Abstract
Van der Waals materials have received a great deal of attention for their exceptional layered structures and exotic properties, which can open up various device applications in nanoelectronics. However, in situ epitaxial growth of dissimilar van der Waals materials remains challenging. Here we demonstrate a solution for fabricating van der Waals heterostructures. Graphene/hexagonal boron nitride (h-BN) heterostructures were synthesized on cobalt substrates by using molecular beam epitaxy. Various characterizations were carried out to evaluate the heterostructures. Wafer-scale heterostructures consisting of single-layer/bilayer graphene and multilayer h-BN were achieved. The mismatch angle between graphene and h-BN is below 1°.
Similar content being viewed by others
Introduction
Van der Waals (vdW) materials are layered structures bonded with vdW forces. This group of materials have received high interest recently for their novel properties and high potential in various device applications1,2,3. While graphene is one of the most prominent vdW members, beyond graphene materials such as MoS2, ZnSe and hexagonal boron nitride (h-BN) are also being eagerly investigated4,5,6,7,8,9,10,11. For exploring new paradigm in the two dimensional (2D) devices, atomic-scale heterostructures, which are made from a combination of alternating layers of graphene, h-BN, MoS2 and so on, have been paid a great deal of attention. Such heterostructures provide a platform to investigate novel phenomenon in fundamental physics and there are reports indicating superior properties for device applications12,13,14,15. Among these vdW heterostructures, the stacking of h-BN with another vdW layer, in particular, graphene16,17, is of imminent interest. H-BN has a hexagonal crystal structure similar to graphene’s with less than 2% lattice mismatch18. H-BN is a dielectric with a dielectric constant of about 419 and a wide bandgap of ~5.9 eV7. H-BN also has exceptional thermal and chemical stabilities10. These properties enable h-BN as an excellent chemical and electrical barrier material for graphene and other vdW materials.
To obtain such heterostructures, mechanical exfoliation and chemical vapor deposition (CVD) growth were widely used20,21,22. Much success has been achieved. Nevertheless, direct deposition of high-quality, wafer-scale vdW heterostructures remains challenging. Therefore, non-CVD approaches have been proposed recently, for example, a plasma-assisted deposition method has been used to achieve epitaxial growth of single-domain graphene on h-BN23. As a versatile tool, molecular beam epitaxy (MBE) has natural advantages in high-quality heterostructure growth thanks to its ultra-high vacuum (UHV) environment, atomic layer epitaxy accuracy and controllability, instant introduction and control of multiple sources, easy of doping of materials and in situ layer-by-layer characterization. As a matter of fact, vdW epitaxy was first demonstrated using MBE process24,25. Most recently, MBE has also been used to successfully synthesize single-layer and bilayer graphene26,27,28,29. In this paper, we report MBE growth of high-quality graphene/h-BN stacked heterostructures on cobalt substrate. Scalable wafer-scale graphene/h-BN films with a misorientation of less than 1° were achieved.
Experiments
Thermally oxidized Si wafers with a SiO2 layer of 300 nm were used as substrates. They were transferred to an E-beam evaporator system for the deposition of a Co film of 400 nm. The wafers were subsequently loaded on to standard 3″ wafer holders and transferred to an MBE system for growth. A Knudsen effusion cell filled with B2O3 powder (Alfa Aesar, 99.999%) was used as B source. A thermocracker was used to crack acetylene gas (Airgas, 99.999%) as C source. The C source was tuned by either acetylene gas flow or cracker temperature. An electron cyclotron resonance (ECR) system was used to form nitrogen gas plasma (Airgas, 99.9999%) as N atomic source. The N source was tuned by either nitrogen gas flow or ECR magnetron current.
For a typical growth, the substrate is firstly annealed at 800 ~ 850 °C under a hydrogen flow of 10 sccm for a duration of 30 minutes. At the end of substrate surface treatment, the hydrogen gas flow is stopped and substrate temperature is further ramped up to 870 ~ 900 °C for graphene/h-BN heterostructure growth. The thermal cracker temperature is ramped to 1200 °C and 3 sccm acetylene is introduced into the chamber for graphene growth. The growth lasts from 10 s to 1 minute. Subsequently, h-BN growth follows with minimal time gap. B cell temperature is precisely ramped to 900 ~ 1100 °C right before h-BN layer growth. Nitrogen flow rate is 10 sccm and the growth lasts 10 ~ 15 minutes. At the end of h-BN growth, the substrate temperature is slowly cooled down towards room temperature at a rate of 10 °C/min. The slow substrate cooling process suggests that the epitaxy undergoes layer-by-layer growth mode, which is in contrast to fast cooling procedure with much higher cooling rates in the growth of graphene by precipitation of carbon atoms from the metal substrate in some CVD process30,31.
Raman characterizations were performed using a HORIBA LabRam system equipped with a 50-mW 514-nm green laser. Scanning electron microscopy (SEM) images were acquired using a Philips XL30-FEG system. X-ray photoelectron spectroscopy (XPS) was carried out using a Kratos AXIS ULTRA XPS system equipped with an Al Kα monochromatic X-ray source and a 165 mm mean radius electron energy hemispherical analyzer. Transmission electron microscopy (TEM) images and electron diffraction patterns were acquired using a FEI/Philips CM-30 TEM. Plan-view TEM sample was prepared using direct transfer method. After spin coated with PMMA, the sample was submerged in FeCl3 solution to etch away the Co metal layer, which often takes several days. The film was then transferred onto carbon coated Cu TEM grid and treated with acetone and DI water to remove PMMA. Cross sectional TEM sample was prepared using focused ion beam technique. The graphene/h-BN thin film was covered by an Ir layer and further protected by electron-beam and ion-beam deposited Pt layers.
Results and Discussion
As grown vdW thin films are transparent and thus not visible for bare eye or through optical microscope (Fig. S1, supporting material). As the samples are characterized by SEM, a surface contrast is observed in secondary electron image because secondary electron signals from h-BN and graphene/Co substrate have different intensity. Figure 1 shows an SEM image of a graphene/h-BN sample (Sample A) on which large triangular domains of ~20 μm are observed. Despite the underlying very rough Co substrate surface, which consists of small grains due to heat treatment, wafer-scale graphene has been grown, followed by the formation of the triangular shaped h-BN domains as inferred by both optical microscope imaging and Raman scattering results (Figs S1 and S2 supporting material).
In order to achieve continuous wafer-scale h-BN single domain instead of discrete flakes, fine-tuning of the sample growth condition was performed. Detailed difference in growth condition is summarized in Table 1 of supporting material, in which four samples are listed. By reducing high-temperature substrate treatment duration, graphene layer thickness and growth temperature for h-BN layer, the resulting sample (Sample B) shows smoother surface morphology under optical microscopy (Fig. S3, supporting material). The shorter growth time and thinner graphene layer clearly improve h-BN layer growth. Sample B (Table 1, supporting material) exhibits the graphene/h-BN film that covers the entire sample surface and triangular h-BN domains are no longer visible (Fig. S4, supporting material). Although wafer-scale h-BN/graphene heterostructure thin films were also obtained for samples (Samples S1 and S2) grown with the same substrate treatment procedure, higher graphene growth temperature and longer h-BN growth time as that of Sample A, these films are not as uniform as that of Sample B (Fig. S5, supporting material). Further detailed characterizations were based on Sample B.
Figure 2a shows an XPS survey scan spectrum, with the peaks of interest circled. Fine scans were performed in these sites and evident energy peaks for B, C and N were observed. Figure 2b–d show XPS spectrum of B1s, C1s and N1s state, respectively. C1s peak is observed at a position of 284.5 eV, which is smaller than environmental C1s peak in XPS and is closer to the sp2 C-C bond at 284.0 eV32. This is an indication of graphene. B1s and N1s exhibit an energy position at 398.0 eV and 190.6 eV, respectively, which are typical characteristics of h-BN33. Based on integrated peak intensity and corrections, B/N ratio was estimated to be 1.1 from the surface of h-BN, indicating that the growth of h-BN is slightly B-rich.
Figure 3 shows Raman spectrum of the sample. The G/2D peak ratio of the graphene signals indicates the existence of single-layer/bilayer graphene. The inset is a spectrum near the graphene D peak, which lies at 1356 cm−1. The appearance of D peak has been observed in other reports of graphene/h-BN heterostructure34. In addition, an h-BN E2g optical phonon peak is evident at 1364 cm−1. Analyzing the 2D peak of graphene to detect the mismatch angle of graphene and h-BN has been reported recently35. In this experiment, the FWHM of the 2D peak of as grown sample is 38 cm−1, which indicates the mismatch angle is below 1°.
Figure 4a shows a plan-view TEM image of the transferred graphene/h-BN heterostructure. Continuous thin film is observed with some areas folded. Black spots originate from PMMA residue during film transfer process. Figure 4b shows a selected area electron diffraction (SAED) pattern of the plan-view graphene/h-BN heterostructure thin film. A clear hexagonal set of diffraction spots is observed. A second set, which has weaker intensity and larger diffraction angle, is also seen. The inset shows a zoom-in image of the area marked with a red square, showing clearly two diffraction spots. The two spots correspond to the electron diffraction from (100) planes of h-BN and graphene, respectively. The calculated interplanar spacings corresponding to the two spots are 2.13 Å and 2.06 Å, which match well with expected numbers for h-BN and graphene, respectively. The strong intensity of h-BN diffraction pattern may indicate a well-aligned, multi-layer h-BN. There is a small rotation (<1°) observed between the two sets, similar to other reports on graphene/h-BN heterostructures36, which also matches our conclusion from Raman spectrum. Figure 4c shows a cross-sectional TEM image of the heterostructure. Lattice fringes are observed in the ~15nm thick band. The inter-fringe distance is 0.33nm, which is in close agreement with the out-of-plane lattice constants of h-BN and graphene.
Conclusion
We have demonstrated direct epitaxial growth of h-BN on graphene utilizing MBE. Signature triangular h-BN flakes with sizes as large as 20 μm were observed. Further improvement on the growth condition results in high-quality wafer-scale graphene/h-BN heterostructure single domain film. The epitaxial single/bi-layer graphene/few-layer h-BN structure is further confirmed by XPS, Raman spectroscopy, electron diffraction and TEM imaging. The misorientation between the graphene and h-BN layers is less than 1°. While MBE synthesis of high-quality graphene/h-BN heterostructures is a critical step toward the realization of 2D electronics, reasonable electronic functionality of heterostructures is of greater concern. In the future work, two- and three-terminal devices will be fabricated and the electrical measurements will be carried out to evaluate their electrical performance.
Additional Information
How to cite this article: Zuo, Z. et al. In-situ epitaxial growth of graphene/h-BN van der Waals heterostructures by molecular beam epitaxy. Sci. Rep. 5, 14760; doi: 10.1038/srep14760 (2015).
References
Fiori, G. et al. Electronics based on two-dimensional materials. Nat. Nanotechnol. 9, 768–779 (2014).
Xia, F., Farmer, D. B., Lin, Y. M. & Avouris, P. Graphene field-effect transistors with high on/off current ratio and large transport band gap at room temperature. Nano Lett. 10, 715–718 (2010).
Bolotina, K. I. et al. Ultrahigh electron mobility in suspended graphene. Solid State Commun. 146, 351–355 (2008).
Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805-1–136805-4 (2010).
Radisavljevic, B., Radenovic, A., Brivio1, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nat. Nanotechnol. 6, 147–150 (2011).
Liu, L., Feng, Y. P. & Shen, Z. X. Structural and electronic properties of h-BN. Phys. Rev. B 68, 104102-1–104102-8 (2002).
Watanabe, K., Taniguchi, T. & Kanda, H. Direct-bandgap properties and evidence for ultraviolet lasing of hexagonal boron nitride single crystal. Nat. Mat. 3, 404–409 (2004).
Mas-Balleste, R., Gomez-Navarro, C., Gomez-Herrero, J. & Zamora, F. 2D materials: to graphene and beyond. Nanoscale 3, 20–30 (2011).
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012).
Xu, M., Lian, T., Shi, M. & Chen, H. Graphene-like two-dimensional materials. Chem. Rev. 113, 3766–3798 (2013).
Butler, S. Z. et al. Progress, challenges and opportunities in two-dimensional materials beyond graphene. ACS Nano 7, 2898–2926 (2013).
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nat. 499, 419–425 (2013).
Ponomarenko, L. A. et al. Tunable metal–insulator transition in double-layer graphene heterostructures. Nat. Phys. 7, 958–961 (2011).
Dean, C. R. et al. Graphene based heterostructures. Solid State Commun. 152, 1275–1282 (2012).
Georgiou T. et al. Vertical field-effect transistor based on graphene–WS2 heterostructures for flexible and transparent electronics. Nat. Nanotechnol. 8, 100–103 (2013).
Dean, C. R. et al. Boron nitride substrates for high-quality graphene electronics. Nat. Nanotechnol. 5, 722–726 (2010).
Kim, K. K. et al. Synthesis and characterization of hexagonal boron nitride film as a dielectric layer for graphene devices. ACS Nano 6, 8583–8590 (2012).
Giovannetti, G., Khomyakov, P. A., Brocks, G., Kelly, P. J. & Van der Brink, J. Substrate-induced band gap in graphene on hexagonal boron nitride: Ab initio density functional calculations. Phys. Rev. B 76, 073103-1–073103-8 (2007).
Young, A. F. et al. Electronic compressibility of gapped bilayer graphene. Phys. Rev. B 85, 235458-1–235458-5 (2012).
Shi, Y. et al. Synthesis of few-layer hexagonal boron nitride thin film by chemical vapor deposition. Nano Lett. 10, 4134–4139 (2010).
Bjelkevig, C. et al. Electronic structure of a graphene/hexagonal-BN heterostructure grown on Ru (0001) by chemical vapor deposition and atomic layer deposition: extrinsically doped graphene. J. Phys.: Condens. Matter. 22, 302002-1–302002-6 (2010).
Liu et al. Direct Growth of Graphene/Hexagonal Boron Nitride Stacked Layers. Nano Lett. 11, 2032–2037 (2011).
Yang, W. et al. Epitaxial growth of single-domain graphene on hexagonal boron nitride. Nat. Mater. 12, 792–797 (2013).
Koma, A., Sunouchi, K. & Miyajima, T. Fabrication of ultrathin heterostructures with van der Waals epitaxy. J. Vac. Sci. Technol. B 3, 724 (1985).
Koma, A. & Yoshimura, K. Van der Waals epitaxy—a new epitaxial growth method for a highly lattice-mismatched system. Thin Solid Films 216, 72–76 (1992).
Zhan, N., Wang, G. & Liu, J. Cobalt-assisted large-area epitaxial graphene growth in thermal cracker enhanced gas source molecular beam epitaxy. Appl. Phys. A: Mater, Sci. Process 105, 341–345 (2011).
Park, J. et al. Epitaxial graphene growth by carbon molecular beam epitaxy (CMBE). Adv. Mater. 22, 4140–4145 (2010).
Garcia, J. M. et al. Graphene growth on h-BN by molecular beam epitaxy. Solid State Commun. 152, 975–978 (2012).
Oliveira, Jr. et al. Mono- and few-layer nanocrystalline graphene grown on Al2O3 (0001) by molecular beam epitaxy. Carbon. 56, 339–350 (2013).
Zhan, N., Olmedo, M., Wang, G. & Liu, J. Layer-by-layer synthesis of large-area graphene films by thermal cracker enhanced gas source molecular beam epitaxy. Carbon 49, 2046–2052 (2011).
Li, X. et al. Large-Area Synthesis of High-Quality and Uniform Graphene Films on Copper Foils. Science 324, 1312–1314 (2009).
Moreau, E., Ferrer, F. J., Vignaud, D., Godey, S. & Wallart, S. Graphene growth by molecular beam epitaxy using a solid carbon source. Phys. Status Solidi A 207, 300–303 (2010).
Park, K. S., Lee, D. Y., Kim, K. J. & Moon, D. W. Observation of a hexagonal BN surface layer on the cubic BN film grown by dual ion beam sputter deposition. Appl. Phys. Lett. 70, 315–317 (1997).
Kim, S. M. et al. Synthesis of patched or stacked graphene and h-BN flakes: a route to hybrid structure discovery. Nano Lett. 13, 933–941 (2013).
Eckmann, A. et al. Raman fingerprint of aligned graphene/h-BN supper lattices. Nano Lett. 13, 5242–5246 (2013).
Wang, M. et al. A platform for large-scale graphene electronics—CVD growth of single-layer graphene on CVD-grown hexagonal boron nitride. Adv. Mater. 25, 2746–2752 (2013).
Acknowledgements
This work was supported in part by FAME, one of six centers of STARnet, a Semiconductor Research Corporation program supported by MACRO and DARPA. Cross-sectional TEM specimen preparation using focus ion beam technique and part of TEM imaging were performed at Irvine Materials Research Institute (IMRI) at UC Irvine, using instrumentation funded in part by the National Science Foundation Center for Chemistry at the Space-Time Limit (CHE-082913).
Author information
Authors and Affiliations
Contributions
J.L. leads the project. Z.Z. designed and performed the epitaxial growth. Z.X. contributed on developing h-BN layer growth condition. Z.X., R.Z. and Z.Z. performed SEM imaging and analysis. R.Z., Z.Z. and J.G.Z. performed TEM imaging and analysis. A.K. fabricated Co substrate and contributed on transferring graphene growth condition. Z.Z. and J.L. wrote the manuscript. All authors contributed to analyzing and reviewing the data in this manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Zuo, Z., Xu, Z., Zheng, R. et al. In-situ epitaxial growth of graphene/h-BN van der Waals heterostructures by molecular beam epitaxy. Sci Rep 5, 14760 (2015). https://doi.org/10.1038/srep14760
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep14760
- Springer Nature Limited
This article is cited by
-
Uniaxial films of maximally controllable response under visible light
Scientific Reports (2020)
-
Widely tunable electronic properties in graphene/two-dimensional silicon carbide van der Waals heterostructures
Journal of Computational Electronics (2019)
-
An atomic carbon source for high temperature molecular beam epitaxy of graphene
Scientific Reports (2017)
-
Deposition of topological silicene, germanene and stanene on graphene-covered SiC substrates
Scientific Reports (2017)
-
A hybrid MBE-based growth method for large-area synthesis of stacked hexagonal boron nitride/graphene heterostructures
Scientific Reports (2017)