Abstract
This paper describes the sintering of an injection molded 17-4 PH stainless steel with additions of nickel boride (NiB), with the aim of producing high mechanical properties. Boron is evaluated as the best sintering enhancing element in terms of densifying the iron-based materials by formation the liquid phase. Sintered density and mechanical properties were increased with the increased amount of NiB while sintering time and temperature were decreased. Sintering to full density and highest mechanical properties were obtained with the addition of 1 wt% NiB at 1280∘C for 45 min. The formation of borides caused the increase of mechanical properties. This material may therefore find a wider technological application, because of its improved mechanical properties.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
R. M. GERMAN, in “Powder Injection Molding” (Metal Powder Industries Federation, Princeton, NJ, 1990) p. 110.
R. M. GERMAN and A. BOSE, in “Injection Molding of Metals and Ceramics” (Metal Powder Industries Federation, Princeton, NJ, 1997) p. 11.
M. T. MARTNY, D. A. ISSITT, B. HAWORTH and P. J. JAMES, Powder Metall. 31 (1998) 106.
H. SUNG, T.K. HA, S. AHN and Y. W. CHANG, J. Mater. Process. Technol. 130 (2002) 321.
Y. WU, R. M. GERMAN, D. BLAINE, B. MARX and C. SCHLAEFER, J. Mater. Sci. 37 (2002) 3573.
Y. WU, D. BALAINE, B. MARX, C. SCHLAEFER and R. M.GERMAN, Metall. Mater. Trans. 33A (2002) 2185.
R. M. GERMAN and D. KUBISH, Int. J. Powder Metall. 29 (1993) 47.
H. ZHANG and R. M. GERMAN, in “Proceedings of The 1992 Powder Injection Molding Symposium”, San Francisco, June 1992, edited by P.H. Booker, J. Gaspervich and R.M. German (Metal Powder Industries Federation, Princeton, NJ, 1992) p. 219.
Y. S. KWON, Y. WU, P. SURI and R. M GERMAN, Metall. Mater. Trans. 35A (2004) 257.
K. KAMADA, M. NAKAMURA and H. HORIE, in “Proceedings of 2000 Powder Metallurgy World Congress”, Kyoto, Japan, October (2000) p. 1021.
H. I. SANDEROW, J. D. RUHKAMP and H. A.RODRIGUES, in “Modern Developments in Powder Metallurgy”, (Metal Powder Industries Federation, Princeton, NJ, 1992) Vol. 16, p. 167.
T. BABA, H. MIURA, T. HONDA and Y. TOKUYAMA, Adv. Powder Metall. Part. Mater. 6 (1995) 271.
J. J. VALENCIA, T. J. MCCABE and H. DONG, Adv. Powder Metall. Part. Mater. 6 (1995) 205.
R. TANDON and R. M. GERMAN, Int. J. Powder Metall. 34 (1998) 40.
D. S. MADAN and R. M. GERMAN, Adv. Powder Metall. Part. Mater. 1 (1989) 147.
C. TOENNES, P. ERNST, G. MEYER and R. M. GERMAN, Adv. Powder Metall. Part. Mater. 2 (1992) 371.
A. LAL, R. IACOCCA and R. M. GERMAN, Metall. Mater. Trans. 30A (1999) 2201.
J. D. BOLTON and B. S. BECKER, in “Proceedings of 2000 Powder Metallurgy World Congress,” Kyoto, Japan (2000) p. 984.
I. H. BAKAN, D. HEANEY and R. M. GERMAN, Powder Metall. 44 (2001) 235.
A. MOLINARI, G. STARAFFELLINI, T. PIECZONKA and J. KAZIOR, Int. J. Powder Metall. 34 (1998) 21.
M. SARASOLA, T. GOMEZ-ACEBO and F. CASTRO, Acta Mater. 52 (2004) 4615.
A. SELECKA, A. SALAK and H. DANNI˙NGER, J. Mater. Process. Technol. 141 (2003) 379.
J. LIU, A. CARDAMONE, T. POTTER, R. M. GERMAN and F. J. SEMEL, Powder Metall. 43 (2003) 57.
R. M. GERMAN, K. S. HWANG and D. S. MADAN, Powder Metall. Int. 19 (1987) 15.
H. O. GULSOY, S. SALMAN and S. OZBEK, J Mater Sci. 39 (2004) 4835.
MPIF Standard 50, “Materials Standards for Metal Injected Molded Parts” (Princeton, NJ, MPIF, 2000).
MPIF Standard 59, “Materials Standards for Metal Injected Molded Parts” (Princeton, NJ, MPIF, 2001).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Gülsoy, H.Ö., Salman, S. Microstructures and mechanical properties of injection molded 17-4PH stainless steel powder with nickel boride additions. J Mater Sci 40, 3415–3421 (2005). https://doi.org/10.1007/s10853-005-0432-2
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10853-005-0432-2