Abstract
When an electronic package encounters thermal fluctuations, cyclical shear strain is imposed on the solder joint interconnections. The thermal cycling leads to a condition of thermal fatigue and eventual solder joint failure. This study was performed in order to understand the microstructural mechanisms that lead to solder joint failures in thermal fatigue. Thermal cycling tests were performed on 60Sn-40Pb joints using a -55° C to 125° C cycle and 19% imposed shear strain. A heterogeneously coarsened region of both Pb and Sn-rich phases develops within the 60Sn-40Pb solder joints. Cracks initiate in the heterogeneously coarsened Sn-rich phase at the Sn-Sn grain boundaries. Heterogeneous coarsening and failure occurs in both high (35 to 125° C) and low (-55 to 35° C) thermal cycles. The elevated temperature portion of the thermal cycle was found to be the most significant factor in the heterogeneous coarsening and failure of the solder joints.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
E. Levine and J. Ordenez, IEEE Trans Components, Hybrids, and Manufacturing Tech.CHMT-4, 515 (1981).
S. K. Rang, N. D. Zommer, D. L. Feucht, and R. W. Heckel, IEEE Trans Parts, Hybrids, and PackagingPHP-13, 318 (1977).
J. T. Lynch, M. R. Ford, and A. Boetti; IEEE Trans Components, Hybrids, and Manufacturing Tech.CHMT-6, 237 (1983).
J. W. Munford, IEEE Trans Parts, Hybrids, and PackagingPHP-11, 296 (1975).
R. N. Wild; “Fatigue properties of solder joints”, Welding Research Supp.51, 521s (1972).
E. A. Wright and W. M. Wolverton; “The effect of the solder reflow method and joint design on the thermal fatigue life of leadless chip carrier solder joints”, Proc. 34th Electron. Components Conf.,34, 149 (1984).
R. Yenawine, M. Wolverton, A. Burkett, B. Waller, B. Russel and D. Spritz; “Today and Tomorrow in Soldering”, Proc 11th Naval Weapons Electronics Manufacturing Seminar, China Lake, CA (1987) p. 339.
H. B. Ellis; “Aspects of surface mounted chip carrier solder joint reliability”, Proc. 11th Naval Weapons Electronics Manufacturing Seminar, China Lake, CA (1987) p. 377.
D. R. Olsen and A. M. Berg, IEEE Trans Components, Hybrids, and Manufacturing Tech.CHMT-2, 257 (1979).
L. S. Goldmann, R. D. Herdzik, N. G. Koopman and V. C. Marcotte, IEEE Trans Parts, Hybrids, and PackagingPHP-13, 194 (1977).
H. S. Rathore, R. C. Yih and A. R. Edenfeld, J. Testing and Evaluation1, 170 (1973).
E. R. Bangs and R. E. Beal, Welding Res. Suppl.54, 377s (1975).
K. C. Norris and A. H. Landzberg, IBM J. Res. Dev.13, 266 (1969).
G. Becker, “Testing and results related to the mechanical strength of solder joints”, IPC Fall meeting IPC-TP-288 (1979).
E. C. Kubik and T. P. L. Li, “Thermal shock and temperature cycling effects on solder joints of hermetic chip carriers mounted on thick films”, Microelectronics Center, Martin Marrietta Aerospace, Orlando, FL 32855.
P. M. Hall, T. D. Dudderar and J. F. Argyle, IEEE Trans Components, Hybrids, and Manufacturing Tech.CHMT-6, 544 (1983).
D. Frear, D. Grivas, M. McCormack, D. Tribula, and J. W. Morris, Jr., “Fatigue and thermal fatigue of Pb-Sn solder joints”, Proc. Effects of Load and Thermal Histories on Mechanical Behavior Symp. AIME Spring Conf., Denver, CO (1987), in press.
D. Frear, D. Grivas, M. McCormack, D. Tribula, and J. W. Morris, Jr. “Fatigue and thermal fatigue testing of Pb-Sn solder joints”, Proc. 3rd Ann. Electronic Packaging and Corrosion in Microelectronics Conf.,3, 269 (1987).
H. N. Keller, IEEE Trans Components, Hybrids, and Manufacturing Tech.CHMT-4, 132 (1981).
P. M. Hall, IEEE Trans Components, Hybrids, and Manufacturing Tech.CHMT-4, 403 (1981).
K. R. Stone, R. Duckett, S. Muckett, and M. E. Warwick, Brazing and Soldering4, 20 (1983).
C. Wright, IEEE Trans Parts, Hybrids, and Packaging,PHP-13, 202 (1977).
M. C. Denlinger and D. W. Becker, Welding Res. Supp.57, 202s (1978).
R. N. Wild, “Some fatigue properties of solders and solder joints”, IBM Report no. 74Z000481, Oct. (1975).
J. T. Lynch, G. M. Dydon, M. R. Hepher and J. P. McCarthy, “Environmental assessment of ceramic chip carriers soldered-attached to thick film alumina substrates”, Proc. 32nd Elec. Comp. Conf.,32, 385 (1982).
W. T. Chen and C. W. Nelson, IBM J. Res. Dev.23,179 (1979).
C. J. Thwaites and W. B. Hampshire, Welding Res. Supp.55, 323s (1976).
D. Grivas,Deformation of Superplastic Alloys at Relatively Low Strain Rates, Ph.D. Thesis, University of California, and Berkeley (1978).
D. Frear, D. Grivas, L. Quan and J. W. Morris, Jr., “Micro-structural observations and mechanical behavior of Pb-Sn solder on Cu plates”, Mat. Res. Soc. Symp.,72, 181 (1986).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Frear, D., Grivas, D. & Morris, J.W. A microstructural study of the thermal fatigue failures of 60sn-40Pb solder joints. J. Electron. Mater. 17, 171–180 (1988). https://doi.org/10.1007/BF02652148
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02652148