Abstract
for the Prototype Fast Breeder Reactor (PFBR), a modified version of 316L stainless steel, designated as 316L(N), has been chosen as the major structural material. In order to reduce the risk of sensitisation, the carbon content has been reduced to less than 0.03 wt-%, and to compensate for the loss in strength due to the reduced carbon content the nitrogen content has been specified to be about 0.08 wt-%. For fuel clad and wrapper applications, a radiation-resistant variation of 316 stainless steel containing titanium about 6 times the carbon content, named Alloy D9, has been chosen. Weld metal and heat-affected zone (HAZ) cracking of austenitic stainless steels Alloy D9 and 316L(N) were investigated. Specifically, the role of titanium in Alloy D9 and nitrogen in 316L(N), along with the impurity elements, were studied. In Alloy D9, cracking increased with Ti/C ratio, but a significant contribution to cracking came from the nitrogen of about 200 ppm picked up during welding even when using high purity argon shielding gas. Titanium to carbon (Ti/C) ratio of about 4 was found to show least susceptibility to solidification as well as HAZ cracking. In modified 316 weld metals with 3–7 FN, nitrogen in the range 0.06–0.12 % had no detrimental effect on weldability. Weldability of Inconel 718 base material was also investigated. From hot cracking considerations, ENiCrFe-3 consumable was found more suitable to weld Inconel 718 than consumable of matching composition. Weldability was tested in various geometrical configurations such as T-, butt- and rod-to-strip in similar as well as dissimilar combination with 9Cr-1Mo steel using ENiCrFe-3 consumable. The studies showed the need for careful joint preparation and use of techniques to enhance weld penetration for minimising defects. This paper discusses the weldability problems associated with these austenitic stainless steels chosen for use in the construction of PFBR. Various criteria in use for weldability evaluation as per codes in relation to the present data on stainless steels and nickel-base alloys are also discussed. The importance of hot cracking evaluations in determining the fabrication weldability of these austenitic stainless steels is also discussed in detail.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Dixon B.F., Welding Journal, 1989, 68, 171s.
ASME Boiler and Presser Vessel Code, Code case N-47, 1989.
Marshall P.: Austenitic stainless steels: Microstructure and mechanical properties, Elsevier Applied Science Publishers, London, 1984, 283.
Lundin C.D., Lee C.H., Qiao C.Y.P.: Group sponsored study — Weldability and hot ductility behaviour of nuclear grade austenitic stainless steels, Final Report, University of Tennessee, Knoxville, USA, 1988.
Brooks J.A., Thompson A.W., International Materials Reviews, 1991, 36, 16.
Robinson J.L., Scott M.H., Philosophical Transactions of the Royal Society of London, 1980, 295A, 105.
Masumoto I., Takami K., Kutsuna M., Journal of the Japanese Welding Society, 1972, 41, 1306.
Rodriguez P., Mannan S.L., Indian Journal of Technology, 1990, 28, 281.
Tamura H., Watanabe T., Transactions of the Japanese Welding Society, 1973, 4, 30.
Brooks J.A., Welding Journal, 1974, 53, 517s.
Zhitnikov N.P., Welding Production, 1981, 3, 14.
Ogawa T., Tsunetomi E., Welding Journal, 1982, 61, 82s.
Matsuda F., Nakagawa H., Katayama S., Arata Y., Transactions of the Japanese Welding Research Institute, 1983, 2, 89.
Lundin C.D., Lingenfelter A., Grotke G., Lessman G., Mathews S., WRC Bulletin, 1982, 280.
Shankar V., Muralidharan B.G., Srinivasan G., Gill T.P.S., Proceedings of International Welding Conference, Indian Institute of Welding, Mumbai, 1996, Paper A-056.
Muralidharan B.G., Shankar V., Gill T.P.S., Proceedings of National Welding Seminar, Indian Institute of Welding, Bangalore, 1997, 329.
Srinivasan G., Shankar V., Gill T.P.S., Sethi V.K., Proceedings of International Welding Conference, Indian Institute of Welding, New Delhi, 1999, 617.
Lundin C.D., Menon R., Lee C.H., Osorio V.: Welding research: The state of the art, Proceedings of JDC University Research Symposium, ASM, 1986, 33.
Lin W., Nelson T., Lippold J.C., Proceedings of 8th Annual North American Welding Research Conference, AWS, EWI and TWI, 1992, 1.
Shankar V.: Role of compositional factors in hot crakking of austenitic stainless steel weldments, Ph.D. Thesis, Indian Institute of Technology, Madras, 2000.
Shankar V., Gill T.P.S., Mannan S.L., Sundaresan S., Science and Technology of Welding and Joining, 2000, 5, 2, 91.
Shankar V., Gill T.P.S., Terrance A.L.E., Mannan S.L., Sundaresan S., Metallurgical and Materials Transactions A, 2000, 31A, 3109.
Shankar V., Gill T.P.S., Mannan S.L., Sundaresan S., Materials Science and Engineering, 2003, 343, 170.
Shankar V., Gill T.P.S., Thamban M., Patel P., Proceedings of Symposium on Joining of Metals, Welding Research Institute, Tiruchirapalli, India, 2000, Paper WM-25.
Kujanpaa V., Suutala N., Takalo T., Moisio T., Welding Research International, 1979, 9, 2, 55.
Kujanpaa V.P., David S.A., White C.L., Welding Journal, 1986, 65, 203s.
Lin W., Lippold J.C., Baeslack W.A., Welding Journal, 1993, 82, 135s.
Li L., Messler R.W., Welding Journal, 1999, 88, 387s.
Miura M., Journal of Sumitomo Metal, 1981, 34, 1, 201.
Matsuda F., Advances in Welding Metallurgy, AWS, 1990, 19.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Srinivasan, G., Bhaduri, A.K., Shankar, V. et al. Evaluation of Hot Cracking Susceptibility of Some Austenitic Stainless Steels and a Nickel-Base Alloy. Weld World 52, 4–17 (2008). https://doi.org/10.1007/BF03266647
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF03266647