Abstract
The factors determining the temperature, heating rate, microstructure, and strain rate in Al 7075-T6 friction stir spot welds are investigated. Stir zone microstructure was examined using a combination of transmission electron microscopy (TEM) and electron backscattered diffraction (EBSD) microscopy, while the strain rate during spot welding was calculated by incorporating measured temperatures and the average subgrain dimensions in the Zener-Hollomon relation. The highest temperature during friction stir spot welding (527 °C) was observed in spot welds made using a tool rotational speed of 3000 rpm. The stir zone regions comprised fine-grained, equiaxed, fully recrystallized microstructures. The calculated strain rate in Al 7075-T6 spot welds decreased from 650 to about 20 s−1 when the tool rotational speed increased from 1000 to 3000 rpm. It is suggested that the decrease in strain rate results when tool slippage occurs when the welding parameter settings facilitate transient local melting during the spot welding operation. Transient local melting and tool slippage are produced when the welding parameters produce sufficiently high heating rates and temperatures during spot welding. However, transient local melting and tool slippage is not produced in Al 7075-T6 spot welds made using a rotational speed of 1000 rpm since the peak temperature is always less than 475 °C.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
W.M. Thomas, E.D. Nicholas, J.D. Needham, M.G. Murch, P. Templesmith, and C.J. Daws: G.B. Patent Application No. 9,125,978.8, Dec. 1991; U.S. Patent No. 5,460,317, Oct. 1995.
C.G. Rhodes, M.W. Mahoney, and W.H. Bingel:Scripta Mater., 1997, vol. 36, pp. 69–75.
T. Shibayanagi and M. Maeda:Trans. JWRI, 2004, vol. 33, pp. 17–23.
R.S. Mishra and M.W. Mahoney:Mater. Sci. Forum, 2001, vol. 357-359, pp. 507–14.
J.-Q. Su, T.W. Nelson, M. Mishra, and M. Mahoney:Acta Mater., 2003, vol. 51, pp. 713–29.
J.-Q. Su, T.W. Nelson, and C.J. Sterling:Scripta Mater., 2005, vol. 52, pp. 135–40.
M.L. Santella, T. Pan, T. Engstrom, and D. Storjohann:SAE Technical Series, SAE, Warrendale, PA, 2005, 2005-01-1249.
K. Nakata, S. Inoki, Y. Nagano, T. Hashimoto, S. Johgan, and M. Ushio:J. Jpn. Inst. Light Met., 2001, vol. 51, pp. 528–33.
P.-C. Lin, S.-H. Lin, J. Pan, T. Pan, J.M. Nicholson, and M.A. Garman:SAE Technical Series, SAE, Warrendale, PA, 2004, 2004-01-1330.
P. Su, A. Gerlich, T.H. North, and G.J. Bendzsak:SAE Technical Series, SAE, Warrendale, PA, 2006, 2006-01-0971.
Ø. Frigaard, Ø. Grong, J. Hjelen, S. Gulbrandsen-Dahl, and O.T. Midling:Proc. 1st Int. Symp. on Friction Stir Welding, Thousand Oaks, CA, 1999, TWI, Great Abington, Cambridge, U.K., 1999.
P.-E. Droenen and N. Ryum:Metall. Trans. A, 1994, vol. 25A, pp. 521–30.
B. Bjørneklett, Ø. Frigaard, Ø. Grong, O.R. Myhr, and O.T. Midling:Proc. 6th Int. Conf. on Aluminium Alloys, Toyoashi, Japan, 1998, Japan Institute of Light Metals, Tokyo, Japan, 1988, pp. 1531–36.
J.R. Davis:Aluminum and Aluminum Alloys, ASM INTERNATIONAL, Materials Park, OH, 1993, p. 699.
H.J. McQueen and J.J. Jonas:Treatise on Materials Science Technology, Academic Press, New York, NY, 1975, vol. 6, pp. 393–493.
H.J. McQueen and J.E. Hocket:Metall. Trans. A, 1970, vol. 1, pp. 2997–3004.
G. Avramovic-Cingara, H.J. McQueen, A. Hopkins, V. Jain, and D. Perovic: inLight Weight Alloys for Aerospace Applications, E.W. Lee, N.J. Kim, and K.V. Jata, eds., Las Vegas, NV, TMS-AIME, Warrendale, PA, pp. 333–47.
G. Avramovic-Cingara and H.J. McQueen:Aluminium, 1994, vol. 70 (3–4), pp. 214–19.
G. Avramovic-Cingara, D.D. Perovic, and H.J. McQueen:Metall. Mater. Trans. A, 1996, vol. 27A, pp. 3478–90.
E. Cerri, E. Evangelista, A. Forcellese, and H.J. McQueen:Mater. Sci. Eng., 1995, vol. A197, pp. 181–98.
T. Sheppard:2nd Int. Conf. on Aluminum Alloys—Their Physical and Mechanical Properties, C.Q. Chen and E.A. Starke, eds., International Academic Publisher, Beijing, pp. 744–54.
K.A.A. Hassan, B.P. Wynne, and P.B. Prangnell:Proc. 4th Int. Conf. Friction Stir Welding, Park City, UT, 2003, TWI, Great Abington, Cambridge, U.K.
P.N. Adler and R. Delasi:Metall. Trans. A, 1977, vol. 8A, pp. 1185–90.
Y.S. Sato, M. Urata, and H. Kokawa:Metall. Mater. Trans. A, 2002, vol. 33A, pp. 625–35.
C.I. Chang, C.J. Lee, and J.C. Huang:Scripta Mater., 2004, vol. 51, pp. 509–14.
C.G. Rhodes, M.W. Mahoney, W.H. Bingel, and M. Calabrese:Scripta Mater., 2003, vol. 48, pp. 1451–55.
K. Nakata, S. Inoki, Y. Nagano, T. Hashimoto, S. Johgan, and M. Ushio:Proc. 3rd Int. Conf. Friction Stir Welding, Kobe, Japan, 2001, TWI, Great Abington, Cambridge, U.K.
A. Gerlich, G.A. Cingara, and T.H. North: inAluminum Alloys 2006, W.J. Poole, M.A. Wells, and D.J. Lloyd, eds., 2006, Materials Science Forum, vol. 519–521, pp. 1107–12.
F.J. Humphreys:J. Mater. Sci., 2001, vol. 36, pp. 3833–54.
M. Karlsen, S. Tangen, J. Hjelen, Ø. Frigaard, and Ø. Grong:Proc. 3rd Int. Conf. Friction Stir Welding, Kobe, Japan, 2001, TWI, Great Abington, Cambridge, U.K.
M.W. Mahoney, C.G. Rhodes, J.G. Flintoff, R.A. Spurling, and W.H. Bingel:Metall. Mater. Trans. A, 1998, vol. 29A, pp. 1955–64.
F.J. Frost and M.F. Ashby:Deformation-Mechanism Maps, Pergamon Press, New York, NY, 1982.
K.V. Jata and S.L. Semiatin:Scripta Mater., 2000, vol. 43 (8), pp. 743–49.
D. Schmitter and I.M. Zylla:J. Phys. IV France, 2004, vol. 120, pp. 677–80.
G.J. Bendzsak, T.H. North, and C.B. Smith:Proc. 2nd Int. Conf. Friction Stir Welding, Gothenburg, Sweden, 2000, TWI, Great Abington, Cambridge, U.K.
F.P. Bowden and K.E.W. Ridler:Proc. R. Soc. London, Ser. A, 1936, vol. 154 (883), pp. 640–56.
F.P. Bowden and P.H. Thomas:Proc. R. Soc. London, Ser. A, 1954, vol. 223 (1152), pp. 29–40.
A. Gerlich, P. Su, G.J. Bendzsak, and T.H. North: inFriction Stir Welding and Processing III, K.V. Jata, M.W. Mahoney, and R.S. Mishra, eds., TMS, Warrendale, PA, 2005.
T.F.J. Quinn and W.O. Winer:Wear, 1985, vol. 102, pp. 67–80.
T.H. North, G.J. Bendzsak, C.B. Smith, and G.H. Luan:Proc. 7th Int. Symp. JWS, Kobe, Japan, 2001, JWS, Tokyo, Japan, pp. 621–32.
T.H. North, G.J. Bendzsak, and C.B. Smith:Proc. 2nd Int. Conf. Friction Stir Welding, Gothenburg, Sweden, 2000, TWI, Great Abington, Cambridge, U.K.
A. Gerlich, P. Su, and T.H. North:Sci. Technol. Welding Joining, 2005, vol. 10, pp. 647–52.
A. Gerlich, P. Su, T.H. North, and G.J. Bendzsak:Mater. Forum, 2005, vol. 29, pp. 290–94.
A. Gerlich, P. Su, and T.H. North:J. Mater. Sci., 2005, vol. 40, pp. 6473–81.
Kh.A.A. Hassan, P.B. Prangnell, A.F. Norman, D.A. Price, and S.W. Williams:Sci. Tech. Welding Joining, 2003, vol. 8, pp. 257–68.
Y. Yan, B. Lui, and C. Zhang:Proc. 6th Int. Conf. on Aluminium Alloys, Toyoashi, Japan, 1998, Japan Institute of Light Metals, Tokyo, Japan, 1988, pp. 1135–40.
C. Dalle-Donne, B. Braun, G. Staniek, A. Jung, and W.A. Kayser:Materialwiss. Werkstofftech., 1998, vol. 29, pp. 609–17.
A. Gerlich, P. Su, and T.H. North: inMagnesium Technology 2005, N.R. Neelameggham, H.I. Kaplan, and B.R. Powell, eds., TMS, Warrendale, PA, 2005, pp. 383–88.
Y.S. Sato, S. Hwan, C. Park, M. Michiuchi, and H. Kokawa:Scripta Mater., 2004, vol. 50 (9), pp. 1233–36.
P.A. Colegrove, H.R. Shercliff, and P.L. Threadgill:Proc. 4th Int. Conf. Friction Stir Welding, Park City, UT, 2003, TWI, Great Abington, Cambridge, U.K.
O. Reiso, H.-G. Øverlie, and N. Ryum:Metall. Trans., 1990, vol. 21A, pp. 1689–95.
S. Kou:Welding Metallurgy, 2nd ed., Wiley & Sons, New York, NY, 2003, pp. 303–39.
W.F. Savage, E.F. Nippes, and J.D. Varsik:Welding J., 1979, vol. 58, pp. 45s-52s.
X.-M. Li and M.J. Starink:Mater. Sci. Technol., 2001, vol. 17, pp. 1324–28.
O.R. Myhr and Ø. Grong:Acta Metall. Mater., 1991, vol. 39, pp. 2693–702.
M.J. Whelan:Met. Sci. J., 1969, vol. 3, pp. 95–97.
P. Su, A. Gerlich, M. Yamamoto, and T.H. North:Proc. Magnesium Technology in the Global Age Symp., 2006, CIM, Montreal, Canada.
H. Hanemann and A. Schrader:Ternäre Legierungen des Aluminiums, Verlag Stahleisen M.B.H., Dusseldorf, 1952, p. 138.
P. Su, A. Gerlich, T.H. North, and G.J. Bendzsak:Sci. Technol. Welding Joining, 2006, vol. 11, pp. 61–71.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Gerlich, A., Avramovic-Cingara, G. & North, T.H. Stir zone microstructure and strain rate during Al 7075-T6 friction stir spot welding. Metall Mater Trans A 37, 2773–2786 (2006). https://doi.org/10.1007/BF02586110
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02586110