Abstract
Mechanism by which nanocrystalline Bi4Ti3O12 is formed in thermal treatment of coprecipitated hydroxides was studied. It was shown that the onset of the active formation is correlated with the melting point of the surface phase based on bismuth oxide. The technological synthesis parameters of Bi4Ti3O12, at which crystallite sizes in the range 35–60 nm are provided, were determined.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Aurrivillius, B., Ark. Kemi, 1949, vol. 1, no. 1, pp. 463–471.
Keeney, L., Maity, T., Schmidt, M., et al., J. Am. Ceram. Soc., 2013, vol. 96, pp. 2339–2357.
Jiang, P.P., Zhang, X.L., Chang, P., et al., J. Appl. Phys., 2014, vol. 115, pp. 144101–144105.
Birenbaum, A.Y. and Ederer, C., Phys. Rev. B, 2014, vol. 90, pp. 214109–214112.
Long, C., Chang, Q., and Fan, H., Sci. Rep., 2017, vol. 7, no. 1, pp. 4193–4215.
Bartkowska, J.A., Dercz, J., and Michalik, D., Sol. St. Phenom., 2015, vol. 226, pp. 17–22.
Chen, K.-H., Diao, C.-C., Yang, C.-F., and Wang, B.-X., Ferroelectr., 2009, vol. 385, pp. 46–53.
Kalinkin, A.N., Kozhbakhteev, E.M., Polyakov, A.E., and Sborikov, V.M., Inorg. Mater., 2013, vol. 49, no. 10, pp. 1031–1043.
Wei, W., Dai, Y., and Huang, B., J. Phys. Chem. C, 2009, vol. 113, no. 14, pp. 5658–5663.
Cui, Z.M., Yang, H., Zhang, M., et al., Mater. Trans., 2016, vol. 57, no. 10, pp. 1766–1770.
Kargin, Yu.F., Ivicheva, S.N., and Volkov, V.V., Russ. J. Inorg. Chem., 2015, vol. 60, no. 5, pp. 619–625.
Esquivel-Elizondo, J.R., Hinojosa, B.B., and Nino, J.C., Chem. Mater., 2011, vol. 23, pp. 4965–4974.
Morozov, M.I., Mezentseva, L.P., and Gusarov, V.V., Russ. J. Gen. Chem., 2002, vol. 72, no. 7, pp. 1110–1113.
Lomanova, N.A., Morozov, M.I., Ugol kov, V.L., and Gusarov, V.V., Inorg. Mater., 2006, vol. 42, no. 2, pp. 189–195.
Navarro-Rojero, M.G., Romero, J.J., Rubio-Marcos, F., and Fernandez, J.F., Ceram. Int., 2010, vol. 36, pp. 1319–1325.
Lomanova, N.A., Semenov, V.G., Panchuk, V.V., and Gusarov, V.V., J. Alloys Compd., 2012, vol. 528, pp. 103–108.
Lomanova, N.A., Ugolkov, V.L., Panchuk, V.V., and Semenov, V.G., Russ. J. Gen. Chem., 2017, vol. 87, pp. 365–372.
Gumiel, C., Bernardo, M.S., Villanueva, P.G., et al., J. Mater. Sci., 2017, vol. 52, pp. 4042–4051.
Wong, Y.J, Hassan, J., Chen, S.K., and Ismail, I., J. Alloys Compd., 2017, vol. 723, pp. 567–579.
Stojanovic, B.D., Paiva-Santos, C.O., Cilense, M., et al., Mater. Res. Bull., 2008, vol. 43, pp. 1743–1753.
Gusarov, V.V., Russ. J. Gen. Chem., 1997, vol. 67, no. 12, pp. 1846–1851.
Xu, G., Yang, Y., Bai, H., et al., Cryst. Eng. Comm., 2016, vol. 18, no. 13, pp. 2268–2274.
Gu, H., Hu, Z., Hu, Y., et al., Colloids Surf. A, 2008, vol. 315, nos. 1–3, pp. 294–298.
Kana, Y., Wang, P., Li, Y., et al., Mater. Lett., 2002, vol. 56, pp. 910–914.
Lisoni,J.G., Millan, P., Vila, E., et al., Chem. Mater., 2001, vol. 13, pp. 2084–2091.
Zhang, F., Karaki, T., and Adachi, M., Jap. J. Appl. Phys., 2006, vol. 45, no. 9B, pp. 7385–7388.
Chen Zhihui, Qiu Junfu, Liu Cheng, et al., Ceram. Int., 2010, vol. 36, pp. 241–244.
Kidcho, T., Malfatti, L., Marongiu, D., et al., J. Am. Ceram. Soc., 2010, vol. 93, no. 9, pp. 2897–2902.
Ma, C.H., Lin, X., Wang, L., and Yan, Y.S., Adv. Mater. Res., 2014, vol. 997, pp. 359–362.
Lomanova, N.A. and Gusarov, V.V., Russ. J. Gen. Chem., 2013, vol. 83, no. 12, pp. 2251–2253.
Kato, T., Jap. J. Appl. Phys., 1983, vol. 22, pp. 47–49.
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © N.A. Lomanova, M.V. Tomkovich, V.L. Ugolkov, V.V. Gusarov, 2017, published in Zhurnal Prikladnoi Khimii, 2017, Vol. 90, No. 6, pp. 673−679.
Rights and permissions
About this article
Cite this article
Lomanova, N.A., Tomkovich, M.V., Ugolkov, V.L. et al. Formation and thermal properties of nanocrystalline Bi4Ti3O12. Russ J Appl Chem 90, 831–837 (2017). https://doi.org/10.1134/S1070427217060015
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1070427217060015