Abstract
A series of hyperbranched polyurethane-benzyltetrazoles (H-PBTZs) with different linkage structures were synthesized via the polycondensation of hexamethylenediisocyanate as an A2 type monomer with (4-(1H-tetrazol-5-yl)benzyl)-diethanolamine (TBDEA) as a BB′2 type monomer in the absence of catalyst at different temperatures. The FTIR, and 13C and 1H-NMR spectroscopy were used to characterize the molecular structures of TBDEA and H-PBTZs as well as the counterpart linear polyurethane-benzyltetrazole (L-PBTZ). The molecular composition was determined by the reaction selectivity that the isocyanate group reacted with the hydroxyl group in diethanolamine segment or the active hydrogen atom on tetrazole ring. Raising reaction temperature was propitious to the reaction of isocyanate group with the active hydrogen atom on tetrazole ring. The degrees of branching (DB) for H-PBTZs obtained from the 1H-NMR spectra increased with raising reaction temperature. The wider molecular weight distribution of 1.7–2.9 for H-PBTZs was obtained via GPC analysis. TGA results showed that H-PBTZs had high thermal stability compared with L-PBTZ.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
Gao, C. and Yan, D.Y., Prog. Polym. Sci., 2004, 29(3): 183
Hao, J.J., Jikei, M. and Kakimoto, M., Macromolecules, 2002, 35(14): 5372
Kricheldorf, H.R., Vakhtangisghvili, L. and Fritsch, D.J., J. Polym. Sci., Part A: Polym. Chem., 2002, 40(17): 2967
Unal, S., Lin, Q., Mourey, T.H. and Long, T.E., Macromolecules, 2005, 38(8): 3246
Unal, S., Yilgor, I., Yilgor, E., Sheth, J.P., Wilkes, G.L. and Long, T.E., Macromolecules, 2004, 21(37): 7081
Fang, J.H., Kita, H. and Okamoto, K., Macromolecules, 2000, 33(13): 4639
Lin, Q. and Long, T.E., Macromolecules, 2003, 36(26): 9809
Hao, J.J., Jikei, M. and Kakimoto, M., Macromolecules, 2003, 36(10): 3519
Yan, D.Y. and Gao, C., Macromolecules, 2000, 32(21): 7693
Gao, C. and Yan, D.Y., Macromolecules, 2001, 34(2): 156
Gao, C. and Yan, D.Y., Macromolecules, 2003, 36(3): 613
Liang, H.B., Hao, M.Y., Guan, J., Xiong, L. and Zhong, W., Acta Polymerica Sinica(in Chinese), 2009, (12): 1211
Tsarevsky, N.V., Bernaerts, K.V., Dufour, B., Prez, P.E.D. and Matyjaszewski, K., Macromolecules, 2004, 37(25): 9308
Moore, D.S. and Robinson, S.D., Adv. Inorg. Chem., 1988, 32: 171
Lavrenova, L.G. and Larionov, S.V., Russ. J. Coord. Chem., 1998, 24(6): 379
Levchik, S.V., Balabanovich, A.I., Ivashkevich, O.A. and Gaponik, P.N., Polym. Degrad. Stab., 1995, 47(3): 333
Celik, S.Ü. and Bozkurt, A., Eur. Polym. J., 2008, 44(1): 213
Johnson, M.R., J. Org. Chem., 1986, 51(6): 835
Finnegan, W.G., Henry, R.A. and Lofquist, R., J. Am. Chem. Soc., 1958, 80(15): 3981
Finnegan, W.G. and Henry, R.A, 1962, US Pat., 3,055,911
Mihina, J.S. and Herbst, R.M., J. Org. Chem., 1950, 15(5): 1082
Zhang, J. and Hu, C.P., Acta Polymerica Sinica(in Chinese), 2009, (9): 867
Denny, G.H., Cragoe, E.J., Rooney, C.S., Springer, J.P., Hirshfield, J.M. and McCauley, J.A., J. Org. Chem., 1980, 45(9): 1662
Höltel, D., Burgath, A. and Frey, H., Acta Polym., 1997, 48: 30
Adelstein, G.W., Yen, G.H., Dajanib, E.Z. and Bianchi, R.G., J. Med. Chem., 1976, 19(10): 1221
Author information
Authors and Affiliations
Corresponding author
Additional information
This work was financially supported by the National Natural Science Foundation of China (Nos. 50633010 and 50973100).
Rights and permissions
About this article
Cite this article
Qiao, Lg., Shi, Wf. Synthesis and characterization of hyperbranched polyurethane-benzyltetrazole. Chin J Polym Sci 29, 670–683 (2011). https://doi.org/10.1007/s10118-011-1080-4
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10118-011-1080-4