Abstract
Nonlinear processes involving frequency-mixing of light fields set the basis for ultrafast coherent spectroscopy of collective modes in solids. In certain semimetals and semiconductors, generation of coherent phonon modes can occur by a displacive force on the lattice at the difference-frequency mixing of a laser pulse excitation on the electronic system. Here, as a low-frequency counterpart of this process, we demonstrate that coherent phonon excitations can be induced by the sum-frequency components of an intense terahertz light field, coupled to intraband electronic transitions. This nonlinear process leads to charge-coupled coherent dynamics of Raman-active phonon modes in the strongly correlated metal V2O3. Our results show an alternative up-conversion pathway for the optical control of Raman-active modes in solids mediated by terahertz-driven electronic excitation.
Similar content being viewed by others
Introduction
Phononics has recently been proposed as a promising avenue towards a new generation of faster and more efficient technologies1. Phenomena associated with lattice dynamics are often analogous to well-known effects involving electrons, for example chirality and the phonon Hall effect2,3,4. Moreover, control over coherent phonons offers potential new pathways to drive transitions between phases in condensed matter and to coherently manipulate the ground state of magnetically ordered phases5,6,7,8,9,10,11. While coherent acoustic phonon modes are commonly generated by wide variety of mechanisms12, higher-frequency coherent optical phonon modes are typically driven from interactions with intense sub-picosecond light pulses13.
In most cases, light pulses can drive optical phonons either directly via resonant electric-dipole interaction14,15, or indirectly via interactions with electronic states or other phonon modes10,16,17,18. The latter case is a generalization of the stimulated Raman mechanism, in which the ultrashort light pulse couples to the electronic system resulting in a nonlinear force on the lattice that resonantly drives coherent phonon modes at the difference frequency mixing Ω = ω1 − ω2, with ω1 and ω2 taken for the pulse spectrum. This is commonly referred to in the literature as either Impulsive Stimulated Raman Scattering (ISRS), when the light field is non-resonantly coupled to the electric system (in optically transparent solids), or Displacive Excitation of Coherent Phonons (DECP), when the light pulse is resonant with intraband or interband electronic transitions (in opaque solids)19,20,21,22,23. Unlike ISRS, which involves non-resonant coupling to electronic states to produce impulsive excitation, in the DECP regime, coherent phonons are generated by a displacive force associated with a sudden change in carrier density or electronic temperature induced by the intense light pulse. A third generation mechanism is called Ionic Raman scattering (IRS) and involves a higher frequency phonon mode that serves as the intermediate18. In all these processes, the driving mechanism involves difference-frequency mixing, and requires the bandwidth of the driving light pulse to be comparable to or larger than the frequency of the optical phonon mode that is to be excited24.
As an alternative to these well-established routes for coherent phonon generation using stimulated Raman schemes, it is also possible to drive coherent Raman-active vibrational modes using sum-frequency excitation (SFE)25,26. Recent experiments, indeed, have demonstrated both photonic and phononic SFE mechanisms25,27,28,29,30, which involve the absorption of two photons or two phonons with frequencies ω1 and ω2 to create one phonon in a Raman-active mode at frequency Ω = ω1 + ω2, as up-conversion counterparts of ISRS and IRS, respectively.
Here, we demonstrate an alternative scheme for coherent generation of Raman-active phonon modes based on terahertz-driven dispacive excitation as up-conversion counterpart of the DECP mechanism. An intense THz pulse, inducing strong transient electronic excitation, is found to generate large-amplitude coherent oscillations of Raman-active phonon modes in the metallic phase of V2O3 at twice the frequency of the driving field. This nonlinear process can be described as a displacive excitation that involves the sum-frequency mixing component of the THz pulse coupled to the electronic system. The temperature dependence of the generated coherent phonons supports the scenario in which the excitation process is strongly enhanced by intra-band electronic transitions driven by the intense THz field.
Results
Coherent phonon oscillations detected by THz pump – near-infrared probe spectroscopy
In V2O3, strong electronic correlations cause a metal-insulator transition (MIT) at TMIT ≃ 150 K, which is accompanied by a first-order structural transition from corundum to monoclinic31,32. Recent experiments have shown that the coherent lattice displacement generated by perturbing the electronic distribution of strongly correlated metallic phase of V2O3 through ultrafast light excitation can drive both longitudinal acoustic waves and optical phonons33,34,35,36,37. In these photoexcitation processes, the electron-phonon coupling plays a central role in the transient atomic displacement of the structure38.
Figure 1a shows the schematic electronic energy levels for the metallic phase of V2O3. The Fermi energy crosses the partially filled a1g and \({e}_{g}^{\pi }\) bands, enabling the direct optical absorption of THz light by intraband electronic transitions31,32. The Γ-point structural dynamics in this phase is largely dominated by a fully-symmetric A1g optical phonon mode at Ω/2π = 7.1 THz, which corresponds to the optical bending mode of the V2O2 unit cell [see displacement vectors in Fig. 1b35,39]. Other Raman-active optical phonons in this frequency range, for example the Eg phonon mode at ~ 6 THz39, have a comparatively lower Raman cross-section, as detailed in the Supplementary Note 3 and Supplementary Fig. 4.
To study the possibilities for driving coherent structural dynamics in V2O3, we performed ultrafast THz pump-optical probe spectroscopy (scheme shown in Fig. 1c). Intense quasi single-cycle THz pulses were focused onto the sample. The THz-induced response was monitored by measuring the optical transmission modulation ΔT/T of a near-infrared (NIR) laser probe at 1.55 eV as a function of the time delay tpp with respect to the pump25,40. The ΔT/T response is able to detect the coherent lattice oscillations from the fully-symmetric A1g via time-dependent modulation of the diagonal elements of the linear optical susceptibility tensor, while it is insensitive to the Eg modes, which effect the probe polarization state through the modulation of the off-diagonal elements of the susceptibility tensor (see detailed discussion in Supplementary Note 4).
The temporal waveform of the THz pump electric field E(t) (see Fig. 1d) was measured at the sample position using electro-optic sampling from a GaP crystal (see Supplementary Methods). The center frequency of the pump is νp ≃ 3.5 THz. The sample is a high-quality, 84 nm thick V2O3 thin film epitaxially grown on an R-plane (1 -1 0 2) − Al2O3 substrate (see Methods). Figure 1e shows the temporal evolution of the THz-induced transmission modulation ΔT/T. The time origin (tpp = 0) is set to the delay where the optical probe interacts with the sample at the same time as does the peak of the square of the pump electric field ∣E(t)∣2. The observed THz-induced dynamics are dominated by coherent oscillations superimposed to a gradually increasing slowly-varying background. This long-lived step-like evolution of ΔT/T is attributed to incoherent dynamics of the electronic thermalization through electron-phonon scattering, as described in refs. 33,35. Strikingly, the oscillating component of ΔT/T clearly displays oscillations with a period shorter than the one of the THz driving field. To better show this feature, in Fig. 1f we compare the oscillatory component, obtained by subtracting the step-like background from ΔT/T, with the intensity profile of the THz field ∣E(t)∣2. The fitting procedure for the background subtraction is reported in the Supplementary Note 4 and consists of Gaussian function to describe the THz excitation and a step-like function for the electronic relaxation dynamics as observed in refs. 33,35. To demonstrate that coherent oscillations originate from the V2O3 thin film, we conducted the same experiment on the bare R-plane Al2O3 substrate showing that there are neither oscillations nor a long-lived signal in the ΔT/T dynamics, see Fig. 1f and Supplementary Note 2 for details. Furthermore, from Fig. 1f we note that the envelope function of the oscillatory response does not merely follow that of ∣E(t)∣2, but instead persists well beyond the times when the THz pulse intensity is negligible. This strongly suggests that the oscillations are indeed due to a coherent excitation of the A1g mode in V2O3 at its resonance frequency39.
Such effect is clearly visible in the frequency domain where Fourier amplitude of the observed optical transmission oscillations show a narrow response where the pump spectrum has a negligible amplitude (Fig. 2a, b). The spectrum of the oscillatory component peaks at the A1g phonon frequency measured by Raman spectroscopy, which matches the double of the frequency of the driving field (Fig. 2c). As one can see, the spectrum of the A1g Raman spectrum shows a narrower line shape than the frequency response of the oscillations of the transmission modulation (Fig. 2b), because its spectral contents also depend on the frequency of the pump stimulus, which give rise to further broadening. This effect is also observed in V2O3 with conventional pump-probe optical spectroscopy36. Furthermore, to exclude the contribution of other modes to the observed dynamics, we repeated the experiment on a V2O3 thin film deposited on a C-plane (0001) Al2O3 substrate, whose orientation results in a diagonal susceptibility tensor allowing only for the fully-symmetric A1g modes to be detected (see Supplementary Note 3). The pump-probe dynamics of this sample also shows coherent oscillations peaked at the frequency of the A1g phonon mode (see Supplementary Fig. 5), further demonstrating that the phonon generated by the THz excitation is the A1g mode.
Figure 2d shows the dependence of the oscillation amplitude A on the electric field amplitude E0 of the incident THz field. The dependence is well described by a quadratic trend \(A=a{({E}^{0})}^{2}\) proving that the mode is nonlinearly coupled to the driving electric field. Moreover, as the spectral content of the pump pulse contains negligible intensity above 5 THz, we exclude a linear (dipolar) coupling of light to the lattice mode, which is in any case symmetry-forbidden since the mode is purely Raman active.
THz displacive excitation of phonons
Next, we discuss the nonlinear excitation mechanism of the vibrational modes by THz driven electronic excitation. We propose that the interaction of the THz-frequency pulse with the metallic phase of V2O3 first leads to the excitation of a time-dependent electronic distribution η(t) in the conduction bands. The time-domain dynamics of η(t) by THz excitation are described by:
where E(t) is the electric field temporal waveform of the THz pump pulse, 1/β is the fast electronic relaxation rate after the THz excitation and c accounts for long-lived thermalization dynamics that last longer than 2 ps as also observed in V2O3 by optical pump-probe spectroscopy36,39. The excited electronic states interact with the A1g lattice mode via electron-phonon coupling and, in a semi-classical picture, they exert an effective force on the A1g mode that has a time-dependence given by the intensity of the THz light field. According to general theory of DECP (see ref. 22), the effective force acting on the lattice associated with the electronic perturbation due to the intense time-varying electric field E(t) leads to the following equation of motion for the phonon displacement field:
where Q is the normal coordinate of the A1g phonon, Ω/2π the phonon eigenfrequency, γ/2π the phonon damping rate36,39 and α the coupling constant. We model the THz-induced transmission modulation as the sum of the lattice and electronic contributions [Eqs. (1) and (2)], as described in ref. 22:
with A and B multiplying constants.
Under this assumption, from Eq. (3) we calculated numerically the time-evolution of the transmission modulation dynamics ΔT/T(tpp) by using the experimental THz driving field shown in Fig. 1c and the following A1g phonon parameters Ω/(2π) = 7.1 THz, γ/(2π) = 0.5 THz obtained by Raman spectroscopy (see Supplementary Note 3 and Supplementary Table 2). For the fast electronic relaxation dynamics after the THz excitation we set 1/β = 80 fs in agreement with ref. 35; For the electron-phonon relaxation dynamics we set c = 0.2 and B/A = 0.002 to fit the amplitude of the experimental data. As expected from the numerical result of Eq. (3), the calculated dynamics by DECP model exhibits coherent lattice oscillations at twice the frequency of the electric field (Fig. 3a, b) and a step-like dynamics in agreement with the experiment, as also shown by the comparison of the corresponding time derivatives, see Fig. 3c. Figure 3d shows both the calculated electronic and lattice components of the dynamics from Eq. (3). As observed, the electronic dynamics has no long-lasting oscillating features.
Furthermore, we compute the lattice dynamics Q(t) by DECP model (Eq. (2)) as a function the driving frequency of THz pump. The numerical calculation of Q(t) is performed for multiple Gaussian THz pulses with a full width half maximum of 0.5 THz and center frequency ω0/2π, spanning from 1 to 10 THz with a frequency step of 0.125 THz. In Fig. 3e, we show the temporal derivative of Q(t) in frequency domain, which shows a maximum when THz driving frequency ω0/2π is half of the phonon frequency ωQ/2π as described by SFE, while no excitation is observed in resonant condition ωQ = ω0/2π.
THz-induced dynamics across the temperature driven insulator-to-metal transition
We now consider the temperature dependence of the oscillatory response. Figure 4a shows the phase diagram of \({({{{{{{{{\rm{V}}}}}}}}}_{1-x}{{{{{{{{\rm{M}}}}}}}}}_{x})}_{2}{{{{{{{{\rm{O}}}}}}}}}_{3}\), where the dopant M is either Cr or Ti. We drive the temperature across the metal-to-insulator transition at x = 0. The temperature evolution of ΔT/T(tpp) across the MIT is shown in Fig. 4b for various temperatures between 77 K and 500 K. In the insulating phase (T < TMIT) the transmission modulation displays a negative step-like component (see Fig. 4c) due to a partial formation of the metallic phase by the intense THz field41,42. However, the amplitude of coherent lattice vibrations is strongly reduced in the insulating phase (see Fig. 4d and Supplementary Fig. 7). In contrast, as the temperature approaches the MIT, we observe an emerging oscillatory signal at 2ωp/2π, which denotes that the phonon excitation mechanism becomes efficient when the THz pump is resonant with the conduction states. By further increasing the temperature, the transmission modulation response rapidly decreases above the coherence temperature (Tch ~ 400 K), see Fig. 4d. This may be due to the suppression of the optical conductivity by means of the enhanced scattering rate of the electrons in the correlated electronic phase of V2O3 at TMIT < T < Tch43,44. The amplitude of the oscillations versus the temperature strongly recalls the THz optical conductivity, as shown in the Fig. 4d, e. At present, an accurate model describing the transmission modulation response as a function of the temperature is still lacking, as it must account for the evolution of both the electronic phase and the lattice structure across the different phases. We can, however, qualitatively understand the data shown in Fig. 4d, e by noting that the THz generated displacive force on the lattice coordinate (see Eq. (1) and ref. 22) is proportional to the deposited THz energy which is, in turn, proportional to the real part of the optical conductivity σ1 according to the Joule heating model: ∫σ1E2(t)dt, being the imaginary part σ2 of metallic phase negligible in the THz range45. Therefore the temperature trend of the phonon amplitude and of σ1 further supports the interpretation that the underlying generation mechanism is displacive rather than impulsive in nature.
Discussion
We propose the following scenario to describe the mechanism for the nonlinear generation of a coherent A1g phonon mode in V2O3. First, the incident THz field drives primarily intraband transitions in the a1g electronic band of 3d vanadium orbitals having the dominant contribution in the Drude spectral weight compared to the ones from the e\({}_{g}^{\pi }\) band32. These newly populated states exert an effective force on the ions, driving a coherent A1g symmetry mode. Okamoto et al.39 have shown that Raman intensity of A1g phonon modes are dominated by the electronic occupancy of a1g band mediated by electron-phonon coupling39,46,47. Phenomenologically, the sum frequency excitation of the phonon mode in metallic V2O3 can be explained because the intense THz transient can temporally control the electronic distribution by intraband transitions in the a1g bands, proportional to the THz intensity, leading to the coherent up-conversion excitation of the A1g phonon mode. It is noteworthy that this process does not take place in insulating phase of V2O3, where the THz pulse is not coupled to a1g electronic states, while non-resonant SFE is not observed because the Raman cross-section is lower than that of diamond crystal25. Finally, we note that time-resolved optical spectroscopy is not a priori able to determine the coefficients in Eq. (3); a quantitative disentangling of the electronic and lattice driven responses requires additional information that could be provided by future ultrafast x-ray or electron diffraction experiments to determine the magnitude of the coherent lattice displacements. An interesting connection exists between our observation of THz light-induced coherent phonon generation via stimulated Raman scattering from conductive electrons and the phenomenon of electrostriction in metals for DC electric fields. In electrostriction mechanism, an intense current in metals creates a strain field, proportional to the square of the electric field (E2), due to interaction of conduction electron states with acoustic phonon modes48. Electrostriction effects at THz frequencies have been reported in metallic films, where the strain waves driven by the intense THz field can generate mechanical fractures41,49.
Our observation of the coherent generation of Raman active phonons by THz excitation in a metallic system provides an interesting counterpart to ISRS- and DECP-based schemes in the infrared and visible ranges, using photons with much lower energy than the excited mode. This has the potential advantage of limiting the inevitable heating of the electronic system that necessarily occurs as a side effect of any scheme using light to coherently control the structure of metallic systems. This displacive excitation scheme may have potential advantages for applying coherent control methods to target other lattice-coupled collective modes, including magnons, for which sum-frequency inonic excitation has been recently discussed theoretically50, and provide new insights about the interplay between the lattice and other coexisting ordered phases.
Methods
Sample characterization and growth
High-quality V2O3 thin films were epitaxially grown on R-plane sapphire substrates by pulsed laser deposition using a KrF excimer laser beam focused with a fluence of 1 J/cm2 onto a ceramic V2O5 bulk target. During the growth, the target was in an argon atmosphere of 2 ⋅ 10−2 mbar and the substrates were maintained at a temperature of 873 K, as described in ref. 51. The high quality of the thin films was confirmed by diffraction analysis and electronic transport measurements as a function of temperature. The 84 nm-thin film of V2O3 used in the experiment shows a resistivity change by more than four orders of magnitude between 40 K and 200 K. Raman spectroscopy of the V2O3 film at 300 K (Fig. 3c) has been carried out using a LabRAM Series Raman Microscope (Horiba Jobin Yvon) equipped with a HeNe excitation laser (λ = 632.8 nm).
Data availability
The data of the results presented in this paper, including those in the Supplementary Information, are available are available in Figshare with the identifier https://doi.org/10.6084/m9.figshare.19312271.v1.
References
Juraschek, M. D. & Spaldin, N. A. Sounding out optical phonons. Science 357, 873 (2017).
Zhu, H. et al. Observation of chiral phonons. Science 359, 579 (2018).
Strohm, C., Rikken, G. L. J. A. & Wyder, P. Phenomenological evidence for the phonon Hall effect. Phys. Rev. Lett. 95, 155901 (2005).
Moya, X. & Mathur, N. D. Caloric materials near ferroic phase transitions. Nat. Mater. 13, 439 (2014).
Rini, M. et al. Control of the electronic phase of a manganite by mode-selective vibrational excitation. Nature (Lond.) 449, 72 (2007).
Fausti, D. et al. Light-induced superconductivity in a stripe-ordered cuprate. Science 331, 189 (2011).
Mitrano, M. et al. Possible light-induced superconductivity in K3C60 at high temperature. Nature (Lond.) 530, 461 (2016).
Buzzi, M. et al. Photomolecular high-temperature superconductivity. Phys. Rev. X 10, 031028 (2020).
De la Torre, A. et al. Colloquium: Nonthermal pathways to ultrafast control in quantum materials. Rev. Mod. Phys. 93, 041002 (2021).
Nova, T. et al. An effective magnetic field from optically driven phonons. Nat. Phys. 13, 132 (2017).
Kubacka, T. et al. Large-amplitude spin dynamics driven by a THz pulse in resonance with an electromagnon. Science 343, 1333 (2014).
Maldovan, M. Sound and heat revolutions in phononics. Nature (Lond.) 503, 209 (2013).
Merlin, R. Generating coherent THz phonons with light pulses. Solid State Commun. 102, 207 (1997).
Huber, T., Ranke, M., Ferrer, A., Huber, L. & Johnson, S. L. Coherent phonon spectroscopy of non-fully symmetric modes using resonant terahertz excitation. Appl. Phys. Lett. 107, 091107 (2015).
Fu, Z. & Yamaguchi, M. Coherent excitation of optical phonons in GaAs by broadband terahertz pulses. Sci. Rep. 6, 38264 (2016).
Hase, M. et al. Optical control of coherent optical phonons in bismuth films. Appl. Phys. Lett. 69, 2474 (1996).
Kozina, M. et al. Terahertz-driven phonon upconversion in SrTiO3. Nat. Phys. 15, 387–392 (2019).
Först, M. et al. Nonlinear phononics as an ultrafast route to lattice control. Nat. Phys. 7, 854 (2011).
Yan, Y. X. et al. Impulsive stimulated scattering: General importance in femtosecond laser pulse interactions with matter, and spectroscopic applications. J. Chem. Phys. 83, 5391 (1985).
Dahr, L. et al. Time-resolved vibrational spectroscopy in the impulsive limit. Chem. Rev. 94, 157 (1994).
Johnson, S. L. et al. Direct observation of non-fully-symmetric coherent optical phonons by femtosecond x-ray diffraction. Phys. Rev. B 87, 054301 (2013).
Zeiger, H. J. et al. Theory for displacive excitation of coherent phonons. Phys. Rev. B 45, 768 (1992).
Stevens, T. E., Kuhl, J. & Merlin, R. Coherent phonon generation and the two stimulated Raman tensors. Phys. Rev. B 65, 144304 (2002).
Shen, Y. R. & Bloembergen, N. Theory of stimulated brillouin and raman scattering. Phys. Rev. 137, A1787 (1965).
Maehrlein, S. F. et al. Terahertz sum-frequency excitation of a Raman-active phonon. Phys. Rev. Lett. 119, 127402 (2017).
Juraschek, D. M. & Maehrlein, S. F. Sum-frequency ionic Raman scattering. Phys. Rev. B 97, 174302 (2018).
Johnson, C. L., Knighton, B. E. & Johnson, J. A. Distinguishing nonlinear terahertz excitation pathways with two-dimensional spectroscopy. Phys. Rev. Lett. 122, 073901 (2019).
Knighton, B. E. et al. Terahertz waveform considerations for nonlinearly driving lattice vibrations. J. Appl. Phys. 125, 144101 (2019).
Melnikov, A. A., Selivanov, Y.G. & Chekalin, S. V. Phonon-driven ultrafast symmetry lowering in a Bi2Se3 crystal. Phys. Rev. B 102, 224301 (2020).
Melnikov, A. A. et al. Coherent phonons in a Bi2Se3 film generated by an intense single-cycle THz pulse. Phys. Rev. B 97, 214304 (2018).
Baldassarre, L. et al. Quasiparticle evolution and pseudogap formation in V2O3: An infrared spectroscopy study. Phys. Rev. B 77, 113107 (2008).
Qazilbash, M. M. et al. Electrodynamics of the vanadium oxides VO2 and V2O3. Phys. Rev. B 77, 115121 (2008).
Liu, M. K. et al. Photoinduced phase transitions by time-resolved far-infrared spectroscopy in V2O3. Phys. Rev. Lett. 107, 066403 (2011).
Abreu, E. et al. Ultrafast electron-lattice coupling dynamics in VO2 and V2O3 thin films. Phys. Rev. B 96, 094309 (2017).
Lantz, G. et al. Ultrafast evolution and transient phases of a prototype out-of-equilibrium Mott-Hubbard material. Nat. Commun. 8, 13917 (2017).
Misochko, O. V. et al. Phonons in V2O3 above and below the Mott transition: A comparison of time- and frequency-domain spectroscopy results. Phys. B: Condens. Matter 263, 57 (1999).
Mansart, B. et al. Mott transition in Cr-doped V2O3 studied by ultrafast reflectivity: Electron correlation effects on the transient response. Europhys. Lett. 92, 37007 (2010).
Gerber, S. et al. Femtosecond electron-phonon lock-in by photoemission and x-ray free-electron laser. Science 357, 71 (2017).
Okamoto, A. et al. Raman Study on the High Temperature Transition in V2O3. J. Phys. Soc. Jpn. 52, 312 (1983).
von Hoegen, A. et al. Probing the interatomic potential of solids with strong-field nonlinear phononics. Nature 555, 79 (2018).
Giorgianni, F., Sakai, J. & Lupi, S. Overcoming the thermal regime for the electric-field driven Mott transition in vanadium sesquioxide. Nat. Commun. 10, 1159 (2019).
Gray, A. X. et al. Ultrafast terahertz field control of electronic and structural interactions in vanadium dioxide. Phys. Rev. B 98, 045104 (2018).
Lo Vecchio, I. et al. Orbital dependent coherence temperature and optical anisotropy of V2O3 quasiparticles. J. Phys.: Condens. Matter 29, 345602 (2017).
Lo Vecchio, I. et al. Optical properties of V2O3 in its whole phase diagram. Phys. Rev. B 91, 155133 (2015).
Luo, Y. Y. et al. Terahertz transport dynamics in the metal-insulator transition of V2O3 thin film. Opt. Commun. 387, 385 (2017).
Tian, Y. T. et al. Ultrafast dynamics Evidence of High Temperature Superconductivity in Single Unit Cell FeSe on SrTiO3. Phys. Rev. Lett. 116, 107001 (2016).
Wu, Q. et al. Ultrafast Quasiparticle Dynamics and Electron-Phonon Coupling in (Li0.84Fe0.16)OHFe0.98Se. Chin. Phys. Lett. 37, 097802 (2020).
Kornreich, P., Callen, H. & Gundjian, A. Current Striction-A Mechanism of Electrostriction in Many-Valley Semiconductors. Phys. Rev. 161, 815 (1967).
Agranet, M. B. et al. Damage in a thin metal film by high-power terahertz radiation. Phys. Rev. Lett. 120, 085704 (2018).
Juraschek, D., Wang, D. S. & Narang, P. Sum-frequency excitation of coherent magnons. Phys. Rev. B 103, 094407 (2021).
Sakai, J., Limelette, P. & Funakubo, H. Transport properties and c/a ratio of V2O3 thin films grown on C- and R-plane sapphire substrates by pulsed laser deposition. Appl. Phys. Lett. 107, 241901 (2015).
Acknowledgements
We thank Lara Benfatto for the fruitful discussion and for critical reading of the manuscript. We are grateful to Hans-Heinrich Braun, Carlo Vicario and the PSI-LNO group for support. We acknowledge financial support by Swiss National Science Foundation project no. IZLRZ2_164051, by MAECI under the Italian-India collaborative project SUPERTOP-PGR04879 and by EC FP7 Graphene Flagship Project No. CNECTICT-604391. The research was supported by the NCCR MUST, founded by the Swiss National Science Foundation, and by ERC Grant Hyper Quantum Criticality (HyperQC). MR and MC acknowledges the support of SNF Project No. 200021_182695.
Author information
Authors and Affiliations
Contributions
F.G. conceived and designed the experiment with S.L.J.’s supervision. E.P., M.C., M.R., and J.S. grew the samples and performed structural characterizations and transport measurements. F.G carried out the THz experiments with the support of the PSI-NLO staff. F.G. prepared the figures for the manuscript. C.W.S. and F.G. performed the Raman spectroscopy measurements. M.U., F.G., and T.C. interpreted the data through DECP theory and performed calculations. L.B. and F.G. performed THz spectroscopy measurements. F.G. and S.L.J. wrote the manuscript. All authors extensively discussed the results.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Communications Physics thanks the anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Giorgianni, F., Udina, M., Cea, T. et al. Terahertz displacive excitation of a coherent Raman-active phonon in V2O3. Commun Phys 5, 103 (2022). https://doi.org/10.1038/s42005-022-00882-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s42005-022-00882-7
- Springer Nature Limited