Abstract
Hot corrosion is one of the damage mechanisms in thermal barrier coatings (TBCs) due to the molten salt effects as a result of combustion of low quality fuel. In this study, the hot corrosion behaviour of alumina–yttria stabilized zirconia particle composite coatings produced by thermal spraying for use as a thermal barriers on industrial gas turbines and in jet engines was evaluated. Plasma sprayed coatings with three different amounts of alumina- yttria stabilized zirconia particle composite have been exposed to 50 wt % Na2SO4 + 50 wt % V2O5 corrosive molten salt temperatures at 1050°C for 60 hours. Damages in the coatings surface and cross section after hot corrosion tests have been studied by using a scanning electron microscope to observe the microstructure and x-ray diffraction techniques to analyze the phase composition. The results have shown that the amount of YVO4 crystals on the surface of YSZ coatings decrease while Al2O3 increases in YSZ + Al2O3 composition, therefore, the hot corrosion resistance of TBC improves with the addition of Al2O3.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Herman, R.B., Plasma-Spray Coating, Principles and Applications, Weinheim, New York, Basel, Cambridge, Tokyo: VCH, 1996, p.100.
Matejka, D. and Benko, B., Plasma Spraying of Metallic and Ceramic Materials, New York: John Wiley & Sons, 1989, p.11.
Handbook of Thermal Spray Technology, Davis, J.R., Ed., Materials Park, OH: ASM Int., 2004, p.1.
Jones, R.L, J. Therm. Spray Technol., 1997, vol. 6, no. 1, p. 77.
Karabas, M., Bal, E., Kilic, A., and Taptik, Y, J. Aust. Ceram. Soc., 2016, vol. 52, no. 2, p. 175.
Bal, E., Karabaş, M., and Taptık, Y, Proc. 25th IRES Int. Conference, India, 2016, p.17.
Afrasiabi, A., Saremi, M., and Kobayashi, A, Mater. Sci. Eng., A, 2008, vol. 478, p. 264.
Parka, S.Y., Kima, J.H., Kimb, M.C., et al, Surf. Coat. Technol., 2005, vol. 190, p. 357.
Karaoglanli, A.C., Altuncu, E., Ozdemir, I., et al, Surf. Coat. Technol., 2011, vol. 205, p. 369.
Gurrappa, I, J. Mater. Sci. Lett., 1998, vol. 17, p. 1267.
Batista, C., Portinha, A., Ribeiro, R., et al, Surf. Coat. Technol., 2006, vol. 200, p. 6783.
Chen, Z., Wu, N.Q., Singh, J., and Mao, S.X, Thin Solid Films, 2003, vol. 443, p. 46.
Chen, H.C., Liu, Z.Y., and Chuang, Y.C, Thin Solid Films, 1992, vol. 223, p. 56.
Keyvani, A., Saremi, M., and Sohi, M.H., J. Alloys Compd., 2011, vol. 509, p. 8370.
Keyvani, A., Saremi, M., Sohi, M., et al., J. Alloys Compd., 2014, vol. 600, p. 151.
Keyvani, A., Saremi, M., and Sohi, M.H., J. Alloys Compd., 2010, vol. 506, p. 103.
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Karabaş, M., Bal, E. & Taptik, Y. Hot corrosion behaviour of plasma sprayed alumina + YSZ particle composite coating. Prot Met Phys Chem Surf 53, 859–863 (2017). https://doi.org/10.1134/S2070205117050069
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S2070205117050069