Diethylenetriamine, melamine, and low molecular weight branched polyethylenimine were functionalized separately with 3-isocyanatopropyltriethoxysilane. Coatings on polycarbonate were prepared from these compounds through the sol-gel process. The extent of reaction and the relative species concentration of the trifunctional silicon atom were obtained from29Si CP-MAS NMR measurements. The sol-gel reaction was found to be limited by vitrification. A variety of silicon species was present in the vitrified coating. The extent of reaction could be increased by increasing the curing temperature, curing for longer times, and increasing the acid concentration. The extent of reaction was also found to be related to the basicity of the functionalized organic backbone.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
B. Wang and G. L. Wilkes, ACS Polymer Preprints, Aug. (1991).
C. Betrabet and G. L. Wilkes, ACS Polymer Preprints, Aug. (1992).
H. L. Vincent, D. J. Kimball, and R. R. Boundy, inPolymer Wear and Its Control, ACS Symposium Series, No. 287, L. H. Lee, eds. (ACS, Washington, DC, 1985), pp. 129–134.
H. Schmidt and H. Wolter,J. Non Cryst. Solids 121, 428–435 (1990).
C. J. Brinker and G. W. Scherer,Sol-Gel Science, The Physics and Chemistry of Sol-Gel Processing (Academic Press, San Diego, 1990).
G. C. Levy, J. D. Cargioli, P. C. Juliano, and T. D. Mitchell,J. Am. Chem. Soc. 95(11), 3445–3454 (1973).
E. A. Williams,Annual Reports on NMR Spectroscopy, Vol. 15 (Academic Press, New York, 1983), pp. 235–289.
J. L. Koenig,Spectroscopy of Polymers, ACS Professional Reference Book (ACS, Washington, DC, 1992).
G. S. Caravajal, D. E. Leyden, and G. E. Maciel, inSilanes, Surfaces and Interfaces, D. E. Leyden, ed. (Gordon and Breach Science, New York, 1985).
K. Hoh, H. Ishida, and J. L. Koenig,Polym. Comp. 11(2), 121–125 (1990).
H. Marsman, inNMR, Oxygen-17 and Silicon-29, P. Diehl, E. Fluck, and R. Kosfield, eds. (Springer Verlag, New York, 1981), pp. 65–235.
B. W. Peace, K. G. Mayhan, and J. F. Montle,Polymer 14, 420–422 (1973).
J. W. De Haan, H. M. Van Den Bogaert, J. J. Ponjee, and L. J. M. Van De Ven,J. Colloid Interface Sci. 110(2), 591–600 (1986).
E. O. Stejskal, J. Schaefer, M. D. Sefcik, and R. A. McKay,Macromolecules 14, 275–279 (1981).
R. H. Glaser, Ph.D. thesis (Virginia Polytechnic Institute and State University, Blacksburg, 1988).
C. J. Brinker, R. J. Kirkpatrick, D. R. Tallant, B. C. Bunker, and B. Montez,J. Non-Cryst. Solids 99, 418–428 (1988).
G. E. Maciel and D. W. Sindorf,J. Am. Chem. Soc. 102, 7606–7607 (1980).
M. P. Besland, C. Guizard, N. Hovnanian, A. Labot, L. Cot, J. Sanz, I. Sobradas, and M. Gregorkiewitz,J. Am. Chem. Soc. 113, 1982–1987 (1991).
D. W. Sindorf and G. E. Maciel,J. Am. Chem. Soc. 105(12), 3767–3776 (1983).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Betrabet, C.S., Wilkes, G.L. Determining the extent of reaction by29Si NMR of abrasion-resistant hybrid sol-gel coatings based on triethoxysilane functionalized organics. J Inorg Organomet Polym 4, 343–366 (1994). https://doi.org/10.1007/BF00683700
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF00683700