Abstract
In-situ ion irradiation and transmission electron microscopy has been used to examine the effects of the He appm to DPA ratio, temperature and dose on the damage structure of tungsten (W). Irradiations were performed with 15 or 60 keV He+ ions, achieving He-appm/displacements per atom (DPA) ratios of ~40,000 and ~2000, respectively, at temperatures between 500 and 1000°C to a dose of ~3 DPA. A high number of small dislocation loops with sizes around 5–20 nm and a He bubble lattice were observed for both He-appm/DPA ratios at 500°C with a bubble size ~1.5 nm. Using the g.b=0 criterion the loops were characterised as b = ±1/2<111> type. At 750°C bubbles do not form an ordered array and are larger in size compared to the irradiations at 500°C, with a diameter of ~3 nm. Fewer dislocation loops were observed at this temperature and were also characterised to be b = ±1/2<111> type. At 1000°C, no dislocation loops were observed and bubbles grew as a function of fluence attributed to vacancy mobility being higher and vacancy clusters becoming mobile.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
H. Bolt, V. Barabash, W. Krauss, J. Linke, R. Neu, S. Suzuki, N. Yoshida, and A. U. Team, “Materials for the plasma-facing components of fusion reactors.”
M. R. Gilbert, S. L. Dudarev, S. Zheng, L. W. Packer, and J.-C. Sublet, “An integrated model for materials in a fusion power plant: transmutation, gas production, and helium embrittlement under neutron irradiation,” Nucl. Fusion, vol. 52, no. 8, p. 083019, 2012.
T. Tanno, A. Hasegawa, J.-C. He, M. Fujiwara, S. Nogami, M. Satou, T. Shishido, and K. Abe, “Effects of Transmutation Elements on Neutron Irradiation Hardening of Tungsten,” Mater. Trans., vol. 48, no. 9, pp. 2399–2402, 2007.
T. Tanno, a. Hasegawa, J. C. He, M. Fujiwara, M. Satou, S. Nogami, K. Abe, and T. Shishido, “Effects of transmutation elements on the microstructural evolution and electrical resistivity of neutron-irradiated tungsten,” J. Nucl. Mater., vol. 386–388, no. 2009, pp. 218–221, 2009.
M. Fukuda, K. Yabuuchi, S. Nogami, A. Hasegawa, and T. Tanaka, “Microstructural development of tungsten and tungsten–rhenium alloys due to neutron irradiation in HFIR,” J. Nucl. Mater., vol. 455, pp. 460–463, 2014.
X. Yi, M. L. Jenkins, M. Briceno, S. G. Roberts, Z. Zhou, and M. A. Kirk, “In-situ study of self-ion irradiation damage in W and W-5Re at 500°C,” Philos. Mag. A, vol. 93, no. 14, pp. 1715–1738, 2012.
X. Yi, M. L. Jenkins, K. Hattar, P. D. Edmondson, and S. G. Roberts, “Characterisation of radiation damage in W and W-based alloys from 2 MeV self-ion near-bulk implantations,” Acta Mater., vol. 92, pp. 163–177, 2015.
O. El-Atwani, K. Hattar, J. A. Hinks, G. Greaves, S. S. Harilal, and A. Hassanein, “Helium bubble formation in ultrafine and nanocrystalline tungsten under different extreme conditions,” J. Nucl. Mater., vol. 458, pp. 216–223, Mar. 2015.
O. El-Atwani, J. A. Hinks, G. Greaves, S. Gonderman, T. Qiu, M. Efe, and J. P. Allain, “In-situ TEM observation of the response of ultrafine- and nanocrystalline-grained tungsten to extreme irradiation environments.,” Sci. Rep., vol. 4, p. 4716, 2014.
H. Iwakiri, K. Yasunaga, K. Morishita, and N. Yoshida, “Microstructure evolution in tungsten during low-energy helium ion irradiation.”
H. T. Lee, A. A. Haasz, J. W. Davis, R. G. Macaulay-Newcombe, D. G. Whyte, and G. M. Wright, “Hydrogen and helium trapping in tungsten under simultaneous irradiations.”
M. Miyamoto, S. Mikami, H. Nagashima, N. Iijima, D. Nishijima, R. P. Doerner, N. Yoshida, H. Watanabe, Y. Ueda, and A. Sagara, “Systematic investigation of the formation behavior of helium bubbles in tungsten,” J. Nucl. Mater., vol. 463, pp. 333–336, Aug. 2015.
D. Nishijima, M. . Ye, N. Ohno, and S. Takamura, “Formation mechanism of bubbles and holes on tungsten surface with low-energy and high-flux helium plasma irradiation in NAGDIS-II,” J. Nucl. Mater., vol. 329–333, pp. 1029–1033, Aug. 2004.
Y. Ueda, M. Fukumoto, J. Yoshida, Y. Ohtsuka, R. Akiyoshi, H. Iwakiri, and N. Yoshida, “Simultaneous irradiation effects of hydrogen and helium ions on tungsten,” J. Nucl. Mater., vol. 386–388, pp. 725–728.
N. Yoshida, H. Iwakiri, K. Tokunaga, and T. Baba, “Impact of low energy helium irradiation on plasma facing metals.”
J. F. Ziegler, “Stopping of energetic light ions in elemental matter,” J. Appl. Phys., vol. 85, no. 3, p. 1249, 1999.
R. E. Stoller, M. B. Toloczko, G. S. Was, A. G. Certain, S. Dwaraknath, and F. A. Garner, “On the use of SRIM for computing radiation damage exposure,” Nucl. Instruments Methods Phys. Res. Sect. B Beam Interact. with Mater. Atoms, vol. 310, pp. 75–80, 2013.
A. E521, “Standard Practice for Neutron Radiation Damage Simulation by Charged-Particle,” Annu. B. ASTM Stand., vol. 12.02, no. Reapproved, pp. 1–21, 2009.
P. B. Johnson and D. J. Mazey, “Gas-bubble superlattice formation in bcc metals,” J. Nucl. Mater., vol. 218, no. 3, pp. 273–288, Mar. 1995.
F. Ferroni, X. Yi, K. Arakawa, S. P. Fitzgerald, P. D. Edmondson, and S. G. Roberts, “High temperature annealing of ion irradiated tungsten,” Acta Mater., vol. 90, pp. 380–393, 2015.
D. R. M. and X. Y. and M. A. K. and S. L. Dudarev, “Elastic trapping of dislocation loops in cascades in ion-irradiated tungsten foils,” J. Phys. Condens. Matter, vol. 26, no. 37, p. 375701, 2014.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Harrison, R.W., Amari, H., Greaves, G. et al. Effect of He-appm/DPA ratio on the damage microstructure of tungsten. MRS Advances 1, 2893–2899 (2016). https://doi.org/10.1557/adv.2016.385
Published:
Issue Date:
DOI: https://doi.org/10.1557/adv.2016.385