Abstract
The color of pink tourmaline gemstone changed to colorless when heating at temperature of 600 °C in air. This colorless tourmaline recovered its pink color when irradiated with an electron beam (e-beam) of 800 kGy. The origin of the color change was investigated in three types of tourmaline gemstones, two pink are from Afghanistan and one green are from Nigeria, by using Ultraviolet-visible spectroscopy (UV-Vis), Fourier-transform infrared spectroscopy (FTIR), Electron paramagnetic resonance (EPR), and Energy Dispersive X-ray Fluorescence (EDXRF). The UV-Vis absorption spectrum of the pink tourmaline with higher Mn concentration (T2, 0.24 wt%) showed characteristic absorption peaks originating from the Mn3+ color center: two absorption bands centered at wavelength of 396 and 520 nm, respectively. Both absorption bands disappeared when heated in air at 600 °C and then reappeared when irradiated with an e-beam at 800 kGy. EPR T2 spectra showed that the color change was related to the valence change of Mn3+ to Mn2+ and vice versa. The pink tourmaline of lower MnO content (T1, 0.08 wt%) also became colorless when heated, but the color was not recovered when the gemstone underwent e-beam irradiation. Instead, a yellow color was obtained. UV-Vis and FTIR spectra indicated that this yellow color originated from a decomposition of the hydroxyl group (−OH) into O− and Ho by the e-beam irradiation. Green tourmaline did not show any color change with either heat treatment or e-beam irradiation.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
P. S. R. Prasad and D. Srinivasa Sarma, Gondzvana Res. 8, 265 (2005).
F. C. Hawthorne and D. J. Henry, Eur. J. Mineral. 11, 201 (1999).
L. V. Bershov, V. O. Martirosyan, A. S. Marfunin, A. N. Platonov and A. N. Tarashehan, Sov. Phys. Crystallogr. 13, 629 (1969).
K. Nassau, Am. Mineral. 60, 710 (1975)
C. Castaneda, S. G. Eeckhout, G. M. da Costa, N. F. Botelho and E. De Grave, Phys. Chem. Minerals 33, 207 (2006).
P. Baèík, D. Ozdín, M. Miglierini, P. Kardosová, M. Pentrák and J. Haloda, Phys. Chem. Minerals 38, 599 (2011).
S. C. Lind and D. C. Bardwell, Am. Mineral. 9, 678 (1923).
F. H. Pough and T. H. Rogers, Am. Mineral. 32, 31 (1947).
P. G. Manning, Can. Mineral. 9, 678 (1969).
K. Nassau, Lapidary J. 28, 1064 (1974).
G. H. Faye, P. G. Manning, J. R. Gosselin and R. J. Tremblay, Can. Mineral. 8, 171 (1974).
M. B. De Camargo and S. Isotani, Am. Mineral. 73, 172 (1988).
I. M. Reinitz and G. R. Rossman, Am. Mineral. 73, 822 (1988).
I. Petrov, Am. Mineral. 75, 237 (1990).
B. M. Laurs, J. C. Zwaan, C. M. Breeding, W. B. Simmons, D. Beaton, K. F. Rijsdijk, R. Befi and A. U. Falster, Gem. Gemol. 44, 4 (2008).
Y. Ahn, J. Seo and J. Park, Vib. Spec. 65, 165 (2013).
P. G. Manning, Can. Mineral. 11, 971 (1973).
G. R. Rossman and S. M Mattson, Am. Mineral. 71, 599 (1986).
B. J. Reddy, R. L. Frost, W. N. Martens, D. L. Wain and J. T. Kloprogge, Vib. Spectrosc. 44, 42 (2007).
D. M. Sherman and N. Vergo, Am. Mineral. 73, 140 (1988).
S. M. Mattson, Dissertation (Ph.D.), California Institute of Technology, 1985.
K. Krambrock, M. V. B. Pinheiro, S. M. Medeiros, K. J. Guedes, S. Schweizer and J. M. Spaeth, Nucl. Instrum. Meth. B 191, 241 (2002).
G. H. Faye, P. G. Manning and E. H. Nickel, Amer. Mineral. 53, 1174 (1968).
S. M. Mattson and G. R. Rossman, Phys. Chem. Minerals 14, 163 (1987).
G. R. Rossman, E. Fritsch and J. E. Shigley, Am. Mineral. 76, 1479 (1991).
G. Smith, Phys. Chem. minerals 3, 375 (1978).
A. Abragam and B. Bleaney, Electron Paramagnetic Resonance of Transition Ions (Clarendon Press, Oxford, 1970), Chap. 1, p. 9.
P. L. Hall, Clay. Miner. 15, 321 (1980).
N. Srisittipokakun, C. KedKaew, J. Kaewkhao, T. Kittiauchawal, K. Thamaphat and P. Limsuwan, Kasetsart J. (Nat. Sci.) 43, 360 (2009).
R. P. S Chakradhar, G. Sivaramaiah, J. L. Rao and N. O. Gopal, Spectrochim. Acta, Part A 62, 761 (2005).
L. B. Glebov, L. N. Glebova, D. E. Jones and R. R. Rakhimov, Non-crystalline Solids 265, 181 (2000).
R. P. S. Chakradhar, K. P. Ramesh, J. L. Rao and J. Ramakrishna, J. Phys. Chem. Solids 64, 641 (2003).
R. S. Muralidharaa, C. R. Kesavulub, J. L. Raob, R. V. Anavekara and R. P. S. Chakradharc, J. Phys. Chem. Solids 71, 1651 (2010).
R. P. S. Chakradhar, A. Murali and J. L. Rao, Opt. Mater. 10, 109 (1998).
S. O. Souza, G. M. Ferraz and S. Watanabe, Nucl. Instr. Meth. Phys. Res. B 218, 259 (2004).
J. Babinska, K. Dyrek, A. Pieczka and Z. Sojka, Eur. J. Mineral. 20, 233 (2008).
S. P. Chaudhuri and S. K. Patra, J. Mater. Sci. 35, 4735 (2000).
T. Gonzalez-Carrefio, M. Fernandez and J. Sanz, Phys. Chem. Minerals 15, 452 (1988).
P. Makreski and G. Jovanovski, Spectrochim. Acta Part A 73, 460 (2009).
V. Sontevska, G. Jovanovski and P. Makreski, J. Mol. Struct. 834, 318 (2007).
X. Liu, X. Feng, J. Fan and S. Guo, Chin. Opt. Lett. 9, 083001 (2011).
D. Cao, G. Zhao, Q. Dong, J. Chen, Y. Cheng, Y. Ding and J. Zou, Chin. Opt. Lett. 8, 199 (2010).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Maneewong, A., Seong, B.S., Shin, E.J. et al. Color change of tourmaline by heat treatment and electron beam irradiation: UV-Visible, EPR, and Mid-IR spectroscopic analyses. Journal of the Korean Physical Society 68, 83–92 (2016). https://doi.org/10.3938/jkps.68.83
Received:
Published:
Issue Date:
DOI: https://doi.org/10.3938/jkps.68.83