Abstract
In this work, zinc chromite (ZnCr2O4) nanostructures have been synthesized through co-precipitation method. The effect of various parameters such as alkaline agent, pH value and capping agent type was investigated on purity, particle size and morphology of samples. It was found that particle size and morphology of the products could be greatly influenced via these parameters. The synthesized products were characterized by field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), fourier transform infrared (FT-IR) spectra, X-ray energy dispersive spectroscopy (EDS), photoluminescence (PL) spectroscopy, diffuse reflectance spectroscopy (DRS) and vibrating sample magnetometry (VSM). The superhydrophilicity of the calcined oxides was investigated by wetting experiments and a sessile drop technique which carried out at room temperature in air to determine the surface and interfacial interactions. Furthermore, the photocatalytic activity of ZnCr2O4 nanoparticles was confirmed by degradation of anionic dyes such as Eosin-Y and phenol red under UV light irradiation. The obtained ZnCr2O4 nanoparticles exhibit a paramagnetic behavior although bulk ZnCr2O4 is antiferromagnetic, this change in magnetic property can be ascribed to finite size effects.
Similar content being viewed by others
Introduction
Spinel compounds have a general formula AB2O4, in which the A-site is tetrahedrally coordinated and generally occupied by divalent cations (Mg, Mn, Ni and Zn) and the B-site is octahedrally coordinated and occupied by trivalent cations (Al, Cr and Fe). In solid-state science, oxides with spinel structures are some of the most studied compounds due to their wide range of applications. Spinels such as ZnCr2O4 containing transition metal ions can act as the efficient catalysts in the number of heterogeneous chemical processes such as carbon monoxide (CO) oxidation1, catalytic combustion of hydrocarbons2, reduction of several organic molecules3, sensing properties4 and effective photocatalysts5,6,7,8. The nanoparticles ZnCr2O4 have been synthesized by various methods including mechanical activation9, high-temperature solid-state reaction10, microemulsion method11, solution method12 and spray pyrolysis13. The use of low temperature chemical methods of synthesis has been a promising direction in the improvement of the technology for producing compounds with spinel structure.
Several chromites have been synthesized in nanocrystal form so far. ZnCr2O4 crystallizes well when the sintering temperature is above 500 °C14 and the product formed at 350 °C is in amorphous phase. Pure MgCr2O4 has been reported to have formed when an appropriate mixture of pure oxides is pressed into bars and sintered for several hours in an electric furnace at 1400 °C15. Some chromites, such as MgCr2O4, CuCr2O4, NiCr2O4, ZnCr2O4 and CoCr2O4, have been prepared using co-precipitation method, by the process of re-crystallization from pyridine followed by ignition in the temperature range of 700–1200 °C16. Nanometer-sized particles having perovskite structure were reported to be formed when partial substitution by alkaline rare earth metals was carried out in lanthanum chromites by urea combustion method and this was followed by calcination at 900 °C17.
In this paper, we describe a precipitation method to synthesis ZnCr2O4 nanostructures with using Zn(NO3)2. 6H2O and CrCl3. 6H2O as starting materials. The aim of this work is to synthesize ZnCr2O4 nanostructures via a co-precipitation method and to investigate the effect of various parameters on their morphology. The photocatalytic activity of ZnCr2O4 nanoparticles (sample 4) was evaluated by the degradation of anionic dyes such as Eosin-Y and phenol red as water pollutants. Also, the photocatalytic degradation of anionic dyes such as Eosin-Y and phenol red using spinel ZnCr2O4 under UV irradiation at pH = 2–3 has been also examined.
Results and Discussion
To investigate the role of different parameters such as alkaline agent, pH value and capping agent type on the morphology, purity and particle size of the products, the various tests were done. All of the preparation conditions of the synthesized samples are presented in Table 1.
Recently, the role of capping agents in the morphology and size of nanomaterials has been studied, widely18. Hence, the different types of capping agent, including of poly vinyl pyrrolidone (PVP), cetyl trimethylammonium bromide (CTAB) and sodium dodecylbenzenesulfonate (SDBS) as polymeric and inert, cationic and anionic capping agents were applied, respectively.
Figure 1 shows the products synthesized in the absence and presence of various capping agents. In Fig. 1a, the 150 nm-sized agglomerated particles are shown that were related to blank sample (without capping agent), it is clear that aggregated nanostructures are formed in the absence of capping agent. According to the Fig. 1a, the particles coalesce and turn into bulk structures. Figure 1 (b–d) depicts the FESEM images of the sample 2, 3 and 4 synthesized by PVP, CTAB and SDBS, respectively. As shown in Fig. 1b,d, the morphology of these samples are particles with average sizes about 70 nm. When PVP was used as capping agent, cubic structures are shown, additionally. Agglomerated and impacted particles obtained by using CTAB as a cationic capping agent. The formation of dense structures in Fig. 1c (sample 3) is due to its cationic head group, CTAB easily interact with free oxygen groups on the surface of nanoparticles and agglomeration of nanoparticles increases. So, SDBS as an anionic capping agent was chosen for achieving the desired product due to its homogeneity that is higher than the others.
The crystalline structures of the ZnCr2O4 nanoparticles were confirmed by XRD. Figure 2 (a–d) shows the XRD patterns of the sample 1–4, respectively. As shown in this figure, by utilizing of various capping agents can be achieved to ZnCr2O4 with different reference codes. All of peaks in these patterns (Fig. 2 (a–d)) can be indexed to cubic phase zinc chromium oxide with space group of Fd/3m (JCPDS: 73–1962, for sample 2 and 3) and (JCPDS: 22-1107 for sample 1 and 4). The crystallite sizes of the samples 1–4 were calculated by Scherrer equation19 and estimated about 78, 55, 28, 13 nm, respectively. According to this figure (Fig. 2d), in the presence of SDBS as capping agent (sample No. 4), the crystallinity of the obtained ZnCr2O4 is increased while in the absence of SDBS the crystallinity and purity are decreased.
ZnCr2O4 is a spinel with cubic phase, space group of Fd/3m and space group number 227. In this work, the all of the peaks in XRD patterns of samples can be indexed to cubic phase zinc chromium oxide but JCPDSs in these patterns are not the same. The various JCPDSs in the same phases of a compound are due to grain orientations of structures, for example: the principle ZnCr2O4 grain orientations are: (311), (200), (422), (440) for JCPDS = = 22–1107; (311), (220) for JCPDS = 73–1962; and (220), (311), (511), (440) for JCPDS = 01–1123. Furthermore, the crystallographic parameters in various JCPDSs aren’t same, so in these patterns can be seen the different crystallographic parameters such as: a = 8.3257 in JCPDS = 22–1107; a = 8.28 in JCPDS = 73–1962; and a = 8.3200 in JCPDS = 01–1123 (cubic phase has a = b = c and α = β = γ = 90°). By considering above explanations, the various JCPDSs in same phases of a compound can be used to determine grain orientations of structures.
To investigate the effect of alkaline agents on morphology of the products, SEM images of ZnCr2O4 were taken and shown in Fig. 3 (a–d). As shown in this figure, when sodium hydroxide (NaOH) was used as alkaline agent, the 70 nm-sized nanoparticles were obtained that smaller than the other alkaline agent (Fig. 3a). The size of particle obtained by using ammonia (NH3) (Fig. 3b), ethylene diamine (en) (Fig. 3c) and propylene diamine (pn) (Fig. 3d) are same and about 100 nm. When NaOH was used as an alkaline agent, pH of the reaction environment increases instantly and its reaction takes place with precursor rapidly, so, the nucleation process happens quicker than the growth step and fine particles are produced. The reactivity of NH3, en and pn is lower than NaOH, hence, the growth process was preferred to nucleation process and were produced larger particles.
Figure 4 (a–c) shows the XRD patterns of the samples synthesized in presence NH3, en and pn, respectively. Figure 4a depicts the XRD pattern of sample 5, in this pattern is shown the mixture of ZnO (JCPDS card No. 80-0075), ZnCr2O4 (JCPDS card No. 01–1123; JCPDS card No. 73–1962) and unknown phases. By changing alkaline agent from NH3 (sample 5) to en (sample 6), all diffraction peaks (Fig. 4b) can be indexed to a pure cubic phase ZnCr2O4 (JCPDS card No. 22–1107) and ZnO was removed. Figure 4c is the pattern of the ZnCr2O4 in the presence of pn as an alkaline agent (sample 7). XRD pattern of sample 7 shows a pure cubic structure with space group and JCPDS card No. 73–1962, no characteristic peaks of other phases are observed. By comparing the XRD pattern of sample 4 to sample 5, 6 and 7 can be found that sample 4 is well crystallized and by considering their SEM images (Fig. 3) can be chosen NaOH as a desired alkaline agent for synthesis of pure ZnCr2O4 nanoparticles. The crystallite sizes of the samples 4, 5, 6 and 7 were calculated by Scherrer equation and estimated about 13, 33, 30, 27 nm, respectively.
The effect of the pH value on the morphology and purity of the products has been investigated. A series of experiments were done by decreasing the pH value from 14 to 11 and 7. Figure 5 (a–c) demonstrates the morphology of sample 4 (pH = 14), 8 (pH = 11) and 9 (pH = 7), respectively. By considering SEM images in Fig. 5 (a–c) can be observed that increasing pH led to the creation of smaller particles. It is obvious that the best nanoparticles are produced at pH = 14. Increase pH of solution can enhance nanoparticles surface charge and the electrostatic repulsive force. So, the agglomeration is decreased and the size of particles is being smaller. Surface charge and hydrodynamic diameter are two important properties of nanoparticle dispersions. The point where the surface charge density equals zero is defined as point of zero charge (PZC), while the point where zeta potential equals zero is defined as the isoelectric point (IEP)20,21. When a nanoparticle is dispersed in an aqueous solution, surface ionization and the adsorption of cations or anions result in the generation of the surface charge and an electric potential will be developed between the particle surface and the bulk of dispersion medium22,23.
The surface of nanoparticles dispersed in water is generally covered by the hydroxyl group as shown in Eq. 1. The surface charge of nanoparticles is a function of solution pH, which is affected by the reactions that occur on the particle surface as shown in Eqs. 2 and 3:
The pH at which the surface of nanoparticles is neutral is the point of zero charge or isoelectric point. If no specific adsorption of the ions presented in the solution takes place on the particle surface, the pH at PZC and IEP would be the same. When pH is less than pHPZC (pHIEP), Eq. 2 results in creation of the positive surface charge and positive zeta potential. When pH is larger than pHPZC (pHIEP), Eq. 3 results in creation of the negative surface charge and negative zeta potential22,23,24. The dispersion hydrodynamic diameter is controlled by nanoparticle agglomeration in the aqueous system.
In the classical Derjaguin–Landau–Verwey– Overbeek (DLVO) theory, the agglomeration of nanoparticles is determined by the sum of the repulsive electrostatic force (the interaction of electrical double layer surrounding each nanoparticle) and the attractive van der Walls force25,26. Increase in particle surface charge (zeta potential) can enhance the electrostatic repulsive force, suppress the agglomeration and subsequently reduce dispersion hydrodynamic size27. The effects of solution pH and ionic strength (IS) on nanoparticles dispersion properties are presented first, followed by discussion about the pH effect of particle size of ZnCr2O4 nanostructures.
Figure 6 is the XRD patterns of the sample 8 and 9 which obtained at pH 11 and 7. The product obtained at pH = 11 (sample 8) is cubic phase ZnCr2O4 (JCPDS card No. 73–1962), no significant diffractions of other phases can be found in the figure (Fig. 6a). A mixture of ZnCr2O4 (JCPDS card No. 73–1962) and ZnO (JCPDS card No. 80–0085) is produced with decreasing of pH to 7 (sample 9) shown in Fig. 6b. Hence, pH = 14 was chosen as an ideal pH for achieving pure and fine particles of ZnCr2O4.
Figure 7a shows the FT-IR spectrum of ZnCr2O4 nanoparticles (sample 4). The two high frequency modes corresponding to peaks at 510 cm−1 and 625 cm−1 involve mainly the displacement of oxide anions relative to the chromium cations along the direction of the octahedral chains and tentatively assigned to Cr (III) – O stretching28. The broad banding in the range 3000–3700 cm−1 belongs to the stretching vibrations of the coordinated water molecules.
Figure 7b shows the energy dispersive X-ray spectrum of ZnCr2O4 nanoparticles. This was carried out to investigate the chemical composition and the purity of ZnCr2O4 (sample 4). The strong peaks related to Zn, Cr and O are found in this spectrum. There was no unidentified peak observed in EDS. This confirms the purity and the composition of the ZnCr2O4 nanoparticles.
Figure 7c depicts the room-temperature photoluminescence emission spectrum of ZnCr2O4 nanoparticles, which was taken under excitation at 225 nm. The emission spectrum of sample 4 gives maxima at 312.5 nm. The determined band gap of this sample in ethanol solution is 3.96 eV.
Figure 8 shows the (Ahν)2 - hν curve for ZnCr2O4 nanoparticles (sample 4). The band gap of the ZnCr2O4 particles is about 3.35 eV.
The band gap of ZnCr2O4 synthesized in this work was estimated about 3.35 eV and 3.96 eV by UV-vis and PL spectroscopy, respectively. As shown the amount of calculated band gap of the product using these methods (Tauc equation in UV-vis and 1240/λmax in PL spectroscopy) is not same, this difference can be explained follow:
Usually, the traditional method of estimating of the band gap of semiconductor materials is based on the results of absorption spectra measurements. An evaluation of bandwidth is based only on the absorption measurements as a result of interband transitions. Fluorescence upconversion signal is the sum of two fluorescence beams, one from the sample itself (which is the actual fluorescence of molecule) and one from the excitation source. Up-converted signal is not due to the relaxation of molecular excited state or you cannot say that we have got a higher optical band gap. In case of two photon absorption, the absorption of the second photon comes from a virtual excited state and not from actual excited state (LUMO or S1). So in both cases, the band gap of the molecule is same, as obtained by UV-visible spectroscopy. So, calculation of band gap through UV-vis spectroscopy is more accurate.
The photocatalytic activities of the obtained particles are evaluated by the decomposition of Eosin-Y and phenol red, as shown in Fig. 9. Under UV light irradiation, the ZnCr2O4 nanoparticles show apparent photocatalytic activities to the two organic pollutants, especially for Eosin-Y. The decomposition rate of Eosin-Y and phenol red reach 95.26% and 13.42 during UV-irradiation for 30 min, respectively. This reveals that ZnCr2O4 has the potential to be used as a new kind of semiconductor photocatalyst.
The photocatalytic activity mechanism of ZnCr2O4 was given in Eqs. 4, 5, 6, 7:
Surface-wetting behaviors have recently attracted significant attention due to their potential photocatalytic applications. It is believed that surface energy, surface roughness and surface chemical composition have strongly affected the surface wettability of the solid materials29, the obtained ZnCr2O4 nanoparticles show superhydrophilic behavior, which can be primarily attributed to the capillary effect30. Figure 10 shows the image of contact angle on the rough surface of zinc chromium oxide material. It was seen that a contact angle (θ) of zinc chromium oxide material is 5ο.
The VSM measurement at room temperature was carried out to understand the magnetic characteristics of ZnCr2O4. Figure 11 shows the M–H curve for ZnCr2O4 nanoparticles (sample 4). It is evidenced from the hysterical behavior of the M–H curve that all the nanoparticles are paramagnetic at room temperature, although bulk ZnCr2O4 is an antiferromagnetic compound31. Changing magnetic property of ZnCr2O4 in two scales, bulk and nano can be ascribed to finite size effects32. It was shown that the magnetic moment per atom and the magnetic anisotropy of nanoparticles can be different than those of a bulk specimen.
The two main features that dominate the magnetic properties of nanoparticles and give them various special properties are:
(a) Finite-size effects (single-domain or multi-domain structures and quantum confinement of the electrons);
(b) Surface effects, which results from the symmetry breaking of the crystal structure at the surface of the particle, oxidation, presence of defects, dangling bonds, fluctuations in the number of atomic neighbors and lattice expansion cause disorder of surface spin and frustration33.
When the magnetic materials obey quantum confinement effect that their dimensions become less than the size of magnetic domain. In large magnetic particles, it is well known that there is a multi-domain structure where regions of uniform magnetization are separated by domain walls. If the particle size is reduced, there is a critical volume below which it costs more energy to create a domain wall than to support the external magnetostatic energy (stray field). Under this critical diameter, which typically lies in the range of a few tens of nanometers (and depends on the type of material), the particle will consist of a single domain, single domain particles are the ferromagnetic material cannot split up further into domains34,35,36.
The MNP might be composed of a single magnetic domain and it might also display a superparamagnetic37,38 behavior. In the superparamagnetic state, the magnetic moments of the nanoparticles fluctuate around the easy axes of magnetization. Thus, each one of the MNPs will possess a large magnetic moment that continuously changes orientation. When a magnetic field is applied, MNPs in the superparamagnetic state display a fast response to the changes in the magnetic field without remnant (residual) magnetization and without coercivity (the magnetic field required to bring the magnetization back to zero). Thus, in the superparamagnetic state, the MNP behaves as a paramagnetic atom with a giant spin39.
Conclusions
In summary, ZnCr2O4 nanoparticles have been successfully synthesized from Zn(NO3)2. 6H2O and CrCl3. 6H2O by a simple co-precipitation method, under low temperature and ambient pressure. The fine and pure ZnCr2O4 nanoparticles were produced through adjusting the pH value, appropriate alkaline and capping agents. Wettability of ZnCr2O4 nanoparticles synthesized in this work, was considered by the contact angle goniometer. The contact angle (θ) was 5ο, which indicates that oxide material was superhydrophilic in nature. In comparison to other similar works, our method is facile, simple, low cost and eco-friendly. The produced zinc chromite nanostructures can be utilized as a remarkable photocatalyst for dye degradation from waste-water such as removal of Eosin-Y and phenol red as water pollutants under UV irradiation. The degradation percentages of Eosin-Y and phenol red under UV-irradiation were calculated about 95.26 and 13.42, respectively. VSM analysis depicted that ZnCr2O4 nanoparticles have a paramagnetic characteristic, although the bulk ZnCr2O4 represents an antiferromagnetic behavior and this change in magnetic property can be ascribed to finite size effects in nano scale materials.
Methods
Synthetic procedure
ZnCr2O4 nanostructures were prepared by reacting between Zn(NO3)2. 6H2O and CrCl3. 6H2O as starting materials with molar ratio is equal to 1: 2, respectively. At first, 0.20 g of Zn(NO3)2. 6H2O as zinc source and 0.2 g of capping agent were dissolved in distilled water and then, a solution including 0.35 g of CrCl3. 6H2O was added to above solution under vigorous magnetic stirring for 20 min. The alkaline solution in order to reach proper pH was slowly added to the former solution, then the obtained mixture was heated at 60 °C for 30 min. The products were washed and dried under vacuum at 70 °C. Finally, the as-prepared precipitates were calcined in air at 700 °C for 3 h.
Experimental details
The preparation mechanism of ZnCr2O4 nanoparticles
The proposed mechanism for the synthesis of ZnCr2O4 nanoparticles could be explained as follows by Eqs. 8, 9, 10:
Determination procedure of optical band gap
The optical band gap (Eg) of semiconductors can be calculated on the basis of the optical absorption spectrum by the equation 11:
where hν is the photo-energy, A is absorbance and B is a constant relative to the material when n depends on whether the transition is direct (n = 2) or indirect (n = 1/2)40,41. The optical band gap for the absorption peak can thus be deducted by extrapolating the linear portion of the (Ahν)n - hν curve to zero. From the function curve of (Ahν)1/2 - hν, no linear relation was found, indicating that the as-prepared ZnCr2O4 sample is a direct band gap semiconductor.
Procedure of photocatalytic experiment
In a typical experiment, 0.1 g of dye solution and 0.05 g of ZnCr2O4 as a photocatalyst were mixed using a magnetic stirrer. After a period of time in the dark, the solution was irradiated. The light source was the Osram ultraviolet lamp with a power of 400 W that placed at a fixed distance of 40 cm away from the reaction vessel. The radiation source of ultraviolet (UV) is very important for photocatalytic activities. Ultraviolet radiation refers to electromagnetic radiation in the 200–400 nm wavelength range. UV-A covers from 315 to 400 nm, UV-B from 280 to 315 nm and UV-C from 200 to 280 nm. Artificial UV lamps can power photocatalytic processes. The band gap of ZnCr2O4 is about 3.5 eV, so UV source should be provided light irradiation in this range, therefore UV-A (λmax is about 365 nm) is appropriate for the photocatalytic activity of this product. To maintain the solution oxygen-saturated throughout the reaction, air was blown into the vessel via a pump. The light source and quartz vessel were placed in a black box that equipped with a fan. Aliquots of the mixture were taken at definite interval of times during the irradiation and after centrifugation; they were analyzed by a UV–vis spectrometer. The dyes degradation percentage was calculated as follows in equation 12:
where C0 and Ct are the absorbance value of the solution at 0 and t min, respectively.
Characterization
Cetyltrimethyl ammonium bromide (CTAB), sodium dodecyl-benzene-sulfonate (SDBS) and poly vinyl pyrrolidone (PVP-25000) were purchased from Merck. The XRD of products was recorded by a Rigaku D-max C III XRD using Ni-filtered Cu Kα radiation. SEM images were obtained on Philips XL-30ESEM equipped with an energy dispersive X-ray spectroscopy. The EDX analysis with 20 kV accelerated voltage was done. Room temperature PL was studied on a Perkin Elmer (LS 55) fluorescence spectrophotometer. Fourier transform infrared (FT-IR) spectrum was recorded on Shimadzu Varian 4300 spectrophotometer in KBr pellets. The magnetic properties of the samples were detected at room temperature using a vibrating sample magnetometer (VSM, Meghnatis Kavir Kashan Co., Kashan, Iran).
Additional Information
How to cite this article: Mousavi, Z. et al. ZnCr2O4 Nanoparticles: Facile Synthesis, Characterization and Photocatalytic Properties. Sci. Rep. 6, 20071; doi: 10.1038/srep20071 (2016).
Change history
23 May 2016
A correction has been published and is appended to both the HTML and PDF versions of this paper. The error has not been fixed in the paper.
References
Ghose, J. & Murthy, R. C. Activity of Cu+2 ions on the tetrahedral and octahedral site of spinal oxide catalysts for CO oxidation. J. Catal. 162, 359–360 (1996).
Guilhaume, N. & Primet, M. Catalytic combustion of methane: copper oxide supported on high-specific-area spinels synthesized by a sol–gel process. J. Chem. Soc. Faraday Trans. 90, 1541–1545 (1994).
Wei, X., Chen, D. & Tang, W. Preparation and characterization of the spinel xoide ZnCo2O4 obtained by sol-gel method. Mater. Chem. Phys. 103, 54–58 (2007).
Pokhrel, S., Jeyaraj, B. & Nagaraja, K. S. Humidity-sensing properties of ZnCr2O4–ZnO composites. Mater. Lett. 57, 3543–3548 (2003).
Thennarasu, G. & Sivasamy, A. Synthesis and characterization of nanolayered ZnO/ZnCr2O4 metal oxide composites and its photocatalytic activity under visible light irradiation. Journal of Chemical Technology and Biotechnology 90, 514–524 (2015).
Yazdanbakhsh, M., Khosravi, I., Goharshadi, E. K. & Youssefi, A. Fabrication of nanospinel ZnCr2O4 using sol-gel method and its application on removal of azo dye from aqueous solution. Journal of Hazardous Materials 184, 684–689 (2010).
He, H. Y. Catalytic and photocatalytic activity of ZnCr2O4 particles synthesized using metallo-organic precursor. Materials Technology 23, 110–113 (2008).
Cheng, P. & Lian, G. Optical and Photocatalytic Properties of Spinel ZnCr2O4 Nanoparticles Synthesized by a Hydrothermal Route. Journal of the American Ceramic Society 91, 2388–2390 (2008).
Marinkovic, Z. V., Mancic, L., Vulic, P. & Milosevic, O. The influence of mechanical activation on the stoichiometry and defect structure of a sintered ZnO-Cr2O3 system. Mater. Sci. Forum. 453, 456–461 (2004).
Levy, S., Diella, D., Pavese, V., Dapiaggi, A. & Sani, M. A P-V equation of state, thermal expansion and P-T stabillity of synthetic (ZnCr2O4 spinel). Am. Mineral 90, 1157–1162 (2005).
Niu, X., Du, W. & Du, W. Preparation and gas sensing properties of ZnM2O4 (M = Fe, Co, Cr). Sens. Actuators B 99, 405–409 (2004).
Chandran, R. G. & Patil, K. C. A Rapid Method to Prepare Crystalline Fine Particle Chromite Powders. Mater. Lett. 12, 437–441 (1992).
Marinkovic, Z. V., Mancic, L., Maric, R. & Milosevic, O. Preparation of nanostructured Zn-Cr-O spinel powders by ultrasonic spray pyrolysis. J. Eur. Ceram. Soc. 21, 2051–2055 (2001).
Chen, X. H., Zhang, H. T., Wang, C. H., Luo, X. G. & Li, P. H. Effect of Particle Size on Magnetic Properties of Zinc Chromite Synthesized by Sol-Gel Method. Appl. Phys. Lett. 81, 4419–4421 (2002).
Verway, E. J. W. & Heilmann, E. L. Physical properties and cation arrangement of oxides with spinel structures. J. Chem. Phys. 15, 174–180 (1947).
West, A. R. Solid state chemistry and its applications. 6–17 (Wiley India, New Delhi, 2007).
Marinho, E. et al. Lanthanum chromites partially substituted by calcium, strontium and barium synthesized by urea combustion Thermogravimetric study. Analysis & Calorimetry 87, 801–804 (2007).
Soofivand, F., Mohandes, F. & Salavati-Niasari, M. AgSCN micro/ nanostructures: Facile sonochemical synthesis, characterization and photoluminescence properties. Journal of Industrial and Engineering Chemistry 20, 3780–3789 (2014).
Jenkins, R. & Snyder, R. L. Introduction to X-ray Powder Diffractometry. 89–91 (John Wiley & Sons Inc., 1996).
Kosmulski, M. Surface Charging and Points of Zero Charge. (CRC Press, Boca Raton, FL, 2009).
Morrison, I. D. & Ross, S. Colloidal Dispersions: Suspensions, Emulsions and Foams. (Wiley-Interscience, New York, 2002).
Stumm, W. & Morgan, J. J. Aquatic Chemistry. (Wiley-Interscience, New York, 1996).
Davis, J. A., James, R. O. & Leckie, J. O. Surface ionization and complexation at the oxide/water interface. I. computation of electrical double layer properties in simples electrolytes. J. Colloid Interface Sci. 1978, 63, 480–499 (1978).
Parks, G. A. The isoelectric points of solid oxides, solid hydroxides and aqueous hydroxo complex systems. Chem. Rev., 65, 177–198 (1965).
Derjaguin, B. V. & Landau, L. D. Theory of the stability of strongly charged lyophobic sols and the adhesion of strongly charged particles in solution of electrolytes. Acta Physicochim URSS 14, 733–762 (1941).
Verwey, E. J. W. & Overbeek, J. T. G. Theory of the Stability of Lyophobic Colloids. (Elsevier, Amsterdam, 1948).
Suttiponparnit, K. et al. Role of Surface Area, Primary Particle Size and Crystal Phase on Titanium Dioxide Nanoparticle Dispersion Properties. Nanoscale Res. Lett. 6, 1–8 (2011).
Marinkovic, Z. V., Mancic, L., Vulic, P. & Milosevi, O. Microstructural Characterization of Mechanically Activated ZnO-Cr2O3 System. J. Eur. Ceram. Soc. 25, 2081–2084 (2005).
Liu, Y., Lin, Z., Lin, W., Moon, K. S. & Wong, C. P. Reversible superhydrophobic-superhydrophilic transition of ZnO nanorod/epoxy composite films. ACS Appl. Mater. Interfaces 4, 3959–3964 (2012).
Feng, X. J. & Jiang, L. Design and creation of superwetting/antiwetting surfaces. Adv. Mater. 18, 3063–3078 (2006).
Martinho, H. et al. Magnetic properties of the frustrated antiferromagnetic spinel ZnCr2O4 and the spin-glass Zn1−xCdxCr2O4 (x = 0.05, 0.10). Physical review B. 64, 024408 (2001).
Ozkaya, T., Baykal, A., Toprak, M. S., Koseoglu, Y. & Durmus, Z. Reflux synthesis of Co3O4 nanoparticles and its magnetic characterization. J. Magn. Magn. Mater. 321, 2145–2149 (2009).
Kisan, B. et al. Finite Size Effects in Magnetic and Optical Properties of Antiferromagnetic NiO Nanoparticles. IEEE TRANSACTIONS ON MAGNETICS. 50, 1–4 (2014).
Frenkel, J. & Doefman, J. Spontaneous and induced magnetisation in ferromagnetic bodies. Nature 126, 274–275 (1930).
Kittel, C. Theory of the structure of ferromagnetic domains in films and small particles. Phys. Rev. 70, 965–971 (1946).
Mørup, S. et al. Comprehensive Nanoscience and Technology. 437–491 Eds; Elsevier-Amsterdam, (The Netherlands, 2011)
Bean, C. P. & Livingston, J. D. Superparamagnetism. J. Appl. Phys. 30, 120S–129S (1959).
Bedanta, S. & Kleemann, W. Supermagnetism. J. Phys. D 42, 013001 (2009).
Issa, B., Obaidat, I. M., Albiss, B. A. & Haik, Y. Magnetic Nanoparticles: Surface Effects and Properties Related to Biomedicine Applications. Int. J. Mol. Sci. 14, 21266–21305 (2013).
Hagfeldt, A. & Graetzel, M. Light-Induced redox reactions in nanocrystalline systems. Chem. Rev. 95, 49–68 (1995).
Li, X., Zhang, X., Li, Z. & Qian, Y. Synthesis and Characterization of NiO Nanoparticles by Thermal Decomposition of Nickel Dimethylglyoximate Rods. Solid State Commun. 137, 581–584 (2006).
Author information
Authors and Affiliations
Contributions
Z.M., F.S. and M.E. wrote the main manuscript text, S.B. and M.S. helped in characterization. All authors reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Mousavi, Z., Soofivand, F., Esmaeili-Zare, M. et al. ZnCr2O4 Nanoparticles: Facile Synthesis, Characterization and Photocatalytic Properties. Sci Rep 6, 20071 (2016). https://doi.org/10.1038/srep20071
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep20071
- Springer Nature Limited
This article is cited by
-
A bio-waste-mediated novel fabrication of ZnCr2O4 nanoparticles: a heterogeneous catalyst in Biginelli reaction
Research on Chemical Intermediates (2024)
-
Structural, photocatalytic, and anticancer activity Ni-substituted Cu nanochromites synthesized by citrate gel auto-combustion method
Chemical Papers (2023)
-
Structurally modulated dielectric relaxation in rhombohedral Cr2O3 mediated by Mn addition
Journal of Materials Science: Materials in Electronics (2019)
-
Adsorption studies of carbamazepine by green-synthesized magnetic nanosorbents
Nanotechnology for Environmental Engineering (2018)
-
Synthesis and Characterization of Hydrophilic and Semiconductor Cadmium Chromite Nanostructures
Journal of Electronic Materials (2016)