Abstract
The development of high efficiency, stable and economical electrocatalysts is an ideal choice for water electrolysis, fuel cells and metal air cells, and an important innovation in the future energy field. Bifunctional or even multifunctional catalysts have higher performance and lower cost than monofunctional catalysts, which is currently an emerging focus in the development of electrocatalysts. The single-atom catalysts (SACs) of two-dimensional (2D) materials-supported transition metal (TM) atoms have attracted great attention because of their ability to make full use of metal atoms and remarkable catalytic performance. In this work, the oxygen evolution reaction (OER) and oxygen reduction reaction (ORR) catalytic properties of B4N and B2O monolayers supported TM atoms have been systematically evaluated based on first-principles calculations. The adsorption free energy of key intermediates (OOH*, O* and OH*) on the catalyst determines the catalytic activity toward OER and ORR. The calculation results exhibit that Ni@B4N and Pd@B2O systems are potential bifunctional electrocatalysts with the overpotential (η) of OER/ORR being just 0.45/0.43 V and 0.56/0.47 V, respectively, which are comparable to the known noble metal catalysts. Therefore, the study of catalytic activity of SACs on 2D substrate materials provides a broad prospect for the development of stable, low-cost, high-activity noble metal-free electrocatalysts, and provides help for solving energy and environmental problems.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Currently, with the human demand for energy bigger and bigger, the traditional fossil energy cannot meet the demand of human society in the future energy [1, 2]. Therefore, water electrolysis [3, 4], metal air batteries [5, 6], fuel cells [7,8,9] and other sustainable energy production technologies are increasingly being people's attention. The electrocatalysts oxygen evolution reaction (OER) and oxygen reduction reaction (ORR) are the two key reaction of the current advanced energy conversion technology [10, 11]. It is well known that both reactions kinetics rate is slow, which limits the development of related energy conversion and storage technology [12]. So far, usual choice is given priority with noble metal or noble metal oxide catalysts to accelerate the reaction rate of OER and ORR. Among them, the most widely used catalysts are Pt for ORR and Ru or Ir oxides for OER [13,14,15,16]. However, the high prices and scarcity of these noble metals restrict their large-scale and wider industrial applications. Hence, development of low-cost and high catalytic activity noble metal-free catalysts has very important practical significance and urgency [5]. Previous research has shown that carbon-based materials, transition metal hydroxides, transition metal sulfides and composites composed of these materials all have good catalytic activity [17,18,19,20].
The deposition of transition metal (TM) atoms on the surface of materials to form single-atom catalysts (SACs) is a new frontier in catalytic research, which opens a new door for us to reveal the catalytic process on atomic scale [21,22,23,24,25]. In the past few years, a growing number of reports indicated that SACs can be widely used for CO oxidation [26, 27], fuel cells [5] and water splitting. SACs can ensure maximum atomic utilization and form more adjustable active sites. However, as the metal particle size reduces to a single atom, the increase in the surface free energy is likely to lead to metal aggregation [24]. Consequently, to keep SACs excellent catalytic performance, choosing reasonable metal atoms and selecting the appropriate substrate materials are very crucial to stabilize the isolated metal atom. In recent years, catalysts based on two-dimension (2D) materials have attracted widespread attention due to their high activity and a large number of reaction sites [28,29,30,31,32,33,34,35]. 2D materials as SACs substrate have been extensively studied, which has opened up a new frontier field for the search of efficient catalysts [36,37,38,39,40,41]. More importantly, 2D catalysts are potential bifunctional catalysts with both OER and ORR activities. For energy conversion technologies, bifunctional catalysts have higher catalytic performance than two single functional catalysts [42, 43]. In addition, compared with two separate single functional catalysts, bifunctional catalysts can reduce product costs due to less equipment usage and simpler production process.
The catalytic activity of single atom and substrate combinations requires a simple and efficient descriptor for design estimation [42, 44,45,46]. Nevertheless, a complete description of how SACs and their coordination environment affect OER and ORR activity remains unclear. In this regard, there is an urgent need to fully understand the catalytic activity trends of different single atom and substrate combinations, which can help guide the direction of adjusting the performance of SACs. Recently, B4N and B2O monolayers materials have been successfully predicted using first-principles calculation methods [47, 48], and a large number of theoretical studies have been carried out to study their applications as cathode materials for batteries and catalysts for hydrogen evolution reactions (HER) [49,50,51,52,53]. All previous studies indicated that B4N and B2O monolayers were two promising SACs substrates [47, 48]. Based on this, using 2D B2O and B4N as substrate materials, this paper utilizes density functional theory (DFT) to study the OER and ORR catalytic activities of TM atoms supporting on its surface, and to explore the mechanism of OER and ORR. We have studied the 3d and 4d group TM atoms, including Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Zn, Cu and Pd. The scale relationship between the Gibbs free energy (ΔG) of OER and ORR intermediate adsorption is used to describe the trend of catalytic activity. It is found that the d band center (εd) of the doped TM atoms is strongly correlated with the catalytic activity of OER and ORR. Finally, our calculated results suggest that Ni@B4N and Pd@B2O systems could be used as bifunctional electrocatalysts with excellent performance, and the overpotentials (η) of ORR and OER are even as low as 0.43/045 V and 0.47/0.56 V, respectively. The effect of single TM atom doping on ORR and OER catalytic activity of 2D materials is further investigated. Our study not only provides electrochemists with a promising bifunctional SACs for ORR and OER, which may stimulate the electrochemists to synthesize it experimentally, but also provides theoretical basis and more opportunities for the design of efficient bifunctional catalysts.
Computational methods
All the calculations in the present study were carried out on spin-polarized DFT using the Vienna ab initio simulation package (VASP) code [54, 55]. The projector augmented wave (PAW) pseudopotentials were used to treat the core electrons [56]. The Perdew–Burke–Ernzerhof (PBE) [57] functional of the generalized gradient approximation (GGA) [58] was used to describe the electronic exchange and correlation interactions. A cutoff energy was set as 500 eV for the plane-wave basis set, and the convergence criteria for energy and force were less than 10−5 eV and 10−2 eV/Å, respectively. Moreover, van der Waals (vdW) corrections were considered by using the dispersion correction of DFT-D3 method of Grimme [59, 60]. A vacuum distance was not less than 15 Å to avoid the interlayer interaction in the z-direction. The Brillouin zones were sampled with 3 × 3 × 1 Monkhorst–Pack meshes for B2O monolayer and 5 × 5 × 1 for B4N monolayer, respectively. The dynamic stability of B4N and B2O monolayers was verified by using the PHONOPY code [61] implemented in VASP using the density functional perturbation theory (DFPT) [62]. A more precise k-mesh of 7 × 7 × 1 and 3 × 3 × 1 was used for electronic structure calculations and ab initio molecular dynamics (AIMD), respectively. In AIMD simulations, integration of the equations of motion proceeds with time steps of 2.0 fs for different temperature ranges. Typical simulations ran for 3000 steps with the time scale about 6 ps. The isokinetic ensemble (NVT) was employed for the ions, where the ion temperature Ti was fixed using velocity scaling. For more computational details, please see the Supporting Information.
Results and discussion
As shown in Fig. 1a, for the atomic structure of 2D B2O, there are two B and one O atoms in a primitive unit, and this structure has the space group Cmmm (No. 65). The optimized B-B (1.709 Å), B-O (1.338 Å) bond lengths, the B-B-B angle (107.5°) and lattice parameters (a = b = 3.937 Å) obtained from our calculations are in accordance with the previous work [48, 51, 53]. For the 2D B4N atomic structure, the structure reveals Cmmm symmetry with orthogonal lattices. The optimized structural parameters are a = 2.97 Å, b = 10.70 Å, and B-N bond length is 1.334 Å (see Fig. 1b). These calculation results are consistent with the previous report [47, 50]. To evaluate the dynamic stability of B2O and B4N monolayers, we calculated their phonon spectra, as shown in Fig. 1c. The absence of negative frequencies confirmed the dynamic stability of B2O and B4N monolayers. The highest frequency of B2O and B4N monolayers is about 50 THz, indicating that B − O, B − B and B − N in B2O and B4N monolayers have strong interactions. The thermal stability of B2O and B4N monolayers was simulated by AIMD. Figure 1d shows that the mean value of the total potential energy during the AIMD simulation oscillates within a narrow range, and the overall configuration of B2O and B4N monolayers remains good after 6 ps AIMD simulation, which confirms their thermal stability. Then, the structural optimization of B2O and B4N monolayers is performed based on a 4 × 4 × 1 and 2 × 2 × 1 supercell.
To explore the catalytic performance of the B2O and B4N monolayers, we study the active sites on the surface. According to the symmetry of the structure, there are three possible sites of TM atoms adsorbed on the monolayers of B2O and B4N. These possible sites are marked as top (T), bridge (B) and center sites, respectively, as shown in Fig. S2(a-b). The stability of TM atoms doping on B2O and B4N monolayers by analyzing the binding energy (Eb), thus finding the optimal active site. Finally, it can be found from Table S1 that after geometry optimization, only the center site of the hexagon has the lowest Eb, while the other sites have higher Eb. In addition, existing studies have shown that atomic defects are regarded as the active site of catalysis [53, 63], and both the B2O and B4N monolayers have the advantage of natural defect structure, so we finally select the defect center site to stabilize solid TM atoms, as shown in Fig. 2a and c. Irreversible detachment of the central transition metal atom from the catalyst significantly limits catalyst durability. To investigate the stability of TM@B4N and TM@B2O systems, we calculated their Eb of TM atoms supporting on the center site. The calculated Eb are shown in Fig. 2b and d, where all negative values of Eb indicate that the B4N and B2O monolayers stabilize these doped TM atoms against clustering. This may be because the boron atom forms a very strong coordination bond when it provides 2p electron pairs to the vacant d orbital of the TM atoms. In order to better understand the interaction between TM atoms and B4N and B2O monolayers, we also plot the charge density difference distribution. In both cases, it has been observed that the center TM atoms are exposed and depleted to the B2O and B4N monolayers, with the yellow and cyan surfaces showing electron accumulation and loss, respectively. The bonding between TM atoms and O or N atoms is more stable than that between TM atoms and B atom so that TM atoms are bound around O and N atoms, thus residing at the center site and reducing the aggregation between TM atoms. These results indicate that there is a strong interaction between TM atoms and B4N and B2O monolayers, and the structure is stable after doping TM atoms.
Different TM atoms anchoring on B4N and B2O monolayers have different electronic structures, which provides a new method for understanding their catalytic properties. We calculate the values of the densities of states of partial wave (PDOS) for d orbitals of different TM atoms anchored on the B4N and B2O monolayers, as shown in Figs. 3 and 4. All the TM@B4N and TM@B2O systems considered in this work exhibit metallic properties, indicating that all structures have good electrical conductivity. It is well known that the εd is used to analyze the descriptor of the strength of the interaction between adsorbates and substrates [64,65,66,67]. The large number of d electrons in TM atoms and low εd energy levels usually result in weaker interactions with OH *, O* and OOH* adsorbates [68]. This is because the interaction between TM atoms and the adsorbates occurs through their electron level hybridization and charge transfer from TM atoms to the adsorbates. The PDOS in the figure displays that as the number of d electrons in TM atoms increases, we can see the εd shift towards the lower energy relative to the Fermi level. The results indicate that the interaction strength of adsorbates on B4N and B2O monolayers presents the following trend: Sc > Ti > V > Cr > Mn > Fe > Co > Ni > Pd. Nørskov et al. believed that the interaction intensity of adsorption intermediates on the catalyst was too strong, and the active center of the catalyst would be poisoned [69]. However, if the interaction is too weak, it is difficult to activate the reactants or intermediates and initiate the catalytic process. Therefore, it is a challenge to identify promising materials with suitable adsorption energies of the reaction intermediates. In order to verify the above conclusions, the ΔG of OER and ORR reaction intermediates corresponding to the εd of TM@B4N and TM@B2O systems is calculated based on Eqs. (S23)-(S25), as shown in Fig. S3. One can find from Fig. S3 that there are good relationships between the εd and ∆GO*, ∆GOH* as well as ∆GOOH*. We can conclude that for TM atoms in the same row of the periodic table, an increase in the number of d electrons tends to weaken the adsorption free energy of adsorbates. Therefore, these results exhibit the negative correlation between the εd and ∆GO*, ∆GOH* and ∆GOOH*. Considering the adsorption properties of intermediates can determine the reaction activity, such linear relationship can help to design catalysts more efficiently. This phenomenon has also been observed in experiments [70] and other theoretical studies [42, 71]. Therefore, we can adjust the interaction strength to the optimal values of OER and ORR performance by changing the doped TM atoms. As shown above, the ΔG of the adsorbed states (OH*, O* and OOH*) on the catalyst determine the rate-determining steps and catalytic activity of OER and ORR. For the ideal catalyst, the total formation energy of ORR is 4.92 eV, and the ideal adsorption values of ΔGOH*, ΔGO* and ΔGOOH* are 1.23, 2.46 and 3.69 eV, respectively, and the energy distance between the two adjacent intermediate states is 1.23 eV (when U = 0 V). Therefore, OER and ORR reaction can occur at the thermodynamic limit, where the corresponding η value is zero. However, in reality, the energy distance between adjacent intermediate states is difficult to satisfy the condition of equality, resulting in limited reaction. The ηOER is determined by the maximum energy distance between two adjacent intermediate states, while the ηORR is determined by the minimum energy distance between two adjacent intermediate states. We calculate the ηOER and ηORR of all TM@B4N and TM@B2O systems as shown in Fig. 5. Our results demonstrate that the stable position of the intermediate on the catalyst is at the top of the TM atoms, and only Ni@B4N and Pd@B2O system has good catalytic activity of ORR and OER, which are two potential bifunctional catalysts. The ηOER of Ni@B4N system is 0.45 V, comparable to the calculated RuO2 catalyst (0.42 V) [72]. The ηORR of Pd@B2O system (0.56 V) is slightly higher than that of conventional RuO2 catalyst. The best catalyst for ORR is Ni@B4N system with the lowest ηORR value of 0.43 V, followed by Pd@B2O system (0.47 V). It is worth noting that their ηORR values are both lower than the reported value of the best catalyst Pt (0.48 V) [73].
The relationship among the Gibbs free energy ΔGOH*, ΔGO* and ΔGOOH* of the intermediate can be used to analyze the OER and ORR trends of the catalyst. The scaling relationships of ΔGOH* and ΔGOOH*, ΔGOH* and ΔGO* in Ni@B4N and Pd@B2O systems are shown in Fig. 6. Obviously, for the Ni@B4N system, ΔGOOH* can be expressed as a function of ΔGOH* by the equation: ΔGOOH* = 0.67ΔGOH* + 2.75. The relationship between ΔGOOH* and ΔGOH* has a very high coefficient of certainty (R2 = 0.94), indicating a strong linear relationship. Similarly, for Pd@B2O system, there is a strong linear relationship between ΔGOOH* and ΔGOH*, which is expressed by the equation: ΔGOOH* = 0.61ΔGOH* + 1.84, and has a high determination coefficient (R2 = 0.77). The slope and constant separation in the relation between ΔGOOH* and ΔGOH* indicate that the intermediate OOH* and OH* form a single bond between oxygen and TM atoms. Then, through linear fitting, we can obtain the scaling relationship of ΔGOH* and ΔGO* for Ni@B4N system: ΔGO* = 1.19ΔGOH* + 1.29, and the R2 is 0.75. For the Pd@B2O system, the scaling relationship is ΔGO* = 0.94ΔGOH* + 0.97 with the corresponding R2 of 0.74. Note that the linear relationship between the ∆GOH* and ∆GO* is not as good as that of ∆GOH* and ∆GOOH* due to the different single metal–oxygen bond nature of the OH* and O*. Different oxidation states have different contributions to the binding strength of oxygen atom and TM atoms, which more or less leads to the deviation from the linear scaling between them. As stated in Eq. (S17) and (S22), the ηOER and ηORR are two function of four variables (ΔG1, ΔG2, ΔG3 and ΔG4). According to the scaling relationship of ΔG1 + ΔG2 + ΔG3 + ΔG4 = 4.92 eV, the ηOER and ηORR can be reduced to two descriptors. On the grounds of the definitions of Eqs. (S13-S16) and (S18-S21), the two descriptors ΔGOH* and ΔGO*—ΔGOH* are sufficient to describe the catalytic performance of OER and ORR. For the TM@B4N and TM@B2O systems, we drew 2D volcano maps. As seen from Fig. 7, it can be found that under the optimum condition (ΔG1 = ΔG2 = ΔG3 = 1.34 eV), limiting ηOER of TM@B4N and TM@B2O systems are as low as 0.39 and 0.41 V, respectively. The blue region of the 2D volcano map shows the highest active area. Among the systems considered, Ni@B4N and Pd@B2O systems are potential catalysts, with ηOER of 0.45 and 0.56 V, respectively. As shown in Fig. 8, for the Ni@B4N system, the fourth step (desorption of O2) are the rate-determining steps, while the second step (O* formation) is the rate-determining step for the Pd@B2O system. Figure 9 shows the trend of activity of ORR for TM@B4N and TM@B2O systems by using ηORR as a function of the independent descriptors of ΔGOH* and ΔGO*—ΔGOH*. Under the optimal conditions (ΔG1 = ΔG4 = -0.91 eV), the theoretical ηORR is as low as 0.39 V. The first step in the ORR pathway is that O2 molecule is hydrogenated to OOH* through coupled proton electron transfer. Then OOH* is attacked by an additional proton electron pair to form O* atom and H2O molecule. O* is then further hydrogenated to OH* before the second H2O molecule formed. The most suitable catalysts for ORR are Ni@B4N and Pd@B2O systems. The ηORR of Ni@B4N system is found to be below 0.43 V, and the rate-determining step is to release of adsorbed OH*, while the release of adsorbed OH* is the rate-determining step for the Pd@B2O system (ηORR = 0.47 V) (see Fig. 8). Obviously, Ni@B4N and Pd@B2O systems, as potential efficient bifunctional catalysts for OER and ORR, can catalyze both OER and ORR at the same active site. Calculated intermediates of ΔGOH*, ΔGOH* and ΔGOOH* for the other systems are summarized in Fig. S4 and Table S2-S3. For the other systems, the formation of O* and OOH* in the second and third steps is the most difficult because it shows the maximum energy range and therefore becomes the most likely rate-determining step. The corresponding ηOER of these systems is too high to effectively catalyze OER. As OER electrocatalysts in practical application, they not only need more energy input, but also cause the lag of kinetic rate. In addition, due to the large required energy and slow reaction kinetics, it is difficult to remove the reaction intermediate products, thus leading to the active center deactivation and making the catalyst poison. Our results reveal that Ni@B4N and Pd@B2O systems are highly efficient and stable OER/ORR bifunctional catalysts and provide useful guidance for screening metal active centers of SACs on 2D materials.
Conclusions
In summary, we have systematically studied the stability and catalytic behavior of TM atoms doped at the center defect site on B2O and B4N monolayers based on the DFT method, aiming to search for potential bifunctional SACs for OER/ORR with high activity and stability. The results show that the adsorption strength of the intermediates on the active center of TM atoms is closely related to the εd. As the number of d electrons of doped TM atoms on the defect B2O and B4N monolayers increases, the εd moves to the lower energy level, which weakens the interaction between the intermediate and the active center of TM atoms. Therefore, the ideal OER and ORR catalysts can be selected by adjusting the doped TM elements. According to the volcanic maps of OER and ORR, it is found that Ni@B4N system (ηOER = 0.45 V, ηORR = 0.43 V) and Pd@B2O system (ηOER = 0.56 V, ηOER = 0.47 V) as ORR/OER bifunctional SACs have a high application prospect, and their catalytic performance can be comparable to that of traditional noble metal-based catalysts. Considering the tons of structural candidates for such 2D substrates as well as the simple and tunable strain-engineering strategy, we wish the present theoretical basis will spur more interests and efforts in designing efficient bifunctional SACs in overall water splitting from both the theory and experiments.
Availability of data and material
All data generated or analyzed during this study are included in this published article and its supplementary information files.
References
Panwar NL, Kaushik SC, Kothari S (2011) Role of renewable energy sources in environmental protection: a review. Renew Sust Energ Rev 15:1513–1524
Kolar JL (2000) Alternative energy technologies. Environ Qual Manage 10:45–54
Jamesh M-I, Sun X (2018) Recent progress on earth abundant electrocatalysts for oxygen evolution reaction (OER) in alkaline medium to achieve efficient water splitting-a review. J Power Sources 400:31–68
Li H, Wu Y, Li L, Gong Y, Niu L, Liu X, Wang T, Sun C, Li C (2018) Adjustable photocatalytic ability of monolayer g-C3N4 utilizing single-metal atom: density functional theory. Appl Surf Sci 457:735–744
Huang Z-F, Wang J, Peng Y, Jung C-Y, Fisher A, Wang X (2017) Design of efficient bifunctional oxygen reduction/evolution electrocatalyst: recent advances and perspectives. Adv Energy Mater 7:1700544
Wang M, Qian T, Liu S, Zhou J, Yan C (2017) Unprecedented activity of bifunctional electrocatalyst for high power density aqueous zinc-air batteries. ACS Appl Mater Inter 9:21216–21224
Jiao Y, Zheng Y, Jaroniec M (2015) Design of electrocatalysts for oxygen and hydrogen-involving energy conversion reactions. Chem Soc Rev 46:2060–2086
Morales-Guio CG, Stern LA, Hu X (2014) Nanostructured hydrotreating catalysts for electrochemical hydrogen evolution. Chem Soc Rev 43:6555–6569
Liu GS, You SJ, Tan Y, Ren NQ (2017) In situ photochemical activation of sulfate for enhanced degradation of organic pollutants in water. Environ Sci Technol 51:2339–2346
Nguyen TV, White RE (1993) A water and heat management model for proton exchange-membrane fuel cells. J Electrochem Soc 140:2178–2186
Liu H, Logan BE (2004) Electricity generation using an air-cathode single chamber microbial fuel cell in the presence and absence of a proton exchange membrane. Environ Sci Technol 38:4040–4046
Rana M, Mondal S, Sahoo L, Chatterjee K, Karthik PE, Gautam UK (2018) Emerging materials in heterogeneous electrocatalysis involving oxygen for energy harvesting. ACS Appl Mater Inter 10:33737–33767
Suen NT, Hung S-F, Quan Q, Zhang N, Xu Y-J, Chen HM (2017) Electrocatalysis for the oxygen evolution reaction: recent development and future perspectives. Chem Soc Rev 46:337–365
Sealy C (2008) The problem with platinum. Mater Today 11:65–68
Rossmeisl J, Qu ZW, Zhu H, Kroes GJ, Nørskov JK (2007) Electrolysis of water on oxide surfaces. J Electroanal Chem 607:83–89
Reier T, Oezaslan M, Strasser P (2012) Electrocatalytic oxygen evolution reaction (OER) on Ru, Ir, and Pt catalysts: a comparative study of nanoparticles and bulk materials. ACS Catal 2:1765–1772
Osgood H, Devaguptapu SV, Xu H, Cho J, Wu G (2016) Transition metal (Fe Co, Ni, and Mn) oxides for oxygen reduction and evolution bifunctional catalysts in alkaline media. Nano Today 11:601–625
Qu K, Zheng Y, Dai S, Qiao SZ (2016) Graphene oxide-polydopamine derived N, S-codoped carbon nanosheets as superior bifunctional electrocatalysts for oxygen reduction and evolution. Nano Energy 19:373–381
Qian L, Lu Z, Xu T, Wu X, Tian Y, Li Y, Huo Z, Sun X, Duan X (2015) Trinary layered double hydroxides as high-performance bifunctional materials for oxygen electrocatalysis. Adv Energy Mater 5:1500245
Sadighi Z, Liu J, Zhao L, Ciucci F, Kim J-K (2018) Metallic MoS2 nanosheets: multifunctional electrocatalyst for the ORR, OER and Li-O2 batteries. Nanoscale 10:22549–22559
Li Y, Zhou Z, Yu G, Chen W, Chen Z (2010) CO catalytic oxidation on iron-embedded graphene: computational quest for low-cost nanocatalysts. J Phys Chem C 114:6250–6254
Qiao B, Wang A, Yang X, Allard LF, Jiang Z, Cui Y (2011) Single-atom catalysis of CO oxidation using Pt1/FeOx. Nat Chem 3:634–641
Yang X-F, Wang A, Qiao B, Li J, Liu J, Zhang T (2013) Single-atom catalysts: a new frontier in heterogeneous catalysis. Acc Chem Res 46:1740–1748
Fei H, Dong J, Feng Y, Allen CS, Wan C, Volosskiy B (2018) General synthesis and definitive structural identification of MN4C4 single-atom catalysts with tunable electrocatalytic activities. Nat Catal 1:63–72
Ling C, Bai X, Ouyang Y, Du A, Wang J (2018) Single molybdenum atom anchored on N-doped carbon as a promising electrocatalyst for nitrogen reduction into ammonia at ambient conditions. J Phys Chem C 122:16842–16847
Wang SY, Yang ZX, Chu XL (2018) Design of efficient catalysts for Co oxidation on titanium carbide-supported platinum via computational study. J Phys Chem C 122:25974–25982
Nie L, Mei D, Xiong H (2017) Activation of surface lattice oxygen in single-atom Pt/CeO2 for low-temperature Co oxidation. Science 358:1419
Lv X, Wei W, Sun Q, Li F, Huang B, Dai Y (2017) Two-dimensional germanium monochalcogenides for photocatalytic water splitting with high carrier mobility. Appl Catal B: Environ 217:275–284
Wei Y, Ma Y, Wei W, Li M, Huang B, Dai Y (2018) Promising photocatalysts for water splitting in BeN2 and MgN2 monolayers. J Phys Chem C 122:8102–8108
Seh ZW, Fredrickson KD, Anasori B, Kibsgaard J, Strickler AL, Lukatskaya MR, Gogotsi Y, Jaramillo TF, Vojvodic A (2016) Two-dimensional molybdenum carbide (MXene) as an efficient electrocatalyst for hydrogen evolution. ACS Energy Lett 1:589–594
Gao G, O’Mullane AP, Du A (2017) 2D MXenes: A new family of promising catalysts for the hydrogen evolution reaction. ACS Catal 7:494–500
Liu X, Wang P, Zhai H, Zhang Q, Huang B, Wang Z, Liu Y, Dai Y, Qin X (2018) Synthesis of synergetic phosphorus and cyano groups (C≡N) modified g-C3N4 for enhanced photocatalytic H2 production and CO2 reduction under visible light irradiation. Appl Catal B: Environ 232:521–530
Li X, Dai Y, Li M, Wei W, Huang B (2015) Stable Si-based pentagonal monolayers: high carrier mobilities and applications in photocatalytic water splitting. J Mater Chem A 3:24055–24063
Zhao P, Ma Y, Lv X, Li M, Huang B, Dai Y (2018) Two-dimensional III2-VI3 materials: promising photocatalysts for overall water splitting under infrared light spectrum. Nano Energy 51:533–538
Wang S, He P, Jia L, He M, Zhang T, Dong F, Liu M, Liu H (2019) Nanocoral-like composite of nickel selenide nanoparticles anchored on two-dimensional multi-layered graphitic carbon nitride: A highly efficient electrocatalyst for oxygen evolution reaction. Appl Catal B: Environ 243:463–469
Zhou YN, Gao GP, Li Y, Chu W, Wang LW (2019) Transition-metal single atoms in nitrogen-doped graphenes as efficient active centers for water splitting: a theoretical study. Phys Chem Chem Phys 21:3024–3032
Zhou YN, Gao GP, Kang J, Chu W, Wang LW (2019) Transition metal-embedded two-dimensional C3N as a highly active electrocatalyst for oxygen evolution and reduction reactions. J Mater Chem A 7:12050
Gao XP, Zhou YN, Tan YJ, Yang BW, Cheng ZW (2019) Single Mo atoms supported on N-doped carbon with N/C edge-site for enhanced electrochemical hydrogen evolution. Int J Hydrogen Energy 44:14861–14868
Gao XP, Zhou YN, Tan YJ, Yang BW, Cheng ZW, Shen ZM (2019) Mo isolated single atoms on S, N-codoped carbon as efficient catalyst for hydrogen evolution reaction: a theoretical evaluation. Appl Surf Sci 473:770–776
Morales-García Á, Calle-Vallejo F, Illas F (2020) MXenes: New Horizons in Catalysis. ACS Catal 10:13487–13503
Oschinski H, Morales-García Á, Illas F (2021) Interaction of first row transition metals with M2C (M = Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, and W) MXenes: a quest for single-atom catalysts. J Phys Chem C 125:2477–2484
Wang H, Lee HW, Deng Y, Lu Z, Hsu PC, Liu Y, Lin D, Cui Y (2015) Bifunctional non-noble metal oxide nanoparticle electrocatalysts through lithium-induced conversion for overall water splitting. Nat Commun 6:7261
Wu Y, Li G-D, Liu Y, Yang L, Lian X, Asefa T, Zou X (2016) Overall water splitting catalyzed efficiently by an ultrathin nanosheet-built, hollow Ni3S2-based electrocatalyst. Adv Funct Mater 26:4839–4847
Xu H, Cheng D, Cao D, Zeng XC (2018) A universal principle for a rational design of single-atom electrocatalysts. Nat Catal 1:339–348
Gao G, Bottle S, Du A (2018) Understanding the activity and selectivity of single atom catalysts for hydrogen and oxygen evolution via ab initial study. Catal Sci Technol 8:996–1001
Zhou Y, Gao G, Kang J, Chu W, Wang L-W (2019) Computational screening of transition-metal single atom doped C9N4 monolayers as efficient electrocatalysts for water splitting. Nanoscale 11:18169–18175
Wang B, Wu Q, Zhang Y, Ma L, Wang J (2019) Auxetic B4N monolayer: a promising 2D material with in-plane negative poisson’s ratio and large anisotropic mechanics. ACS Appl Mater Inter 11:33231–33237
Zhong CY, Wu WK, Ding GG, Liu Y, Li DF (2019) Two-dimensional honeycomb borophene oxide: strong anisotropy and nodal loop transformation. Nanoscale 11:2468–2475
Zhao XF, Yang XY, Singh D, Panda PK, Luo W, Li YX (2020) Strain-engineered metal-free h-B2O monolayer as a mechanocatalyst for photocatalysis and improved hydrogen evolution reaction. J Phys Chem C 124:7884–7892
Guo J, Tian B, Shu H (2020) Multidimensional B4N materials as novel anode materials for lithium ion batteries. Phys Chem Chem Phys 22:19913–19922
Hu JP, Zhong CY, Wu WK, Liu N (2020) 2D honeycomb borophene oxide: a promising anode material offering super high capacity for Li/Na-ion batteries. J Phys Condens Matter 32:065001
Li HF, Hao YQ, Sun D, Zhou D, Liu GT, Wanga H (2019) Mechanical properties and superconductivity in two-dimensional B2O under extreme strain. Phys Chem Chem Phys 21:25859
Yan L, Liu PF, Li H (2020) Theoretical dissection of superconductivity in two-dimensional honeycomb borophene oxide B2O crystal with a high stability. npj Comput Mater 6:94
Kresse G, Furthmiller J (1996) Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comp Mater Sci 6:15–50
Kresse G, Furthmiller J (1996) Efficient iterative schemes for ab Initiototal-energy calculations using a plane-wave basis set. Phys Rev B 54:11169–11186
Blöchl PE (1994) Projector augmented-wave method. Phys Rev B 50:17953–17979
Perdew JP, Chevary JA, Vosko SH (1992) Atoms, molecules, solids, and surfaces: applications of the generalized gradient approximation for exchange and correlation. Phys Rev B 46:6671–6687
Kresse G, Hafner J (1994) Ab Initio Molecular-dynamics Simulation of the Liquid-metal-amorphous-semiconductor Transition in Germanium. Phys Rev B 49:14251
Grimme S, Ehrlich S, Goerigk L (2011) Effect of the damping function in dispersion corrected density functional theory. J Comput Chem 32:1456–1465
Grimme S, Antony J, Ehrlich S, Krieg HA (2010) consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J Chem Phys 132:154104
Togo A, Tanaka I (2015) First principles phonon calculations in materials science. Scr Mater 108:1–5
Gonze X, Lee C (1997) Dynamical matrices, Born effective charges, dielectric permittivity tensors, and interatomic force constants from density-functional perturbation theory. Phys Rev B 55:10355
Liang XY, Wu CML (2020) Metal-free two-dimensional phosphorus carbide as an efficient electrocatalyst for hydrogen evolution reaction comparable to platinum. Nano Energy 71:104603
Mavrikakis M, Hammer B, Nørskov JK (1998) Effect of strain on the reactivity of metal surfaces. Phys Rev Lett 81:2819–2822
Hammer B, Nørskov JK (2000) Theoretical surface science and catalysis-calculations and concepts. Adv Catal 45:71–129
Kitchin JR, Norskov JK, Barteau MA, Chen JG (2004) Role of strain and ligand effects in the modification of the electronic and chemical properties of bimetallic surfaces. Phys Rev Lett 93:156801–156805
Stamenkovic V, Mun BS, Mayrhofer KJ, Ross PN, Markovic NM, Rossmeisl J, Greeley J, Nørskov JK (2006) Changing the activity of electrocatalysts for oxygen reduction by tuning the surface electronic structure. Angew. Chem. Int Ed 118:2963–2967
Calle-Vallejo F, Krabbe A, Garcia-Lastra JM (2017) How covalence breaks adsorption-energy scaling relations and solvation restores them. Chem Sci 8:124–130
Nørskov JK, Bligaard T, Logadottir A, Kitchin JR, Chen JG, Pandelov S, Stimming U (2005) Trends in the exchange current for hydrogen evolution. Electrochem Soc 152:J23–J26
de Groot MT, Koper MT (2008) Redox transitions of chromium, manganese, iron, cobalt and nickel protoporphyrins in aqueous solution. Phys Chem Chem Phys 10:1023–1031
Ling CY, Shi L, Ouyang YX, Zeng XC, Wang JL (2017) Nanosheet supported single-metal atom bifunctional catalyst for overall water splitting. Nano Lett 17:5133–5139
Man IC, Su HY, Calle-Vallejo F, Hansen HA, Inoglu NG, Kitchin J (2011) Universality in oxygen evolution electrocatalysis on oxide surfaces. ChemCatChem 3:1159–1165
Greeley J, Stephens IE, Bondarenko AS, Johansson TP, Hansen HA, Jaramillo TF (2009) Alloys of platinum and early transition metals as oxygen reduction electrocatalysts. Nat Chem 1:552–556
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors report no conflicts of interest. The authors alone are responsible for the content and writing of the paper.
Additional information
Handling Editor: Pedro Camargo.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Gao, F., Wei, Y., Du, J. et al. B2O and B4N monolayers supported single-metal atom as highly efficient bifunctional electrocatalyst for OER and ORR. J Mater Sci 57, 398–410 (2022). https://doi.org/10.1007/s10853-021-06578-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-021-06578-7