Abstract
We have studied the transformation of carbides in AISI M42 high-speed steels in the temperature window used for forging. The annealing was found to result in the partial transformation of the large, metastable M2C carbides into small, more stable grains of M6C, with an associated change in the crystal orientation. In addition, MC carbides form during the transformation of M2C to M6C. From the high-speed-steel production point of view, it is beneficial to have large, metastable carbides in the cast structure, which later during annealing, before the forging, transform into a structure of polycrystalline carbides. Such carbides can be easily decomposed into several small carbides, which are then randomly distributed in the microstructure. The results also show an interesting difference in the carbide-transformation reactions on the surface versus the bulk of the alloy, which has implications for in-situ studies of bulk phenomena that are based on surface observations.
Similar content being viewed by others
Introduction
High-speed steel (HSS), which has been in use for almost 100 years, remains as one of the most important of today’s tool materials and is employed in the manufacture of taps, dies, drills, saw blades and other cutting equipment. The name “high-speed steel” derives from the fact that tools made from this material are capable of cutting materials at much higher speeds than conventional carbon tool steel, retaining their hardness and ability to cut even when the tip of the tool reaches low red heat1. In addition to carbon, high-speed steels are usually alloyed with tungsten, molybdenum, vanadium and cobalt, all of which are known for their ability to form carbides. In fact, it is these carbides that give high-speed steels their high hardness and excellent wear resistance. However, these useful properties of high-speed steels are very much dependent on the type, size, shape, amount and distribution of the carbides2,3,4,5,6,7. As a consequence, a detailed investigation and evaluation of the carbides that form in high-speed steel is crucial.
The AISI M42 super-high-speed steel is characterized by its high molybdenum content and belongs to the ledeburitic group of steels, because the last transformation during solidification is eutectic. The cast microstructure of these ledeburitic steels generally consists of dendrites surrounded by a more-or-less connected network of eutectic carbides8; however, due to the wide solidification range and the complex eutectic reaction it tends to segregate and form different types of carbides: either M2C or M6C in the case of conventional high-speed steels. The final microstructure of the steel consists of ferrite with fine carbide precipitates and ledeburite with primary carbides in between9.
During conventional tool-steel production, the steel is cast and then forged in the ideal temperature window of 1100–1200 °C. At these temperatures the metastable M2C carbide phase transforms into other, more stable, carbides. The reports in the literature indicate that the M2C carbides transform to M6C and MC carbides following the path M2C + matrix → M6C + MC2,3,10,11,12,13,14. These primary and eutectic carbides can then be broken down into smaller carbides as a result of hot deformation (e.g., forging) or mechanical fragmentation. Another possibility is to anneal the steel, so that the exchange of elements is driven by diffusion processes. During annealing, the primary and eutectic carbides decompose, which means the compositions of the carbides change. Furthermore, when held at an elevated temperature for sufficient time, all types of carbides can agglomerate and spheroidize in order to decrease their surface energy and achieve a more stable state13. Thus, it is beneficial to optimize the heat treatment prior to forging in order to obtain the desired size and distribution of the carbides.
Electron-backscatter diffraction (EBSD) is an excellent technique for characterising microstructures and analysing carbide phases4,15,16,17,18. In recent years, in-situ EBSD analysis has attracted researchers wishing to study the deformation of HSS19 as well as grain growth and phase transformation by employing a heating stage20,21,22. It is also possible to conduct a form of quasi-in-situ EBSD by marking the area of interest on the sample, annealing/heating the sample and then replacing it in the microscope and repeating the EBSD analysis at the same location on the sample23. In this way, changes to the microstructure, especially the eutectic carbides, caused by the annealing, can be investigated and analysed.
The aim of our work was to investigate the cast microstructure of the super-high-speed steel AISI M42 and to examine the changes to the eutectic carbides during annealing at 1100 °C for various times. We wanted to test the hypothesis that the processes we observe on the surface are the same as the processes taking place in the bulk of the material. In order to do this we performed quasi-in-situ studies of the carbide transformations on the surface and in the bulk. We also wanted to determine whether the different conditions that necessarily occur at a free surface, compared to the bulk, during a heat treatment can prevent us from obtaining truly representative results.
Experimental Details
Material and specimen preparation
The composition of the AISI M42 molybdenum super-high-speed steel is listed in Table 1. This steel was delivered in the as-cast condition, without any additional electro slag remelting. After casting, the steel ingot was cut in half, with the specimens being taken from the middle section. Because the main goal of the experiment was to observe the transformation of the carbides on the free surface and in the bulk during annealing, two sets of specimens were prepared. For the observation of the processes on the free surface, a specimen was prepared for EBSD analysis—with the final steps being diamond polishing and OPS (silica oxide colloidal suspension of 40 nm size) polishing for 5 minutes—prior to annealing. In this way, the specimens could be observed immediately after annealing and no additional surface preparation was necessary. For the observation of the processes in the bulk, the specimens were first annealed and then cut in half and prepared for an optimal EBDS analysis (ground, polished, OPS).
Annealing
The specimens were annealed in a vacuum system using a stub-like heating stage in an argon atmosphere at 100 mbar to ensure an optimally homogeneous heat distribution in the specimens. The specimens were first stabilized in the vacuum system at 400 °C, followed by high-temperature annealing, which was performed at 1100 °C and 1150 °C for 15 to 60 minutes, in order to follow the transformation of the carbides. The temperature was monitored at all times using a thermocouple mounted on the surface of the specimen. After the annealing step, the specimens were left to cool in the vacuum chamber in the Ar atmosphere. Due to the small size of the specimens and the presence of Ar in the vacuum chamber, the cooling was quite rapid at around 10 K/s, which effectively froze the microstructure. The residual contents of oxygen and carbon in the chamber were negligible, so no oxidation or carbon contamination was expected. In our previous experiments24 a similar heating system and heating conditions were employed. However, subsequent detailed analyses revealed that local short circuits caused material melting, leading to an incorrect interpretation of the data. This melting results in the deposition of material on the surface and in a different surface-carbide transformation than would be expected in totally clean conditions. Here we must stress that the carbide transformation is extremely dependent on the quality of the vacuum. Therefore, a heating-system modification involving high-temperature annealing in argon gas was introduced.
Analysis
The specimens in the first set, which were intended for an analysis of the carbides in the bulk, were prepared as described above to ensure good-quality diffraction patterns. The specimens prepared for the observation of carbide transformations on the free surface were immediately analysed after annealing with no subsequent surface preparation. Due to the relatively large size of the carbides, the area of interest on the specimen surface could be marked and the same area could be subsequently analysed after different annealing times.
The imaging and EBSD analyses were performed using a FEG SEM JEOL 6500F field-emission scanning electron microscope with energy-dispersive spectroscopy (an INCA X-SIGHT LH2-type detector, INCA ENERGY 450 software) and EBSD (HKL Nordlys II EBSD camera using Channel 5 software). The instrument was operated at 15 kV and a 1.3-nA current for the EBSD analysis, with a tilting angle of 72 degrees. Individual diffraction patterns were obtained, as well as mapping of the areas of interest. The detection was set to 5–7 bands, 4 × 4 binning. The typical step size was 0.5 μm and the indexing rate was between 95% and 97%. Minimal post-processing was performed in the case of the mappings, which was limited to removing the so-called “wild spikes”. A summary of the EBSD “match units” for the individual carbides is given in Table 2. It is important to point out that the EBSD determination of the carbides is based on their crystallography and not necessarily on their composition. Thus, the Fe3W3C “match unit” is a representative of the M6C carbide, but, for example, Mo, or other elements, could also be present in this carbide type.
Results and Discussion
Starting material
The AISI M42 steel has a ledeburitic microstructure. It consists of a dendritic matrix of α-ferrite and smaller carbides, mostly M6C, M7C3, M2C, large primary M2C carbides and a ledeburite of carbides and ferrite. This microstructure develops during the solidification process, which is sketched in Fig. 1. First, a skeleton of the primary delta-ferrite dendrites is formed, with a progressive enrichment of the remaining adjacent liquid8. As the temperature is reduced, a peritectic reaction occurs and consumes the ferrite, forming a rim of austenite around the delta ferrite and the primary carbides. The ledeburitic eutectic is a fine-grained mixture of eutectic carbides and austenite nucleates and grows in the remaining liquid phase in the interdendritic spaces. The final cast microstructure of AISI M42 ledeburitic steel is compounded by dendrites surrounded by a more-or-less connected net of eutectic carbides. Depending on the chemical composition of the M42 steel and the solidification conditions, either the eutectic metastable M2C or the stable M6C phase forms8,25.
A backscattered-electron (BE) image of the microstructure of the specimen is shown in Fig. 2(a), where all the phases in the microstructure can be seen. A large number of small carbides are present in the ferrite phase26. Figure 2(b) is a close-up of the ferrite phase, where the smaller carbides can be seen. Due to the small size of these carbides and their overlapping Kikuchi patterns, it is rather difficult to identify them. However, three different types of small carbides were successfully indexed in the matrix. The brighter, spherical carbides were determined to be M6C carbides (Fig. 2c), the needle-like carbides were successfully identified as M2C carbides (Fig. 2d) and the darker, spherical carbides were determined to be M7C3-type carbides (Fig. 2e). Most of the carbides are bound together and form clusters of two or more different types of carbides. Carbides smaller than 100 nm cannot be accurately analysed by EBSD due to the presence of overlapping patterns. Hetzner and Van Geertruyden26 reported that the AISI M62 high-speed-steel matrix consists of martensite and a large volume fraction of carbides with two morphologies, i.e., rods and globular. In their study, the rods were identified as M2C carbides and the globular-shaped carbides were determined to be M6C carbides. This is consistent with our experiment, where the needle-shaped carbides were also determined to be M2C carbides with an orthorhombic symmetry, which is reflected in their form.
Figure 3 shows a typical example of a eutectic carbide that is present in the steel. These carbides are in the form of M2C, with a small amount of the M6C-type carbides, most likely not eutectic. The presence of MC carbides is not confirmed, blue spots in Fig. 3(c) are too small to be indexed in the EBSD mapping, which means that the carbides are not present or too small for analysis. The carbide dendritic shape, a result of the EBDS spot analysis, is a resolved Kikuchi pattern representing the M2C-type carbide, Fig. 3(a). The EBSD band-contrast image (Fig. 3b) reveals the details in the microstructure, especially the grain boundaries. From this it is clear that the M2C carbide is monocrystalline, as no grain boundaries can be observed. The EBSD phase-map analysis, shown in Fig. 3(c), supports the idea that the primary and eutectic carbides are homogeneous M2C. Although it is rather difficult to distinguish any chemical inhomogeneity using the energy-dispersive spectroscopy (EDS) technique due to the large analysis volume, the EDS spot line analysis performed across the matrix-carbide boundary indicates a homogeneous composition throughout the carbide phase. As shown in Fig. 3d, the analysed M2C carbide contains mainly Mo, with minor amounts of W, V, Cr and Fe atoms.
Carbide transformation in the bulk during annealing
In our research the SEM-based EBSD technique was applied to track the carbide transformation during the annealing at 1100 °C ad 1150 °C for different annealing times. The microstructural changes taking place during the annealing are shown in Fig. 4. The as-cast steel contains metastable M2C carbides (Fig. 4a), which transform mostly into M6C carbides and a very small amount of MC during the high-temperature annealing. In the case of AISI M42 the amount of MC depends on the vanadium concentration. The evidence from the EBSD mapping shows that the transformation starts on the boundary between the carbide and the ferrite and then grows towards the inner region. Due to low vanadium concentration and consequent most probably small amount of MC, during annealing for 15 minutes at 1100 °C the expected transformation: M2C + matrix → M6C + MC + matrix was not observed. A large specimen area was observed and no MC carbides were found in the EBSD maps or observed as hills in the tilted secondary-electron (SE) image. However, we did observe the M6C carbides. A longer annealing time (30 minutes) caused almost half of the metastable M2C carbides to transform to M6C carbides, which grew from all directions towards the centre of the M2C carbide. The previously monocrystalline M2C carbide transforms to polycrystalline M6C carbides with different orientations (Fig. 4c). Again, no MC carbides were observed in the microstructure. However, after annealing for an hour at the same temperature, the MC carbides were confirmed in the microstructure. In addition most of MC carbides were observed in the ledeburitic areas at the M6C grain boundaries (Fig. 4d).
The results of the EBSD phase-map analysis of the specimen annealed at 1100 °C for 60 minutes are shown in Fig. 5. It appears that during annealing at 1100 °C for 60 minutes part of the M2C carbides transformed into the M6C carbide type, with some additional MC carbides (Fig. 5c). The EDS analyses of the individual carbides showed that the M6C carbides were rich in both iron and molybdenum, while the M2C carbides were mostly molybdenum. However, some other carbide-forming elements can be exchanged in the crystal structure. The EDS line profile across the M6C carbide growth boundary, as shown in Fig. 5d, clearly indicates that the transformation of the carbide is driven by the atomic diffusion of molybdenum and iron. The M6C carbide transformation starts on the carbide surface, after which the phase boundary moves towards the centre of the carbide. At the same time, the crystal structure transforms from orthorhombic M2C to cubic M6C. However, as long as the concentration of elements remains below a certain level, the crystal transformation cannot occur. A comparison of the EBSD band-contrast and phase maps for the as-cast and annealed specimens reveals a change in microstructure occurring during the annealing (Fig. 5b). During annealing, the MC carbides form alongside the transformation of the M2C carbides into M6C, with the large M2C carbides transforming mainly into a few, small-grained M6C carbides with a different crystal orientation. This phenomenon has a beneficial effect on the final microstructure of forged-and-annealed AISI M42 steel. During production, the AISI M42 high-speed steel goes through a plastic deformation, which is the result of the forging process at high temperature. During this plastic deformation the eutectic carbides transform to a more stable form and break into smaller and more uniformly shaped carbides24,25. Because the large monocrystal M2C carbides transform into differently oriented M6C carbides, they can be broken down more easily during forging. Due to the carbide transformation, the final microstructure of the forged-and-annealed AISI M42 steel has smaller M6C and MC carbides, the same as if the starting material already contained stable M6C carbides.
Reports in the literature suggest that, in general, the M2C carbide transformation follows the path: M2C + matrix → M6C + MC + matrix2,3,10,11,12,13,14. Figure 5d shows that the M2C carbide is richer in V than the M6C carbide; therefore, it can be concluded that the content of vanadium controls the amount of MC carbides formed. The vanadium has to diffuse out of M2C carbides in order to make way for the newly formed M6C carbides that have decreased solubility of vanadium. This might provide an explanation as to why the MC carbides are mostly formed at the M6C carbide grain boundaries.
To better understand the process of carbide transformation, let us take a look at what is happening during the solidification. Based on our observations, we propose the following transformation. The metastable, primarily M2C monocrystalline carbide plus the matrix transform into stable polycrystalline M6C carbides. The metastable ledeburitic M2C monocrystalline carbide plus the matrix transform into stable polycrystalline M6C and monocrystalline MC carbides. At higher temperatures, due to an increased vanadium concentration more MC carbides form in the ledeburitic area. It is obvious that during the solidification process a higher concentration of vanadium is present in the last solidified region, which is the ledeburitic area.
Figure 6 shows ledeburite in the centre image and a larger primary carbide on the top-right of the ledeburite. All the M2C carbides, both primary and those from the ledeburite, are transformed into the M6C carbide. In the ledeburite region the MC carbides are easily observed. This is typical for most of the observed microstructure. The other area where the MC carbides form is on the phase boundary of the M6C carbides transformed from the primary M2C carbide.
Carbide transformation during annealing on the free surface
From the in-situ-analysis point of view it is very important to identify what is happening with the microstructure on the free surface and compare it with the process in the bulk. Figure 7 shows the microstructure development of the free surface during annealing at 1100 °C for 30 minutes in a protective atmosphere of argon. As is clear from the image, this process is not the same as that occurring in the bulk.
In comparison with the processes in the bulk, the surface is slightly different: many M6C carbides were found on the top of the M2C carbides and in the matrix and small MC carbides are also present on the surface of the annealed specimen. Most probably, the M6C carbides start to form on the surface in the matrix-M2C phase boundary. The EDS spot line analysis showed a similar composition for the M6C carbides formed in the bulk (Fig. 5d) and on the in-situ-annealed surface specimens (Fig. 7d), while the M2C carbides had a higher concentration of Fe atoms in the case of the in-situ-annealed surface specimens.
In an earlier investigation24 we looked at a different annealing set-up: the specimens were kept in a vacuum on Mo boats and were heated by a large direct current sent through the specimens. However, we discovered later that this set-up could introduce some Mo contamination on the surface of the specimens due to evaporation from the Mo boat. For this reason we introduced a completely different vacuum-annealing procedure using a stub heater in a protective atmosphere of Ar to ensure that there was no contamination from the heating element.
Discussion
Mechanism of carbide transformation in the bulk and on the free surface
Figure 8 shows a sketch of the bulk-microstructure development process during annealing, while Fig. 9 is a sketch of the process for the surface-microstructure development during annealing. In both cases the starting microstructure consists of unstable M2C eutectic carbides in a ferrite matrix. In the case of a bulk transformation during the annealing, the unstable M2C carbides transform into small, stable M6C and MC carbides with a different crystal orientation.
The sketch of the surface-microstructure development shows a different route for the carbide transformation due to the effect of the free surface and, consequently, the different diffusion processes. High-temperature annealing leads to all of the M2C carbides being covered with a thin layer of M6C carbides. At higher temperatures the matrix surface becomes covered with M6C carbides.
This difference seems to be due to the migration of carbide forming atoms on the surface as a result of the surface diffusion, which is much faster than the bulk diffusion27 and is very likely the reason for the different carbide-transformation phenomena. in-situ and quasi-in-situ studies of the phase transformations might not always give results that are representative of the actual processes taking place in the bulk of the material, which could be attributed to completely different diffusion conditions in the bulk and on the free surface, but also the temperature variations within the specimen and the compositional inhomogeneity could play a role. Nonetheless, it is important to note that the results obtained when using the in-situ studies on surfaces need to be interpreted carefully when referring to the material properties.
Conclusions
In summary, the microstructure development of the as-cast, molybdenum-containing, super-high-speed steel AISI M42 was studied in order to clarify the carbide-transformation phenomena and to show that in-situ observations do not always accurately represent the transformation phenomena taking place in the bulk of the material. An as-cast microstructure was chosen with unstable primary and eutectic M2C carbides in the ferrite matrix. Annealing resulted in a partial transformation of the large M2C carbides into several small and more stable grains of M6C and small MC carbides, with an associated change in the crystal orientation. This carbide transformation phenomenon has a beneficial effect during forging and therefore it can contribute to the design of future thermo-mechanical processes for high-speed steels.
The results have also shown an interesting difference in the carbide-transformation reactions on the surface versus the bulk of the alloy, presumably due to the operation of different diffusion processes. An in-situ study of surface-driven phenomena during the annealing of AISI M42 super-high-speed steel was found to give different results compared to the bulk. In the case of the bulk, the M2C-to-M6C transformation starts at the M2C/matrix boundary and uniformly propagates inwards. However, on the free-surface, although starting at the M2C/matrix boundary, the transformation kinetics are non-uniform. Due to faster surface diffusion the atoms tend to migrate on top of the existing carbide and form a new, stable carbide. Similar processes can also be observed in the matrix, where the stable carbides precipitate and form a new carbide layer.
This study shows that special attention should be paid during the in-situ studies of diffusion-driven transformations where the phenomena observed on the free surface are not necessarily the same as those observed in the bulk. This was demonstrated in the case of carbide transformations and it is reasonable to expect that there are other, similar examples.
Additional Information
How to cite this article: Godec, M. et al. Surface and Bulk Carbide Transformations in High-Speed Steel. Sci. Rep. 5, 16202; doi: 10.1038/srep16202 (2015).
References
Llewellyn, D. T. & Hudd, R. C. In Steels: Metallurgy and Applications 3rd edn, Ch. 3, 199–290 (Butterworth-Heinemann, Oxford 1998).
Pan, F. S. et al. Phase transformation refinement of coarse primary carbides in M2 high speed steel. Prog Nat Sci: Mater Int 21, 180–186 (2011).
Hwang, K. C., Lee, S. & Lee, H. C. Effects of alloying elements on microstructure and fracture properties of cast high speed steel rolls: Part I: Microstructural analysis. Mat Sci Eng A-Struct 254, 282–296 (1998).
Godec, M. et al. Characterization of the carbides and the martensite phase in powder-metallurgy high-speed steel. Mater Charact 61, 452–458 (2010).
Colaço, R., Gordo, E., Ruiz-Navas, E. M., Otasevic, M. & Vilar, R. A comparative study of the wear behaviour of sintered and laser surface melted AISI M42 high speed steel diluted with iron. Wear 260, 949–956 (2006).
Zhang, X., Liu, W. L., Sun, D. & Li, Y. The transformation of carbides during austenization and its effect ion the wear resistance of high speed steel rolls. Metall Mater Trans A, 38A, 499–505 (2007).
Ding, P., Shi, G. & Zhou, S. As-Cast Carbides in High-Speed Steels. Metall Mater Trans A, 24, 1265–1272 (1993).
Hoyle, G. High Speed Steels. Butterworth-Heinemann, Oxford 1988.
Guo, J. et al. Characterization on carbide of a novel steel for cold work roll during solidification process. Mater Charact 79, 100–109 (2013).
Karagöz, S., Liem, I., Bischoff, E. & Fischmeister, H. F. Determination of carbide and matrix compositions in high-speed steels by analytical electron microscopy. Metall Mater Trans A 20, 2695–2701 (1989).
Ghomashchi, M. R. Quantitative microstructural analysis of M2 grade high speed steel during high temperature treatment. Acta Mater 46, 5207–5220 (1998).
Fischmeister, H. F., Riedl, R. & Karagöz, S. Solidification of high-speed tool steels. Metall Mater Trans A 20, 2133–2148 (1989).
Zhou, B., Shen, Y., Chen, J. & Cui, Z. S. Breakdown Behavior of Eutectic Carbide in High Speed Steel During Hot Compression. J Iron Steel Res Int 18, 41–48 (2011).
Lee, E. S., Park, W. J., Jung, J. Y. & Ahn, S. Solidification microstructure and M2C carbide decomposition in a spray-formed high-speed steel. Metall Mater Trans A 29, 1395–1404 (1998).
Morris, R. A., Wang, B., Matson, L. E. & Thompson, G. B. Microstructural formations and phase transformation pathways in hot isostatically pressed tantalum carbides. Acta Mater 60, 139–148 (2012).
Borgh, I. et al. On the three-dimensional structure of WC grains in cemented carbides. Acta Mater 61, 4726–4733 (2013).
Laigo, J., Christien, F., Le Gall, R., Tancret, F. & Furtado, J. SEM, EDS, EPMA-WDS and EBSD characterization of carbides in HP type heat resistant alloys. Mater Charact 59, 1580–1586 (2008).
Godec, M., Kocjan, A. & Jenko, M. Characterization of the carbides in a Ni-Ti shape-memory alloy wire. Mater Tehnol 1, 61–65 (2011).
Park, K. K. et al. In situ deformation behavior of retained austenite in TRIP steel. Mater Sci Forum 408–412, 571–576 (2002).
Seward, G. G. E., Celotto, S., Prior, D. J., Wheeler, J. & Pond, R. C. In situ SEM-EBSD observations of the hcp to bcc phase transformation in commercially pure titanium. Acta Mater 52, 821–832 (2004).
Hurley, P. J. & Humphreys, F. J. A study of recrystallization in single-phase aluminium using in-situ annealing in the scanning electron microscope. J Microsc 213, 225–234 (2004).
Guo, L. Q. et al. Annealing effects on the microstructure and magnetic domain structures of duplex stainless steel studied by in situ technique, Appl Surf Sci 259, 213–218 (2012).
Huang, Y. M., Fu, Q. & Pan, C. X. In Situ-Tracking Observation of Stainless Steel Microstructural Development during Elevated Service Using EBSD and SEM, Mater Sci Forum 561–565, 2087–2090 (2007).
Godec, M., Šetina Batič, B. & Večko Pirtovšek, T. In Characterization of Minerals, Metals and Materials (eds Carpenter J. S. et al.) in-situ EBSD investigation of carbides during annealing of AISI M42 steel, 187–190 (TMS, 2014).
Večko Pirtovšek, T., Kugler, G. & Terčelj, M. The behaviour of the carbides of ledeburitic AISI D2 tool steel during multiple hot deformation cycles. Mater Charact 83, 97–108 (2013).
Hetzner, D. W. & Van Geertruyden, W. Crystallography and metallography of carbides in high alloy steels. Mater Charact 59, 825–841 (2008).
Cahn, R. W. & Haasen, P., Physical Metallugy, 4th Edition, Elsevier Science B.V., Amsterdam, 1996.
Acknowledgements
This work was financially supported by the Ministry of Education, Science and Sport of the Republic of Slovenia as part of the Research program P2-0132 Physics and Chemistry of Surfaces of Metallic Materials and the Research program P2-0056 Vacuum Science and Materials for Electronics. The authors would like to thank dr. Črtomir Donik for his help with the analytical equipment.
Author information
Authors and Affiliations
Contributions
M.G. performed electron microscopy EDS/EBSD studies and wrote the paper. B.S.B. carried out annealing experiments. All authors assisted with interpreting the data. All authors discussed the results and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Godec, M., Večko Pirtovšek, T., Šetina Batič, B. et al. Surface and Bulk Carbide Transformations in High-Speed Steel. Sci Rep 5, 16202 (2015). https://doi.org/10.1038/srep16202
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep16202
- Springer Nature Limited
This article is cited by
-
High-Temperature Annealing Significantly Enhances Intrinsic Hot Workability of the As-cast High-Nitrogen M42 High-Speed Steel
Metallurgical and Materials Transactions A (2022)
-
Effects of Nitrogen on the Morphology and Evolution of M2C Eutectic Carbides in Fe-Mo-W-Co-Cr-V-C Alloy
JOM (2020)
-
Influence of the Nitrogen Content on the Carbide Transformation of AISI M42 High-Speed Steels during Annealing
Scientific Reports (2018)