Nanostructured powders of pseudoalloys of immiscible Cu and Mo metals are prepared by highenergy ball milling (HEBM). Mechanical alloying in an Activator-2S planetary ball mill for 60 min provides a uniform distribution of refractory Mo particles in a moldable Cu matrix on submicron and nanoscopic levels. Nanostructured Cu–Mo powders are consolidated by spark plasma sintering (SPS) in a temperature range of 700–950°C at a pressure of 50 MPa for 10 min. The effect of preparation conditions on the microstructure, crystal structure, and properties (density, hardness, electric resistivity) of the nanostructured Cu–Mo pseudoalloys is studied. It is shown that a combination of HEBM and SPS provides the formation of a high-density (97%) nanostructured consolidated Cu–Mo composite with a hardness of 3.68–3.88 GPa and an electric resistivity of 6.1–6.2 μΩ cm; these parameters made the composite promising for use as an electric-contact material.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
N. K. Myshkin, V. V. Konchits, and M. Braunovic, Electrical Contacts: Fundamentals, Applications and Technology, Electrical and Computer Engineering (CRC, Boca Raton, 2006; Intellekt, Moscow, 2008).
K. Maki, Y. Ito, H. Matsunaga, and H. Mori, Scr. Mater. 68, 777 (2013).
K. Lu, Scince 328, 319 (2010).
J. R. Davis, Copper and Copper Alloys (ASM Int., Materials Park, OH, 2001).
Z. K. Fan, S. H. Liang, and P. Xiao, in (China Machine Press, Bejing, 2004), p.1.
J. F. Garay, S. C. Glade, U. Anselmi-Tamburini, et al., Appl. Phys. Lett. 85, 573 (2004).
Yu. I. Gordeev, G. M. Zeer, A. K. Zelenkova, et al., Izv. Vyssh. Uchebn. Zaved., Poroshk. Metall. Funkts. Pokryt., No. 4, 47 (2010).
A. Kumar, K. Jayasankar, M. Debata, et al., J. Alloys Compd. 647, 1040 (2015).
V. P. Martinez, C. Aguilar, J. Marin, et al., Mater. Lett. 61, 929 (2007).
C. Aguilar, D. Guzman, P. A. Rojas, et al., Mater. Chem. Phys. 128, 539 (2011).
C. Aguilar, S. Ordonez, J. Marin, et al., Mater. Sci. Eng. A 464, 288 (2007).
Shengqi Xi, Kesheng Zuo, Xiaogang Li, et al., Acta Mater. 56, 6050 (2008).
G. Q. Chen, L. T. Jiang, G. H. Wu, et al., Trans. Nonferr. Metal. Soc. 17, 580 (2007).
J. L. Johnson, Int. J. Powder Metall. 35 (8), 39 (1999).
T. W. Kirk, S. G. Caldwell, and J. J. Oakes, Adv. Powder Metall. 9, 115 (1992).
Binary Alloy Phase Diagrams, Ed. by T. B. Massalski, H. Okamoto, P. R. Subramanian, and L. Kasprzak (ASM Int., Materials Park, OH, 1990).
Q. V. Nhon, S. Odunuga, P. Bellon, et al., Acta Mater. 57, 3012 (2009).
X. Yang, S. Liang, X. Wang, et al., Int. J. Refract. Met. Hard Mater. 28, 305 (2010).
Z. F. Li, H. P. Tang, H. Y. Liu, and Y. P. Huang, Rare Met. Lett. 29, 29 (2006).
Xian-liang Zhou, Ying-hu Dong, Xiao-zhen Hua, et al., Mater. Des. 31, 1603 (2010).
C. Aguilar, F. Castro, V. Martinez, et al., Mater. Sci. Eng., A 548, 189 (2012).
N. F. Shkodich, A. S. Rogachev, S. G. Vadchenko, et al., J. Alloys Compd. 617, 39 (2014).
D. A. Romanov, O. V. Olesyuk, E. A. Budovskikh, et al., Vestn. Sib. Ind. Univ. SGIU 1 (7), 7 (2014).
Yu. S. Avraamov and A. D. Shlyapin, Alloys Based on Systems with Limited Solubility in Liquid State (Theory, Technology, Structure and Properties) (Interkontakt Nauka, Moscow, 2002) [in Russian].
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © N.F. Shkodich, A.S. Rogachev, A.S. Mukasyan, D.O. Moskovskikh, K.V. Kuskov, A.S. Schukin, N.Yu. Khomenko, 2017, published in Khimicheskaya Fizika, 2017, Vol. 36, No. 1, pp. 72–79.
Rights and permissions
About this article
Cite this article
Shkodich, N.F., Rogachev, A.S., Mukasyan, A.S. et al. Preparation of copper–molybdenum nanocrystalline pseudoalloys using a combination of mechanical activation and spark plasma sintering techniques. Russ. J. Phys. Chem. B 11, 173–179 (2017). https://doi.org/10.1134/S1990793116060269
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1990793116060269