Abstract
The weldability of two TiAl-based alloys, Ti-45Al-2Nb-2Mn and Ti-48Al-2Nb-2Mn, was investigated with the electron-beam welding process. It was found that the alloys were susceptible to solid-state cracking due to high thermally induced stresses and, more significantly, to the intrinsic brittleness of the microstructures. This work correlated the quality of the TiAl welds, made using different sets of welding parameters which gave rise to different cooling rates, to the microstructures that developed during welding. It was found that the welds were crack-free if the weld cooling rates were such that decomposition of the high-temperature α phase in the weld was not suppressed. It was shown that the Ti-48Al-based alloy was less susceptible to the solid-state cracking and, thus, was more weldable than the Ti-45Al-based alloy because the α phase in the alloy with a higher aluminum content could decompose more readily. A continuous cooling transformation (CCT) diagram is suggested to be used as an appropriate reference for the selection of welding parameters which induce suitable microstructures in the welds and result in crack-free welds.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
R.A. Patterson, P.L. Martin, B.K. Damkroger, and L. Christodoulou: Weld. J., 1990, vol. 69 (1), pp. 39-s–44-s.
P.L. Threadgill: Mater. Sci. Eng. A, 1995, vols. A192–A193, pp. 640–46.
M.C. Chaturvedi, N.L. Richards, and Q. Xu: Mater. Sci. Eng. A, 1997, vols. A239–A240, pp. 605–12.
C.M. Austin, T.J. Kelly, K.G. McAllister, and J.C. Chesnutt: in Structural Intermetallics, M.V. Nathal, R. Darolia, C.T. Liu, P.L. Martin, D.B. Miracle, R. Wagner, and M. Yamaguchi, eds., TMS, Warrendale, PA, 1997, pp. 413–25.
V. Acoff and D. Bharani: Proc. Materials Solution ’97 on Joining and Repair of Gas Turbine Components, [Indianapolis, IN,] ASM International, OH, 1997, pp. 137–42.
H. Clemons, N. Eberhardt, W. Glatz, H.P. Martinz, W. Knabl, and N. Reheis: in Structural Intermetallics, M.V. Nathal, R. Darolia, C.T. Liu, P.L. Martin, D.B. Miracle, R. Wagner, and M. Yamaguchi, eds., TMS, Warrendale, PA, 1997, pp. 277–86.
W.A. Baeslack III, P.L. Threagill, E.D. Nicholas, and T.F. Broderick: in Titanium ’95: Science and Technology, P.A. Blenkinsop, W.J. Evans, and H.M. Flower, eds., The Institute of Materials, London, United Kingdom, 1996, pp. 424–31.
W.A. Baeslack III, H. Zhang, P.L. Threagill, and B.G.I. Dance: Mater. Characterization, 1997, vol. 39, pp. 43–52.
G. Çam, K.-H. Bohm, J. Mullauer, and M. Koçak: JOM, 1996, No. 11, pp. 66–68.
P. Yan and E.R. Wallach: Intermetallics, 1993, vol. 1, pp. 83–97.
Q. Xu, M.C. Chaturvedi, N.L. Richards, and N. Goel: in Structural Intermetallics, M.V. Nathal, R. Darolia, C.T. Liu, P.L. Martin, D.B. Miracle, R. Wagner, and M. Yamaguchi, eds., TMS, Warrendale, PA, 1997, pp. 323–29.
K. Easterling: in Introduction to the Physical Metallurgy of Welding, 2nd ed., Butterworth-Heinemann, London, 1992.
M. Yamaguchi and H. Inui: in Structural Intermetallics, R. Darolia, J.J. Lewandowski, C.T. Liu, P.L. Martin, D.B. Miracle, and M.V. Nathal, eds., TMS, Warrendale, PA, 1993, pp. 127–42.
S.-C. Huang and D.S. Shih: in Microstructure/Property Relationships in Titanium Aluminides and Alloys, Y.W. Kim and R.R. Boyer, eds., TMS, Warrendale, PA, 1990, pp. 105–22.
Y.W. Kim and D.M. Dimiduk: in Structural Intermetallics, M.V. Nathal, R. Darolia, C.T. Liu, P.L. Martin, D.B. Miracle, R. Wagner, and M. Yamaguchi, eds., TMS, Warrendale, PA, 1997, pp. 531–43.
S.A. Jones and M.J. Kaufman: Acta Metall. Mater., 1993, vol. 41(2), pp. 387–98.
“Guide to the Welding and Weldability of C-Mn Steels and C-Mn Microalloyed Steels,” International Institute of Welding, Paris, France, Publications Document II S/IIW-382-71, 1971.
L.L. Rothenflue and H.A. Lipsitt: in Titanium ’95: Science and Technology, P.A. Blenkinsop, W.J. Evans, and H.M. Flower, eds., The Institute of Materials, London, United Kingdom, 1996, pp. 176–83
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Xu, Q., Chaturvedi, M.C. & Richards, N.L. The role of phase transformation in electron-beam welding of TiAl-based alloys. Metall Mater Trans A 30, 1717–1726 (1999). https://doi.org/10.1007/s11661-999-0171-0
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-999-0171-0