Abstract
The fatigue properties of two types of cold-work tool steels tempered at various temperatures were evaluated. The microstructure and fracture surface morphology were correlated to the fatigue behavior. Cold-work tool steels using this study were a conventional tool steel (JIS SKD11; 1.4C-11Cr-0.8Mo-0.2V) and its modified steel (M-SKD11; 0.8C-8Cr-2Mo-0.5V). The fatigue strength of the M-SKD11 steel increased 20 pct over that of the SKD11 steel for any number of cycles. This is attributed to the refinement of primary M7C3 carbides. These M7C3 carbides fractured during fatigue and were found at the sites of fatigue crack initiation. Change in crack initiation behavior was confirmed by acoustic emission testing. The S-N curves of the steels are similar to those of most structural steels. However, the subsurface fatigue crack initiation was dominant at lower alternating stresses. This study points to a general approach of carbide refinement that can be used for the enhancement of fatigue properties.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
F.A. Kivk: Met. Technol., 1982, vol. 9, pp. 198–2024.
S. Inoue: J. Jpn. Inst. Iron Steel, 1987, vol. 73, pp. 1461–69.
T. Arakawa and M. Suzuki: Bull. Jpn. Inst. Met., 1966, vol. 5, pp. 269–83.
N. Tsujii and G. Abe: Sanyo Tech. Rep., 1995, vol. 2, pp. 77–83.
K. Ozaki, Y. Matsuda, and K. Sudoh: CAMP-ISIJ, Jpn., 1994, vol. 7, p. 724.
J. Yoshida, M. Katsumata, and Y. Yamasaki: CAMP-ISIJ, Jpn., 1991, vol. 4, p. 1896.
M. Knoe, K. Lange, and T. Altan: J. Mater. Processing Technol., 1994, vol. 46, pp. 57–71.
K. Aramoti and G. Urano: Bull. Jpn. Inst. Met., 1969, vol. 8, pp. 117–26.
K. Itoh, K. Sudou, Y. Tokiwa, and K. Matsuda: J. Jpn. Elect. Furnace, 1984, vol. 55, pp. 248–56.
T. Abe and K. Kanazawa: J. Jpn. Soc. Mater. Sci., 1996, vol. 45, pp. 9–15.
N. Tsujii and G. Abe: Sanyo Tech. Rep., 1994, vol. 1, p. 69.
J. Yoshida, M. Katsumata, and K. Kashiwagi: CAMP-ISIJ, Jpn., 1992, vol. 5, p. 927.
N.M.A. Eid and P.F. Thomason: Acta Metall., 1979, vol. 27, pp. 1239–49.
J. Lankford: Engg. Fract. Mech., 1977, vol. 9, pp. 617–24.
Y. Murakami and M. Shimizu: Trans. Jpn. Soc. Mech. Eng. A, 1988, vol. 54, pp. 413–25.
H. Berns, J. Leng, W. Trojahn, R. Wahling, and H. Wisell: Powder Metall. Int., 1987, vol. 19 (4), pp. 22–26.
J. Yoshida, M. Katsumata, and Y. Yamazaki: J. Jpn. Inst. Iron Steel, 1988, vol. 84, pp. 79–84.
Y. Natsume, K. Murakami, and T. Miyamoto: Proc. Jpn. Soc. Mech. Eng., 1990, vol. 900 (86), pp. 323–25.
G. Abe, H. Nakamura, and H. Tyoh: Bull. Jpn. Inst. Met., 1986, vol. 25, p. 438.
H. Sunada, K. Fukaura, K. Teramoto, N. Tsujii, and D. Yokoi: Proc. 45th Meeting, Mater. Sci. Jpn., 1996, p. 149.
R.H.K. Honeycombe: Steels—Microstructure and Properties, Edward Arnold, London, 1990, pp. 156–60.
J. Durinin and K.A. Ridal: J. Iron Steel Inst., 1968, Jan., pp. 60–67.
Anon: Manual for X-Ray Diffraction, 4th ed., Rigaku Denki Co., Tokyo, 1991, p. 56.
K. Fukaura and K. Ono: in Progress in Acoustic Emission X, T. Kishi et al., eds., Japan Soc. for non-destructive Inspection, Tokyo, 2000, pp. 337–43.
P. Villars, A. Prince, and H. Okamoto: Handbook of Ternary Alloy Phase Diagram, ASM, Materials Park, OH, 1995, pp. 6632–33.
R.W. Hertzberg: Deformation and Fracture Mechanics of Engineering Materials, Wiley, New York, NY, 1989, p. 495.
Metals Handbook, 10th ed., Materials Park, OH, 2000, vol. 8, pp. 785–86.
S. Matsuoka, M. Yuyama, and B. Nishijima: Trans. JSME, 1986, vol. A52 (480), pp. 1831–38.
Y. Murakami: Metal Fatigue: Effects of Small Defects and Nonmetallic Inclusions, Yokendo Ltd., Tokyo, 1993, p. 78.90.106.
H. Berns: Proc. Fatigue ’87, Charlottesville, VA, 1987, EMAS Ltd., London, 1987, vol. 1, pp. 527–36.
Y. Natsume, S. Miyagawa, Y. Uemura, and Y. Murakami: J. Jpn. Inst. Mater. Sci., 1989, vol. 38 (10), pp. 1133–38.
Y. Murakami and T. Endo: Int. J. Fatigue, 1980, vol. 2 (1), pp. 23–30.
Y. Murakami, T. Ueda, and T. Nomoto: Proc. Eur. Conf. on Fatigue, Sept. 2000, Paper No. 069, pp. 1–8.
O. Vosikovsky: Eng. Frac. Mech., 1979, vol. 11, pp. 595–602.
Y. Natsume, S. Miyagawa, and M. Muramatsu: J. Jpn. Inst. Mater. Sci., 1988, vol. 37, pp. 606–11.
D. Yokoi: Sanyo Special Steel Co. Ltd., Hyogo, Japan, unpublished research, 1997.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Fukaura, K., Yokoyama, Y., Yokoi, D. et al. Fatigue of cold-work tool steels: Effect of heat treatment and carbide morphology on fatigue crack formation, life, and fracture surface observations. Metall Mater Trans A 35, 1289–1300 (2004). https://doi.org/10.1007/s11661-004-0303-5
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-004-0303-5