Abstract
The impact of a marine environment on Sn-Ag-Cu interconnect reliability is examined using salt spray exposure followed by thermal cycling. Sn-Ag-Cu solder alloy wafer-level packages, with and without pretreatment with 5% NaCl salt spray, were thermally cycled to failure. The prior salt spray reduced the characteristic lifetime of the Sn-Ag-Cu solder joints by over 43%. Although Sn-based materials show strong resistance to corrosion, the nature of localized corroded areas at critical locations in the solder joint caused significant degradation in the Sn-Ag-Cu solder joints. An important link between the corrosion path and Sn grain orientation was observed using orientation imaging microscopy (OIM). A strong correlation between the corrosion path and grain orientation was identified, indicating that the corrosion attack preferentially followed the basal plane of the Sn lattice.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
F. Song and R. Lee, Proceeding of the 56th Electronic Components and Technology Conference, San Diego, California, May (2006).
M. Abtew and G. Selvaduray, Mater. Sci. Eng. R 27, 95 (2000).
A.J. Hale and H.S. Fosteh, J. Soc. Chem. Ind. 9, 2371 (1915).
A. Jermstad and A. Gaule, J. Inst. Met. 13, 1370 (1919).
B. Liu, T.-K. Lee, and K.-C. Liu, 42nd International Symposium on Microelectronics (IMAPS 2009) Proceedings, San Jose, 3rd November (2009).
M. Mori, K. Miura, T. Sasaki, and T. Ohtsuka, Corros. Sci. 44, 887 (2002).
U.S. Mohanty and K. Lin, Corros. Sci. 50, 2437 (2008).
R.P. Frankenthal and D.J. Siconolfi, Corros. Sci. 21, 479 (1981).
T. Farrell, Met. Sci. 10, 87 (1976).
B.Y. Wu, Y.C. Chan, and M.O. Alam, J. Mater. Res. 21, 62 (2006).
J.Y. Jung, S.B. Lee, H.Y. Lee, Y.C. Joo, and Y.B. Park, J. Electron. Mater. 37, 1111 (2008).
D. Frear, H. Morgan, and J.H. Lau, eds., The Mechanics of Solder Alloy Interconnects (New York: Van Nostrand Reinhold, 1994).
J.A. Rayne and B.S. Chandrasekhar, Phys. Rev. 120, 1658 (1960).
D.G. House and E.V. Vernon, Br. J. Appl. Phys. 11, 254 (1960).
V.T. Deshpande and D.B. Sirdeshmukh, Acta Cryst. 15, 294 (1962).
T.-K. Lee, B. Zhou, L. Blair, K.-C. Liu, and T.R. Bieler, J. Electron. Mater. 39, 2588 (2010).
T.R. Bieler, H. Jiang, L.P. Lehman, T. Kirkpatrick, E.J. Cotts, and B. Nandagopal, IEEE Trans. Compon. Packag. Technol. 31, 370 (2008).
A.U. Telang, T.R. Bieler, J.P. Lucas, K.N. Subramanian, L.P. Lehman, Y. Xing, and E.J. Cotts, J. Electron. Mater. 33, 1412 (2004).
B. Zhou, T.R. Bieler, T.-K. Lee, and K.-C. Liu, J. Electron. Mater. 38, 2702 (2009).
T.-K. Lee, K.-C. Liu, and T.R. Bieler, J. Electron. Mater. 38, 2685 (2009).
S. Park, R. Dhakal, L. Lehman, and E. Cotts, Acta Mater. 55, 3253 (2007).
S. Terashima, T. Kobayashi, and M. Tanaka, Sci. Technol. Weld. Join. 13, 732 (2008).
M.A. Matin, E.W.C. Coenen, W.P. Vellinga, and M.G.D. Geers, Scripta Mater. 53, 927 (2005).
A.U. Telang and T.R. Bieler, Scripta Mater. 52, 1027 (2005).
A.U. Telang, T.R. Bieler, A. Zamiri, and F. Pourboghrat, Acta Mater. 55, 2265 (2007).
M.A. Matin, W.P. Vellinga, and M.G.D. Geers, Mater. Sci. Eng. A 445, 73 (2007).
A. LaLonde, D. Emelander, J. Jeannette, C. Larson, W. Rietz, D. Swenson, and D.W. Henderson, J. Electron. Mater. 33, 1545 (2004).
T.R. Bieler, T.-K. Lee, and K.-C. Liu, J. Electron. Mater. 38, 2712 (2009).
ASTM B117-09, Standard Practice for Operating Salt Spray (Fog) Apparatus (2009).
B. Zhou, T.R. Bieler, G. Wu, S. Zaefferer, T.-K. Lee, and K.-C. Liu, 42nd International Symposium on Microelectronics (IMAPS 2009) Proceedings, San Jose, 3rd November (2009).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lee, TK., Liu, B., Zhou, B. et al. Correlation Between Sn Grain Orientation and Corrosion in Sn-Ag-Cu Solder Interconnects. J. Electron. Mater. 40, 1895–1902 (2011). https://doi.org/10.1007/s11664-011-1654-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-011-1654-5