, T. Liang, Q. Zhang, X. Cheng, D. Yang, H. Chi, X. Tang, Q. Zhang, and C. Uher, Nat. Commun. 5, 4908 (2014).
J.G. Santanach, C. Estournès, A. Weibel, G. Chevallier, V. Bley, C. Laurent, and A. Peigney, J. Eur. Ceram. Soc. 31, 2247 (2011).
K. Sairam, J.K. Sonber, T.S.R.C. Murthy, C. Subramanian, R.K. Fotedar, P. Nanekar, and R.C. Hubli, Int. J. Refract. Met. Hard Mater. 42, 185 (2014).
A.M. Abyzov, M.J. Kruszewski, Ł. Ciupiński, M. Mazurkiewicz, A. Michalski, and K.J. KurzydŁowski, Mater. Des. 76, 97 (2015).
J. Grzonka, J. Kruszewski, M. Rosiński, Ł. Ciupiński, A. Michalski, and K.J. KurzydŁowski, Mater. Charact. 99, 188 (2015).
M. Rosiński, J. Wachowicz, T. Płociński, T. Truszkowski, and A. Michalski, Ceram. Trans. 243, 181 (2014).
M. Rosiński, M.J. Kruszewski, A. Michalski, E. Fortuna-Zaleśna, Ł. Ciupiński, and K.J. KurzydŁowski, Fusion Eng. Des. 86, 2573 (2011).
M.J. Kruszewski, Ł. Ciupiński, M. Rosiński, A. Michalski, and K.J. KurzydŁowski, Fusion Eng. Des. 88, 2573 (2013).
A.T. Krawczynska, T. Brynk, M. Rosinski, A. Michalski, S. Gierlotka, E. Grzanka, S. Stelmakh, B. Palosz, M. Lewandowska, and K.J. Kurzydlowski, in Nanometals-Status Perspect. Proceedings of 33rd Risø International Symposium on Materials Science (Roskilde, Denmark: Department of Wind Energy, Technical University of Denmark, 2012), p. 8.
X. Su, H. Li, G. Wang, H. Chi, X. Zhou, X. Tang, Q. Zhang, and C. Uher, Chem. Mater. 23, 2948 (2011).
G. Xie, O. Ohashi, K. Chiba, N. Yamaguchi, M. Song, K. Furuya, and T. Noda, Mater. Sci. Eng. A 359, 384 (2003).
U. Anselmi-Tamburini, J.E. Garay, and Z.A. Munir, Mater. Sci. Eng. A 407, 24 (2005).
Y. Cai, D. Zhao, X. Zhao, L. Chen, W. Jiang, and P. Zhai, Mater. Trans. 50, 782 (2009).
T. Caillat, A. Borshchevsky, and J.-P. Fleurial, J. Appl. Phys. 80, 4442 (1996).
M.-J. Kim and I.-H. Kim, Met. Mater. Int. 16, 459 (2010).
L. Yang, J.S. Wu, and L.T. Zhang, Mater. Des. 25, 97 (2004).
H. Nakagawa, H. Tanaka, A. Kasama, H. Anno, and K. Matsubara, in XVI ICT“97. Proc. ICT”97. 16th International Conference on Thermoelectrics (Cat. No. 97TH8291) (IEEE, 1997), pp. 351–355.
K.T. Wojciechowski, J. Toboła, and J. Leszczynski, J. Alloys Compd. 361, 19 (2003).
M.S. Toprak, C. Stiewe, D. Platzek, S. Williams, L. Bertini, E. Müller, C. Gatti, Y. Zhang, M. Rowe, and M. Muhammed, Adv. Funct. Mater. 14, 1189 (2004).
J.X. Zhang, Q.M. Lu, K.G. Liu, L. Zhang, and M.L. Zhou, Mater. Lett. 58, 1981 (2004).
S. Katsuyama, Y. Shichijo, M. Ito, K. Majima, and H. Nagai, J. Appl. Phys. 84, 6708 (1998).
K. Wojciechowski, P. Nieroda, J. Toboła, and R. Zybała, Ceram. Mater. 62, 60 (2010).
T. Dahal, Q. Jie, W. Liu, K. Dahal, C. Guo, Y. Lan, and Z. Ren, J. Alloys Compd. 623, 104 (2015).
G. Rogl, A. Grytsiv, P. Rogl, E. Bauer, M. Kerber, M. Zehetbauer, and S. Puchegger, Intermetallics 18, 2435 (2010).
G. Rogl, A. Grytsiv, P. Rogl, E. Royanian, E. Bauer, J. Horky, D. Setman, E. Schafler, and M. Zehetbauer, Acta Mater. 61, 6778 (2013).
C. Soon-Mok, L. Jae-Ki, S. Won-Seon, L. Hong-Lim, and K. Il-Ho, J. Korean Phys. Soc. 57, 1010 (2010).
W.-S. Liu, B.-P. Zhang, J.-F. Li, H.-L. Zhang, and L.-D. Zhao, J. Appl. Phys. 102, 103717 (2007).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Kruszewski, M., Zybała, R., Ciupiński, Ł. et al. Microstructure and Thermoelectric Properties of Bulk Cobalt Antimonide (CoSb3) Skutterudites Obtained by Pulse Plasma Sintering. J. Electron. Mater. 45, 1369–1376 (2016). https://doi.org/10.1007/s11664-015-4037-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-015-4037-5