Abstract
Transformation of austenite during cyclic loading was studied in AISI 301 and 304 alloys whose stability was adjusted by heat treatment and temperature changes. Fatigue life was determined under controlled strain amplitude tension-compression conditions. The amount of transformation to α’ (bcc) martensite was continuously indicated magnetically during testing, and the α’ and ∈ (hcp) phases were observed metallographically at failure. It was found in room temperature testing that at strain amplitudes in excess of 0.4 pct the formation of α’ (bcc) martensite was detrimental to the fatigue life. At 200°F (366 K) the fatigue life of an unstable alloy was increased, while in a completely stable austenitic alloy (20Cr, 6Ni, 9Mn), the life at 200°F (366 K) was less than that at room temperature for the same cyclic strain amplitude. The differing effect of temperature on life of these two types of alloy is attributed to the alteration of the austenite stacking fault energy and the relative free energies of the α’ (bcc), ∈ (hcp) and γ (fcc) phases in the unstable alloys. It has been observed that within the standard composition ranges of the two 300 series stainless steel grades there can be marked differences in the degree of transformation resulting from cyclic loading. This has the implication that for fatigue applications modifications in the specifications for the different grades of stainless would be advantageous.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J. P. Bressanelli and A. Moskowitz:Trans. ASM, 1966, vol. 59, pp. 223–39.
T. Angel:J. Iron Steel Inst., 1954, vol. 177, pp. 165–72.
C. Guntner and R. Reed:Trans. ASM, 1962, vol. 55, pp. 399–419.
D. Neff, T. Mitchell and A. Troiano:Trans. ASM, 1969, vol. 62, pp. 858–62.
G. Stone and G. Thomas:Met. Trans., 1974, vol. 5, pp. 2095–102.
B. Cina:Acta Met., 1958, vol. 6, pp. 748–62.
R. Lagneborg:Acta Met., 1964, vol. 12, pp. 823–43.
P. Mangonon and G. Thomas:Met. Trans., 1970, vol. 1, pp. 1577–86.
F. Lecroisey and A. Pineau:Met. Trans., 1972, vol. 3, pp. 387–96.
G. Chanani, S. Antolovich, and W. Gerberich:Met. Trans., 1972, vol. 3, pp. 2661–72.
C. Bathias and R. Pelloux:Met. Trans., 1973, vol. 4, pp. 1265–73.
A. Pineau and R. Pelloux:Met. Trans., 1974, vol. 5, pp. 1103–12.
G. Chanani and S. Antolovich:Met. Trans., 1974, vol. 5, pp. 217–29.
C. Altstetter and D. Hennessy:The Microstructure and Design of Alloys, pp. 437–40, Institute of Metals, London, 1974.
J. Breedis and L. Kaufman:Met. Trans., 1971, vol. 2, pp. 2359–71.
G. Eichelman and F. Hull:Trans. ASM, 1953, vol. 45, pp. 77–104.
D. Brandarkar, V. Zackay, and E. Parker:Met. Trans., 1972, vol. 3, pp. 2619–31.
A. Rosen, R. Jago, and T. Kjer:J. Mater. Sci., 1972, vol. 7, pp. 870–76.
R. Smith, M. Hirschberg, and S. Manson: NASA technical note Dl 574, 1963.
R. Landgraf: ASTM, STP 467, pp. 3–36, 1970.
J. Morrow: ASTM, STP 378, pp. 45–87, 1965.
C. Feltner and M. Mitchell: ASTM, STP 465, pp. 27–66, 1970.
L. Coffin:Ann. Rev. Mater. Sci., 1972, vol. 2, pp. 313–48.
C. Bathias and R. Pelloux (discussion of Ref. 12):Met. Trans., 1974, vol. 5, pp. 306–07.
R. Karz: Ph.D. dissertation, 1972, University of Illinois, Urbana, Il.
A. Cochardt:Magnetic Properties of Metals and Alloys, pp. 251–79, ASM, Metals Park, Ohio, 1959.
D. Goodchild, W. Roberts, and D. Wilson:Acta Met., 1970, vol. 18, pp. 1137–45.
J. Breedis and W. Robertson:Acta Met., 1962, vol. 10, pp. 1077–88.
J. Dash and H. Otte:Acta Met., 1963, vol. 11, pp. 1169–78.
J. Breedis:Trans. TMS-AIME, 1964, vol. 230, pp. 1583–96.
M. Holzworth and M. Louthan:Corrosion, 1968, vol. 24, pp. 110–24.
Author information
Authors and Affiliations
Additional information
Formerly a Research Assistant
Rights and permissions
About this article
Cite this article
Hennessy, D., Steckel, G. & Altstetter, C. Phase transformation of stainless steel during fatigue. Metall Trans A 7, 415–424 (1976). https://doi.org/10.1007/BF02642838
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02642838