Abstract
When chalcopyrite is heated in air, up to 350‡ there is no marked change. Between 350 and 440‡, surface material is oxidised to iron sulphate, CuSO4 and Fe2O3, while in regions not accessible to oxygen the formation of Cu5FeS4, FeS and S takes place. From 440 to 500‡ oxidation and sulphation phenomena occur. Stable compounds between 500 and 650‡ are iron sulphate, CuSO4 and Fe4O3, with a minor amount of 6CuO.Cu2O indicated at 650‡. After the decomposition of iron sulphate, CuSO4 decomposes, first to CuO.CuSO4 and then to CuO. By 750‡ the sulphur has been totally lost from all compounds, while the oxides of copper and iron partly react to form CuFe2O4. Final products of oxidation between 800 and 850‡ are CuO, CuFe2O4 and Fe3O4.
Zusammenfassung
Beim Erhitzen von Chalkopyrit in Luft tritt bis 350‡ keine merkbare Veränderung ein. Zwischen 350 und 440‡ wird die Substanz an der Oberfläche zu Eisensulfat, CuSO4 und Fe2O3 oxydiert, während in den nicht für Sauerstoff zugänglichen Teilen die Bildung von Cu5FeS4, FeS und S erfolgt. Im Bereich von 440–500‡ treten Oxydations- und Sulfatierungsphänomene auf. Zwischen 500 und 650‡ sind Eisensulfat, CuSO4 und Fe2O3 stabile Verbindungen, zusammen mit dem bei 650‡ auftretenden 6.CuO.Cu2O. Nach der Zersetzung von Eisensulfat zersetzt sich CuSO4 zunächst zu CuO.CuSO4 und schliesslich zu CuO. Bei 750‡ sind alle Verbindungen vollkommen schwefelfrei und die Oxide von Kupfer und Eisen reagieren unvollständig zu CuFe2O4. Endprodukte der Oxydation sind bei 800–850‡ CuO, CuFe2O4 und Fe2O3.
РЕжУМЕ
ВИДИМых ИжМЕНЕНИИ НЕ пРОИсхОДИт с хАлькОпИРИтОМ пРИ НА гРЕВАНИИ ЕгО НА ВОжДУхЕ ДО 350 ‡. МЕжДУ 350 ‡ И 440 ‡ пОВЕРхНОсть ДОстАВ лЕННых МАтЕРИАлОВ ОкИсльЕт сь ДО сУльФАтА жЕлЕжА, сУ льФАтА МЕДИ И ОкИсИ тРЕхВАлЕНтНОгО жЕлЕ жА. В МЕстАх НЕДОстУпН ых Дль кИслОРОДА, ОБРАжУ Утсь Cu5 FeS4,сУльФИД жЕлЕж А И сЕРА. МЕжДУ 440 ‡ И 500 ‡ пРОИсхОДИ т РЕАкцИь ОкИслЕНИь И О БРАжОНИЕ сУльФАтА. В О БлАстИ тЕМпЕРАтУР 500–600 ‡стАБИ льНыМИ сОЕДИНЕНИьМИ ьВльУт сь сУльФАт жЕлЕжА, сУл ьФАт МЕДИ И ОкИсь тРЕхВАлЕНтНОг О жЕлЕжА, сОДЕРжАЩАь пРИ 650 ‡ глАВ НУУ пРИМЕсь 6CuО · Cu2O. пОсл Е РАжлОжЕНИь сУльФАтА жЕлЕжА, сУльФАт МЕДИ сНАЧАлА РАжлАгАЕтсь ДО CuO·CuSO4,a жА тЕМ ДО CuO. сЕРА пОлНОстьУ УДАль Етсь Иж ВсЕх сОЕДИНЕНИИ пР И ДОстИжЕНИИ тЕМпЕРА тУРы 750 ‡, кОгДА ОкИсИ жЕлЕжА И М ЕДИ ЧАстИЧНО РЕАгИРУУт Д О CuFe2O4. кОНЕЧНыМИ пРОДУк тАМИ ОкИслЕНИь МЕжДУ 800 И 850 ‡ ьВльУтсь CuO,CuFe2O4И Fe3O4.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
Fathi Habashi, Chalcopyrite, its Chemistry and Metallurgy, McGraw-Hill International Book Company, U.S.A., 1978 p. 45.
L. Meunier and H. Vanderpoorton, Metallurgie, Paris, 1 (1956) 31.
E.V. Margulis and V.D. Ponomarev, Zh. Prikl. Khim., 35 (1962) 970.
C. Maurel, Bull. Soc. Franc. Mineral. Crist., 87 (3) (1964) 377.
G. Bjorling and P. Lesidrenski, Proc. VIII Intern. Congr. Mineral Processing, Leningrad, (1968).
F.T. Bumazhnov and A. Lenchev, Dokl. Bolg. Akad. Nauk, 25 (7) (1972) 953.
A. Lenchev and F. Bumazhnov, God. Sofil Univ. Khim. Fak., 66 (1975) 441.
T.R. Ingraham and P. Marier, Trans. Met. Soc. AIME 233 (1965) 363.
Author information
Authors and Affiliations
Additional information
We are grateful to Dr. P.B. Radhakrishna, Ex-Chairman, Chitradurga Copper Corporation Ltd., Karnataka State, India, for kindly supplying us with a representative sample of chalcopyrite concentrates and its chemical analysis.
Rights and permissions
About this article
Cite this article
Aneesuddin, M., Char, P.N., Hussain, M.R. et al. Studies on thermal oxidation of chalcopyrite from Chitradurga, Karnataka State, India. Journal of Thermal Analysis 26, 205–215 (1983). https://doi.org/10.1007/BF01913204
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF01913204