Abstract
Because of their austenitic-ferritic microstructures, duplex stainless steels offer a good combination of mechanical and corrosion resistance properties. However, heat treatments can lower the mechanical strength of these stainless steels as well as render them susceptible to intergranular corrosion (IGC) and pitting corrosion. In this study, a low-carbon (0.02%) duplex stainless steel is subjected to various heat treatments at 450 to 950 °C for 30 min to 10 h. The heat-treated samples then undergo ASTM IGC and pitting corrosion tests, and the results are correlated with the microstructures obtained after each heat treatment. In the absence of Cr23C6 precipitation, σ-phase precipitates render this duplex stainless steel susceptible to IGC and pitting corrosion. Even submicroscopic σ-phase precipitates are deleterious for IGC resistance. Longer-duration heat treatments (at 750 to 850 °C) induce chromium diffusion to replenish the chromium-depleted regions around the σ-phase precipitates and improve IGC resistance; pitting resistance, however, is not fully restored. Various mechanisms of σ-phase formation are discussed to show that regions adjacent to σ-phase are depleted of chromium and molybdenum. The effect of chemical composition (pitting resistance equivalent) on the pitting resistance of various stainless steels is also noted.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
G. Bergland and P. Wilhelmsson, Fabrication and Practical Experience of Duplex Stainless Steels,Mater. Des., Vol 10 (No. 1), 1989, p 23–28
R. Longneberg and J. Johnson, Stainless Steels in the ’90s,Mater. Des., Vol 10 (No. 3), 1989, p 144–152
H. Solomon and T. Devine, Jr., Tale of Two Phases,Duplex Stainless Steels, R.A. Lula, Ed., American Society for Metals, 1983, p 693-756
J.O. Nilsson, Superduplex Stainless Steels,Mater. Sci. Technol., Vol 8,1992, p 685–700
R.L. Cowan and C.S. Tedman, Intergranular Corrosion for Iron-Nickel-Chromium Alloys,Advances in Corrosion Science and Technology, Vol 13, M.G. Fontana and R.W. Staehle, Ed., Plenum Press, 1973, p 293-400
C.S. Tedman, D.A. Vermilyea, and J.H. Rosolowski, Intergranular Corrosion of Austenitic Stainless Steels,Electrochem. Soc, Vol 118 (No. 2), 1971, p 192–202
T.M. Devine, Mechanism of Intergranular Corrosion and Pitting Corrosion of Austenitic and Duplex 308 Stainless Steel,J. Electrochem. Soc, Vol 126 (No. 3), 1979, p 374–385
T.M. Devine, Influence of Carbon Content and Ferrite Morphology on the Sensitization of Duplex Stainless Steel,Metall. Trans., Vol 11 A, 1980, p 791–800
K. Ravindranath and S.N. Malhotra, The Influence of Aging on the Intergranular Corrosion of 22 Chromium-5 Nickel Duplex Stainless Steel,Corros. Sci, Vol 37 (No. 1), 1994, p 121–132
J.R. Galvele, J.B. Lumsden, and R.W. Staehle, Effect of Molybdenum on the Pitting Potential of High Purity 18% Cr Stainless Ferritic Steel,J. Electrochem. Soc, Vol 125 (No. 8), 1978, p 1204–1208
R.J. Brigham, Pitting and Crevice Corrosion Resistance of Commercial 18%Cr Stainless Steel,Mater. Perform., Vol 13 (No. 11), 1974, p 29–31
G.C. Palit, V. Kain, and H.S. Gadiyar, Electrochemical Investigations of Pitting Corrosion in Nitrogen Bearing Type 316 LN Stainless Steel,Corrosion, Vol 49 (No. 12), 1993, p 977–991
J.E. Truman,Met. Mater. Technol, Jan 1980, p 15
J.H. Potgieter, Influence of a Phase on General and Pitting Corrosion Resistance of SAF 2205 Duplex Stainless Steel,Br. Corros. J., Vol 27 (No. 3), 1992, p 219–223
J.H. Potgieter, Discussion on Influence of σ Phase on General and Pitting Corrosion Resistance of SAF 2205 Duplex Stainless Steel,Br. Corros. J., Vol 27 (No. 4), 1992, p 319–320
V. Kain, G.C Palit, S.S. Chouthai, and H.S. Gadiyar, Effect of Heat Treatment on the Critical Pitting Potential of SS 304 in 0.01 N NaCl,J. Electrochem. Soc. India, Vol 38 (No 1), 1989, p 50–54
H.D. Solomon and T.M. Devine,Influence of Microstructure on the Mechanical Properties and Localized Corrosion of a Duplex Stainless Steel, STP672, ASTM, 1979, p 430-461
Y. Maehara, Y. Ohmori, and T. Kunitake,Met. Technol., Vol 10, 1983, p 296–303
M.E. Wilms, V.J. Gadgil, J.M. Krougmen, and B.H. Kolster, The Effect of σ Phase Precipitation at 800 °C on the Mechanical Properties of a High Alloyed Duplex Stainless Steel,Mater. High Temp., Vol 9 (No. 3), 1991, p 160–166
M.E. Wilms, V.J. Gadgil, J.M. Krougmen, and F.A. Ijsseling, The Effect of σ Phase Precipitation at 800 °C on the Corrosion Resistance in Sea Water of a High Alloyed Duplex Stainless Steel,Corros. Sci., Vol 36 (No. 5), 1994, p 871–881
A.J. Sedricks, New Stainless Steels for Sea Water Service,Corrosion, Vol 45 (No. 6), 1989, p 510–518
T.M. Devine and B. J. Drummand, Use of Accelerated Intergranular Tests and Pitting Corrosion Tests to Detect Sensitization and Susceptibility to Intergranular Stress Corrosion Cracking in High Temperature Water of Duplex 308 Stainless Steel,Corrosion, Vol 37 (No. 2), 1981, p 104–115
“Recommended Practice for Detecting Susceptibility to Intergranular Attack in Stainless Steels”, A 262,Annual Book of ASTM Standards, ASTM, 1989, p 1-18
“Test for Pitting and Crevice Corrosion Resistance of Stainless Steels and Related Alloys by the Use of Ferric Chloride Solution,” G 48,Annual Book of ASTM Standards, ASTM, 1989
H.D. Solomon, Age Hardening in a Duplex Stainless Steel,Duplex Stainless Steels, R.A. Lula, Ed., American Society for Metals, 1983, p 41-70
Y. Maehara, Y. Ohmori, J. Murayama, N. Fujino, and T. Kunitake,Mater. Sci., Vol 17, 1983, p 541–547
M.A. Streicher, General and Intergranular Corrosion of Austenitic Stainless Steels in Acids,J. Electrochem. Soc, Vol 106,1959, p 161–180
D. Warren, Effect of Sigma Phase vs Chromium Carbides on the Intergranular Corrosion of Type 316 and 316 L Stainless Steels, Parts I and II,Corrosion, Vol 15 (No. 4 and 5), 1959, p 213t-232t
P. Sury,Mater. Chem., Vol 1, 1976, p 151
K.N. Adhe, V. Kain, S.S. Chouthai, and H.S. Gadiyar, Effect of Time and Temperature of Desensitization on the Chromium Depleted Region in AISI 304 Stainless Steel,Indian J. Technol., Vol 28,1990, p 139–142
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Adhe, K.M., Kain, V., Madangopal, K. et al. Influence of sigma-phase formation on the localized corrosion behavior of a duplex stainless steel. JMEP 5, 500–506 (1996). https://doi.org/10.1007/BF02648847
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF02648847