Abstract
Cu, as an austenitic stable element, is added to steel in order to suppress the adverse effects of high content of C and Mn on welding. Based on C partitioning, Cu and Mn partitioning can further improve the stability of retained austenite in the intercritical annealing process. A sample of low carbon steel containing Cu was treated by the intercritical annealing, then quenching process (I&Q). Subsequently, another sample was treated by the intercritical annealing, subsequent austenitizing, then quenching and partitioning process (I&Q&P). The effects of element partitioning behavior in intercritical region on the microstructure and mechanical properties of the steel were studied. The results showed that after the I&Q process ferrite and martensite could be obtained, with C, Cu and Mn enriched in the martensite. When intercritically heated at 800 °C, Cu and Mn were partitioned from ferrite to austenite, which was enhanced gradually as the heating time was increased. This partitioning effect was the most obvious when the sample was heated at 800 °C for 40 min. At the early stage of α → γ transformation, the formation of γ was controlled by the partitioning of carbon, while at the later stage, it was mainly affected by the partitioning of Cu and Mn. After the I&Q&P process, the partitioning effect of Cu and Mn element could be retained. C was assembled in retained austenite during the quenching and partitioning process. The strength and elongation of I&Q&P steel was increased by 5 305 MPa% compared with that subjected to Q&P process. The volume fraction of retained autensite was increased from 8.5% to 11.2%. Hence, the content of retained austenite could be improved significantly by Mn and Cu partitioning, which increased the elongation of steel.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
Speer J G, Assuncão F C R, Matlock D K, et al. The” Quenching and Partitioning” Process: Background and Recent Progress[J]. Materials Research, 2005, 8(4): 417–423
Edmonds D V, He K, Rizzo F C, et al. Quenching and Partitioning Martensite-A Novel Steel Heat Treatment[J]. Materials Science and Engineering: A, 2006, 438: 25–34
Santofimia M J, Zhao L, Petrov R, et al. Characterization of the Microstructure Obtained by the Quenching and Partitioning Process in a Low-carbon Steel[J]. Materials Characterization, 2008, 59(12): 1758–1764
De Moor E, Matlock D K, Speer J G, et al. Austenite Stabilization through Manganese Enrichment[J]. Scripta Materialia, 2011, 64(2): 185–188
Xiong X C, Chen B, Huang M X, et al. The Effect of Morphology on the Stability of Retained Austenite in a Quenched and Partitioned Steel[J]. Scripta Materialia, 2013, 68(5): 321–324
Li D Z, Wei Y H, Liu C Y, et al. Fundamental Research of TWIP Steel for Automobile[J]. Journal of Iron and Steel Research, 2009, 21(2): 1–5
Zhang M. Study on New High Strength and Super High Strength TRIP Steels[D]. Shanghai: Shanghai University, 2007
Tian Y Q, Zhang H J, Chen L S, et al. Effect of Alloy Elements Partitioning Behavior on Retained Austenite and Mechanical Property in Low Carbon High Strength Steel[J]. Acta Metall. Sin., 2014, 50(5): 531–539
Chen L S, Zhang J Y, Tian Y Q, et al. Effect of Mn Pre-partitioning on C Partitioning and Retained Austenite of Q&P Steel[J]. Acta Metall. Sin., 2015, 51(5): 527–536
Chen L S, Zhang J Y, Tian Y Q, et al. Mn Partitioning Behavior and Its Effect on Structure and Mechanical Property of C-Si-Mn Dual-phase Steel[J]. Journal of Iron and Steel Research, 2014; 26(5): 72
Lee S, Lee S J, De Cooman B C. Austenite Stability of Ultrafine-grained Transformation-induced Plasticity Steel with Mn Partitioning[J]. Scripta Materialia, 2011, 65(3): 225–228
Toji Y, Yamashita T, Nakajima K, et al. Effect of Mn Partitioning during Intercritical Annealing on Following Transformation and Resultant Mechanical Properties of Cold-rolled Dual Phase Steels[J]. ISIJ International, 2011, 51(5): 818–825
Kang J, Wang C, Li Y, et al. Effect of Direct Quenching and Partitioning Treatment on Mechanical Properties of a Hot Rolled Strip Steel[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2016, 31(1): 178–185
Garcia C I, De Ardo A J. Formation of Austenite in 1.5 pct Mn Steels[J]. Metallurgical Transactions A, 1981, 12(3): 521–530
Zhong N, Wang X D, Wang L, et al. Enhancement of the Mechanical Properties of a Nb-microalloyed Advanced High-strength Steel Treated by Quenching-partitioning-tempering Process[J]. Materials Science and Engineering: A, 2009, 506(1): 111–116
Wang X D, Zhong N, Rong Y H, et al. Novel Ultrahigh-strength Nanolath Martensitic Steel by Quenching-partitioning-tempering Process[J]. Journal of Materials Research, 2009, 24(01): 260–267
Nayak S S, Anumolu R, Misra R D K, et al. Microstructure–hardness Relationship in Quenched and Partitioned Medium-carbon and High-carbon Steels Containing Silicon[J]. Materials Science and Engineering: A, 2008, 498(1): 442–456
Yang F C, Liu X Z, Chai F, et al. Strength and Toughness of Austenite Decomposition Products in High Strength Cu-bearing Steel during Continuous Cooling[J]. Journal of University of Science and Technology Beijing, 2014, 36(4): 438–445
Ouyang H S, Pan T, Su H, et al. Effect of Copper on Strength and Cryogenic Toughness of 9Ni Steel[J]. Chinese Journal of Materials Research, 2012, 26(3): 215–320
Liu Q D. Atom Probe Tomography Study on Copper Precipitation Strengthening and Reverse Austenite Toughening in HSLA Ferritic Steel[D]. Shanghai: Shanghai University, 2012
Kasuya T, Izawa T, Kakeshita T, et al. Hydrogen Evolution of Cu Precipitation 780 MPa Grade Steel HAZ with Consideration of Its Cold Cracking Susceptibility[J]. Welding in the World, 2015, 59(3): 353–364
Cano H, Neff D, Morcillo M, et al. Characterization of Corrosion Products Formed on Ni 2.4 wt%-Cu 0.5 wt%-Cr 0.5 wt% Weathering Steel Exposed in Marine Atmospheres[J]. Corrosion Science, 2014, 87: 438–451
Zhang C L, Cai D Y, Kong Y T, et al. Hot Deformation Behaviour and Microstrcture in Intercritical Region of Cu-P-Cr-Ni-Mo Weathering Steel[J]. Transactions of Materials and Heat Treatment, 2014, 35(2): 127–134
Wang S, Yang C G, Xu D K, et al. Effect of Heat Treatment on Antibacterial Performance of 3Cr13MoCu Martensitic Stainless Steel[J]. Acta Metall. Sin., 2014, 50(12): 1453–1460
Xin W B, Song B, Hu C L, et al. Influence of As and Cu-As on Hot Ductility of C-Mn Steels[J]. Transactions of Materials and Heat Treatment, 2014, 35(7): 69–74
Kolli R P, Seidman D N. Co-Precipitated and Collocated Carbides and Cu-Rich Precipitates in a Fe-Cu Steel Characterized by Atom-Probe Tomography[J]. Microscopy and Microanalysis, 2014, 20(06): 1727–1739
Avazkonandeh-Gharavol M H, Haddad-Sabzevar M, Haerian A. Effect of Copper Content on the Microstructure and Mechanical Properties of Multipass MMA, Low Alloy Steel Weld Metal Deposits[J]. Materials & Design, 2009, 30(6): 1902–1912
Author information
Authors and Affiliations
Corresponding author
Additional information
Funded by National Natural Science Foundation of China (Nos. 51574107, 51304186), Natural Science Foundation of Hebei Province(Nos. E2016209048, E2017209048), and Tangshan High Performance Metal and Composite Materials Science and Technical Innovation Team(No. 15130202C)
Rights and permissions
About this article
Cite this article
Chen, L., Hu, B., Xu, J. et al. Cu partitioning behavior and its effect on microstructure and mechanical properties of 0.12C-1.33Mn-0.55Cu Q&P steel. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 32, 1179–1185 (2017). https://doi.org/10.1007/s11595-017-1728-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-017-1728-1