Abstract
To investigate the hydrophobicity of slippery zones, static contact angle measurement and microstructure observation of slippery surfaces from two Nepenthes species and a hybrid were conducted. Marginally different static contact angles were observed, as the smallest (133.83°) and greatest (143.63°) values were recorded for the N. alata and N. miranda respectively and the median value (140.40°) was presented for the N. khasiana. The slippery zones under investigation exhibited rather similar surface morphologies, but different structural dimensions. These findings probably suggest that the geometrical dimensions of surface architecture exert primary effects on differences in the hydrophobicity of the slippery zone. Based on the Wenzel and Cassie-Baxter equations, models were proposed to analyze the manner in which geometrical dimensions affect the hydrophobicity of the slippery surfaces. The results of our analysis demonstrated that the different structural dimensions of lunate cells and wax platelets make the slippery zones present different real area of the rough surface and thereby generate somewhat distinguishable hydrophobicity. The results support a supplementary interpretation of surface hydrophobicity in plant leaves and provide a theoretical foundation for developing bioinspired materials with hydrophobic properties and self-cleaning abilities.
Similar content being viewed by others
Introduction
Carnivorous plants of the genus Nepenthes depend on highly evolved organs called pitchers situated at the tips of their conspicuous leaves1,2 to efficiently capture and digest predominant arthropods3,4,5. This process can provide almost the entire nutrients supply to the Nepenthes plants that grow in infertile habitats6,7. Considering the wide divergence in macro-morphologies and surface architecture that perform various functions, the Nepenthes pitchers have been typically distinguished by several functional parts: a leaf-shaped lid, a collar-formed peristome, a transitional part, a slippery zone and a digestive region8,9. Evolutionarily optimized, these different parts fulfill the functions of attracting and trapping insects, retaining and digesting prey and absorbing nutrients8. In recent years, both the morphological structure and the predation function of the pitchers have gradually become the focus of numerous studies, attempting to not only explore their prey efficiency and anti-attachment mechanism8,10, but also establish biological models for the biomimetic development of insect slippery trapping plate11,12 and other bio-inspired materials with excellent anti-adhesive properties13,14,15.
Within most Nepenthes plants, the slippery zone bears numerous downward-oriented lunate cells and a layer of irregular epicuticular wax coverings12,16,17,18,19. These extraordinary structures present rather unique slippage property to most arthropods, thereby perform the role of trapping and retaining prey20,21,22. Microstructure studies have confirmed that the relatively dense wax coverage is well distinguished by two superimposed layers, namely the upper layer and the lower layer, which differ in ultrastructure, composition and mechanical properties16,18,19,23,24. Studies involving behavioral observations and force measurements revealed that the platelet-shaped wax coverings via the contamination effect on insect adhesive pads and/or the reduction contact area between the slippery surface and the pads to restrict insect attachment ability10,11,18,24. Recent studies have stressed that the wax coverings are mechanically stable enough to resist insect attachment and the roughness of the microscopic surface is sufficient to prevent the smooth flexible insect pads from attaching to the slippery surface24. In addition, with aspect to morphological characteristics and distribution density, lunate cells also contribute considerably to the anti-attachment function by reducing the real contact area10,25. To maintain these superior anti-attachment properties, it is essential to preserve the architecture of the slippery surface from being contaminated by dust and other contaminants. From a macroscopic view, the slippery surface of Nepenthes pitchers in natural habitats appears glaucous and considerably clean, indicating that the slippery surface probably possesses both self-cleaning ability and hydrophobicity. Previous investigations reported the wettability of different regions in Nepenthes alata pitchers, revealing that the slippery zone bears a rather high static contact angle and considerably low free surface energy23. However, this study did not present the reasons why the slippery surface possesses considerable hydrophobicity.
In the present study, the principal objective of our investigation involved the static contact angle measurement and the three-dimensional microstructure examination, is to explore the hydrophobicity of the slippery surfaces of three types of Nepenthes pitchers, also propose a scientific explanation for the hydrophobic mechanism.
Results
Hydrophobicity of various slippery surfaces
To quantify the wettability of slippery surfaces in Nepenthes pitchers, we measured the static contact angle with distilled water droplets and calculated the corresponding surface energy. The static contact angles recorded for the studied Nepenthes species and hybrid under investigation, as well as other Nepenthes species only presented in the supplementary information, approximately ranged from 128° to 156° (Fig. 1 and S1–S3), indicating that the slippery surfaces of these selected Nepenthes pitchers possess hydrophobic property. Statistical results (Fig. 1 and S3) suggested that the slippery surface of N. alata pitcher bears the lowest value of the static contact angle (mean ± SD: 133.83 ± 3.16°), whereas that of N. miranda and N. khasiana exhibit the highest (143.63 ± 4.47°) and the median values (140.40 ± 3.34°) respectively. For the slippery surface of a given Nepenthes species, the static contact angle values are usually within a relatively small range (Fig. 2a and S4). Furthermore, for the Nepenthes species and hybrid under investigation, the static contact angles recorded were somewhat different (Fig. 2a and S4, t-test, P < 0.001), suggesting that the slippery surfaces of the investigated Nepenthes species possess slightly disparate wettability.
Since the surface energy of these slippery zones was automatically calculated from their static contact angle values, these results exhibited an extremely divergent tendency (Fig. 2b and S4). Slippery surfaces of the N. alata pitchers possessed the highest value of surface energy (5.41 ± 1.11 mN/m), whereas that of N. miranda presented the lowest value (2.51 ± 0.92 mN/m) and that of N. khasiana exhibited the median values (3.28 ± 0.91 mN/m). For the selected Nepenthes species and hybrid, the surface energy of the slippery zones exhibited different values (Fig. 2b, t-test, P < 0.001, S4).
Surface morphology and structure of the slippery zones
The slippery zones of the Nepenthes species and hybrid under investigation contribute from one third to a half of the entire pitcher length and the inner surface of these slippery zones presented a glaucous and spotless macro-morphology. As described in previous studies10,12,16,19,22,26, scanning electron microscope (SEM) images of the slippery surfaces of the Nepenthes plants under investigation, revealed that they were covered by relatively dense and continuous epicuticular wax coverings, with an ambulance of scattered prominent lunate cells (Fig. 3). The wax coverings emerged as discernible platelet-formed wax crystals with an irregular pattern, arranging extremely dense on the slippery surfaces, most of which overlapped each other, in such a manner that the generated cavities were hardly distinguishable (Fig. 3). A large number of lunate cells with relatively great geometrical dimensions were singly distributed over the slippery surfaces. Each lunate cell had both ends bent toward the pitcher bottom corresponds to an exclusive and enlarged overlapping guard cell, generating a crescent-shaped profile with an asymmetrical convex surface.
The platelet-formed wax crystals exhibited highly similar arrangements and shapes on different parts of the slippery surfaces in the Nepenthes species and hybrid under investigation. Geometrical dimensions of the wax platelets showed slight variations among the Nepenthes species and hybrid, as values for the apparent length and thickness ranged from 0.8–1.1 μm and 80–100 nm, respectively. The cavities formed by adjacent wax platelets presented an irregular appearance and varied noticeably among the three Nepenthes plants under investigation. Lunate cells from these Nepenthes species possessed high similarity in morphology, but presented apparent differences in size and distribution density. Since the geometrical dimensions of wax crystals and lunate cells in many Nepenthes species have been statistically analysed in previous studies10,18,21,25,26, we analysed and reported only those structural parameters related to surface hydrophobicity in the present study, as shown in Table 1 and supplementary information S5.
To acquire morphological and structural information of the slippery surfaces in a vertical orientation, such as height and surface roughness, we conducted scanning white-light interferometer (SWLI) observations and atomic force microscopic (AFM) measurements. In the Nepenthes species and hybrid under investigation, the overall slippery surfaces were undulating and exhibited rather uneven morphologies (Fig. 4). The lunate cells protruded from the slippery surfaces (about 8–15 μm higher) and exhibited noticeable variations in elevation, shifting slowly from underside to upside in an upward direction and sharply from upside to underside in a downward direction, thereby forming ‘slope’ and ‘precipice’ respectively (Fig. 4a,b,d,e,g,h) and generating the slope and precipice angles (Fig. 4c,f,i). Geometrical dimensions and their statistical analysis of the lunate cells in a vertical orientation are presented in Table 1. As relatively large values in height were recorded for these lunate cells (Table 1), they contributed significantly to the degree of surface roughness of the slippery zones. When examining the slippery surfaces over a large expanse (containing several lunate cells), the surface roughness presented rather high values (Ra 2.207–3.239 μm, Fig. 4a,d,g). Within a small scanning area (4 × 4 μm2, excluding the lunate cell), AFM images revealed that the wax coverings possess a relatively smooth surface and present rather small values of surface roughness (Ra 69.25–84.70 nm, Fig. 5a,c,e). The height data for the platelet-shaped wax coverings were statistically derived according to the height variations in the slippery surfaces (Fig. 5b,d,f) and are exhibited in Table 1 and supplementary information S5.
Discussion
Our exhibited results concerning the static contact angle quantitatively described the hydrophobicity of the slippery surfaces from two Nepenthes species and a hybrid; we also presented the micro-morphology and surface architecture of these slippery zones. Based on these results, in the following section, we propose models to theoretically analyze the influence of surface structures on the slippery zone’s hydrophobicity.
Comparison of the slippery surface’s hydrophobicity
During insect capturing, the slippery zones of most Nepenthes species depend on their particular surface structures to conspicuously restrict insect’s attachment ability, thereby performing the functions of insect trapping and prey retention9,16,17,19. The slippery zones of Nepenthes plants growing in natural habitats are frequently subjected to contamination by dust and rainwater. It is therefore crucial to possess self-cleaning abilities, which enables the surface morphology to render superior slippage function continually for the efficient capture of prey. In the Nepenthes plants under investigation, relatively high values of static contact angles (128–156°, Fig. 1 and S1–S4) and rather low surface energy (0.54–7.46 mN/m, Fig. 2b and S1–S4) were recorded for all slippery surfaces, suggesting that these slippery zones present significant surface hydrophobicity. A previous study presented similar results for the slippery surface of N. alata pitchers, the static contact angle reported was approximately 160° and the surface energy was about 4 mN/m23. These results probably suggest that the slippery surfaces of various Nepenthes species and hybrids exhibit hydrophobic property. However, slight differences in values recorded for both the static contact angle and the surface energy in our study potentially suggest that the slippery surfaces from these Nepenthes plants possess marginally distinguishable hydrophobic property.
Effects of surface structure on hydrophobicity
In the past decade, interest in the surface structures and hydrophobicity of various plant leaves has increased rapidly, attempting to use these biostructures as templates to create materials with self-cleaning capability and other desirable properties. The leaf surface of lotus plants, which bears hierarchical structures on a micro-nano scale, yields a rather high static contact angle and has been considered as the typical bio-template to create biomimetic materials14,27,28. Chemical composition and surface topography are two crucial factors that determine the surface hydrophobicity29 and almost the entire primary surface of plant leaves is covered by a mixture of hydrophobic compounds referred to as wax crystals30,31. Since water contact angles on smooth hydrophobic surfaces are generally lower than 120°, the surface micro/nanostructure and their generated roughness is primarily responsible for hydrophobicity at much greater contact angles32.
To describe the effects of roughness on hydrophobicity, Wenzel first hypothesized that the existence of a rough surface makes the real contact area between solid and liquid is much higher than their geometrical contact area, leading to the improvement in hydrophobicity or hydrophilicity33,34. Furthermore, according to this hypothesis, an equation was proposed to quantitatively express the effect of surface roughness on contact angle, as follows:
where and respectively represent the contact angle on rough and smooth surfaces and represents the roughness factor defined as the ratio between the real rough surface area and the geometrical surface area or projected area of the rough surface. The essential condition of this equation is that there is adequate contact between the liquid and solid, without air between the two substances. In fact, however, when the material surface exhibits hydrophobicity (contact angle higher than 90°), the air is usually entrapped between the water droplet and the surface topography. Therefore, Cassie and Baxter35 modified Wenzel’s model to propose the composite liquid-gas-solid interface and an extended equation to calculate the contact angle on the composite interface, as follows:
where is the fractional flat geometrical area of the solid-liquid under the liquid droplet and is the roughness factor of the solid-liquid interface. This equation is generally employed to analyse the contact angle of almost all the composite liquid-solid interfaces and predicts the entrapped air between the liquid droplet and the solid surface serves a crucial role in surface hydrophobicity.
According to the foregoing equations, the surface topography and its generated roughness performs a crucial role in affecting the apparent contact angle of material surface, as enhancing or decreasing the contact angle when the material surface possesses hydrophobicity or hydrophilicity, respectively. In the slippery surfaces of Nepenthe plants, the roughness induced by the presence of both lunate cells and wax crystals causes the apparent contact angle () to be greater than the smooth contact angle (). Moreover, the wax coverings with structural dimensions in the nano-micro range are responsible for the first generation of surface roughness and the lunate cells with the micrometer ranged dimensions contribute to the second generation of surface roughness. This dual-scale surface topography is very similar to the hierarchical architecture of the lotus leaf, possibly conferring a similar function for the surface hydrophobicity.
Hydrophobicity induced by micron-sized lunate cells
In our static contact angle measurements, the volume of a water droplet was approximately 3–5 μL, generating the static contact angle ranges of 128–156° (including the static contact angle values presented in supplementary information S1–S4), indicating that the contact radius of the water droplet on the slippery surfaces is approximately 0.364–0.836 mm, thus covering quite a large number (approx. 65–525) of lunate cells. Moreover, the lunate cells with structural dimensions of ~10 μm contribute significantly to the surface roughness of slippery zones, possibly serving an important role in conferring hydrophobicity. In order to analyze this possibility succinctly, we simplify the lunate cell as a triangular prism, retaining its slope and precipice angles. Consequently, the slippery surface is considered as a flat smooth plane with equally distributed triangular prisms of same dimensions, as presented in Fig. 6a.
In this simplified model, following the Wenzel equation (Eq. 1), the equation regarding the theoretical contact angle of a water droplet on the slippery surfaces can be deduced (Supplementary information S6 showing the derivation) as follows:
where and are the slope and precipice angles respectively, formed by the lunate cell’s particular structure (Fig. 4); is the width of the simplified slippery surface; and are the height and interval distance of the adjacent lunate cells (Table 1) respectively; and is the length of the simplified lunate cell (triangular prism), where . In previous investigations, the true contact angle () for water droplets on smooth wax coverings of plants has been reported as 100°36,37. Based on the mean values of the structural dimensions (Table 1 and S5) and the true contact angle (), the contact angle () can be theoretically calculated. The calculation results (Fig. 6b) present the maximal values of () as approximate 102.7° in N. alata, 101.8° in N. miranda and 101.5° in N. khasiana, exhibiting marginal differences that could be exclusively attributed to the different structural parameters of the lunate cells from the two Nepenthes species and a hybrid under investigation. These theoretically calculated values are considerably lower than their actual measured results, probably suggesting that the lunate cells are not the only features that confer properties of superior hydrophobicity to the slippery surfaces.
Hydrophobicity induced by nano-scale wax coverings
On slippery surfaces, wax coverings consisting of platelet-shaped crystals with nano-scale structural parameters are interactively distributed (Fig. 3b,d,f), forming numerous cavities which probably entrap air when a water droplet makes contact with the wax surface. According to a previous theory35, the existence of entrapped air can greatly improve the surface hydrophobicity. To succinctly analyze the influence of nano-scale wax coverings on the hydrophobicity of the slippery surface, as well as based on the structural parameters recorded with AFM and SEM equipments, the wax coverings and their generated cavities were simplified as convex cylinders with a particular interval distance. Therefore, the slippery surface was considered as a flat smooth plane with equal-distance distributed triangular prisms and an array of convex cylinders with a particular interval distance (Fig. 7a).
In this simplification, the wax platelets not only significantly improve the real rough surface area, but also depend on the spaces generated by the nano-scale convex cylinders to give the possibility of entrapping air. The real rough surface area results form two aspects basically: the triangular prisms (lunate cells) and the convex cylinders (platelet-shaped wax coverings); therefore, we can deduce the roughness factor (Supplementary information S7 showing the derivation), as follows:
where is the ratio between the area of platelet-shaped epicuticular wax coverings and the area of the entire slippery surface, and represent the radius and the height of the simplified platelet-formed wax crystal (convex cylinder, Fig. 7b), respectively. Furthermore, the projection of the single platelet-profiled wax crystal is succinctly considered as a circular region; therefore, based on the exhibited area values of the wax platelets (Table 1 and S5), we obtained the . Combined with the Cassie-Baxter equation (Eq. 2), the relationship between theoretical contact angle and the structural parameters of the slippery surfaces can be deduced, as follows:
where, represents the ratio between the area of the platelet-shaped epicuticular wax coverings and the area of the entire slippery surface, namely . Based on the mean values of the structural dimensions (Table 1 and S5) of the slippery surfaces, the contact angle () can be theoretically evaluated. The results of this evaluation (Fig. 7c) reveal the contact angle values of N. alata as 132.9–138.2°, whereas those of N. miranda and N. khasiana as 135.3–137.5° and 134.1–136.7° respectively, presenting somewhat detectable differences among the Nepenthes plants under study.
In comparison to the evaluation results, the simplified model, in which the surface is barely covered by triangular prisms, these calculated contact angle values are noticeably greater, attributing to the conspicuous enhancement of the roughness factor () provided by the array of convex cylinders (simplified wax coverings). These findings suggest that the lunate cell is not the only factor that confers strong hydrophobicity to the slippery surfaces present and the platelet-shaped wax coverings potentially serve a rather important function. From another aspect, the theoretically acquired results present marginally smaller values than the experimentally measured static contact angles of the slippery zones from the two Nepenthes species and a hybrid (Fig. 1). In fact, because the selected Nepenthes pitchers were grown in a nursery, they were continually subjected to a variety of insults, such as dust contamination or physical damage inflicted by captured insects, which attributed to the damage of the slippery zone’s surface topography in some extent, thereby the theoretical results should be moderately greater than the measured results. The precision required in acquiring the dimensions of the surface architecture, especially those of the nano-ranged wax crystals, is presumably responsible for the presented deviation between the theoretical and measured results of the contact angle. Besides the existed instruments used in our studies, more advanced apparatus and analytical procedures are propitious to obtain highly accurate parameters, thereby enabling a better confirmation of our proposed models.
The theoretical calculations based on the proposed models possibly provide a scientific explanation to the surface hydrophobicity of the slippery zones in Nepenthes pitchers and present a reasonable interpretation to the marginal differences in static contact angle of a water droplet on those slippery surfaces. According to our analysis, geometrical parameters of the triangular prisms and the array of convex cylinders lead to the divergent static contact angle values. In the Nepenthes species and hybrid under investigation, platelet-shaped wax coverings and lunate cells exhibited discrepant structural dimensions (Table 1 and S5), thereby leading to marginal differences in surface hydrophobicity of the three Nepenthes’ slippery zones. However, our investigations and proposed theoretical models are preliminary; future studies should focus on dynamic contact angle measurement, which should explain how the anisotropy of the slippery surface mainly results from the orientation-growing lunate cells, affects the hydrophobicity. The expected results would presumably present a much more comprehensive and detailed understanding of the surface wettability of various slippery zones.
In summary, the surface hydrophobicity of the slippery zones from two Nepenthes species and a hybrid was investigated, including static contact angle measurement, microstructure observation and theoretical analysis. Results showed that the static contact angle values of the slippery surfaces range from approximately 128° to 156° and present marginal differences among the three varieties of slippery zones. Based on the architecture and geometrical dimensions of the slippery surfaces, theoretical models were proposed to analyze the hydrophobic mechanism. Results of our analysis demonstrated that the platelet-shaped wax coverings and the lunate cells are the primary factors to confer strong hydrophobicity to the slippery surfaces and that the discrepant structural dimensions contribute to the marginal differences in static contact angle values. Our acquired conclusions possibly support another interpretation of the surface hydrophobicity of plant leaves and provide a theoretical reference for the development of biomimetic materials with hydrophobic properties and self-cleaning abilities.
Materials and Methods
Nepenthes pitchers
To investigate the hydrophobicity of the slippery surfaces, three varieties (two species and a hybrid) of Nepenthes plants (Fig. 8) were commercially acquired from a nursery (Hangzhou City, China) and cultivated in a small greenhouse under continuously controlled environmental conditions: temperature of 25–30 °C and relative humidity of 70–90%. Mature pitchers were clipped from the selected varieties and measured their length, as N. alata, 11.85 ± 0.57 cm, n = 4; N. miranda (a hybrid), 8.12 ± 0.36 cm, n = 4; and N. khasiana, 6.49 ± 0.34 cm, n = 4, mean length ± SD. For definitely presenting the range of the slippery zone, half of each pitcher was longitudinally cut with a pair of scissors, thereby allowing the slippery surface to be easily distinguished (Fig. 8). When growing, the pitchers were more or less exposed to contamination by various diverse particles, such as dust and wing scales of trapped insects. Therefore, each selected pitcher was rinsed several times with distilled water, to remove the contaminants without causing damage to the surface architecture of the slippery zones. The prepared slippery zones were used for static contact angle measurement and surface microstructure observation.
Static contact angle measurement and surface energy estimation
Static contact angle measurement and surface energy estimation were conducted with an optical contact angle analyzer SL 150S (Solon Corp., USA). This equipment consists mainly of a high-speed (charge-couple device) CCD video system, a three-dimension manual micro-regulation unit and a micro-control module for syringes. The related software (CAST 2.0) performs static contact angle measurement and surface energy estimation according to standard evaluation methods and procedures. For measurement, several small pieces measuring 2 × 2 cm2 were cut from the central part of the rinsed slippery zones with a razor blade and attached to a measuring platform using double-sided adhesive tape. Static contact angles of distilled water droplets on the slippery surfaces were measured with a needle-in sessile drop method, which the similar approach has been described in detail in previous literatures23,38,39. The volume of a distilled water droplet was approximate 3–5 μL. The static contact angles were evaluated by firstly using the circle-fitting estimation, followed by the Young-Laplace equation fitting calculation. For the slippery surfaces of each Nepenthes species and hybrid, 16 measurements were executed and all the measurements were conducted under ambient conditions as follows: temperature of about 28 °C and relative humidity of about 45%. To minimize the shrinking effect induced by evaporation, the static contact angle measurements of the specimens were rapidly finished as soon as possible after being cut from the slippery zones.
When acquired the static contact angle value, surface energy of the slippery zones was calculated and presented automatically by the software CAST 2.0 belonged to the optical contact angle analyzer SL 150S. For this calculation, the Kwok method40 which universally applied for diverse surfaces was adopted.
Surface architecture examinations
For obtaining structural information of the lunate cells and the wax coverings used to scientifically explain the hydrophobic mechanism, we examined the three-dimension architectures of the slippery surfaces in detail with a scanning electron microscope (SEM, Hitachi S-4800, Hitachi Corp., Japan), a atomic force microscope (AFM, MFP-3D Classic, Asylum Research, Oxford Instrument Corp., UK) and a scanning white-light interferometer (SWLI, Zygo NV-5000, Zygo Corp., USA).
Our SEM observation, followed similar methods of previous studies10,25,41, several pieces of approximately 1 × 1 cm2 were cut from the prepared slippery surfaces and completely dried by natural evaporation in a dust-free environment. These dried samples were mounted on alloy blocks, sputter coated (Bal-Tec SCD005, Balzers, Switzerland) and observed. Geometrical dimensions of the surface architectures in a horizontal direction, including the area of a single wax platelet in the epicuticular wax coverings, the ratio between the area of platelet-shaped epicuticular wax coverings and the area of the entire slippery surface, as well as the length, width and interval distance of the lunate cells, were quantitatively analyzed from the saved images with the ImageJ software (ImageJ 1.38e/Java 1.5.0_09, National Institutes of Health, USA) and the acquisition process of some structural parameters is presented in supplementary information S8.
The SWLI examination was carried out to acquire geometrical information concerning the surface topography in a vertical direction. Fresh specimens (about 2 cm2) were cut from the processed slippery zones, attached to an aluminum block and observed in the SWLI apparatus. The height information (~10 μm) of lunate cells was obtained via analyzing the saved images with the software (Scanning Probe Image Processor, Version 4.3.3.0, Image Metrology, Denmark) of the SWLI equipment. This software can definitively present the variation in height of the lunate cell’s profile along an established line and the maximum height value during the variation can be derived.
For the AFM measurement, a high reflection coated triangular silicon nitride cantilever (Multi75E-G, Bugdetsensor, Nanoworld, Switzerland) was adopted to exhibit the topography of the wax coverings. Each specimen (about 2 cm2) was freshly cut from the prepared slippery zones and glued to a circular glass side and completely submerged in ultrapure water to avoid structural shrinkage caused by evaporation. Scanning was conducted in tapping mode with an applied scanning force of about 13 nN and a constant scanning velocity (5 μm/s). Because the densely distributed lunate cells are characterised by relatively large values in height (~10 μm), the movement of the cantilever was frequently interrupted while scanning the wax coverings interspersed among the lunate cells. The scanning areas were therefore adjusted to within 4 × 4 μm2. After the AFM measurement, height data and surface roughness of the wax coverings were derived and presented.
Additional Information
How to cite this article: Wang, L. and Zhou, Q. Surface hydrophobicity of slippery zones in the pitchers of two Nepenthes species and a hybrid. Sci. Rep. 6, 19907; doi: 10.1038/srep19907 (2016).
References
Ellison, A. M. & Gotelli, N. J. Evolutionary ecology of carnivorous plants. TREE 16, 623–629 (2001).
Ellison, A. M. & Gotelli, N. J. Energetics and the evolution of carnivorous plants–Darwin’s most wonderful plants in the world. J. Exp. Bot. 60, 19–42 (2009).
Moran, J. A., Booth, W. E. & Charles, J. K. Aspects of pitcher morphology and spectral characteristics of six Bornean Nepenthes pitcher plant species: implications for prey capture. Ann. Bot. 83, 521–528 (1999).
Moran, J. A. Pitcher dimorphism, prey composition and the mechanisms of prey attraction in the pitcher plant Nepenthes rafflesiana in Borneo. J. Ecol. 84, 515–525 (1996).
Thornham, D. G., Smith, J. M., Grafe, T. U. & Federle, W. Setting the trap: cleaning behavior of Camponotus schmitzi ants increases long-term capture efficiency of their pitcher plant host Nepenthes bicalcarata. Funct. Ecol. 26, 11–19 (2012).
Ellison, A. M. Nutrient limitation and stoichiometry of carnivorous plants. Plant Biol. 8, 740–747 (2006).
Moran, J. A. & Clarke, C. M. The carnivorous syndrome in Nepenthes pitcher plants: current state of knowledge and potential future directions. Plant Signal. Behav. 5, 644–648 (2010).
Gaume, L., Gorb, S. & Rowe, N. Function of epidermal surfaces in the trapping efficiency of Nepenthes alata pitchers. New Phytol. 156, 479–489 (2002).
Benz, M., Gorb, E. & Gorb, S. Diversity of the slippery zone microstructure in pitchers of nine carnivorous Nepenthes taxa. Arthropod-Plant Inte. 6, 147–158 (2012).
Wang, L. X. & Zhou, Q. Numerical characterization of surface structures of slippery zone in Nepenthes alata pitchers and its mechanism of reducing locust’s attachment force. Adv. Nat. Sci. 2, 152–160 (2010).
Wang, L. X., Zhou, Q., Zheng, Y. J. & Xu, S. Y. Composite structure and properties of pitcher surface of carnivorous plant Nepenthes and its influence on insect attachment system. Prog. Nat. Sci. 19, 1657–1664 (2009).
Wang, L. X. & Zhou, Q. Nepenthes pitchers: surface structure, physical property, anti-attachment function and potential application in mechanical controlling plague locust. Chin. Sci. Bull. 59, 2513–2523 (2014).
Koch, K. & Barthlott, W. Superhydrophobic and superhydrophilic plant surfaces: an inspiration for biomimetic materials. Phil. Trans. R. Soc. A 367, 1487–1509 (2009).
Koch, K., Bhushan, B. & Barthlott, W. Multifunctional surface structures of plants: an inspiration for biomimetics. Prog. Mater. Sci. 54, 137–178 (2009).
Wong, T. S. et al. Bioinspired self-repairing slippery surfaces with pressure-stable omniphobicity. Nature 477, 443–447 (2011).
Riedel, M., Eichner, A. & Jetter, R. Slippery surfaces of carnivorous plants: composition of epicuticular wax crystals in Nepenthes alata Blanco pitchers. Planta. 218, 87–97 (2003).
Juniper, B. E. & Burras, J. K. How pitcher plant trap insects. New Sci. 269, 75–77 (1962).
Gorb, E. et al. Composite structure of the crystalline epicuticular wax layer of the slippery zone in the pitchers of the carnivorous plant Nepenthes alata and its effect on insect attachment. J. Exp. Biol. 208, 4651–4662 (2005).
Riedel, M., Eichner, A., Meimberg, H. & Jetter, R. Chemical composition of epicuticular wax crystals on the slippery zone in pitchers of five Nepenthes species and hybrids. Planta 225, 1517–1534 (2007).
Pant, D. & Bhatnagar, S. Morphological studies in Nepenthes (Nepenthaceae). Phytomorphology 27, 13–34 (1977).
Gorb, E. V. & Gorb, S. N. The effect of surface anisotropy in the slippery zone of Nepenthes alata pitchers on beetle attachment. Beilstein J. Nanotechnol. 2, 302–310 (2011).
Gaume, L., Perret, P. & Gorb, E. How do plant waxes cause flies to slide? Experimental tests of wax-based trapping mechanisms in three pitfall carnivorous plants. Arth. Struct. Dev. 33, 103–111 (2004).
Gorb, E. & Gorb, S. Physicochemical properties of functional surface in pitchers of the carnivorous plant Nepenthes alata blanco (Nepenthaceae). Plant Biol. 8, 841–848 (2006).
Scholz, I. et al. Slippery surfaces of pitcher plants: Nepenthes wax crystals minimize insect attachment via microscopic surface roughness. J. Exp. Biol. 213, 1115–1125 (2010).
Wang, L. X. & Zhou, Q. Friction force of locust Locusta migratoria manilensis (Orthoptera, Locustidae) on slippery zones surface of pitchers from four Nepenthes species. Tribol. Lett. 44, 345–353 (2011).
Gorb, E. V., Baum, M. J. & Gorb, S. N. Development and regeneration ability of the wax coverage in Nepenthes alata pitchers: a cryo-SEM approach. Sci. Rep. 3, 1–6 (2013).
Tuteja, A., Choi, W. & Ma, M. L. Designing superoleophobic surfaces. Science 318, 1618–1622 (2007).
Wang, T. C. et al. Preparation and hydrophobicity of biomorphic ZnO/carbon based on a lotus-leaf template. Mater. Sci. Eng. C 43, 310–316 (2014).
Blossey, R. Self-cleaning surfaces — virtual realities. Nat. Mater. 2, 301–306 (2003).
Meusel, I., Barthlott, W., Kutzke, H. & Barbier, B. Crystallographic studies of plant waxes. Powder Diffr. 15, pp 123–129 (2000).
Koch, K., Dommisse, A. & Barthlott, W. Chemistry and crystal growth of plant wax tubules of lotus (Nelumbonucifera) and nasturtium (Tropaeolum majus) leaves on technical substrates. Cryst. Growth Des. 6, 2571–2578 (2006).
Lafuma, A. & Quéré, D. Superhydrophobic states. Nat. Mater. 2, 457–460 (2003).
Wenzel, R. N. Resistance of solid surfaces to wetting by water. Ind. Eng. Chem. 28, 988–994 (1936).
Wenzel, R. N. Surface roughness and contact angle. J. Phys. Coll. Chem. 53, 1466–1467 (1949).
Cassie, A. & Baxter, S. Wettability of porous surface. Trans. Faraday Soc. 40, 546–551 (1944).
Neelesh, A. P. Mimicking the Lotus Effect: Influence of double roughness structures and slender pillars. Langmuir. 20, 8209–8213 (2004).
Wang, J., Chen, H., Sui, T., Li, A. & Chen, D. Investigation on hydrophobicity of lotus leaf: Experiment and theory. Plant Sci., 176, 687–695 (2009).
Anna, J., Schulte, A. J., Droste, D. M., Koch, K. & Barthlott, W. Hierarchically structured superhydrophobic flowers with low hysteresis of the wild pansy (Viola tricolor) – new design principles for biomimetic materials. Beilstein J. Nanotechnol. 2, 228–236 (2011).
Koch, K., Bennemann, M., Bohn, H. F., Albach, D. & Barthlott, W. Surface microstructures of daisy florets (Asteraceae) and characterization of their anisotropic wetting. Bioinspir. Biomim. 8, 036005 (2013).
Kwok, D. Y. & Neumann, A. W. Contact angle measurement and contact angle interpretation. Adv. Colloid interface Sci. 81, 167–249 (1999).
Wang, L. X., Zhou, Q. & Xu, S. Y. Role of locust Locusta migratoria manilensis claws and pads in attaching to substrates. Chin. Sci. Bull. 56, 789–795 (2011).
Acknowledgements
We acknowledge Weiqi Wang (The State Key Laboratory of Tribology, TsingHua University) for the help in performing the AFM measurements, Lei Zhao (The State Key Laboratory of Tribology, TsingHua University) for the help in SWLI observations and Ligang Zhai (School of Mechanical Engineering, Hebei University of Science and Technology) for the help in the static contact angle measurements. This study was financially supported by the National Natural Science Foundation of China (51205107), the Natural Science Foundation of Hebei province (E2014208056) and the Tribology Science Fund of State Key Laboratory of Tribology (SKLTKF13B05).
Author information
Authors and Affiliations
Contributions
L.X.W. designed and performed the measurements and examinations, conducted the results analysis and wrote this manuscript. Q.Z. assisted in revising the experiment design. Both authors edited the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Wang, L., Zhou, Q. Surface hydrophobicity of slippery zones in the pitchers of two Nepenthes species and a hybrid. Sci Rep 6, 19907 (2016). https://doi.org/10.1038/srep19907
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep19907
- Springer Nature Limited
This article is cited by
-
Progress on Bionic Textured Cutting Tools: A Review and Prospects
Journal of Bionic Engineering (2024)
-
Thermal Alternating Polymer Nanocomposite (TAPNC) Coating Designed to Prevent Aerodynamic Insect Fouling
Scientific Reports (2016)