Conclusions
-
1.
In correcting the coarse-grained structure of cast hypereutectoid steels 100KhGMF and 150Kh2MF the recrystallization of austenite is the controlling process.
-
2.
A heat treatment consisting of double normalization was developed for cast rolls of hypereutectoid steels used for hot rolling. For the first normalization we recommend a temperature at which austenite recrystallizes, and for the second normalization 850–880°C. Operating tests of rolls treated by this method have given positive results.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Literature cited
A. A. Astaf'ev and I. A. Borisov, Metal. i Term. Obrabotka Metal., No. 1 (1968).
Additional information
TsNIITMASh. Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 3, pp. 64–65, March, 1969.
Rights and permissions
About this article
Cite this article
Astaf'ev, A.A., Potapova, M.S. & Borisov, I.A. Correcting the coarse-grained structure of cast hypereutectoid steels. Met Sci Heat Treat 11, 232–233 (1969). https://doi.org/10.1007/BF00658742
Issue Date:
DOI: https://doi.org/10.1007/BF00658742