Abstract
Barium hexaferrite (BaFe12O19) was synthesized from a Ba(NO3)2, Fe(NO3)3 and KOH mixed solution by hydrothermal treatment of the solution using a supercritical water flow apparatus. The first step is the hydrolysis of the nitrates of barium and iron in potassium hydroxide; the pressure and temperature were adjusted in the respective range of 25–40 MPa and 100-250 ‡C in tee reactor (MP2). The second one is the dehydration of the formed hydrolytic products, under the supercritical state of the solvent in the range of 25–40 MPa, 300-450 ‡C and 40–100 s in tubular flow reactor (MP3). All samples of barium hexaferrite were prepared without calcination of the dehydrated products. Using this method, smaller, uniform-size and single-phase BaFe12O19 nanocrystals could be easily obtained.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Adschiri, T., Kanazawa, K. and Arai, K., “Rapid and Continuous Hydrothermal Crystallization of Metal Oxide Particles in Supercritical Water,”J. Amer. Cercan. Soc,75, 1019 (1992).
Adschiri, T., Kanazawa, K. and Arai, K., “Rapid and Continuous Hydrothermal Synthesis of Boehmite Particles in Subcritical and Supercritical Water,”J. Amer. Ceram. Soc,75, 2615 (1992).
Arai, K., “Science and Technology of Supercritical Fluids,” Tohoku University (1996).
Fujiwara, T., “Barium Ferrite Media for Perpendicular Recording,”IEEE. Trans. on Magn.,5, 1480 (1985).
Hakuta, Y, Adschiri, T., Suzuki, T., Chida, T., Seino, K. and Arai, K., “Flow Method for Rapidly Producing Barium Hexaferrite Particles in Supercritical Water,”J. Amer. Ceram. Soc,81, 2461 (1998).
Hakuta, Y., Onai, S., Adschiri, T. and Arai, K., “Production of Ultrafine Ceria Particles by Hydrothermal Synthesis under Supercritical Conditions,”J. Matter. Sci. Lett.,17, 1211 (1998).
Kumazawa, H., Cho, H. M. and Sack, E., “Hydrothermal Synthesis of Barium Ferrite Fine Particles from Goethite,”J. Mater. Sci.,28, 5247 (1993).
Kumazawa, H., Maeda, Y. and Sada, E., “Further Consideration of Hydrothermal Synthesis of Barium Ferrite Fine Particles,”J. Mater. Sci. Lett.,14, 68 (1995).
Nam, S. C. and Kim, G. J., “Preparation of Ba-Ferrite Particles Using the SuperCritical Water Crystallization Method,”J. Ind. Eng. Chem.,7, 38 (2001).
Rho, S. W., “Influence of Stoichiometry and Alkalinity on Barium Hexaferrite Formation via the Supercritical Water Crystallization Method,”Korean J. Chem. Eng.,19, 120 (2002).
Sada, E., Kumazawa, H. and Cho, H M., “Synthesis of Barium Ferrite Ultrafine Particles by a Hydrothermal Method,”Ind. Eng. Chem. Res.,30, 1319 (1991).
Wang, M. L., Shih, Z. W. and Lin, C. H., “Reaction of Μ-Fe2O3 with Ba(OH)2 under Hydrothermal Conditions,”J. Crystal Growth,139, 47 (1994).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Nam, SC., Kim, GJ. Characterization of barium hexaferrite produced by varying the reaction parameters at the mixing-points in a supercritical water crystallization process. Korean J. Chem. Eng. 21, 582–588 (2004). https://doi.org/10.1007/BF02705491
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02705491