The interfacial phases were studied in pressure-cast Saffil/Al-4.5Cu-3Mg composite material using a variety of characterization techniques. The magnesium- and copper-rich phases were found to segregate near the fibre-matrix interfaces. The major phases were identified as MgAl2O4, Al2CuMg and CuAl2. Significant diffusion of silicon from the fibres into the matrix took place during the pressure-casting. A conclusion was drawn that solidification started with the less alloyed aluminium in the bulk of the matrix and proceeded towards the fibres. Auger and XPS analyses of composite materials fracturedin situ showed the fracture surface to lie within magnesium-rich (and not copper-rich) phases, most likely within the MgAl2O4 spinel phase. The fibre surface treatments which are being developed to improve interfacial wetting may also reverse the direction of crystallization and prevent formation of brittle phases in the vicinity of fibres, thereby improving the toughness of the composite materials.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
G. Cappleman, J. F. Watts andT. W. Clyne,J. Mater. Sci. 20 (1985) 2159.
T. W. Clyne, M. G. Bader, G. Cappleman andP. A. Hubert,ibid. 20 (1985) 85.
M. N. Gungor, J. A. Cornie andM. C. Fleming, in “Interfaces in Metal-Matrix Composites”, Proceedings of Symposium sponsored by AIME-ASM Composite Committee, TMS-AIME Annual Meeting, New Orleans, March 1986, edited by A. K. Dhingra and S. Fishman, pp. 121–135.
A. Mortensen, M. N. Gungor, J. A. Cornie andM. C. Fleming,J. Metals (1986) 30.
C. G. Levi, G. J. Abbaschian andR. Mehrabian,Met. Trans. 9A (1978) 697.
Idem, Failure Modes Compos. 4 (1979) 370.
A. Munitz, M. Metzger andR. Mehrabian,Met. Trans. 10A (1979) 1491.
A. G. Metcalfe,J. Compos. Mater. 1 (1967) 356.
M. Naka, Y. Hirono andI. Okamoto,Trans. JWRI 13 (1984) 201.
J. A. Pask andA. P. Tomsia,Mater. Sci. Res. 14 (1981) 410.
F. P. Bailey andW. E. Borbidge,ibid. 14 (1981) 525.
S. T. Mileiko, in “Fabrication of Composites”, edited by A. Kelly and S. T. Mileiko (North-Holland, Amsterdam, 1983) pp. 221–294.
B. F. Quigley, G. J. Abbaschian, R. Wunderlin andR. Mehrabian,Met. Trans. 13A (1982) 93.
R. E. Reed-Hill, “Physical Metallurgy Principles”, 2nd Edn (Van Nostrand, New York, 1973).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Fishkis, M. Interfaces and fracture surfaces in Saffil/Al-Mg-Cu metal-matrix composites. J Mater Sci 26, 2651–2661 (1991). https://doi.org/10.1007/BF02387733
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02387733