Abstract
It is explained with a simple model why the reduction of threading dislocation (TD) densities in epitaxial lattice and thermal expansion mismatched IV–VI layers such as PbSe(111) on Si(111) substrates follows a 1/h 2 dependence where h is the thickness of the layer. This is in contrast to the 1/h dependence for III–V and II–VI layers grown on mismatched substrates. The 1/h 2 dependence results since the thermal mismatch strain is mainly reduced by glide and reactions of the TD in their main {100}-type glide system of the NaCl-type IV–VI semiconductors. In addition, multiple thermal cycles lead to further reduction of the TD densities by glide and fusion since fusion does not cause dislocation blocking.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
H. Kroemer, T.-Y. Liu, and P.M. Petroff, J. Cryst. Growth 95, 96 (1989).
M. Tachikawa and M. Yamaguchi, Appl. Phys. Lett. 56, 484 (1990).
G. Badano, P. Gergaud, I.C. Robin, X. Baudry, B. Amstatt, and Fréderique. Gemain, J. Electron. Mater. 39, 908 (2010).
J.D. Benson, S. Farrell, G. Brill, Y. Chen, P.S. Wijewarnasuriya, L.O. Bubulac, P.J. Smith, R.N. Jacobs, J.K. Markunas, M. Jaime-Vasquez, L.A. Almeida, A. Stoltz, U. Lee, M.F. Vilela, J. Peterson, S.M. Johnson, D.D. Lofgreen, D. Rhiger, E.A. Patten, and P.M. Goetz, J. Electron. Mater. 40, 1847 (2011).
S. Farrell, G. Brill, Y.P. Chen, P.S. Wijewarnasuriya, M.V. Rao, N. Dhar, and K. Harris, J. Electron. Mater. 39, 43 (2010).
J.S. Speck, M.A. Brewer, G. Beltz, A.E. Romanov, and W. Pompe, J. Appl. Phys. 80, 3808 (1996).
P. Müller, H. Zogg, A. Fach, J. John, C. Paglino, A.N. Tiwari, M. Krejci, and G. Kostorz, Phys. Rev. Lett. 78, 3007 (1997).
H. Zogg, K. Alchalabi, and D. Gössi, Proc. 9th Int. Conf. on Narrow Gap Semiconductors (NG9), ed. N. Puhlmann, H.-U.Müller, and M. von Ortenberg (Humboldt University at Berlin, Germany, 1999).
H. Zogg and J. John, Opto-Electron. Rev. 6, 37 (1998).
H. Zogg, S. Blunier, A. Fach, C. Maissen, P. Müller, S. Teodoropol, V. Meyer, G. Kostorz, A. Dommann, and T. Richmond, Phys. Rev. B 50, 10801 (1994).
P. Müller (Ph.D. thesis, ETH Nr. 12011, 1997).
P. Müller, A. Fach, J. John, J. Masek, C. Paglino, and H. Zogg, Appl. Surf. Sci. 102, 130 (1996).
G. Wang, R. Loo, E. Simoen, L. Souriau, M. Caymax, M.M. Heyns, and B. Blanpain, Appl. Phys. Lett. 94, 102115 (2009).
H. Zogg, K. Alchalabi, D. Zimin, and K. Kellermann, IEEE Trans. Electron Dev. 50, 209 (2003).
H. Zogg, M. Arnold, F. Felder, M. Rahim, C. Ebneter, I. Zasavitskiy, N. Quack, S. Blunier, and J. Dual, J. Electron. Mater. 37, 1497 (2008).
M. Rahim, A. Khiar, M. Fill, F. Felder, and H. Zogg, Electron. Lett. 47, 1037 (2011).
A.Y. Ueta, G. Springholz, and G. Bauer, J Cryst. Growth 175/176, 1022 (1997).
H. Böttner, G. Chen, and R. Venkatasubramanian, MRS Bull. 31, 211 (2006).
J. Nurnus, J. John, and H. Griessmann, Proceedings 4th European Workshop on Thermoelectrics (Madrid, 1998).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zogg, H. Dislocation Reduction by Glide in Epitaxial IV–VI Layers on Si Substrates. J. Electron. Mater. 41, 1931–1935 (2012). https://doi.org/10.1007/s11664-012-2031-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-012-2031-8