Abstract
We present a new digitally controlled, optically induced electrochemical deposition (OED) method for fabricating silver nanostructures. Projected light patterns were used to induce an electrochemical reaction in a specialized sandwich-like microfluidic device composed of one indium tin oxide (ITO) glass electrode and an optically sensitive-layer-covered ITO electrode. Silver polyhedral nanoparticles, triangular and hexagonal nanoplates and nanobelts were controllably synthesized in specific positions at which projected light was illuminated. The silver nanobelts had rectangular cross-sections with an average width of 300 nm and an average thickness of 100 nm. By controlling the applied voltage, frequency and time, different silver nanostructure morphologies were obtained. Based on the classic electric double-layer theory, a dynamic process of reduction and crystallization can be described in terms of three phases. Because it is template- and surfactant-free, the digitally controlled OED method facilitates the easy, low cost, efficient and flexible synthesis of functional silver nanostructures, especially quasi-one-dimensional nanobelts.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Compared with their bulk counterparts, nanostructured materials (NSMs) are fascinating topics of research because of their size-dependent novel physical, chemical, optical and magnetic properties1. The dimensionality of NSMs and its influence on their applications have been fully studied2, especially one-dimensional (1D) nanostructures3,4. Besides dimensionality, morphology is another important factor that influences the unique properties of NSMs5,6. Metallic nanostructures with fine size- and shape-controllability show great potential applications in electronic nanodevices, biological diagnostics and surface-enhanced Raman scattering (SERS) detection7,8,9. For example, the controllability of the dimensions and aspect ratios of one-dimensional silver nanostructures such as nanowires and nanorods has been extensively studied for applications in flexible conductors and sensors10,11,12,13. Nanobelts, or nanoribbons, as quasi-one-dimensional nanostructures, were first proposed for semiconducting oxides14 and have attracted extensive attention for those substrates15 as well as various metal materials16,17 because of their well-defined geometrical morphologies with rectangular cross-sections, potential applications in bio-nanodevices18,19 and better inherent high-temperature stability20.
To date, a wealth of methods is available for generating silver nanobelts, including template-directed methods, seed-mediated methods, galvanic-cell reaction approaches and electrochemical reduction methods. Liu et al. presented an electrochemical silver mirror reaction in anodic aluminum oxide (AAO) nanochannel templates to grow silver nanobelts with dimensions that depended on the AAO template21. It has been demonstrated that large-scale ultralong silver nanobelts can be synthesized at the interface between dibutyl sebacate (DBS) and silver nitrate solutions, which serves as a soft template, via a chemical electro-deposition technique22. By using biomass-derived monolithic activated carbon (MAC) as a template, Zhao et al. reported a galvanic-cell reaction method to obtain silver nanobelts with widths of 1.09 μm and a thickness of 0.29 μm, in high yield23. Recently, they improved the method by forming metallic particles on the MAC surface as growth initiators prior to nanobelt growth and harvested silver nanobelts with widths as low as tens of nanometers and thicknesses of ca. 13 nm24. Zhu et al. reported an electrochemically modulated reduction method using a sacrificial cathode electrode with a nanochannel template to fabricate silver nanobelt-bundle arrays that were 25 nm thick, 300 nm wide and 50 μm long25. These methods always require templates, or complex surfactants as capping agents, to guide the anisotropic quasi-1D nanobelt growth, which makes the fabrication process complex and inflexible. Additionally, external templates and agents have the potential to introduce impurities and contaminants into the final product. In this paper, we present a template- and surfactant-free method for producing different silver nanostructure morphologies, especially silver nanobelts with rectangular cross-sections, via optically induced electrochemical deposition (OED) in a microfluidic device. By virtue of an optically induced electrokinetics (OEK) platform26,27 previously developed by our group, we use programmable light patterns to produce controlled and localized electric fields in a photosensitive microfluidic chip, thus inducing the local electrochemical deposition of silver nanostructures. This new method has several advantages over traditional electrochemical reduction approaches: it offers a significant reduction in fabrication time (in terms of several seconds), is reagent-free (without the need for extra reductant or surfactant) and is template-free (with no lithographic process or complicated pre-elaboration). We have studied the parameters to controllably tune the final morphology of the silver nanostructures. We believe that this simple approach provides new opportunities to flexibly produce structured and functional nanomaterials for applications in fields such as photonics, biology, electronics and other interdisciplinary areas.
Methods
Materials and OED system
Silver nitrate (AgNO3, >99.8%; AR), purchased from Sigma Aldrich, was dissolved in Millipore water (resistivity, 18.2 MΩ, Millipore Systems) to prepare sample precursor solutions at concentrations of 10, 50, 100 and 200 mmol/L. The solutions were degassed in an ultrasonic cleaner at 40 kHz for 20 min (KUDOS, SK5210LHC) and further filtered through a 0.22 μm Millipore filter to remove undissolved solute. Figure 1 shows a schematic diagram of the experimental OED system, which includes three modules, as described in our earlier papers26,27. In brief, we use a computer equipped with graphics software to generate programmable light patterns on demand, which are projected on the sandwiched OEK microfluidic chip by an LCD projector (VPL-F400X, Sony, Japan) and an objective (CF Plan 50 X/0.55 EPI ELWD, Nikon, Japan). As shown in the enlarged circular area (Fig. 1), the sandwich-like OEK microfluidic chip, assembled from a top layer of indium tin oxide (ITO) glass and a bottom layer of ITO glass coated with a 1 μm film of hydrogenated amorphous silicon (α-Si:H) by the plasma-enhanced chemical vapor deposition (PECVD) method, is separated by a 60 μm spacer to form a reaction chamber. The α-Si:H film is a photoconductive layer which has a low dark conductivity of 10−11 S/m and an augmented illuminated conductivity of 10−5 S/m due to its photo-activated electron-hole pairs28. The entire microfluidic module is mounted on a three-dimensional adjustable platform for automatic motion control, monitored by a charge-coupled device camera (CCD, DaHeng Image DH-SV1411FC, China) and the alternating current (AC) voltage is applied by a signal generator (Agilent 33522A, USA).
Preparation and characterization of silver nanostructures
The formulated silver precursors with different concentrations were injected into the OEK chip and powered by a sinusoidal AC voltage with a frequency and magnitude in the range of 1 to 100 kHz and 2 to 15 Vpp, respectively. After the fabrication process, the prepared silver nanostructures were placed on the substrate, gently rinsed with anhydrous ethanol and air dried at room temperature. Morphology observation was performed on a scanning electron microscope (SEM, Zeiss EVO MA, Germany). Dimensional data were characterized and collected via atomic force microscopy (AFM, Bruker Dimensional Icon, USA).
Results and Discussion
Virtual electrode-solution interface process
In an electrochemical reduction system, the kinetics at the interface between the electrode and bulk solution plays a pivotal role in the formation of the final products29,30. In our OED system, at the interface between the illuminated solid α-Si:H substrate (namely, the virtual electrode) and bulk solution, a thin electric double layer (EDL, typically several nanometers) provides the voltage potential, reactive species and environment for the overall reaction. Figure 2(a) shows a simplified equivalent circuit model of the OEK chip, where Ca and Ra denote the capacitance and resistance of the α-Si:H layer, CL and RL denote the capacitance and resistance of the bulk solution and CEDL and REDL indicate the equivalent capacitance and resistance of the EDL between the solid electrode and bulk solution, respectively, which vary depending on the applied voltage. The OED process described in Fig. 2(b) can be divided into three phases. Phase I represents the reduction of silver ions (Ag(I)) to elemental silver atoms (Ag(0)). This stage includes the mass transfer of Ag(I) from the bulk solution to the electrode-solution interface and the electrochemical reduction of Ag(I) into Ag(0) at the EDL layer close to the virtual electrode under the effects of dynamic electron transfer. Phase II encompasses the nucleation and growth of the reduced silver atoms to form nuclei, seeds and primary silver crystal structures. These silver atoms are transferred to the illuminated substrate and interact with each other, aggregating into small clusters. The clusters initially formed by the random collisions of the reduced silver atoms are too small to be stable and are re-dissolved into the precursor solution. With continuous reduction, oversaturation occurs and at a certain point defined by the nucleation energy barrier, the clusters grow beyond a critical size to form stable nuclei. These nuclei will serve as crystallization seeds for subsequent deposition. We are able to control the external applied voltage parameters to tune the reduction speed and kinetically control the nucleation process. Phase III depicts the crystal growth stage, in which the final silver nanostructures are formed. The growth process is a complex thermodynamically and kinetically controlled process that cannot be clearly divided31. When the reduction speed is fast, nuclei are formed in large quantity, which suppresses the continuing growth of the already formed nucleation sites. As a result, the final silver deposition products are homogenous small nanoparticles. When the reduction speed is relatively slow, the subsequent reduced silver atoms are deposited on the previously formed seeds (nucleation sites) and crystal growth proceeds, which is energetically favorable. The primary crystal seeds included silver nanospheres, polyhedral nanoparticles and triangular or hexagonal nanoplates. As the seeding and growth continued, the final nanostructures included larger polyhedra, nanoplates and nanobelts.
Optimal parameters for synthesis of silver nanostructures
We examined the influence of the external parameters on silver deposition in the OED system. The concentration of the silver nitrate precursor solution was important for the formation of silver nanostructures. For the concentration series 10, 50, 100 and 200 mmol/L, larger precursor concentrations were found to increase the deposition speed, which is favorable for silver electrode deposition, as described in our previous paper27. On the other hand, the synthesis of silver nanobelts requires anisotropic control over the deposition process, which needs a relatively slow deposition speed, so the medium concentration of 50 mmol/L was selected for further experiments.
As the voltage was increased from 2 to 15 Vpp, the silver reduction speed was increased. When the voltage was below 2 Vpp, the current density in the EDL near the virtual electrode was insufficient for reduction of the Ag(I) into Ag(0). In contrast, when the voltage exceeded 15 Vpp, the stronger voltage potential usually damaged the α-Si:H layer, which should preferably be avoided. The voltage range of 5 to 10 Vpp was selected as favorable.
The frequency of the applied voltage is a key factor in the control of the final product’s nano-structural morphology, because it greatly influences the properties of the EDL. As shown in Fig. 3, we investigated the influence of the frequency on the deposition sites of the silver nanostructures. When the voltage frequency is below 10 kHz, the reduced silver nanostructures seem to be repelled from the grid-shaped illuminated virtual electrode area and settle instead at the boundaries of the illuminated pattern. When the voltage frequency exceeds 10 kHz, deposition occurs mainly in the illuminated areas, in accordance with the defined virtual electrode. From our experimental results, a frequency between 20 and 50 kHz should be optimal for silver electrode deposition and will reproduce the designed light pattern with high fidelity. When the frequency is increased above 50 kHz but below 100 kHz, the silver deposition is somewhat sparse due to the reduced deposition cycle. In this range of frequency, the depositions tend to form anisotropic nanostructures such as thin silver nanosheets, triangular nanoplates and nanobelts.
The deposition time was another important factor. The deposition thickness of the silver structures is positively correlated to the deposition time, at the proper frequency and amplitude of the applied voltage27. Here, we focused on the fabrication of silver nanobelts at a frequency of 50 kHz and amplitude of 5 Vpp. Figure 4 shows a sequence of silver deposition images recorded at times from 1 to 13 s by SEM. Over time, the continuously reduced Ag(0) is adsorbed on the active sites of already formed primary seeds, crystallizes and grows into tiny silver fragments and then, thin silver sheets. These freshly formed silver thin sheets are potential sites for the subsequent growth of silver nanobelts, which can be found in Fig. 4(e–m).
Morphologically controlled synthesis of silver nanostructures
Compared to traditional electrochemical systems, our OED system is sufficiently flexible and programmable for producing optically defined diverse virtual electrodes to control the growth of silver nanostructures. Figure 5 shows silver nanostructures deposited in different electrode configurations, which were defined by optical patterns. The large illuminated area of a solid circle in Fig. 5(a) resulted in massive polyhedral nanoparticles, whereas the relatively focused and reduced areas in Fig. 5(c) obtained larger polyhedral nanoparticles including octahedra and stacked hexagonal nanoplates under a voltage amplitude of 5 Vpp. Figure 5(b,d) reveal denser and larger structures assembled from plate-like silver polyhedra under augmented voltage amplitudes of 10 Vpp. Larger light pattern areas provide correspondingly larger virtual electrode areas which simultaneously increase the quantity of reduced silver atoms at the same solution concentration and thus favor homogenous nucleation and the synthesis of small nanoparticles. With decreased virtual electrode areas triggered by focused light patterns, the deposited silver nanostructures tend to ripen and form larger nanostructures, such as silver octahedral nanoparticles and hexagonal nanoplates.
To obtain silver nanobelts, we set the applied voltage at 50 kHz and 5 Vpp, which is favorable for the synthesis of silver anisotropic nanostructures rather than compact silver electrodes. By kinetically controlling the deposition process, the reduced silver atoms were deposited on already formed seeds in phase II and crystallized into primary polyhedral nanostructures, rather than forming fresh nucleation sites and resulting in massive silver nanoparticles. Figure 6(a) displays a grid-shaped silver deposit decorated with interconnected silver nanobelts and Fig. 6(b) presents an array of silver nanobelts stemming from dot-shaped silver deposits, which form a functional silver nanobelt network and probe array that could have potential applications in biosensors and nanodevices. These results show that silver nanobelts with different configurations can be obtained by simply tuning the projected light pattern, which is a flexible and time-saving approach. Figure 6(c) shows silver nanobelts as long as 300 μm that were fabricated by our method. Figure 6(d,e) show the details of the silver nanobelts. Figure 6(d1,d2) show close-ups of the stem and terminal tip of the silver nanobelt in Fig. 6(d), which demonstrate that the silver nanobelts originate from a sheet-like structure and end with a tip of 120°. Figure 6(e) shows a curled silver nanobelt, confirming its flexibility. Figure 6(f–h) show the supposed growth process for the silver nanobelts. The silver nanobelts are formed from 2D silver nanosheets in accord with a specific crystallographic orientation. Some silver nanobelts were found to alter their growth direction under dislocation fluctuations, forming silver nanobelts with zigzag shapes and a constant angle of 120°. This phenomenon implies that the silver nanobelts originate from the primary hexagonal nanoplates and grow along two adjacent edges to form the anisotropic belt-like structures. The AFM images of two crossed silver nanobelts in Fig. 6(i,j) show a smooth surface and a rectangular cross section, with a width of ca. 500 nm and thickness of ca. 50 nm.
Conclusion
In summary, we have presented a flexible OED system for the controllable synthesis of silver nanostructures with various morphologies and configurations. By fine-tuning the applied voltage and deposition time, silver polyhedral nanoparticles, hexagonal silver nanoplates and especially, silver nanobelts, were synthesized. The fabrication process is template-free and agentless. The obtained silver nanobelts were rectangular in cross-section with an average width of 300 nm, average thickness of 100 nm and length of about 300 μm. A possible theory of silver nanobelt formation process is also discussed in this paper in terms of growth along two neighboring sides of a primary hexagonal silver nanoplate. We believe that the OED system described in this paper has the potential for use in the deposition of other metals as well as nanostructure synthesis with diverse functional configurations.
Additional Information
How to cite this article: Li, P. et al. Silver nanostructures synthesis via optically induced electrochemical deposition. Sci. Rep. 6, 28035; doi: 10.1038/srep28035 (2016).
References
Moriarty, P. Nanostructured materials. Rep Prog Phys 64, 297–381 (2001).
Tiwari, J. N., Tiwari, R. N. & Kim, K. S. Zero-dimensional, one-dimensional, two-dimensional and three-dimensional nanostructured materials for advanced electrochemical energy devices. Prog Mater Sci 57, 724–803 (2012).
Kuchibhatla, S. V. N. T., Karakoti, A. S., Bera, D. & Seal, S. One dimensional nanostructured materials. Prog Mater Sci 52, 699–913 (2007).
Xia, Y. N. et al. One-dimensional nanostructures: Synthesis, characterization and applications. Adv Mater 15, 353–389 (2003).
Tian, G. et al. 3D hierarchical flower-like TiO2 nanostructure: morphology control and its photocatalytic property. CrystEngComm 13, 2994 (2011).
Zhai, T. et al. Morphology-dependent stimulated emission and field emission of ordered CdS nanostructure arrays. ACS Nano 3, 949–959 (2009).
Xia, Y. N. & Halas, N. J. Shape-controlled synthesis and surface plasmonic properties of metallic nanostructures. Mrs Bull 30, 338–344 (2005).
Santoro, G. et al. Silver substrates for surface enhanced Raman scattering: Correlation between nanostructure and Raman scattering enhancement. Appl Phys Lett 104, 243107 (2014).
Chen, J., Wiley, B. J. & Xia, Y. One-dimensional nanostructures of metals: large-scale synthesis and some potential applications. Langmuir 23, 4120–4129 (2007).
Langley, D. et al. Flexible transparent conductive materials based on silver nanowire networks: a review. Nanotechnology 24, 452001 (2013).
Zhu, S. et al. Transferable self-welding silver nanowire network as high performance transparent flexible electrode. Nanotechnology 24, 335202 (2013).
He, B., Morrow, T. J. & Keating, C. D. Nanowire sensors for multiplexed detection of biomolecules. Curr Opin Chem Biol 12, 522–528 (2008).
Patolsky, F. & Lieber, C. M. Nanowire nanosensors. Materials Today 8, 20–28 (2005).
Pan, Z. W., Dai, Z. R. & Wang, Z. L. Nanobelts of semiconducting oxides. Science 291, 1947–1949 (2001).
Sun, T. J., Qiu, J. S. & Liang, C. H. Controllable fabrication and photocatalytic activity of ZnO nanobelt arrays. J Phys Chem C 112, 715–721 (2008).
Xu, Y. et al. High-yield synthesis of gold nanoribbons by using binary surfactants. J Mater Chem C 3, 1447–1451 (2015).
Kubo, W., Hayakawa, H., Miyoshi, K. & Fujikawa, S. Size-Controlled Simple Fabrication of Free-Standing, Ultralong Metal Nanobelt Array. Journal of Nanoscience and Nanotechnology 11, 131–137 (2011).
Wang, Z. L. Functional oxide nanobelts: materials, properties and potential applications in nanosystems and biotechnology. Annu Rev Phys Chem 55, 159–196 (2004).
Qi, D. et al. Highly stretchable gold nanobelts with sinusoidal structures for recording electrocorticograms. Adv Mater 27, 3145–3151 (2015).
Marzbanrad, E., Rivers, G., Peng, P., Zhao, B. & Zhou, N. Y. How morphology and surface crystal texture affect thermal stability of a metallic nanoparticle: the case of silver nanobelts and pentagonal silver nanowires. Phys Chem Chem Phys 17, 315–324 (2015).
Liu, L., Yoo, S.-H., Lee, S. A. & Park, S. Electrochemical Growth of Silver Nanobelts in Cylindrical Alumina Nanochannels. Crystal Growth & Design 11, 3731–3734 (2011).
Liu, B., Luo, W. & Zhao, X. A facile synthesis of ordered ultralong silver nanobelts. Materials Research Bulletin 44, 682–687 (2009).
Zhao, H. et al. Green “planting” nanostructured single crystal silver. Sci Rep 3, 1511 (2013).
Zhao, H. et al. Tunable growth of silver nanobelts on monolithic activated carbon with size-dependent plasmonic response. Sci Rep 5, 13587 (2015).
Zhu, J. W. & Xue, D. F. Crystallography and interfacial kinetic controlled ultra-uniform single crystal silver nanobelts and their optical properties. Crystengcomm 16, 642–648 (2014).
Liu, N. et al. Rapid Fabrication of Nanomaterial Electrodes Using Digitally Controlled Electrokinetics. Ieee T Nanotechnol 13, 245–253 (2014).
Liu, N. et al. Optically-controlled digital electrodeposition of thin-film metals for fabrication of nano-devices. Opt Mater Express 5, 838–848 (2015).
Staebler, D. L. & Wronski, C. R. Optically Induced Conductivity Changes in Discharge-Produced Hydrogenated Amorphous-Silicon. J Appl Phys 51, 3262–3268 (1980).
Fang, Y. H. & Liu, Z. P. Electrochemical reactions at the electrode/solution interface: Theory and applications to water electrolysis and oxygen reduction. Sci China Chem 53, 543–552 (2010).
Trasatti, S. Physical, Chemical and Structural Aspects of the Electrode Solution Interface. Electrochim Acta 28, 1083–1093 (1983).
Wang, Y., He, J., Liu, C., Chong, W. H. & Chen, H. Thermodynamics versus Kinetics in Nanosynthesis. Angewandte Chemie 54, 2022–2051 (2014).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (Project No. 61475183, 61433017), the NSFC/RGC Joint Research Scheme (Project No. 51461165501 and N_CityU132/14), CityU Internal Grant (Project No. 7004073) and the CAS-FEA International Partnership Program for Creative Research Teams.
Author information
Authors and Affiliations
Contributions
W.J.L. and P.L. proposed the basic idea. W.J.L., H.Y., L.L., G.L. and Y.W. supervised the project. P.L. designed and carried out the experiments and analyzed the data. F.W. assisted in the experimental processes. P.L. and N.L. participated in the discussion and writing of the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Li, P., Liu, N., Yu, H. et al. Silver nanostructures synthesis via optically induced electrochemical deposition. Sci Rep 6, 28035 (2016). https://doi.org/10.1038/srep28035
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep28035
- Springer Nature Limited
This article is cited by
-
Recent advances in optically induced di-electrophoresis and its biomedical applications
Biomedical Microdevices (2022)
-
Design and Fabrication of a Disposable Nanoactuator Using 3D Printing
International Journal of Precision Engineering and Manufacturing (2021)
-
Thermometry of photosensitive and optically induced electrokinetics chips
Microsystems & Nanoengineering (2018)
-
Fabrication of periodically micropatterned magnetite nanoparticles by laser-interference-controlled electrodeposition
Journal of Materials Science (2018)