It is common experience that aged surfaces are often difficult to bond to. We report an examination of bonding to thermally-aged epoxy surfaces, using as the adhesive the same epoxy as that of the aged surface. The cured and postcured epoxy was aged at 200 ° C, with the ageing time varying from 2 to 8 h. The fracture energy of the bond line was measured by mode I cleavage under conditions of relatively slow crack growth. The bondline fracture energy was found to decrease logarithmically with ageing time. The fracture energies for bonds to surfaces aged for 2, 4, and 8 h at 200 ° C were 0.077, 0.059, and 0.050 kJ M−2, respectively. These compare to 0.13 kJ M−2 for a bond to an unaged surface and 0.21 kJ m−2 for bulk fracture. Fracture surfaces resulting from both slow and rapid fracture were examined by optical and scanning electron microscopy. Fracture features different from those arising from bulk fracture were found. Areas with ‘good’ adhesion occurred amidst fields of featureless fracture surface; the frequency and size of these areas decreased with increased ageing time. Evidence of plastic deformation was found, always occurring on the new side of the bond: ridges parallel with crack propagation at high crack speeds and subsurface undulations perpendicular to crack propagation at low speeds. The bond has the effect of channelling the crack along the bondline, but fracture does not always remain exactly at the interface. Fracture often occurred a relatively constant distance away from the interface, suggesting that the presence of the interface was felt for some distance.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
V. B. Gupta et al., J. Mater. Sci 20 (1985) 3439.
R. E. Robertson andV. E. Mindroiu,Polym. Sci. Engng 27 (1987) 55.
J. E. Masters et al., in “Engineered Materials Handbook”, Vol 1: “Composites” (ASM International, Metals Park, Ohio, 1987) p. 765.
W. J. Cantwell, A. C. Roulin-Maloney andT. Kaiser,J. Mater. Sci. 23 (1988) 1615.
M. F. Kanninen,Int. J. Fracture 9 (1973) 83.
R. E. Robertson,J. Adhesion 7 (1975) 121.
R. E. Robertson, V. E. Mindroiu andM. F. Cheung,Compos. Sci. Tech. 22 (1985) 197.
R. E. Robertson et al., J. Mater. Sci. 24 (1989) 4106.
J. S. Covavisaruch, private communication (1988).
J. S. Covavisaruch, J.-K. Kim, andR. E. Robertson, to be published.
R. P. Kambour andR. E. Robertson, in “Polymer Science” Vol. 1, edited byA. D. Jenkins (North-Holland, Amsterdam, 1972) p. 687.
R. E. Robertson, in “Toughness and Brittleness of Plastics,” edited byR. D. Deanin andA. M. Crugnola (Americal Chemical Society, Washington, 1976) p. 89.
R. P. Kusy andD. T. Turner,Polymer 17 (1976) 161.
A. Ankara, D. Weisgerber andJ. Vilsmeier,Mater. Sci. Tech. 2 (1986) 647.
S. T. J. Peng,J. Mater. Sci. 20 (1985) 1920.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sporer, M.G., Robertson, R.E. Bonding to aged surfaces: A thermally-aged epoxy. J Mater Sci 25, 2690–2704 (1990). https://doi.org/10.1007/BF00584867
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00584867