Abstract
Bi2Te3-y Se y (y = 0 - 0.6) solid solutions were prepared by using mechanical alloying and hot pressing. The lattice constants decreased with increasing Se content, which revealed the successful formation of solid solutions by using a planetary mill. The relative densities of hot-pressed specimens were higher than 96%. All specimens indicated n-type conductions in the measuring temperature range from 323 K to 523 K, and the electrical conductivity slightly decreased with increasing temperature. The Seebeck coefficient increased with increasing Se content, and the electrical and the thermal conductivities decreased; thus, the dimensionless figure of merit was improved. A maximum dimensionless figure of merit of 0.76 was obtained at 473 K for Bi2Te2.55Se0.45.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J. F. Li, W. S. Liu, L. D. Zhao and M. Zhou, NPG Asia Mater. 2, 152 (2010).
M. S. Dresselhaus, G. Chen, M. Y. Tang, R. G. Yang, H. Lee, D. Z. Wang, Z. F. Rem, J. P. Fleurial and P. Gogna, Adv. Mater. 19, 1043 (2007).
H. J. Goldsmid, Thermoelectric Refrigeration (Plenum, New York, 1964), p. 43.
G. J. Snyder and E. S. Toberer, Nat. Mater. 7, 105 (2008).
H. Scherrer and S. Scherrer, Handbook of Thermoelectrics, edited by D. M. Rowe (CRC Press, London, 1995), chap. 19.
H. J. Goldsmid, J. Appl. Phys. 32, 2198 (1961).
L. V. Prokof’eva, D. A. Pshenai-Severin, P. P. Konstan-Tinov and A. A. Shabaldin, Semicond. 43, 1155 (2009).
D. Vasilevskiy, A. Sami, J. M. Simard and R. Masut, J. Appl. Phys. 92, 2610 (2002).
S. Y. Wang, W. J. Xie, H. Li and X. F. Tang, Intermet. 19, 1024 (2011).
X. F. Tang, W. J. Xie, H. Li, W. Y. Zhao and Q. J. Zhang, Appl. Phys. Lett. 90, 012102 (2007).
O. B. Sokolov, S. Y. Skipidarov and N. I. Duvankov, J. Cryst. Grow. 236, 181 (2002).
X. F. Tang, W. J. Xie, H. Li, W. Y. Zhao and Q. J. Zhang, J. Appl. Phys. Lett. 90, 012102 (2007).
M. Ferhat, G. Brun, J. C. Tedenac, M. Nouaoura and L. Lassabatere, J. Cryst. Grow. 167, 122 (1996).
B. Poudel et al., Sci. 320, 634 (2008).
G. E. Lee, I. H. Kim, S. M. Choi, Y. S. Lim, W. S. Seo, J. S. Park and S. H. Yang, J. Kor. Phys. Soc. 65, 2066 (2014).
X. Yan, B. Poudel, Y. Ma, W. Liu, G. Joshi, H. Wang, Y. Lan, D. Wang, G. Chen and Z. Ren, Nano Lett. 10, 3373 (2010).
G. E. Lee, I. H. Kim, S. M. Choi, Y. S. Lim, W. S. Seo, J. S. Park and S. H. Yang, J. Kor. Phys. Soc. 65, 1908 (2014).
H. Scherrer and S. Scherrer, Thermoelectrics Handbook, edited by D. M. Rowe (CRC Press, New York, 2006), chap. 27.
T. S. Oh, D. B. Hyun and N. V. Kolomoets, Scr. Mater. 42, 849 (2000).
S. Cho, Y. Kim, A. DiVenere, G. K. Wong, J. B. Ketterson and J. R. Meyer, Appl. Phys. Lett. 75, 1401 (1999).
S. Wang, W. Xie, H. Li and X. Tang, Intermet. 19, 1024 (2011).
F. Gascoin, S. Ottensmann, D. Stark, S. M. Haile and G. J. Snyder, Adv. Funct. Mater. 15, 1860 (2005).
L. Hu, H. Gao, X. Liu, H. Xie, J. Shen, T. Zhu and X. Zhao, J. Mater. Chem. 22, 16484 (2012).
H. Cailat, A. Borshchevsky and J. P. Fleurial, J. Appl. Phys. 80, 4442 (1996).
B. Jariwala, D. Shah and N. M. Ravindra, J. Electron. Mater. 44, 1509 (2015).
G. E. Lee, I. H. Kim, S. M. Choi, Y. S. Lim, W. S. Seo, J. S. Park and S. H. Yang, J. Kor. Phys. Soc. 65, 1908 (2014).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Eum, AY., Kim, IH., Choi, SM. et al. Thermoelectric and transport properties of mechanically-alloyed Bi2Te3-y Se y solid solutions. Journal of the Korean Physical Society 67, 1809–1813 (2015). https://doi.org/10.3938/jkps.67.1809
Received:
Published:
Issue Date:
DOI: https://doi.org/10.3938/jkps.67.1809