Abstract
C-S-H series are synthesized at different temperatures and ages by pozzolanic reaction. The change of particle size distribution, phase composition, morphology and nanostructure of C-S-H with temperatures and ages, and the effects of C-S-H seeds and seeds parameters on the hydration behavior and mechanical properties development of cement were investigated by DLS, XRD, SEM, 29Si NMR, TAM-air isothermal calorimeter and mechanical properties test. The results show that the particle size, crystallinity, basal spacing and Q2/Q1 ratio of C-S-H increases with the increase of synthesis temperature and age. The addition of synthesized C-S-H seeds to cement pastes results in the strong acceleration effect on cement hydration and significant improvement of the early strength of cement paste and mortar. The 1 day-C-S-H seeds synthesized at room temperature can increase the strength of cement paste by about 30 MPa at 12 h. The effect does not show a very regular change with the increase of the temperature and age of seeds synthesis. Considering the effect of C-S-H seeds on the hydration and mechanical properties of cement, and economy and short cycle of seeds synthesis, the C-S-H seeds synthesized at room temperature for 1 day or 55 °C water bath for 12 hours is recommended.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Lincen Yu, Biacun Zheng. Preparation of Calcium Silicate (C-S-H) and the Effect on the Cement Hydration Process[D]. Beijing: National Knowledge Infrastructure, 2018
Elisabeth John, Thomas Matschei. Nucleation Seeding with Calcium Silicate Hydrate - A Review[J]. Cement and Concrete Research, 2018(113): 74–85
Luc Nicoleau. New Calcium Silicate Hydrate Network[J]. Journal of the Transportation Research Board, 2010(2 142): 42–51
Zheng Wang, Yingzi Yang. Preparation of C-S-H Phase Nuclei and Its Effects on Compressive Strength of Cement[J]. Materials Science and Technology, 2007(15): 789–791
J P Liu, Y J Wang, Q Tian, et a1. Modeling Hydration Process of Magnesia Based on Nucleation and Growth Theory: The Isothermal Calorimetry Study[J]. Thermochimica Acta, 2012(550): 27–32
G Land, D Stephan. The Synthesis of C-S-H Seeds Methods, Variables and Their Impact on the Ability to Accelerate Cement Hydration[C]. International Conference on Coordination Chemistry, Beijing, China, 2015
Yongjia He, Xiaogang Zhao, Linnu Lu, et a1. Effect of C/S Ratio on Morphology and Structure of Hydrothermally Synthesized Calcium Silicate Hydrate[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2011, 26(4): 770–773
R W Davis, J F Young. Hydration and Strength Development in Tricalcium Silicate Pastes Seeded with Afwillite[J]. Journal of the American Ceramic Society, 1975 (58): 67–70
Taylor H F W. Nanostructure of C-S-H: Current Status[J]. Advanced Cement Based Materials, 1993(1): 38–46
Thomas J J, Jennings H M. A Colloidal Interpretation of Chemical Aging of the C-S-H Gel and Its Effects on the Properties of Cement Paste[J]. Cement and Concrete Research, 2006, 36(1): 30–38
Juenger M G, Jennings H M. Examining the Relationship Between the Microstructure of Calcium Silicate Hydrate and Drying Shrinkage of Cement Pastes[J]. Cement and Concrete Research, 2002, 32(2): 289–296
Yongjia HE, Ruitao MAO, Linnü LÜ, et a1. Hydration Products of Cement-Silica Fume-Quartz Powder Mixture under Different Curing Regimes[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2017, 32(3): 598–602
I G Richardson. The Nature of C-S-H in Hardened Cements[J]. Cement and Concrete Research, 1999(29): 1 131–1 147
Xiandong Cong and R James Kirkpatrick. 29Si MAS NMR Study of the Structure of Calcium Silicate Hydrate[J]. Cement Based Materials, 1996(3): 144–156
Yongjia He, Linnu Lu, Leslie J. Struble, et al. Effect of Calcium-Silicon Ratio on Microstructure and Nanostructure of Calcium Silicate Hydrate Synthesized by Reaction of Fumed Silica and Calcium Oxide at Room Temperature[J]. Materials and Structures, 2014(47): 311–322
B Lothenbach, A Nonat. Calcium Silicate Hydrates: Solid and Liquid Phase Composition[J]. Cement and Concrete Research, 2015(78): 57–70
Yongjia He, Xiaohui Zheng, Linnu Lu, et al. Dehydration Characteristics of C-S-H with Ca/Si Ratio 1.0 Prepared Via Precipitation[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2018, 619–624
J Plank. Study on the Early Crystallization of Calcium Silicate Hydrate (C-S-H) in the Presence of Polycarboxylate Superplasticizers[J]. Journal of Organometallic Chemistry, 2018(869): 227–232
E M Gartner, J F Young. Structure and Performance of Cements[M]. Boca Raton: CRC Press LLC, 2002
V Kanchanason, J Plank. C-S-H - PCE Nanocomposites for Enhancement of Early Strength of Portland Cement[C]. International Conference on Coordination Chemistry, 2015
L Nicoleau. The Acceleration of Cement Hydration by Seeding: Influence of the Cement Mineralogy[J]. ZKG INTERNATIONAL, 2013, 1(1): 40–49
G Land, D Stephan. The Effect of Synthesis Conditions on the Efficiency of C-S-H Seeds to Accelerate Cement Hydration[J]. Cement and Concrete Composites, 2018(87): 73–78
X F Wang, T R Li. Computational Study of the Nanoscale Mechanical Properties of C-S-H Composites under Different Temperatures[J]. Computational Materials Science, 2018(146): 42–53
Author information
Authors and Affiliations
Corresponding author
Additional information
Funded by National Key R&D Program of China (No. 2017YFB0310001) and the National Natural Science Foundation of China (Nos. 51772226, 51972249, 51872216)
Rights and permissions
About this article
Cite this article
Wang, Y., Lü, L., He, Y. et al. Effect of Calcium Silicate Hydrate Seeds on Hydration and Mechanical Properties of Cement. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 36, 103–110 (2021). https://doi.org/10.1007/s11595-021-2382-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-021-2382-1