Abstract
The In-Sn-Ni alloys of various compositions were prepared and annealed at 160°C and 240°C. No ternary compounds were found; however, most of the binary compounds had extensive ternary solubility. There was a continuous solid solution between the Ni3Sn phase and Ni3In phase. The Sn-In/Ni couples, made of Sn-In alloys with various compositions, were reacted at 160°C and 240°C and formed only one compound for all the Sn-In alloys/Ni couples reacted up to 8 h. At 240°C, Ni28In72 phase formed in the couples made with pure indium, In-10at.%Sn and In-11at.%Sn alloys, while Ni3Sn4 phase formed in the couples made of alloys with compositions varied from pure Sn to In-12at.%Sn. At 160°C, except in the In/Ni couple, Ni3Sn4 formed by interfacial reaction.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
P.T. Vianco and D.R. Frear, JOM 45, 14 (1993).
J. Glazer, Int. Mater. Rev. 40, 65 (1995).
W.J. Plumbridge, J. Mater. Sci. 31, 2501 (1996).
R. Dietz, Adv. Packaging 8, 44 (1999).
J.L. Freer and J.W. Morris, Jr., J. Electron. Mater. 21, 647 (1992).
J.W. Morris, Jr., J.L. Freer Goldstein, and Z. Mei, JOM 45, 25 (1993).
K. Shimizu, T. Nakanishi, K. Karasawa, K. Hashimoto, and K. Niwa, J. Electron. Mater. 24, 39 (1995).
K.-L. Lin and C.-J. Chen, J. Mater. Sci. 7, 397 (1996).
Y.H. Tseng, M.S. Yeh, and T.H. Chuang, J. Mater. Sci. 28, 105 (1999).
F.J.J. van Loo, Progr. Solid State Chem. 20, 47 (1990).
A.D. Romig, Jr., Y.A. Chang, J.J. Stephens, D.R. Frear, V. Marcotte, and C. Lea, Solder Mechanics: A State of the Art Assessment, ed. D.R. Frear, W.B. Jones, and K.R. Kinsman (Warrendale, PA: TMS, 1991), pp. 29–104.
F.J.J. van Loo and A.A. Kodentsov, Pure Appl. Chem. 70, 501 (1998).
H.-T. Luo and S.-W. Chen, J. Mater. Sci. 31, 5059 (1996).
L.-H. Su, Y.-W. Yen, C.-C. Lin, and S.-W. Chen, Metall. Mater. Trans. B 28B, 927 (1997).
B.-R. Shie, S.-W. Chen, and J.-L. Wang, J. Non-Crystalline Solids 231, 240 (1998).
H. Okamoto, Indium Alloys and Their Engineering Applications, ed. C.E.T. White and H. Okamoto (Materials Park, OH: ASM Int., 1992), pp. 255–257.
B.-J. Lee, C.-S. Oh, and J.-H. Shim, J. Electron. Mater. 25, 983 (1996).
M.F. Singleton and P. Nash, Indium Alloys and Their Engineering Applications, eds. C.E.T. White and H. Okamoto (Materials Park, OH: ASM Int., 1992), pp. 186–190.
P. Nash and A. Nash, Phase Diagrams of Binary Nickel Alloys, ed. P. Nash (Materials Park, OH: ASM Int., 1992), pp. 310–318.
W. Burkhardt and K. Schubert, Z. Metallkd. 50, 442 (1959).
M.K. Bhargava and K. Schubert, Z. Metallkd. 67, 318 (1976).
K.N. Tu and R. Rosenberg, Jpn. J. Appl. Phys., Suppl. 2, Part I 633 (1974).
S.K. Kang and V. Ramachandran, Scripta Metall. 14, 421 (1980).
Z. Marinkovic and V. Simic, Thin Solid Films 98, 95 (1982).
J.A. van Beek, S.A. Stolk, and F.J.J. van Loo, Z. Metallkd. 73, 439 (1982).
W.J. Tomlinson and H.G. Rhodes, J. Mater. Sci. 22, 1769 (1987).
S. Bader, W. Gust, and H. Hieber, Acta Metall. Mater. 43, 329 (1995).
S.-W. Chen, C.-M. Chen, and W.-C. Liu, J. Electron. Mater. 27, 1193 (1998).
K.-L. Lin and C.-J. Chen, Int. J. Microcircuits Electron. Packaging 20, 46 (1997).
J.-I. Lee, H.-Y. Chang, and S.-W. Chen, National Tsing-Hua University, Taiwan, unpublished research (2001).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Huang, CY., Chen, SW. Interfacial reactions in In-Sn/Ni couples and phase equilibria of the In-Sn-Ni system. J. Electron. Mater. 31, 152–160 (2002). https://doi.org/10.1007/s11664-002-0162-z
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-002-0162-z