Abstract
Solution-processed zinc oxide (ZnO) thin-film transistors (TFTs) obtained via hydrolysis/pyrolysis of an organic precursor present an excellent technique to obtain high performance electronic devices with low manufacturing cost. In the current work, we propose the use of an alternative deposition method, based on a polymeric precursor route (known as Pechini), to obtain solution-processed ZnO compact films as the active layer of TFTs. The elimination of the organic phase and the formation of inorganic thin-films was carried out by thermal treatment at different temperatures (ranging from 200oC to 500oC) and at different times (from 5 min to 2 hours), being monitored by UV-vis and infrared (IR) optical absorption spectroscopy. It was observed that, for temperatures above 400oC and treatment times superior to 30 min, the organic phase was completely eliminated, remaining only the inorganic (metal oxide) phase. The optical bandgap of the resulting ZnO films, determined from UV-vis absorption, is about 3.4 eV. The electrical characteristics (output and transfer curves) of the obtained devices demonstrate the feasibility of Pecchini method to build solution-processed metal oxide TFTs. The results for the electrical mobility of the majority charge-carriers (electrons) and for the threshold voltage were 0.39 cm2.V-1.s-1 and 0.45 V, respectively.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
T. Kamiya, K. Nomura and H. Hosono, Sci. Technol. Adv. Mater. 11, 044305 (2010).
E. Fortunato, P. Barquinha and R. Martins, Adv. Mater. DOI: 10.1002/adma.201103228 (2011).
Y. J. Kim, S. Oh, B. S. Yang, S. J. Han, H. W. Lee, H. J. Kim, J. K. Jeong, C. S. Hwang and H. J. Kim, ACS Applied Materials & Interfaces 6, 14026–14036 (2014).
W. J. Lee, W. T. Park, S. Park, S. Sung, Y. Y. Noh and M. H. Yoon, Adv. Mater. DOI: 10.1002/adma.201502239 (2015).
C. S. Li, Y. N. Li, Y. L. Wu, B. S. Ong and R. O. Loutfy, J. Phys. D: Appl. Phys. 41, 125102 (2008).
T. O. L. Sunde, E. Garskaite, B. Otter, H. E. Fossheim, R. Saeterli, R. Holmestad, M. A. Einarsrud and T. Grande, J. Mater. Chem. 22, 15740 (2012).
S. A. Kamaruddin, K. Y. Chan, H. K. Yow, M. Z. Sahdan, H. Saim and D. Knipp, Appl. Phys. A 104, 263–268 (2011).
K. H. Kim, G. H. Kim and H. J. Kim, Phys. Status Solidi 207 1660–1663 (2010).
K. K. Banger, Y. Yamashita, K. Mori, R. L. Peterson, T. Leedham, J. Rickard and H. Sirringhaus, Nature Materials DOI: 10.1038/NMAT2914 (2010).
C. Sánchez, J. Doria, C. Paucar, M. Hernandez, A. Mósquera, J. E. Rodríguez, A. Gómez, E. Baca and O. Morán, Physica B 405, 3679–3684 (2010).
G. He, J. H. Cai, G. Ni, Mater. Chem. Phys. 110 110–114 (2008).
M. P. Pechini, US Patent 3330697 (July 11, 1967).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Amorim, C.A., Gozzi, G., Chinaglia, D.L. et al. Synthesis of Transparent Semiconducting Metal-oxides via Polymeric Precursor Route for Application in Thin-film Field-Effect Transistors. MRS Advances 1, 489–494 (2016). https://doi.org/10.1557/adv.2016.224
Published:
Issue Date:
DOI: https://doi.org/10.1557/adv.2016.224