Abstract
This study investigated the nature of hydration products of white portland cement (WPC) containing 20 mM malic acid or 1 M calcium chloride hydrated for 11 years. The study identified the hydration products and characterized the chemical composition, morphology, micro/nano structure of C-S-H and the main binding phase in cementitious materials. Calcium hydroxide (CH), ettringite and C-S-H were identified in WPC with 20 mM malic acid paste hydrated for 11 years. WPC with 1 M calcium chloride paste hydrated for 11 years contained the same phases, but with less CH, and the presence of Friedel’s salt (Ca2Al(OH)6Cl·2H2O). There were still small amount of anhydrous cement particles remaining in both pastes after 11 years hydration according to the SEM and 29Si MAS NMR results. The hydration products of paste containing malic acid had a lower porosity than those prepared with calcium chloride upon visual inspection under SEM. The morphology of the outer product (Op) C-S-H was coarse fibrillar and the inner product (Ip) C-S-H had a very fine microstructure in both pastes under TEM. Both Ip and Op C-S-H formed in paste containing malic acid had lower Ca/Si and higher Al/Si than those in paste containing calcium chloride. C-S-H in paste containing calcium chloride had longer MCL and less percentage of bridging tetrahedra occupied by aluminum in silicon/aluminum chains due to relatively less Q 1 and more Q 2. A new type of silicon tetrahedra, Q 2B, was introduced during deconvolution of 29Si MAS NMR results. Ip and Op C-S-H in both pastes had aluminum substituted tobermorite-type and jennite-type structure, and all the charges caused by aluminum substituting silicon bridging tetrahedra were balanced by Ca2+.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Richardson IG. The Calcium Silicate Hydrates [J]. Cement and ConcreteResearch, 2008, 38: 137–158
Taylor HFW. Cement Chemistry[M]. London: Thomas Telford ServicesLtd., 1997
Traetteberg A, Ramachandran VS, Grattan-Bellew PE. A Study of theMicrostructure and Hydration Characteristics of Tricalcium Silicate inthe presence Of Calcium Chloride [J]. Cement and Concrete Research, 1974, 4: 203–221
Collepardi M, Marchese B. Morphology and Surface Properties ofHydrated Tricalcium Silicate Pastes [J]. Cement and ConcreteResearch, 1972, 2: 57–65
Young JF, Berger RL, FVL Jr. Studies on The Hydration of TricalciumSilicate Pastes: III. Influence of Admixtures on Hydration and StrengthDevelopment [J]. Cement and Concrete Research, 1973,3: 689–700
Groves GW, LeSueur PJ, Sinclair W. Transmission Electron Microscopyand Microanalystical Studies of Ion-Beam-Thinned Sections ofTricalcium Silicate Paste [J]. J. Am. Ceram. Soc., 1986, 89: 353–356
Juenger MCG, Jennings HM. The Use of Nitrogen Adsorption toAssess the Microstructure of Cement Pastes [J]. Cement and ConcreteResearch, 2001, 31: 883–892
Juenger MCG, Monteiro PJM, Gartner EM, et al. Soft X-ray MicroscopeInvestigation into the Effects of Calcium Chloride on TricalciumSilicate Hydration [J]. Cement and Concrete Research, 2005, 35: 19–25
Peterson VK, Juenger MCG. Time-Resolved Quasielastic NeutronScattering Study of the Hydration of Tricalcium Silicate: Effects ofCaCl2 and Sucrose [J]. Physica B-Condensed Matter, 2006, 385: 222–224
Wilding CR, Walter A, Double DD. A Calssification of Inorganic andOrganic Admixtures by Conduction Calorimetry [J]. Cement andConcrete Research, 1984, 14: 185–194
Brough AR, Holloway M, Sykes J, et al. Sodium Silicate-Based Alkali-Activated Slag Mortars Part II. The Retarding Effect of Additions ofSodium Chloride or Malic Acid [J]. Cement and Concrete Research, 2000, 20: 1375–1379
Ersen A, Smith A, Chotard T. Effect of Malic and Citric Acid on theCrystallisation of Gypsum Investigated by Coupled Acoustic EmissionAnd Electrical Conductivity Techniques [J]. Journal of MaterialsScience, 2006, 41: 7210–7217
Wang XP, Ye JD, Wang YJ. Effect of Additives on the Morphology ofthe Hydrated Product and Physical Properties of a Calcium PhosphateCement [J]. Journal of Materials Science & Technology, 2008, 24: 285–288
Rai S, Chaturvedi S, Singh NB. Examination of Portland Cement PasteHydrated in the Presence of Malic Acid [J]. Cement and ConcreteResearch, 2004, 34: 455–462
Brough AR. NMR Studies of Inorganic Solids[D]. Oxford: Universityof Oxford, 1993
Richardson IG, Groves GW. Microstructure and Microanalysis ofHardened Ordinary Portland Cement Pastes [J]. Journal of MaterialsScience, 1993, 28: 265–277
Rai S, Chaturvedi S, Singh H. Examination of Portland Cement PasteHydrated in the Presence of Malic Acid [J]. Cement and ConcreteResearch, 2004, 34: 455–462
Birnin-Yauri UA, Glasser FP. Friedel's salt, Ca2Al(OH)6(Cl,OH) 2H2O:Its Solid Solutions and Their Role in Chloride Binding [J]. Cement andConcrete Research, 1998, 28: 1713–1723
Cheeseman CR, Asavapisit S. Effect of Calcium Chloride on theHydration and Leaching of Lead-Retarded Cement [J]. Cement andConcrete Research, 1999, 29: 885–892
Richardson IG. Tobermorite/jennite-and Tobermorite/calciumHydroxide-Based Models for the Structure of C-S-H: Applicabilityto Hardened Pastes of Tricalcium Silicate, Beta-Dicalcium Silicate,Portland Cement, and Blends of Portland Cement With Blast-FumaceSlag, Metakaolin, or Silica Fume [J]. Cement and Concrete Research, 2004, 34: 1733–1777
Klur I, Jacquinot JF, Brunet F, et al. NMR Cross-Polarization WhenTIS>T1p; Examples From Silica Gel and Calcium Silicate Hydrates [J]. J. Phys. Chem. B, 2000, 104: 10162–10167
Brunet F, Bertani P, Charpentier T, et al. Application of 29SiHomonuclear and 1H-29Si Heteronuclear NMR Correlation toStructural Studies of Calcium Silicate Hydrates [J]. Journal of PhysicalChemistry B, 2004, 108: 15494–15502
Taylor R, Richardson IG, Brydson RMD. Composition andMicrostructure of 20-Year-Old Ordinary Portland Cement-GroundGranulated Blast-Furnace Slag Blends Containing 0 to 100% Slag [J]. Cement and Concrete Research, 2010, 40: 971–983
Akhter H, Cartledge FK, Roy A, et al. A Study of the Effects of NickelChloride and Calcium Chloride on the Hydration of Portland Cement[J]. Cement and Concrete Research, 1993, 23: 833–842
Rodger SA. The Chemistry of Admixture Interaction During CementHydration[M]. Oxford: Department of Materials, University of Oxford, 1986
Andersen MD, Jakobsen HJ, Skibsted J. Characterization of WhitePortland Cement Hydration and the C-S-H Structure in the Presenceof Sodium Aluminate by 27Al and 29Si MAS NMR Spectroscopy [J]. Cement and Concrete Research, 2004, 34: 857–868
Love CA, Richardson IG, Brough AR. Composition and Structure ofC-S-H in White Portland Cement-20% Metakaolin Pastes Hydrated at25 ?[J]. Cement and Concrete Research, 2007, 37: 109–117
Girao AV, Richardson IG, Porteneuve CB, et al. Composition,Morphology and Nanostructure of C-S-H in White Portland Cement-Fly Ash Blends Hydrated at 85 ?[J]. Adv. Appl. Ceram., 2007, 106: 283–293
Taylor R, Richardson IG, Brydson R. Nature of C-S-H in 20 YearOld Neat Ordinary Portland Cement and 10% Portland Cement-90%Ground Granulated Blast Furnace Slag Pastes[J]. Adv. Appl. Ceram., 2007, 106: 294–301
Richardson IG, Groves GW. Models for the Composition and Structureof Calcium Silicate Hydrate (C-S-H) Gel in Hardened TricalciumSilicate Pastes [J]. Cement and Concrete Research, 1999, 22: 1001–1010
Richardson IG, Groves GW. The Incorporation of Minor and Trace-Elements into Calcium Silicate Hydrate (C-S-H) Gel in HardenedCement Pastes [J]. Cement and Concrete Research, 1993, 23: 131–138
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Li, Q. Chemical composition and microstructure of hydration products of hardened white portland cement pastes containing admixtures. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 30, 758–767 (2015). https://doi.org/10.1007/s11595-015-1224-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-015-1224-4