Abstract
Graphite–lead dioxide electrodes doped with rare earth Cerium (Ce-PbO2/C electrodes) were prepared by electrodeposition. The scanning electron microscope results showed that the microstructure and crystal orientation of electrode surface were changed by Cerium doping. CeO2 was detected from modified electrodes by X-ray diffraction analysis. The cyclic voltammetry spectra indicated that the oxidation peak potential of cerium-doped electrode was smaller than pure PbO2 electrode. Effects of the novel electrode on acid red B degradation were evaluated systematically under different parameters, including applied voltage, initial pH, supporting electrolyte concentration, electrode spacing, and influent concentration. The results indicated that chemical oxygen demand, decolorization, and ammonia nitrogen removal rate of Ce-PbO2/C electrodes reached 90.17, 99.98, and 97.23 %, respectively, after 60-min electrolysis at initial 1000 mg L−1 acid red B concentration. The possible mechanism of acid red B degradation over Ce-PbO2/C electrodes was monitored by gas chromatography-mass spectrometer.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Azo dye is a typical pollutant in textile industry, food colorants, printing, and cosmetics manufacturing [1]. Acid red B (ARB) is one widely used dye for fiber, silk, nylon, wool, and leather [2]. The composition of dye wastewater is complicated, including high COD, high pH range, and biological toxicity [3]. Azo dyes have azo groups and aromatic rings with sulfonate groups. The structure of dyes determines their color and poor biodegradability. Dyes would weaken photosynthesis, which is mortal for a large number of aquatic plants. The toxicity of azo dyes and their intermediates would break the balance of ecological system [4]. Phenols are the intermediates affecting the growth and reproduction of aquatic creatures.
Traditional degradation methods are coagulation, adsorption, biodegradation, and chemical degradation. However, both coagulation and adsorption are ineffective and will generate large amounts of sludge and waste which cannot satisfy the discharge standards. Therefore, further treatments for disposal are needed [5-7].
As dyes are stable under sunlight and resistance to microbial attack, they may be toxic to the microorganisms and are not affected by biodegradation [8].
It is necessary to find effective technologies to treat dye wastewater. Electrochemical oxidation has been proved highly efficient, cost saving, and simple in degrading complex compounds [9-11]. The most important merit is that it is friendly to the environment, because it does not need any other reagents. The anode materials determine the removal of dye and COD. PbO2 is used widely in industry wastewater treatment because of its high stability, electrical conductivity, and easy availability [12]. PbO2 can be prepared by electrodeposition in acidic and alkaline solution containing Pb2+.
Recently, a lot of research studies on doping species in the deposition bath were reported, including F [13], Ni, Fe [14], Co [15], Bi [16, 17], and rare earth elements. The results showed that doping species could change the characteristics of PbO2 electrode, including catalytic activity and oxygen evolution potential. Recently, there were many studies on doping of rare earth, such as La2O3 and Er2O3 [18, 19], which can distract internal stress of PbO2 to enhance the stability of electrode and achieve high removal efficiency [20]. Cerium and its oxide have been widely used in oxidation catalyst as they have strong oxidation ability [21].
In this work, graphite–lead dioxide electrodes doped with rare earth Cerium were prepared by electrodeposition. The characteristics of the novel electrode were investigated by SEM, XRD, and CV. ARB was selected as the model target. The effects of different parameters on ARB degradation on the novel electrode were evaluated systematically, such as applied voltage, initial pH, supporting electrolyte concentration, interelectrode spacing, and influent concentration. Gas chromatography-mass spectrometer (GC-MS) spectra of ARB solution were recorded to investigate the removal process of ARB.
Experimental
Materials and instruments
The Ce-PbO2/C electrodes were prepared by electrodeposition. First, α-PbO2 was formed in the alkaline solution consisting of NaOH and PbO. The α-PbO2/C as anode was placed in the acid solution consisting of Pb(NO3)2, NaOH, NaF, Cu (NO3)2, HNO3, and Ce(SO4)2 to form Ce-PbO2. All other chemicals used for the experiments were analytical grade.
The surface morphologies of electrodes were studied by SEM (S-4700) and XRD (D/Max 2500 VB2+/PC). The thicknesses of layers were measured by Thickness Meter (PD-CT2). The removal of color and COD was tested by UV-2000 and COD digestion apparatus (HACH). The intermediate products of ARB degradation were detected by GC7890/MS5975.
The electrolytic cell was a cylindrical beaker whose capacity was 250 mL. There was 130-mL solution that contained ARB and sodium sulfate in the electrolytic cell.
Electrode preparations
Graphite substrate was polished by sandpaper to reduce the edge effects. Then, the polished graphite was soaked in the solution of 2 mol L−1 NaOH for 1 h under 70–80 °C, then in 1 mol L−1 HNO3 for 20 min, and finally washed with distilled water.
The anode preparation procedures included α-PbO2 preliminary deposition and β-PbO2 deposition. Lead oxide includes α-PbO2 and β-PbO2. Two kinds of lead dioxide vary considerably, and the function in electrochemistry is also different. α-PbO2 is the skeleton of the active substance, and its electrical charge capacity is relatively small. β-PbO2 which has higher electrical charge capacity clings to the skeleton composed of α-PbO2. α-PbO2 has high structural strength and low discharge capacity. On the contrary, β-PbO2 has low structural strength and high discharge capacity. The discharge capacity of β-PbO2 is 1.5–3 times as great as α-PbO2, while α-PbO2 has good mechanical strength. The positive plate active material should not soften and exfoliate with the existence of α-PbO2. So, α-PbO2 needs to be electrodeposited firstly [22].
The α-PbO2 was formed in the solution consisting of PbO and NaOH (3.5 mol L−1) for 1 h. The current density was 60 mA cm−2, and the temperature was 40 °C. Then, β-PbO2 was formed in the acid solution including Pb(NO3)2, CTAB, NaF, Cu(NO3)2, and HNO3. The current density was 50 mA cm−2, the temperature was 45 °C, and the time of the deposition is 3 h. It is important to emphasize that Cu(NO3)2 was essential. Electrodeposition of lead nitrate acid solution could be obtained in lead dioxide anode active layer, and its main component was β-PbO2. Mechanism of electrodeposition was that Cu2+ of the electrodeposition bath reduction reaction in the cathode and Pb2+ occurs oxidation reaction in the anode. The chemical equation could be expressed as
The main purpose of adding copper nitrate in electrodeposition solution was that it could inhibit the precipitation of lead on the cathode. Last, Ce-PbO2/C were formed in the acid solution including CTAB (0.05 mol L−1), Ce(SO4)2 (0.05 mol L−1), HNO3 (0.2 mol L−1). The current density was 60 mA cm−2, and the temperature was 40 °C.
Analysis
The removal of color was analyzed by measuring the absorbance at 514 nm, which is the maximum absorbance wavelength of ARB. COD was detected by the potassium dichromate oxidation method. The removal rate of COD, decolorization, and ammonia nitrogen was all calculated by the following formula [1]:
in which A 0 is the initial absorbance, COD, or ammonia nitrogen of dye waster, and A t is the absorbance, COD, or ammonia nitrogen of dye after the reaction time t.
The intermediates were monitored by GC7890/MS5975 with HP-5 capillary column. The sampling mouth temperature is 250 °C. The oven temperature was initially 50 °C, rising at 15 °C min−1 to a final temperature of 250 °C, and kept for 20 min. The flow rate of He as the carrier gas was 1 mL min−1, and 1-μL sample was injected.
Result and discussion
Characterization of electrodes
SEM and XRD
Figure 1 shows the SEM micrographs of the modified PbO2 and pure PbO2 anode. Pure PbO2 has an incompact structure, and the crystal facet contains slight crack and uneven surface. Its crystal size is larger than modified PbO2. Compared with the pure PbO2, the Ce-PbO2 anode has a smaller crystal size and a very compact structure. It can be inferred from the results that Ce doping can increase specific surface area and the active points and improve oxidation ability of the modified electrode.
The XRD spectrums of Ce-PbO2/C and PbO2/C electrodes are shown in Fig. 2. PbO2/C shows the characteristic reflections of β-PbO2 at 25.38°, 31.95°, and 62.48° [23]. The strongest diffraction peak is (301) crystal plane. Cerium doping weakens the intensity of β-PbO2 and broadens the diffraction peak at 62.48°. The results show that Cerium doping diminishes the size of the crystal particles. At the same time, new diffraction peaks appeared at 29° and fit well with the diffraction peak of CeO2 [18]. Above all, Cerium was enriched to the modified electrode surface, which greatly increased the contact area of the active substance and organic pollutants, and improved the catalytic performance of the electrode. The result of XRD is consistent with the SEM analysis.
The thicknesses of layers were also measured. The test result indicates that the thicknesses of layers were 200 μm.
Cyclic voltammetry
A three-electrode system was used to conduct cyclic voltammetry. The reference electrode was saturated calomel electrode (SCE). The counter electrode was platinum wire electrode (Pt). The working electrodes were Ce-PbO2/C and PbO2/C, respectively. The scan rate was 50 mV S−1, and the dye concentration was 100 mg L−1. The electrolytic cell was also a cylindrical beaker. Its capacity was 250 mL. The cyclic voltammograms are shown in Fig. 3, in which the dash line represents Ce-PbO2/C and the solid line represents PbO2/C.
Figure 3a shows that both Ce-PbO2/C electrode and PbO2/C electrode had apparent oxidation peaks. The oxidation current was also high. The system of H2SO4 had no obvious oxidation peak. This indicated that ARB could be directly oxidized at the electrode surface in alkaline and neutral system. However, in acid system, contaminants were hardly oxidized directly. Its degradation was mainly through the reaction with reactive groups of the solution-indirect oxidation [24]. Thus, alkaline and neutral systems are favorable for the degradation of ARB if the effects of electrolyte are omitted.
The cyclic voltammograms of Ce-PbO2/C and PbO2/C electrode in NaOH and Na2SO4 solution are shown in Fig. 3b. The blue lines represent NaOH system, while the red lines represent Na2SO4 system.
In Na2SO4 system, Ce-PbO2/C electrode has two oxidation peaks, E p = 0.698 and 1.143 V, and the corresponding current peaks are i p = 1.217 e−2 A and 1.974 e−2 A. The potential and oxidative peak current of PbO2/C electrode is 0.762 V and 1.581 e−2 A. It is clearly seen that the oxidation potential of cerium-doped electrode diminishes, while the peak current becomes large. It can rapidly degrade organic contaminants because the speed and quantity of active matrix that the electrodes generate have increased [25]. In the catalytic oxidation process, when the current of oxidation peak or reduction peak was larger, the electrode surface is more uniform and dense, which is better for catalytic performance. It can provide more active sites to improve the catalytic ability of electrode in reaction [26, 27]. In NaOH system, the oxidation potential of cerium-modified electrode is small. This indicates that the oxidation peak of cerium-doped electrodes undergone some positive movement and dyes are more susceptible to oxidation.
The cyclic voltammograms for PbO2/C electrode and Ce-PbO2/C electrode in acetic acid-sodium acetate buffer solution are shown in Fig. 3c. Red line and blue line indicated the cyclic voltammograms of PbO2/C electrode and Ce-PbO2/C electrode, respectively. It could be seen from the figure that both of the two curves appeared oxidation peak, but reduction peak was not visible. This phenomenon indicated that the electrolysis reaction of ARB was an irreversible reaction. In addition, we could see that the oxidation peak potential of PbO2/C electrode was 1.746 V and the peak current is 1.997 e−2 A. This result was similar to the conclusions of document 28 [28]. However, the Ce-doped electrode had lower oxidation peak potential and higher current. The peak potential shifted toward lower potential value and the peak current increased sharply. It suggested that ARB had a more sensitive electrochemical response in Ce-PbO2/C electrode. So, the degradation efficiency of ARB was higher. It was also consistent with the results of single factor experimental. The reduction of the peak potential was advantageous to the reaction; meanwhile, it could restrain oxygen evolution reaction to some extent, which should further increase the degradation efficiency of ARB.
In addition, other buffer solutions such as phosphate buffer solution and carbonic acid-sodium carbonate buffer solution were also used for cyclic voltammetry. No oxidation peak was found in these solutions. Therefore, the acetic acid-sodium acetate buffer solution was selected as the supporting electrolyte of cyclic voltammetry.
Electrode stability
Electrode stability test
A basic condition of electrodes to achieve large-scale industrial application was the stability of the electrode. Oxygen generated from oxygen evolution reaction diffused into the surface of the substrate, and it would cause deactivation of the electrode. After prolonged use, the oxygen evolution reaction occurred frequently, and the ability to degrade organic matter declined. Figure 4 shows the treatment effect of electrode after continuous repeated use under the conditions that include that voltage was 10 V, pH was 7, the supporting electrolyte concentration was 4 g L−1, the reaction time was 1 h. It indicated that the treatment efficiency of electrode was almost unchanged after working 1–15 times. The decolorization rate, ammonia removal rate, and COD removal rate decreased 1.64, 4.34, and 1.66 % after working 20 times. The treatment effect reduced slightly faster after working 20 times. The decolorization rate, ammonia removal rate, and COD removal rate decreased 5.33, 6.52, and 12.91 % after working 40 times compared with the first use of the electrode. Under the experimental conditions that voltage was 10 V, current density was selected between 200 and 500 mA cm−2, and the removal rate achieved half of the original efficiency after working at least 70 times as the view of descending rate of 20 times to 40 times, according to the COD removal rate. Electrode surface was intact. It indicated that the electrode had good stability. The changes of before and after using electrode were compared by SEM and XRD. The reason that treatment efficiency reduced was revealed.
Characterization of used electrode
SEM
Figure 5 shows the morphology and crystal of electrode surface by SEM analysis (before reaction (Fig. 5a), after reaction (Fig. 5b)). Magnification was × 5000. Before using, the electrode surface was dense and crystal was symmetrical. However, it becomes rough and there were white spots on the grain, which were impurities. Grain surface was covered with a layer of film. The possible reason was acid corrosion, or oxygen evolution reaction occurs during the process of use. The roughness of electrode surface and the amount of contaminants increased. Thereby, the effective area of the electrode reduced. Therefore, the catalytic performance and treatment efficiency of electrode reduced correspondingly. Judging from the results of the experiment, the significant reduction of decolorization, ammonia removal rate, and COD removal rate after 20 times reaction accorded with this rule. The oxidation reaction, oxygen evolution reaction, and acid corrosion led to the increase of electrode roughness when the time of using electrode increased [29]. Although adsorption of organic matter was more serious, the catalytic efficiency of organic matter reduced.
XRD
Figure 6 shows XRD test of electrode used 40 times continuously. It was found that the peak position of the diffraction peaks does not change comparing with used electrode and unused electrode. Nevertheless, the peak intensity of the latter was weakened. After using, the width of 62° narrowed and it indicated that the particle size become large. Electrode diffraction peak appeared at 29.67° and 31.9° which are Ce (111) and β (101) before using. A slight change that the only diffraction peaks appeared at 31.92° after using. The reason why a small amount of the original CeO2 crystals were decreasing as the electrode use time increased was that crystal particles could be cracked and damaged during the electrode use. Therefore, the characteristic diffraction peaks of Ce at 31.92° decreased. It mainly showed the diffraction peaks of β-PbO2. These results suggested that the relative intensity of each element weakened and the crystal form had not changed.
Effect of operating parameters
Effect of applied voltage
Voltage determines the electron transfer rate, affects the generation speed of active groups, and thus determines the degradation rate of organic materials. Electrolysis was conducted when the initial ARB concentration was 1 g L−1, electrode spacing was 1.5 cm, pH was 6, and the supporting electrolyte concentration was 5 g L−1. pH was adjusted by dilute H2SO4 and NaOH. Figure 7a shows the results of decolorization, COD, and ammonia nitrogen removal under different applied voltage after 1-h electrolysis. The decolorization rate increased from 60.75 to 99.98 %, as the applied voltage increased from 2 to 6 V, and the COD removal rate was increased by 52 % approximately. The removal efficiency of COD and ammonia nitrogen was greater than decolorization rate with the increase of applied voltage. When the applied voltage increases, the mass transfer, hydroxyl radical generation, electron transfer, and the adsorption and desorption of organics on the electrode were accelerated. These effects speeded up the ARB degradation. However, the decolorization rate and ammonia nitrogen removal rate remained nearly unchanged, while the COD removal rate continued to rise. The COD removal rate reached 86.00 % when the applied voltage increased to 10 V. Although the applied voltage influenced the mineralization of organic pollutants, hydrogen and oxygen evolution easily happened at higher voltage. This phenomenon hampers the formation, mass transfer, and diffusion of hydroxyl radicals, making the degradation of ARB no longer conspicuous at higher voltage. On the other hand, excessive voltage may also affect the stability and service life of electrodes [30]. As a result, the suitable applied voltage should be 10 V.
Effect of initial pH
pH values will affect the type of reactive groups in solution and influences conversion between HClO, Cl2, and ClO−. These reactive groups will have a huge impact on degradation of ARB. Figure 7b shows that the influence of pH values ranged from 4 to 12 on decolorization, COD, and ammonia nitrogen removal. The remaining conditions remained unchanged except that the applied voltage was 10 V. The results indicate that the decolorization rate was above 99.00 % and stayed nearly unchanged regardless of the applied pH. The removal rate of ammonia nitrogen had the same phenomenon. However, COD was more easily influenced by pH. The removal of COD was above 83.00 % in the pH range of 4–8. The result was determined by different oxidizing ability of reactive species in different pH ranges. The majority of chlorine is in the form of HClO at pH ≥ 4 and when pH ≥ 6, they were converted to ClO−. At pH = 6, COD removal rate reached a maximum of 88.90 %. However, COD removal rate is only 68.57 % when pH is 12. Based on the experimental date, the degradation of COD would take place more rapidly in an acidic or neutral condition. There are two possible reasons. One is that pH affects the form of chlorine in solution. The chlorine is in the form of active Cl2 when pH is 3. Chlorine evolution is apt to happen due to Cl2 oxidation potential (1.36 V), which hinders the degradation of the dye molecules. The main specie of chlorine is HClO in pH range between 3 and 8. When pH is greater than 8, main form of chlorine is ClO−. As the oxidizing ability of HClO (E θ = 1.5 V) is stronger than ClO− (E θ = 0.89 V), ARB is easy to mineralize in an acidic or neutral condition [31]. Another reason is that Na+ can combine with ClO− to inhibit the oxidation of ARB [32]. So, the appropriate initial pH value ought to be 6.
Effect of supporting electrolyte concentration
Sodium chloride was selected as supporting electrolyte, which can improve the degradation efficiency and increase the formation of chlorine or hypochlorite during the electrolysis [33]. Effects of different supporting electrolyte concentration on the treatment effect are shown in Fig. 7c. The results show that removal rate of decolorization and ammonia nitrogen reached 99.97 and 97.23 %, respectively, when the supporting electrolyte concentration was 4 g L−1. The decolorization rate nearly did not increase at higher supporting electrolyte concentration. However, it can be seen that COD removal rate continues to rise with the increase of supporting electrolyte concentration. The highest COD removal rate reached more than 90 % at the supporting electrolyte concentration of 6 g L−1. The increased supporting electrolyte concentration not only enhanced conductivity but also strengthened the indirect oxidation ability due to higher concentration of Cl2/HClO/ClO− [34]. If the supporting electrolyte concentration continued to increase, too much electrical energy will be converted to heat, and the temperature of the solution will be significantly increased. A higher removal rate is not expected; instead, a decline in the efficiency of the current would happen. Therefore, the suitable supporting electrolyte concentration is 6 g L−1.
Effect of electrode spacing
Figure 7d shows the influence of different electrode spacing on the removal effect. It can be seen in Fig. 8 that smaller electrode spacing gave better removal rate. Decolorization rate decreased from 99.98 to 99.95 %, COD removal rate reduced from 90.17 to 53.75 %, and ammonia nitrogen removal rate was reduced by 1.4 %, as electrode spacing increases from 1.5 to 4 cm. The decolorization rate and COD removal rate decreased significantly when the electrode spacing varied from 1.5 to 3 cm. When the electrode spacing is greater than 3 cm, removal rate leveled off. Smaller electrode spacing decreased the electric resistance and enhanced the current, production of reactive group, and oxidation capacity. When the electrode spacing is large, the decreased electron transfer rate would lead to the untimely degradation of intermediate products. They gradually deposited on the surface of electrode, causing contamination and decreased activity to the electrode. This phenomenon is harmful to the migration of contaminants on the electrode surface and the degradation effect [35]. However, larger electrode spacing increased the mass transfer resistance and thus inhibits the degradation process. As shown in Fig. 8, when electrode spacing is less than 1.5 cm, the processing efficiency may continue to rise. However, it is prone to short circuit when the electrode spacing is too small, besides, excessive current density will shorten the life of the electrode.
Effect of influent concentration
Dye concentration and COD in the industrial wastewater are not constant. Therefore, the research on influent concentration has a certain value on treatment effect.
Figure 8a shows the decolorization rate of different ARB concentration. The low concentration had high decolorization rate with reaction time ranging from 2 to 15 min. Outside this range, the decolorization rate was slow. After 5 min, the decolorization rate of 200 mg L−1 influent concentration reached 99.85 %. When the influent concentration was 1 mg L−1, the decolorization rate was 99.01 %. Decolorization rate showed a downward trend with the increase of concentration. The decolorization rate increased rapidly in low concentration and remained almost unchanged in high concentration. The decolorization rate of dye wastewater was almost 100 % after 30 min, regardless of the influent concentration.
Figure 8b shows that the COD removal rate changed with influent concentration. When the reaction time was 15 min, we observed that COD removal rate had a downward trend with increasing concentration. Assuming that organic contaminants were oxidized by hypochloric acid at the electrode surface, the above results can be explained by diffusion control theory. At low concentration, the electrochemical oxidation rate of dye is faster than its diffusion rate, and the intermediates produced by dye electrolysis are completely oxidized on the electrode surface. When the influent concentration increases, ARB and intermediate product are transferred to the electrode surface, but the restricted diffusion of hypochlorite could not effectively oxidize contaminants, making COD decrease [36]. Both COD removal rate and amount showed an increasing trend after 50 min, while COD removal amount increases at higher influent concentration. Therefore, under the same conditions, higher current efficiency can be obtained in the treatment of high concentration wastewater to save more energy.
Figure 8c indicates the relationship between ammonia nitrogen removal rate and influent concentration. Ammonia nitrogen removal rate reached a stable value after 50 min as influent concentration changed from low to high. When the influent concentration was greater than 200 mg L−1, ammonia nitrogen removal rate was above 94 %. Moreover, it had reached more than 96 % at the concentration of 800–1000 mg L−1. At the same time, ARB removal amount increases with the increase of initial ARB concentration. From the processing ability of pollutants and energy utilization rate, this method can be applied to the treatment of high concentration dye wastewater.
Overall, when dealing with low concentration dye wastewater, higher energy and time efficiency can be obtained. The reaction time may be extended or large applied voltage is needed to achieve the desired results in high concentration dye wastewater.
GC-MS analysis
GC-MS technique was applied to detect intermediates after electrolysis for 30 min. The technology is useful to analyze the degradation mechanism of dyes. The result in Table 1 showed that the structure of ARB was broken to form different intermediates, including phthalandione diethyl phthalate, and methyl hexadecanoate.
The break of azo bond would be the first step of dye degradation, which led to the rapid removal of color. The possible intermediates were A and B (hydrazo derivative). The sulfonic group in the hydrazo derivative was highly stable and soluble in solution [37]. A is easily degradable under aerobic condition. Therefore, it was not detected in the GC/MS analysis. As shown in Fig. 9, B was oxidized to some naphthalene-type intermediates or compounds containing benzene ring, such as phthalic anhydride, diethyl phthalate, and phthalic acid [38-40]. These intermediates were further oxidized to long-chain organic acids, e.g., palmitic acid and lauric acid. These compounds were further degraded to form oxalic acid and acetone. Finally, these small molecules were decomposed to CO2 and H2O.
The process of electrochemical oxidation of ARB was gradual. At first, ARB was degraded to aromatic intermediates, then oxidized to chain structure products and decomposed to CO2 and H2O at last.
Conclusions
A novel Ce-PbO2/C electrode was prepared by electrodeposition. The SEM and XRD tests show that Ce doping in lead dioxide films can decrease the crystal size of anodes, increase their specific surface area, and improve the oxidation ability of the electrode. The cyclic voltammetry tests show that Ce-PbO2/C electrodes had a wider oxidation peak and stronger capacity to generate reactive groups, and the oxidation peak potential of Ce-PbO2/C electrode was smaller than pure PbO2 electrode. Electrochemical removal of ARB in aqueous solution on Ce-PbO2/C electrode was investigated to achieve desirable removal efficiency. The results show that the COD, decolorization, and ammonia nitrogen removal efficiency in 6 g L−1 NaCl solution containing 1000 mg L−1 ARB could achieve 90.17, 99.98, and 97.23 %, respectively, with an applied voltage of 10 V, pH value of 6, and electrode spacing of 1.5 cm after 50 min. Through the GC-MS analysis, ARB was firstly degraded to aromatic intermediates, then oxidized to chain structure products, and decomposed to CO2 and H2O.
References
Zhou MH, He JJ (2008) Degradation of cationic red X-GRL by electrochemical oxidation on modified PbO2 electrode. J Hazard Mater 153:357–363
Wang J, Jiang Z, Zhang ZH, Xie YP, Wang XF, Xing ZQ, Xu R, Zhang XD (2008) Sonocatalytic degradation of acid red B and rhodamine B catalyzed by nano-sized ZnO powder under ultrasonic irradiation. Ultrason Sonochem 15:768–774
Aquino JM, Pereira GF, Rocha-Filho RC, Bocchi N, Biaggio SR (2011) Electrochemical degradation of a real textile effluent using boron-doped diamond or β-PbO2 as anode. J Hazard Mater 192:1275–1282
Körbahti BK, Artut K, Geçgel C, Özer A (2011) Electrochemical decolorization of textile dyes and removal of metal ions from textile dye and metal ion binary mixtures. Chem Eng J 173:677–688
Banat F, AI-Bastaki N (2004) Treating dye wastewater by an integrated process of adsorption using activated carbon and ultrafiltration. Desalination 170:69–75
Gupta VK, Mittal A, Gajbe V (2005) Adsorption and desorption studies of a water soluble dye, Quinoline Yellow, using waste materials. J Colloid Interface Sci 284:89–98
Anouzla A, Abrouki Y, Souabi S, Safi M, Rhbal H (2009) Colour and COD removal of disperse dye solution by a novel coagulant: application of statistical design for the optimization and regression analysis. J Hazard Mater 166:1302–1306
Alaton IA, Insel G, Eremektar G, Babuna FG, Orhon D (2006) Effect of textile auxiliaries on the biodegradation of dyehouse effluent in activated sludge. Chemosphere 62:1549–1557
Zhu XP, Ni JR, Wei JJ, Xing X, Li HN (2011) Destination of organic pollutants during electrochemical oxidation of biologically-pretreated dye wastewater using boron-doped diamond anode. J Hazard Mater 189:127–133
Kariyajjanavar P, Jogttappa N, Nayaka YA (2011) Studies on degradation of reactive textile dyes solution by electrochemical method. J Hazard Mater 190:952–961
Sanroma’n MA, Pazos M, Cameselle C (2004) Optimisation of electrochemical decolourisation process of an azo dye, Methyl Orange. J Chem Technol Biotechnol 79:1349–1353
Duan XY, Ma F, Yuan ZX, Chang LM, Jin XT (2013) Electrochemical degradation of phenol in aqueous solution using PbO2 anode. J Taiwan Inst Chem Eng 44:95–102
Velichenko AB, Devilliers D (2007) Electrodeposition of fluorine-doped lead dioxide. J Fluor Chem 128:269–276
Andrade LS, Ruotolo LAM, Rocha-Filho RC, Bocchi N, Biaggio SR, Iniesta J, García-Garcia V, Montiel V (2007) On the performance of Fe and Fe, F doped Ti–Pt/PbO2 electrodes in the electrooxidation of the Blue Reactive 19 dye in simulated textile wastewater. Chemosphere 66:2035–2043
Velichenko AB, Amadelli R, Baranova EA, Girenko DV, Danilov FI (2002) Electrodeposition of Co-doped lead dioxide and its physicochemical properties. J Electroanal Chem 527:56–64
Borrás C, Laredo T, Mostany J, Scharifker BR (2004) Study of the oxidation of solutions of p-chlorophenol and p-nitrophenol on Bi-doped PbO2 electrodes by UV-Vis and FTIR in situ spectroscopy. Electrochim Acta 49:641–648
Liu Y, Liu HL (2008) Comparative studies on the electrocatalytic properties of modified PbO2 anodes. Electrochim Acta 53:5077–5083
Dai QZ, Shen H, Xia YJ, Chen JM (2012) Typical rare earth doped lead dioxide electrode: preparation and application. Int J Electrochem Sci 7:10054–10062
Wang Y, Shen ZY, Li Y, Niu JF (2010) Electrochemical properties of the erbium–chitosan–fluorine–modified PbO2 electrode for the degradation of 2, 4-dichlorophenol in aqueous solution. Chemosphere 79:987–996
Kong JT, Shi SY, Kong LC, Zhu XP, Ni JR (2007) Preparation and characterization of PbO2 electrodes doped with different rare earth oxides. Electrochim Acta 53:2048–2054
Ai SY, Gao MN, Zhang W, Wang QJ, Xie YF, Jin LT (2004) Preparation of Ce-PbO2 modified electrode and its application in detection of anilines. Talanta 62:445–450
Petersson I, Ahlberg E, Berghult B (1998) Parameters influencing the ratio between electrochemically formed α-and β-PbO2. J Power Sources 76:98–105
Liu HL, Liu Y, Zhang C, Shen RS (2008) Electrocatalytic oxidation of nitrophenols in aqueous solution using modified PbO2 electrodes. J Appl Electrochem 38:101–108
Koehne JE, Marsh M, Boakye A, Douglas B, Kim IY, Chang S, Jang D, Bennet KE, Kimble C, Andrews R, Meyyappan M, Lee KH (2011) Carbon nanofiber electrode array for electrochemical detection of dopamine using fast scan cyclic voltammetry. Analyst 136:1802–1805
Masek A, Zaborski M, Chrzescijanska E (2011) Electrooxidation of flavonoids at platinum electrode studied by cyclic voltammetry. Food Chem 127:699–704
Santos DMF, Sequeira CAC (2010) Cyclic voltammetry investigation of borohydride oxidation at a gold electrode. Electrochim Acta 55:6775–6781
Kariyajjanavar P, Narayana J, Nayaka YA, Umanaik M (2010) Electrochemical degradation and cyclic voltammetric studies of textile reactive azo dye cibacron navy WB. Port Electrochim Acta 28:265–277
Yu NF, Gao LJ, Zhao SH, Wang ZD (2009) Electrodeposited PbO2 thin film as positive electrode in PbO2/AC hybrid capacitor. Electrochim Acta 54:3835–3841
Tong SP, Ma CA, Feng H (2008) A novel PbO2 electrode preparation and its application in organic degradation. Electrochim Acta 53:3002–3006
Alaton IA, Balcioglu IA, Bahnemann DW (2002) Advanced oxidation of a reactive dye bath effluent: comparison of O3, H2O2/UV-C and TiO2 /UV-A processes. Water Res 36:1143–1154
Mascia M, Vacca A, Polcaro AM, Palmas S, Ruiz JR, Pozzo AD (2010) Electrochemical treatment of phenolic waters in presence of chloride with boron-doped diamond (BDD) anodes: experimental study and mathematical model. J Hazard Mater 174:314–322
Mukimin A, Wijaya K, Kuncaka A (2012) Oxidation of removal brilliant blue R (RB.19) with in situ electro-generated active chlorine using Ti/PbO2 electrode. Sep Purif Technol 95:1–9
Rajkumar D, Song BJ, Kim JG (2007) Electrochemical degradation of Reactive Blue 19 in chloride medium for the treatment of textile dyeing wastewater with identification of intermediate compounds. Dyes Pigments 72:1–7
Shen ZM, Wu D, Yang J, Yuan T, Wang WH, Jia JP (2006) Methods to improve electrochemical treatment effect of dye wastewater. J Hazard Mater 131:90–97
Wang YQ, Gu B, Xu WL (2009) Electro-catalytic degradation of phenol on several metal-oxide anodes. J Hazard Mater 162:1159–1164
Song S, Fan JQ, He ZQ, Zhan LY, Liu ZW, Chen JM, Xu XH (2010) Electrochemical degradation of azo dye C.I. Reactive Red 195 by anodic oxidation on Ti/SnO2–Sb/PbO2 electrodes. Electrochim Acta 55:3606–3613
Zhao HZ, Sun Y, Xu LN, Ni JR (2010) Removal of Acid Orange 7 in simulated wastewater using a three-dimensional electrode reactor: removal mechanisms and dye degradation pathway. Chemosphere 78:46–51
Zhao WR, Shi HX, Wang DH (2003) Kinetics of the react ion between ozone and cat ionic red X-GRL. Chin J Chem Eng 11:388–394
Martins MAM, Lima N, Silvestre AJD, Queiroz MJ (2003) Comparative studies of fungal degradation of single or mixed bioaccessible reactive azo dyes. Chemosphere 52:967–973
Siddique M, Farooq R, Khan ZM, Khan Z, Shaukat SF (2011) Enhanced decomposition of reactive blue 19 dye in ultrasound assisted electrochemical reactor. Ultrason Sonochem 18:190–196
Acknowledgments
We thank the National Key Technology R&D Program of China (Project No. 2011BAE07B09-2) for financial support. Additionally, the analytical work was supported by the Water Pollution Control Laboratory of Beijing University of Chemical Technology.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hu, X., Yu, Y. & Yang, L. Electrocatalytic activity of Ce-PbO2/C anode for acid red B reduction in aqueous solution. J Solid State Electrochem 19, 1599–1609 (2015). https://doi.org/10.1007/s10008-015-2781-3
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10008-015-2781-3