Conclusions
A study was made of the influence of the type of periclase, the form and amount of bond, the concentration of graphite and milled periclase, the pressing pressure, and the firing temperature on the compressive strength, apparent density, and open porosity of periclase-carbon refractories.
We developed an industrial, scrap-free technology for the manufacture of periclase-carbon refractories from fused and sintered periclase and graphite with organic bonds SFP + LSB-1 and nontoxic SFP + LST, with the use of scrap from electromelting, and scrap products.
We determined the technological parameters for obtaining high-quality periclase-carbon refractories, including those with nontoxic bonds, with good strength, porosity, and refractoriness under load factors.
The resulting periclase-carbon materials ensure high wear resistance and efficiency to the lining of walls in high-capacity arc, steel-melting furnaces with water-cooled panels, in comparison with PKhP refractories and PKhS materials, which facilitates a reduction in the specific consumption of refractories, including fused. Replacing PKhP and PKhS materials with periclase-carbon will eliminate loss in firing and the consumption of fuel for preparing the goods, and it will also release fusion-grain refractories PKhP for UVS units.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Literature cited
I. G. Ochagova, Review of Information on Periclase-Carbon Refractories [in Russian], Inst. Chermetinformatsiya, No. 1 (1985).
V. G. Borisov, I. Ya. Prokhorova, et al., Ogneupory, No. 12, 5–9 (1986).
Yu. D. Sagalevich, V. G. Borisov, and E. Ya. Shapiro, Ogneupory, No. 8, 4–8 (1986).
S. A. Suvorov, A. M. Smilovitskii, and V. I. Sizov, Ogneupory, No. 10, 47–50 (1985).
I. G. Ochagova, Ogneupory, No. 8, 59–62 (1987).
Authors' Patent No. 1316994, USSR, K. V. Simonov, E. P. Mezentsev, et al., Otkrytiya Izobret., No. 22, 90 (1987).
Inventor's Cert. No. 1318578 USSR, K. V. Simonov, E. P. Mesentsev, et al., Otkrytiya Izobret., No. 23, 84 (1987).
Inventor's Cert. No. 1375617 USSR, K. V. Simonov, E. P. Mezentsev et al., Otkrytiya Izobret., No. 7, 100 (1988).
Inventors' Cert. No. 1244130, K. V. Simonov, V. A. Kryuchov, S. I. Ravochkin, et al., Otkrytiya Izobret., No. 26, 102 (1986).
Inventors' Cert. No. 1335553, K. V. Simonov, E. P. Mezentsev, et al., Otkrytiya Izobret., No. 33, 84 (1987).
Yu. N. Tuluevskii, I. Yu. Zinurov, et al., Saving Electric Energy in Arc Steel-Melting Furnaces [in Russian], Energoatomizdat, Moscow (1987), p. 102.
K. V. Simonov and A. P. Masalova, Ogneupory, No. 4, 45–49 (1983).
Author information
Authors and Affiliations
Additional information
Translated from Ogneupory, No. 12, pp. 27–33, December, 1988.
Rights and permissions
About this article
Cite this article
Simonov, K.V., Zagnoiko, V.V., Burdina, G.V. et al. Influence of technological parameters on the properties and wear resistance of periclase-carbon refractories. Refractories 29, 734–741 (1988). https://doi.org/10.1007/BF01280348
Issue Date:
DOI: https://doi.org/10.1007/BF01280348