Abstract
The failure mechanisms of SnAgCu solder on Al/Ni(V)/Cu thin-film, underbump metallurgy (UBM) were investigated after multiple reflows and high-temperature storage using a ball shear test, fracture-surface analysis, and cross-sectional microstructure examination. The results were also compared with those of eutectic SnPb solder. The Al/Ni (V)/Cu thin-film UBM was found to be robust enough to resist multiple reflows and thermal aging at conditions used for normal production purposes in both SnAgCu and eutectic SnPb systems. It was found that, in the SnAgCu system, the failure mode changed with the number of reflows, relating to the consumption of the thin-film UBM because of the severe interfacial reaction between the solder and the UBM layer. After high-temperature storage, the solder joints failed inside the solder ball in a ductile manner in both SnAgCu and SnPb systems. Very fine Ag3Sn particles were formed during multiple reflows in the SnAgCu system. They were found to be able to strengthen the bulk solder. The dispersion-strengthening effect of Ag3Sn was lost after a short period of thermal aging, caused by the rapid coarsening of these fine particles.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
International Roadmap for Semiconductor Technology (San Jose, CA: Semiconductor Industry Association, 1999), pp. 223–225.
K.N. Tu and K. Zeng, Mater. Sci. Eng. R 34, 1 (2001).
D.R. Frear, J.W. Jang, J.K. Lin, and C. Zhang, JOM 53 (6), 38 (2001).
S.-Y. Jang and K.-W. Paik, Solder. Surf. Mount Technol. 10, 29 (1998).
T.M. Korhonen, P. Su, S.J. Hong, M.A. Korhonen, and C.-Y. Li, J. Electron. Mater. 29, 1194 (2000).
T.M. Korhonen, P. Su, S.J. Hong, M.A. Korhonen, and C.-Y. Li, Proc. 50th Electron. Comp. Technol. Conf. 1106 (2000).
H.K. Kim, H.K. Liou, and K.N. Tu, Appl. Phys. Lett. 66, 2337 (1995).
R.S. Rai, S.K. Kang, and S. Purushothaman, Proc. 45th Electron. Comp. Technol. Conf. 1197 (1995).
J.W. Jang, P.G. Kim, K.N. Tu, D.R. Frear, and P. Thompson, J. Appl. Phys. 85, 8456 (1999).
C.Y. Liu, K.N. Tu, T.T. Sheng, C.H. Tung, D.R. Frear, and P. Elenius, J. Appl. Phys. 87, 750 (2000).
P.S. Teo, Y.W. Huang, C.H. Tung, M.R. Marks, and T.B. Lim, Proc. 50th Electron. Comp. Technol. Conf. 33 (2000).
K. Zeng, V. Vuorinen, and J.K. Kivilahti, Proc. 51st Electron. Comp. Technol. Conf. 693 (2001).
W.T. Chen, C.E. Ho, and C.R. Kao, J. Mater. Res. 17, 263 (2002).
J.W. Jang, A.P. De Silva, T.Y. Lee, J.K. Lin, and D.R. Frear, Appl. Phys. Lett. 79, 482 (2001).
H.K. Kim and K.N. Tu, Phys. Rev. B 53, 16027 (1996).
M. Schaefer, R.A. Fournelle, and J. Liang, J. Electron. Mater. 27, 1167 (1998).
K. Zeng and J.K. Kivilahti, J. Electron. Mater. 30, 35 (2001).
M. Li, F. Zhang, W.T. Chen, K. Zeng, K.N. Tu, H. Balkan, and P. Ellinus, J. Mater. Res. 17, 1612 (2002).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zhang, F., Li, M., Balakrisnan, B. et al. Failure mechanism of lead-free solder joints in flip chip packages. J. Electron. Mater. 31, 1256–1263 (2002). https://doi.org/10.1007/s11664-002-0018-6
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-002-0018-6