Abstract
This investigation examines the effect of thermal cycle on the microstructural development in a powder metallurgy (P/M) superalloy braze material. Using a vertical quench furnace, samples were quenched at various stages within the heat treatment. Microstructures were analyzed using optical microscopy and an electron microprobe. The results show that borides having a blocky morphology are stable at all temperatures, both compositionally and morphologically. Script phase undergoes a drastic change in chemistry; however, it remains morphologically stable throughout. The chemical analysis of the microstructure supports the conclusion that the extended heat treatment, which is employed in industry to homogenize the microstructure and dissolve detrimental phases, does not have a significant effect in preventing these phases from forming. By using shorter times at elevated temperatures, similar microstructures can be produced.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
R.M. German:Liquid Phase Sintering, Plenum Press, New York, NY, 1985, pp. 164–72.
F.V. Lenel:Powder Metallurgy—Principles and Applications, MPIF, Princeton, NJ, 1980, pp. 301–05.
B. Reiger, W. Schatt, and C. Sauer:Int. J. Powder Metall Powder Technol., 1983, vol. 19, pp. 29–41.
F.J. Puckert, W.A. Kaysser, and G. Petzow:Z. Metallkd., 1980, vol. 28, pp. 737–43.
L.I. Kivalo, V.V. Skorokhod, and V.Y. Petrishchev:Sov. Powder Metall. Met. Ceram., 1982, vol. 21, pp. 534–36.
V.V. Rana, S.M. Copley, and J.M. Whelan: inCeramic Microstructures ’76, R.M. Fulrath and J.A. Pask, eds., Westview Press, Boulder, Co, 1977, pp. 434–43.
S. Banerjee, V. Gemenitzis, and F. Thummler:Powder Metall., 1980, vol. 23, pp. 126–29.
M.R. Pickus:Int. J. Powder Metall. Powder Technol., 1984, vol. 20, pp. 311–23.
T. Kohno and M.J. Kiczak:Prog. Powder Metall., 1982, vol. 38, pp. 463–81.
I. Barin:Thermochemical Data of Pure Substances, VCH, Weinheim, 1993.
H.J. Beattie, Jr. and W.C. Hagel:Trans. AIME, 1965, vol. 233 (2), p. 277.
C.T. Sims, N.S. Stoloff, and W.C. Hagel: inSuperalloys II, Sims, Stoloff, and Hagel, eds., Wiley, New York, NY, 1987, p. 220.
E.W. Ross:J. Met., 1967, vol. 19 (12), pp. 12–14.
W. Wallace, H.B. Dunthorpe, and R.A. Sprague:Can. Metall. Q., 1974, vol. 13 (3), p. 517.
D. Billard and J.P. Trottier:Powder Metall. Int., 1978, vol. 10 (2), p. 83.
R.E. Waters: Ph.D. Thesis, Cambridge University, Cambridge, United Kingdom, Sept. 1979.
C.T. Sims, N.S. Stoloff, and W.C. Hagel: inSuperalloys II, Sims, Stoloff, and Hagel, eds., Wiley, New York, NY, 1987, p. 112.
M.C. Witt and J.A. Charles:Mater. Sci. Technol., 1985, vol. 1, pp. 1063–68.
J.S. Crompton and R.W. Hertzberg:J. Mater. Sci., 1986, vol. 21, pp. 3445–54.
W.J. Boesch and H.B. Canada:J. Met., 1968, vol. 20 (4), pp. 46–50.
H.J. Beattie:Acta Crystallogr, 1958, vol. 11, p. 607.
R.G. Iacocca: The Pennsylvania State University, University Park, PA, unpublished research, 1995.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Iacocca, R.G. The effect of thermal cycle on the microstructural development of a powder metallurgy superalloy braze material. Metall Mater Trans A 27, 145–153 (1996). https://doi.org/10.1007/BF02647755
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02647755