Abstract
The glass-ceramic composites were prepared from low-softening glass CaO–B2O3–SiO2, micrometer and nanometer alumina. The influences of nano-Al2O3 on the sinterability, microstructure, dielectric property, mechanical strength, and thermal expansion of glass-alumina composites were investigated. The densification mechanism of nano-Al2O3 modified glass-alumina composites was revealed further. The results show that nano-Al2O3 effectively lowers the densification temperature of glass-alumina ≤900°C. The density gradually increases with increasing nano-Al2O3 to 15 wt %, and then decreases. Dielectric constant, dielectric loss, and flexural strength respectively versus nano-Al2O3 exhibit a similar change trend to the density. The sample with 15 wt % nano-Al2O3 sintered at 900°C could form the dense microstructure (~2.95 g/cm3) and achieve the high performance: low dielectric constant (6.13), low dielectric loss (5.2 × 10−4), low thermal expansion (4.21 × 10−6/°C), and high mechanical strength (178 MPa).
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Tummala, R.R., Ceramic and glass-ceramic packaging in the 1990s, J. Am. Ceram. Soc., 1991, vol. 74, no. 5, pp. 895–908.
Sebastian, M.T. and Jantunen, H., Low loss dielectric materials for LTCC applications: A review, Int. Mater. Rev., 2008, vol. 53, no. 2, pp. 57–90.
Knickerbocker, S.H., Kumar, A.H., and Herron, L.W., Cordierite glass-ceramics for multilayer ceramic packaging, Am. Ceram. Soc. Bull., 1993, vol. 72, no. 1, pp. 90–95.
Zhou, X., Li, B., Zhang, S., and Ning, H., Effect of Ca/Si ratio on the microstructures and properties of CaO–B2O3–SiO2 glass-ceramics, J. Mater. Sci.: Mater. Electron., 2009, vol. 20, no. 3, pp. 262–266.
Jean, J.-H. and Lin, S.C., Effect of borosilicate glass on densification and properties of borosilicate glass + TiO2 ceramic, J. Mater. Res., 1999, vol. 14, no. 4, pp. 1359–1363.
Jean, J.-H., Chang, C.-R., Chang, R.-L., and Kuan, T.-H., Effect of alumina particle size on prevention of crystal growth in low-k silica dielectric composite, Mater. Chem. Phys., 1995, vol. 40, no. 1, pp. 50–55.
Zawrah, M.F. and Hamzawy, E.M.A., Effect of cristobalite formation on sinterability, microstructure, and properties of glass-ceramic composites, Ceram. Int., 2002, vol. 28, no. 2, pp. 123–130.
Jean, J.-H. and Gupta, T.K., Liquid-phase sintering in the glass–cordierite system, J. Mater. Sci., 1992, vol. 27, no. 6, pp. 1575–1584.
Li, B., Zhang, S., Zhou, X., Wang, S., and Chen, Z., Preparation of BaTiO3-based ceramics by nanocomposite doping process, J. Mater. Sci., 2007, vol. 42, no. 6, pp. 2090–2096.
Monteiro, R.C.C. and Lima, M.M.R.A., Effect of compaction on the sintering of borosilicate glass–alumina composites, J. Eur. Ceram. Soc., 2003, vol. 23, no. 11, pp. 1813–1818.
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Li, B., Xu, Y. & Zhang, S. The size-effect of Al2O3 on the sinterability, microstructure and properties of glass-alumina composites. Glass Phys Chem 41, 503–508 (2015). https://doi.org/10.1134/S1087659615050041
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1087659615050041