Abstract
Sporopollenin is a mechanically robust and chemically inert biopolymer that constitutes the outer protective exine layer of plant spores and pollen grains. Recent investigation of the molecular structure of pine sporopollenin revealed unique monomeric units and inter-unit linkages distinct from other previously known biopolymers, which could be harnessed for new material design. Herein, we report the bioinspired synthesis of a series of sporopollenin analogues. This exercise confirms large portions of our previously proposed pine sporopollenin structural model, while the measured chemical, thermal, and mechanical properties of the synthetic sporopollenins constitute favorable attributes of a new kind of robust material. This study explores a new design framework of robust materials inspired by natural sporopollenins, and provides insights and reagents for future elucidation and engineering of sporopollenin biosynthesis in plants.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Sporopollenin (the portmanteau1,2 of the archaic “sporonin3” and “pollenin4”) is the general designation for a class of chemically related and ubiquitous biopolymers that comprise the exine of plant spores and pollen grains (Fig. 1A)1,2,3,4,5,6,7,8. These exines adopt a wide variety of complex supramolecular structures ranging widely in size, shape, and porosity1,2,3,4,5,6,7,8. In its natural role, sporopollenin serves to protect the fragile gametes of land plants against myriad environmental insults including desiccation, ultraviolet irradiation, chemical degradation, and mechanical stress5,6,7,8. As a result, sporopollenin has evolved to be one of the strongest and most chemically resistant known materials of direct biological origin boasting elastic moduli as high as 16 ± 2.5 GPa9, resistance to hydrostatic pressures in excess of 10 GPa10, and inertness towards a wide variety of organic solvents5,6,7,8,11. Due to the inexorable nature of the supramolecular and molecular structure of natural sporopollenins, it is difficult to deconvolute the exact contributions of each to the aforementioned properties. Nevertheless, these properties have led to the successful application of natural sporopollenin to chromatography12,13,14, solid phase peptide synthesis15, catalyst solid supports16,17,18, magnetic nanoparticle synthesis19,20, and the encapsulation of enzymes21,22, pharmaceuticals23,24,25,26, and whole cells27. Despite these early successes, the implementation of sporopollenin-based technologies has been stymied by an historically limited understanding of the molecular structure of sporopollenin and lack of consistent supply of nature-derived sporopollenin materials.
For over 200 years, the chemical community has painstakingly engaged in structural elucidation studies of plant sporopollenins spanning myriad degradative, spectroscopic, and spectrometric methodologies with limited progress1,2,3,4,5,6,7,8,11,28,29,30,31,32,33,34,35. Recently, our own efforts in this area have culminated in the most detailed hypothesis for the molecular structure of P. rigida sporopollenin to date, facilitated by the implementation of 13C magic angle spinning solid state nuclear magnetic resonance (MAS ssNMR) spectroscopy and degradative thioacidolysis/liquid chromatography-mass spectrometry (DT/LC-MS) (Fig. 1B)35. These studies suggest that P. rigida sporopollenin is principally comprised of aliphatic polyketide-derived polyvinyl alcohol units crosslinked by p-coumaryl-substituted fatty acid-derived C16 aliphatic units via acetal linkages (Fig. 1C)35. This proposed structure has withstood recent spectroscopic scrutiny28 and, therefore, represents a validated starting point for synthesis of structural analogues that retain sporopollenin’s fascinating properties.
Herein, we describe a synthetic strategy towards the preparation of a library of bioinspired synthetic sporopollenin analogues and the chemical, thermal, and mechanical assessment thereof. As a result of this work, we have (1) validated significant portions of our recently proposed35 molecular structure of P. rigida sporopollenin through chemical synthesis, (2) provided general access to an underexplored class of bioinspired and biocompatible polymers, (3) identified key structure-property relationships (SPRs) enabling purpose-guided design of bespoke sporopollenin analogues, and (4) established chemical tools for the elucidation of sporopollenin biosynthesis empowering future development of ectopic sporopollenin-accumulating organisms for carbon sequestration. Through these efforts, we aim to further demystify one of Nature’s most robust materials and facilitate its potential commercial application in the areas of pharmaceutical encapsulation, anti-fouling agents, and chemically-inert coatings, inter alia.
Results and discussion
Chemical synthesis of sporopollenin-inspired polymers
Thus, a library of bioinspired synthetic sporopollenin analogues was envisioned to arise from the well-precedented acid-catalyzed crosslinking of commercial polyvinyl alcohol36,37,38,39,40,41,42 with a suite of synthetically accessed α,ω-dialdehydes43. The central feature of this approach is the divergent preparation of variously substituted α,ω-dialdehyde crosslinkers via either oxidation of simple α,ω-alkanols or an alkylation/ring expansion sequence that permits variability of chain length, substituent identity/position, and chirality. This approach would permit the rapid and divergent preparation of myriad sporopollenin-like polymers with discrete control over linker length, linker substituent(s), degree of crosslinking, and polyvinyl alcohol backbone properties, including average molecular weight, polydispersity, and tacticity.
To those ends, a series of unsubstituted α,ω-dialdehydes (1–5), prepared by oxidation of the corresponding commercially available α,ω-alkanols (S1–S5)43, were crosslinked with 5% polyvinyl alcohol (PVA) in DMSO under acid-catalyzed conditions (Fig. 2A)36,37,38,39,40,41,42. While a temperature of ≥55 °C was required for efficient crosslinking, extended periods of drying at ≥55 °C resulted in pronounced discoloration of the crosslinked material. This is likely due to the known acid-catalyzed decomposition of DMSO at elevated temperature44,45. In order to minimize the impact of this undesired side-reaction, polymers were cured at 55–60 °C and 760 torr for 2 h under air, then dried at 40 °C and 250 torr for 72 h under air resulting in nearly colorless, transparent crosslinked polymers. With an efficient synthetic methodology in hand, a suite of simplified sporopollenin analogues with theoretical degrees of crosslinking ranging from 5–50% (Table S1), crosslinker length ranging from C8-C16, and PVA average molecular weight ranging from 31,000–186,000 g/mol were prepared for physical, thermal, and chemical evaluation, totaling 13 discrete analogues (6–18, see Supplementary Methods, Supplementary Note 1, and Table S2 for numbering convention).
While these simplified sporopollenin analogues facilitated the optimization of the aforementioned curing method and the rapid establishment of preliminary structure-property relationships, we sought to more closely reproduce the authentic sporopollenin linker to both test the validity of the prior P. rigida sporopollenin structural model35 and provide precedent for the divergent preparation of myriad functionalized linkers bearing substituents both natural and previously unobserved in sporopollenin across plant families (Fig. 2B)1,2,3,4,5,6,7,8,11,28,29,30,31,32,33,34,35. Accordingly, alkylation of cyclohexylimine 1946 with bromoolefin 20 (nBuLi, DIPA, THF, 0–23 °C, 22 h, 69%) provided, after subsequent oxidative cleavage (NaIO4, KMnO4, acetone/H2O, 23 °C, 20 h, 81%) and alkylation (MeI, K2CO3, acetone, reflux, 24 h, 89%), ester 21. Ring expansion under Baeyer-Villiger conditions47,48 afforded the corresponding caprolactone 22 (mCPBA, CH2Cl2, 0–23 °C, 20 h, 91%) which underwent smooth one-pot ring opening and esterification to afford diester 23 (NaOMe, MeOH, 23 °C, 3.5 h, 85%). This simultaneously exposed a key alcohol moiety for further functionalization. Steglich esterification49 with TBS-protected p-coumaric acid (S8)50,51 provided triester 24 (S8, DMAP, DCC, CH2Cl2, 23–40 °C, 20 h, 69%), which, after reduction (LiBH4, Et2O, 23 °C, 3 h, 64%), deprotection (TBAF, THF, 23 °C, 5 min, 90%), and oxidation (SO3·py, Et3N, DMSO/CH2Cl2, 0 °C, 2.5 h, 58%), was converted to the target dialdehyde 25 (9 steps from commercial, 9% overall yield, see Figs. S1–S10 for spectra). It is notable that many intermediates en route to dialdehyde 25 (e.g., 23, 24) are closely related to proposed biosynthetic pathway intermediates and, thus, may be implemented in the future validation of sporopollenin biosynthetic hypotheses52,53,54,55,56,57,58,59,60,61. While yet unexplored, we anticipate this synthetic route will permit rapid divergence to myriad sporopollenin linker analogues in the future (Fig. 2C). Analogous to the simple α,ω-dialdehyde crosslinkers43, synthetically accessed dialdehyde 25 was crosslinked with PVA36,37,38,39,40,41,42 to afford synthetic linker sporopollenin analogue 26 (Fig. 3A), representing the closest synthetic recapitulation of P. rigida sporopollenin disclosed to date35.
Spectroscopic characterization and chemical stability of sporopollenin-inspired polymers
Initial comparison of synthetic analogues 15 and 26 with authentic P. rigida sporopollenin35 revealed a high degree of similarity in both 13C MAS ssNMR29,62 (Fig. 3B) and attenuated total reflectance Fourier-transform infrared (ATR-FTIR, Fig. 3C) spectroscopies (Figs. S11–18)28,63,64. The presence of acetal cross-linkages in all three samples was confirmed by a broad NMR signal from 97–103 ppm corroborated by an IR band at ~1100 cm−1 corresponding to an asymmetric stretching of aliphatic ethers. The broadness of both signals coupled with the fine structure of the IR band suggest the acetals are present in a variety of subtly distinct chemical environments as anticipated in a highly crosslinked, three-dimensional polymeric structure. Further mutual upfield NMR signals from 62–80 ppm and 20–52 ppm were consistent with oxygen-bearing and aliphatic methylene carbons, respectively, attributed to the skipped polyol backbone and aliphatic crosslinkers. The latter is further corroborated by the presence of methylene C–H asymmetric and symmetric stretches in the IR spectra at 2920 and 2850 cm−1, respectively. More detailed comparison of synthetic linker sporopollenin analogue 26 and authentic P. rigida sporopollenin revealed a series of remarkably similar downfield NMR signals corresponding to the arene (111–121, 123–135, 155–162 ppm), olefin (111–121, 164–170 ppm), and carbonyl (164–170 ppm) of the p-coumaryl ester moiety with a sharp IR signal at ~1514 cm−1 attributed to an aromatic ring mode of the coumaryl ester28. As chemical moieties previously predicted to be secondary to the structural linkages of sporopollenin were not included in current synthetic efforts, NMR signals at 87 and 96 ppm, diagnostic of α-pyrones, were observed only in the authentic P. rigida sporopollenin35. Curiously, a medium to sharp IR signal at ~830 cm−1 previously attributed in P. ponderosa sporopollenin to an aromatic CH out-of-plane bending28 is present in all three samples, suggesting a nonaromatic origin. In addition to the highlighted signals, the IR fingerprint regions across samples demonstrate excellent overlap strongly supporting the highly similar nature of the authentic and synthetic samples.
In analogy to our prior P. rigida sporopollenin structural elucidation efforts, synthetic analogues 15 and 26 were submitted to degradative thioacidolysis followed by liquid chromatography-high resolution mass spectrometry (DT/LC-HRMS) analysis35, and compared with authentic material to assess similarities in chemical reactivity (Fig. 3D, Figs. S19–20). Spectrometry revealed the presence of analogous bis-thioenol ether degradation products in each sample, likely resulting from the in-source fragmentation of the corresponding bis-dithioacetal of the relevant crosslinking α,ω-dialdehyde, suggesting similar mechanisms of degradation across synthetic (15, 26) and authentic sporopollenins35. The chemical stability of analogue 15 was further examined by calculating mass differences in samples exposed to organic solvents over 24 h. These solvolysis studies revealed no significant mass changes suggesting broad resistance of sporopollenin analogues to organic solvents, consistent with prior reports of the chemical resilience of natural sporopollenins (see Table S3)11.
Taken together, the spectroscopic, spectrometric, and chemical reactivity data across synthetic sporopollenin analogues 15 and 26 bear remarkable similarities to authentic P. rigida sporopollenin35, thus demonstrating, through chemical synthesis, the accuracy of large portions of our previous structural hypothesis, and providing access to both an underexplored class of bioinspired and biocompatible polymer and tools for sporopollenin biosynthetic pathway elucidation52,53,54,55,56,57,58,59,60,61. While independent 13C MAS ssNMR studies are currently unreported, the ATR-FTIR data disclosed herein are broadly consistent with recent analyses of P. ponderosa sporopollenin by ref. 28 and suggest high structural similarity between P. rigida and P. ponderosa sporopollenin.
Thermal and mechanical characterization of sporopollenin-inspired polymers
With our structural hypothesis for P. rigida sporopollenin largely confirmed, we set out to examine the thermal and mechanical properties of the synthetic sporopollenin analogues. Prior studies on a variety of natural sporopollenins have revealed appealing properties including high modulus9 and resistance to significant hydrostatic pressures10. Though direct comparison of natural and synthetic sporopollenins is not yet possible due to differences in supramolecular structure, we anticipated synthetic analogues would exhibit broadly similar properties to their natural counterparts that would permit wide application in materials science. To those ends, thermogravimetric analysis (TGA) was conducted on all analogues disclosed to ascertain their thermal stability and extent of contamination by low molecular weight solvents and process aids (Table S9, Figs. S44–S57). Across all analogues, a series of three mass losses of 34.6 ± 2.4% at 213 ± 9.8 °C, 54.1 ± 4.0% at 453 ± 5.9 °C, and 9.8 ± 1.4% at 535 ± 8.0 °C corresponded to loss of residual solvents and process aids, thermal decomposition of the base polymer, and combustion, respectively. Differential scanning calorimetry (DSC) was also conducted on simplified sporopollenin analogue 15, which revealed no significant thermal features below 110 °C, above which data interpretation was complicated by the loss of residual solvent (Figs. S58–S62). Taken together, these data demonstrate that the method for polymer crosslinking is consistent in producing sporopollenin analogues containing approximately 35 wt/wt% DMSO which resist thermal decomposition to approximately 453 °C and do not exhibit supramolecular organization into crystalline or semi-crystalline domains.
In addition to thermal analysis, all synthetic sporopollenin analogues disclosed were submitted to a battery of mechanical property evaluations to assess both similarity to previously disclosed properties of natural sporopollenins9 and potential commercial utility as structurally sound polymeric materials. Durometer hardness testing of the analogues revealed almost uniform results averaging 71 ± 5 Shore D regardless of crosslinker length, crosslinking density, and PVA average molecular weight (Table S4). This value is higher than that of high-density polyethylene (65 Shore D)65, commonly utilized in commercial thermoplastic hard hats. Compression testing of the analogues was performed with controlled crosslinker length, crosslinker density, and PVA average molecular weight up to a stress of approximately 200 MPa, measuring their nominal stress versus nominal strain curves, Young’s moduli, and hysteresis ratios (Tables S5–S6, Figs. S21–S40). Compressive moduli ranged from 97 ± 8 MPa to 230 ± 36 MPa across all analogues with a crosslinker length of C12 yielding the maximal observed modulus value (Fig. 4A). Due to the low solvent content of the polymers, both elastically active chain density and inter-/intramolecular interactions likely contribute to the moduli of all analogues66. Since crosslinker density is proportional to elastically active chain density but inversely proportional to inter-/intramolecular interactions, there is no strong dependence of moduli on crosslinker density observed experimentally (Fig. 4B). In addition, no strong dependence on PVA average molecular weight on moduli was observed (Fig. 4C), which suggests inter-/intramolecular interactions of analogues with different PVA average molecular weights are similar. It is notable that in all instances observed, synthetic analogue 26 demonstrated decreased modulus compared to the analogous simplified synthetic analogue 15, suggesting that the presence of p-coumaryl substituents suppresses inter-/intramolecular interactions of analogues, thereby leading to reduced modulus67. The hysteresis ratio across analogues varied between 0.48 ± 0.01 and 0.63 ± 0.01, indicating significant dissipation of energy over one compressive cycle. The dissipation of energy is recoverable (Fig. S42). In addition, large plasticity and rate dependency are observed across all analogues in tensile testing (Figs. S41, S43). The recoverable dissipation of energy, large plasticity, and rate dependency suggests the presence of residual acetic or sulfuric acid, utilized as a catalyst for polymer crosslinking, renders the dynamic forming and reforming of crosslinks between α,ω-dialdehydes and PVA chains at highly deformed states. In addition to compression and tensile tests, the swelling ratios of all analogues were also measured (Tables S7–S8). As shown in Fig. 4D, the weight swelling ratio decreases from 1.71 to 1.02 as crosslinker density increases from 5 to 50%. Notably, a plateau in the decrease in swelling ratio with increasing crosslinker density occurs between 20 and 30% crosslinking; the same level of crosslinking previously observed in natural P. rigida sporopollenin35. This suggests that plants might have been subject to evolutionary pressure to minimize the swelling of their sporopollenin and demonstrates that they have successfully adapted in the most efficient manner possible. No clear relationship between swelling ratio and PVA average molecular weight or crosslinker length were observed. Overall, these thermal and mechanical analyses reveal the unique properties of natural and unnatural sporopollenin analogues and their potential to broadly impact the field of materials science.
Broader impact, limitations, and future directions
Plant molecular biologists have long searched for plant genes likely involved in plant sporopollenin biosynthesis52,53,54,55,56,57,58,59,60,61. At present, at least 11 enzyme-encoding genes from the model plant Arabidopsis thaliana have been implicated, on the basis of single and multiple mutant phenotypes, in pollen exine development52,53,54,55,56,57,58,59,60,61. These genes include fatty acid reductase MALE STERILITY 2 (MS2)53, ACYL-COA SYNTHETASE 5 (ACOS5)54, POLYKETIDE SYNTHASE A/B (PKSA/B)55,56, TETRAKETIDE ɑ-PYRONE REDUCTASE 1/2 (TKPR1/2)57,58, LESS ADHESIVE POLLEN 3 (LAP3)59, CYP703A260, CYP704B161, and IRREGULAR POLLEN EXINE 1/2 (IPE1/2)52. As the precise roles and ordering of these enzymes in the sporopollenin biosynthetic pathway remain an open field for future research52,53,54,55,56,57,58,59,60,61, we note that our current study provides a framework for synthesizing a variety of isotopically labeled, stable pathway intermediates that can be used as chemical tools to probe various sporopollenin biosynthetic hypotheses. Such efforts may ultimately enable bioengineering of sporopollenin biosynthesis in non-reproductive tissues of plants with potential applications ranging from enhancing plant biotic and abiotic stress resistance to carbon sequestration52,53,54,55,56,57,58,59,60,61.
Though the work herein provides detailed evaluation of numerous synthetic sporopollenin analogues, it is noteworthy that direct comparison of some properties of natural and synthetic sporopollenins remains out of reach due, in large part, to the intricate supramolecular structure of the natural material (Fig. 1A)1,2,3,4,5,6,7,8,35. For example, compressive testing of natural sporopollenin provides moduli that likely reflect contributions from both molecular and supramolecular structural elements and, thus, cannot be directly compared to a result from the synthetic samples which, while comparable in molecular structure, lack a similar supramolecular shape. Only evaluation of the properties of the powdered samples are directly comparable as the supramolecular structures are disrupted. To achieve a more direct comparison, it will be necessary to achieve discrete control over supramolecular structure during the synthesis of sporopollenin analogues. Studies towards these ends are ongoing. In addition, future efforts may include exploration of alternative crosslinker substituents with the goal of imparting the polymers with auxiliary properties (i.e., larger π-systems for optical properties).
In summary, we report the first synthetic recapitulation of plant sporopollenin and analogues thereof based upon that of P. rigida35. The synthetic sporopollenin analogues harbor numerous favorable chemical, thermal, and mechanical properties of robust polymers with potential industrial applications. These efforts have resulted in the validation of significant portions of our previous structural model for P. rigida sporopollenin35, granted chemical access to an underexplored class of bioinspired and biocompatible polymers, revealed key structure-property relationships for the engineering of sporopollenin analogues, and provided chemical tools for the future elucidation of sporopollenin biosynthesis52,53,54,55,56,57,58,59,60,61. This work affords foundational principles which will inform the development and application of robust sporopollenin-inspired polymers in the areas of pharmaceutical encapsulation, anti-fouling agents, and chemically-inert coatings while simultaneously demystifying one of Nature’s most enigmatic materials.
Methods
General method for the preparation of α,ω-Alkyldialdehydes (1–5)
A solution of α,ω-alkyldiol S1–S5 (1.00 mmol) in CH2Cl2 (10.0 mL) at 23 °C was treated with DMP (2.20 mmol). The resulting solution was stirred at 23 °C for 2 h, then diluted to a total volume of 110 mL with Et2O, washed sequentially with 1 N NaOH(aq) (2 × 100 mL) and sat. NH4Cl(aq) (1 × 100 mL), dried over Na2SO4, concentrated on a rotary evaporator, and purified by flash chromatography (SiO2, 20–50% Et2O/Hexanes) to provide α,ω-alkyldialdehydes (1–5) as clear, colorless oils (5) or amorphous white solids (1–4)43.
1,16-Hexadecanedial (1)68. 1H NMR (CDCl3, 400 MHz) δ 9.76 (t, J = 1.9 Hz, 2H), 2.41 (td, J = 7.4, 1.9, 4H), 1.65–1.58 (m, 4H), 1.38–1.22 (m, 20H).
1,14-Tetradecanedial (2)69. 1H NMR (CDCl3, 500 MHz) δ 9.76 (t, J = 1.9 Hz, 2H), 2.42 (td, J = 7.4, 1.9 Hz, 4H), 1.63 (p, J = 7.4 Hz, 4H), 1.36–1.23 (m, H16).
1,12-Dodecanedial (3)70. 1H NMR (CDCl3, 500 MHz) δ 9.77 (s, 2H), 2.42 (td, J = 7.6, 1.9 Hz, 4H), 1.63 (p, J = 7.4 Hz, 4H), 1.41–1.23 (m, 12 H).
1,10-Decanedial (4)71. 1H NMR (CDCl3, 500 MHz) δ 9.76 (s, 2H), 2.44 (dt, J = 7.3, 1.8 Hz, 4H), 1.65–1.60 (m, 4H), 1.40–1.22 (m, 8H).
1,8-Ocatanedial (5)72. 1H NMR (CDCl3, 500 MHz) δ 9.77 (t, J = 1.5 Hz, 2H), 2.44 (td, J = 7.3, 1.5 Hz, 4H), 1.64 (t, J = 7.3, 4H), 1.40–1.33 (m, 4H).
2-(Undec-10-en-1-yl)cyclohexan-1-one (S6)
A solution of freshly distilled diisopropylamine (6.77 mL, 48.0 mmol) in dry THF (575 mL) at 0 °C was treated dropwise with 2.45 M nBuLi in hexanes (16.3 mL, 40.0 mmol) over 5 min. The resulting solution was stirred at 0 °C for 10 min and then treated with a solution of freshly distilled N-cyclohexylcyclohexanimine (19)46 (5.75 g, 32.1 mmol) in dry THF (50.0 mL). The bright yellow solution, thus obtained, was stirred at 0 °C for 1 h and then treated with a solution of 11-bromoundec-1-ene (20) (3.73 g, 16.0 mmol) in dry THF (100 mL). The reaction mixture was warmed to 23 °C and allowed to stir at 23 °C for 20 h. After 20 h, the resulting solution was poured into sat. NH4Cl(aq) (300 mL) and extracted with EtOAc (3 × 200 mL). The combined organic layers were washed with 1 N HCl(aq) (1 × 200 mL) and sat. NaCl(aq) (200 mL), dried over Na2SO4, concentrated on a rotary evaporator, and purified by flash chromatography (SiO2, 5% Et2O/Pet. Ether) to provide alkene S6 as a pale yellow oil (2.75 g, 69%): 1H NMR (CDCl3, 400 MHz) δ 5.81 (ddt, J = 17.0, 10.2, 6.7 Hz, 1H), 4.99 (dq, J = 17.2, 1.7 Hz, 1H), 4.93 (ddt, J = 10.2, 2.4, 1.3 Hz, 1H), 2.38 (dtd, J = 13.6, 4.3, 1.3 Hz, 1H), 2.32–2.22 (m, 2H), 2.13–2.07 (m, 1H), 2.06–1.99 (m, 3H), 1.87–1.82 (m, 1H), 1.80–1.72 (m, 1H), 1.71–1.60 (m, 2H), 1.42–1.33 (m, 3H), 1.29–1.16 (m, 13H); 13C NMR (CDCl3, 100 MHz) δ 213.8, 139.4, 114.2, 50.9, 42.1, 34.0, 29.9, 29.7, 29.7, 29.6, 29.6, 29.3, 29.1, 28.2, 27.3, 25.0; IR (film) νmax 2923, 2853, 1710, 1640, 1462, 1448, 1126, 993, 908 cm−1; HRMS (DART-TOF) m/z 251.2390 (C17H30O + H+ requires 251.2375).
10-(2-Oxocyclohexyl)decanoic acid (S7)
A solution of KMnO4 (42.6 mg, 0.270 mmol) in 1:6 acetone/H2O (13.5 mL) at 23 °C was treated with NaIO4 (2.31 g, 10.8 mmol), then dropwise with neat alkene S6 (135 mg, 0.539 mmol) over 5 min. The resulting solution was stirred at 23 °C for 20 h, then diluted to 200 mL total volume with H2O and extracted with EtOAc (2 × 100 mL). The combined organic layers were dried over Na2SO4, concentrated on a rotary evaporator, and purified by flash chromatography (SiO2, 35% Et2O/Pet. Ether) to provide carboxylic acid S7 as an amorphous white solid (109 mg, 81%): mp 39–42 °C; 1H NMR (CDCl3, 400 MHz) δ 10.57 (bs, 1H), 2.41–2.22 (m, 5H), 2.12–2.00 (m, 2H), 1.87–1.59 (m, 6H), 1.43–1.15 (m, 14H); 13C NMR (CDCl3, 100 MHz) δ 214.0, 180.0, 50.9, 42.1, 34.2, 34.0, 29.8, 29.6, 29.5, 29.5, 29.3, 29.2, 28.2, 27.3, 24.9, 24.8; IR (film) νmax 2917, 2849, 1700, 1429, 1289, 1216, 952 cm−1; HRMS (DART-TOF) m/z 269.2137 (C16H28O3 + H+ requires 269.2117).
Methyl 10-(2-Oxocyclohexyl)decanoate (21)
A solution of carboxylic acid S7 (372 mg, 1.39 mmol) in acetone (14.2 mL) at 23 °C was treated sequentially with MeI (430 μL, 6.93 mmol) and K2CO3 (958 mg, 6.93 mmol). The resulting solution was refluxed for 24 h, then diluted with EtOAc to a total volume of 50 mL, washed with 1 N HCl(aq) (1 × 50 mL), dried over Na2SO4 and concentrated on a rotary evaporator. The resulting residue was purified by flash chromatography (SiO2, 20% Et2O/Pet. Ether) to provide methyl ester 21 as a pale yellow oil (349 mg, 89%): 1H NMR (CDCl3, 400 MHz) δ 3.66 (s, 3H), 2.38 (dt, J = 14.0, 4.5 Hz, 1H), 2.32–2.23 (m, 4H), 2.13–1.97 (m, 2H), 1.87–1.57 (m, 6H), 1.44–1.14 (m, 14H); 13C NMR (CDCl3, 100 MHz) δ 213.8, 174.5, 51.6, 50.9, 42.1, 34.3, 34.0, 29.9, 29.6, 29.5, 29.5, 29.4, 29.3, 28.2, 27.3, 25.1, 25.0; IR (film) νmax 2925, 2854, 1737, 1709, 1448, 1435, 1196, 1170 cm−1; HRMS (DART-TOF) m/z 283.2309 (C17H30O3 + H+ requires 283.2273).
Methyl 10-(7-Oxooxepan-2-yl)decanoate (22)
A solution of methyl ester 21 (78.6 mg, 0.278 mmol) in CH2Cl2 (1.40 mL) at 0 °C was treated with mCPBA (125 mg, 0.556 mmol). The resulting solution was warmed to 23 °C and stirred at 23 °C for 20 h. After 20 h, the reaction mixture was diluted with CH2Cl2 to a total volume of 3 mL, washed with sat. NaHCO3(aq) (2 × 3 mL), dried over Na2SO4, concentrated on a rotary evaporator, and purified by flash chromatography (SiO2, 20–40% Et2O/Hexanes) to provide caprolactone 22 as an amorphous white solid (75.3 mg, 91%): mp 29–31 °C; 1H NMR (CDCl3, 400 MHz) δ 4.21 (dt, J = 8.2, 3.9 Hz, 1H), 3.65 (s, 3H), 2.62 (qd, J = 13.7, 8.7 Hz, 2H), 2.29 (t, J = 7.6 Hz, 2H), 1.94–1.86 (m, 3H), 1.74–1.41 (m, 8H), 1.34–1.25 (m, 11H); 13C NMR (CDCl3, 100 MHz) δ 175.9, 174,4, 80.7, 51.6, 36.5, 35.1, 34.7, 34.2, 29.5, 29.5, 29.4, 29.3, 29.2. 28.5, 25.5, 25.1, 23.2; IR (film) νmax 2925, 2855, 1726, 1437, 1172, 1011 cm−1; HRMS (DART-TOF) m/z 299.2270 (C17H30O4 + H+ requires 299.2222).
Dimethyl 6-Hydroxyhexadecanedioate (23)
To neat caprolactone 22 (1.27 g, 4.26 mmol) at 23 °C was added a 0.5 M solution of NaOMe in MeOH (42.0 mL, 21.0 mmol). The resulting solution was stirred at 23 °C for 3.5 h. After 3.5 h, the reaction mixture was poured into sat. NH4Cl(aq) (100 mL) and extracted with EtOAc (3 × 75 mL). The combined organic layers were dried over Na2SO4, concentrated on a rotary evaporator, and purified by flash chromatography (SiO2, 20–40% EtOAc/Hexanes) to provide diester 23 as an amorphous white solid (141 mg, 85%): mp 47–51 °C; 1H NMR (CDCl3, 400 MHz) δ 3.67 (s, 3H), 3.67 (s, 3H), 3.61–3.57 (m, 1H), 2.31 (dt, J = 11.2, 7.5 Hz, 4H), 1.71–1.58 (m, 4H), 1.50–1.35 (m, 7H), 1.32–1.24 (m, 12H); 13C NMR (CDCl3, 100 MHz) δ 174.5, 174.3, 71.8, 51.6, 51.6, 37.7, 37.2, 34.2, 34.2, 29.8, 29.7, 29.5, 29.3, 29.3, 25.8, 25.3, 25.1, 25.0; IR (film) νmax 3532, 2911, 2850, 1733, 1717, 1246, 1206, 1174 cm−1; HRMS (DART-TOF) m/z 331.2488 (C18H34O5 + H+ requires 331.2484).
Dimethyl (E)-6-((3-(4-((tert-Butyldimethylsilyl)oxy)phenyl)acryloyl)oxy)hexadecaned-ioate (24)
A solution of diester 23 (600 mg, 1.82 mmol) in dry CH2Cl2 (18.0 mL) at 23 °C was treated sequentially with protected coumaric acid S850,51 (811 mg, 2.91 mmol), DMAP (44.4 mg, 0.363 mmol), and DCC (563 mg, 2.73 mmol). The resulting solution was warmed to 40 °C and stirred at 40 °C for 20 h. After 20 h, the reaction mixture was diluted with Et2O (50 mL), filtered through Celite, concentrated on a rotary evaporator, and purified by flash chromatography (SiO2, 15–30% Et2O/Hexanes) to provide coumaric ester 24 as a clear, colorless oil (743 mg, 69%): 1H NMR (CDCl3, 500 MHz) δ 7.61 (d, J = 15.9 Hz, 1H), 7.42 (d, J = 8.6 Hz, 2H), 6.83 (d, J = 8.6 Hz, 2H), 6.29 (d, J = 16.0 Hz, 1H), 4.99 (qd, J = 7.2, 5.2 Hz, 1H), 3.65 (s, 3H), 3.65 (s, 3H), 2.29 (dt, J = 10.5, 7.6 Hz, 4H), 1.71–1.51 (m, 8H), 1.43–1.24 (m, 14H), 0.98 (s, 9H), 0.21 (s, 6H); 13C NMR (CDCl3, 125 MHz) δ 174.5, 174.2, 167.3, 157.9, 144.3, 129.8, 128.0, 120.6, 116.4, 74.0, 51.6, 51.6, 34.4, 34.2, 34.1, 29.6, 29.6, 29.5, 29.3, 29.3, 25.8, 25.8, 25.8, 25.5, 25.1, 25.0, 18.4, –4.3; IR (film) νmax 2929, 2856, 1737, 1706, 1634, 1509, 1254, 1164, 908, 836, 781 cm−1; HRMS (DART-TOF) m/z 591.3795 (C33H54O7Si + H+ requires 591.3717).
1,16-Dihydroxyhexadecan-6-yl (E)-3-(4-((tert-Butyldimethylsilyl)oxy)phenyl)acrylate (S9)
A solution of coumaric ester 24 (742 mg, 1.26 mmol) in dry Et2O (15.0 mL) at 23 °C was treated with solid LiBH4 (222 mg, 10.0 mmol). The resulting solution was stirred at 23 °C for 3 h. After 3 h, the reaction mixture was treated dropwise with sat. NaHCO3(aq) (15 mL). Stirring was continued until off-gassing ceased. The biphasic mixture, thus obtained, was extracted with Et2O (3 × 10 mL) and the combined organic layers were dried over Na2SO4, concentrated on a rotary evaporator, and purified by flash chromatography (SiO2, 20–60% EtOAc/Hexanes) to provide a clear, colorless oil containing the product (S9, 432 mg, 64%) and over-reduced byproduct (S10, 109 mg) as an inseparable mixture. For S9: 1H NMR (CDCl3, 500 MHz) δ 7.61 (d, J = 15.9 Hz, 1H), 7.42 (d, J = 8.6 Hz, 2H), 6.83 (d, J = 8.6 Hz, 2H), 6.30 (d, J = 15.9 Hz, 1H), 5.01 (qd, J = 7.4, 5.1 Hz, 1H), 3.63 (t, J = 6.6 Hz, 4H), 1.66–1.45 (m, 8H), 1.44–1.18 (m, 18H), 0.98 (s, 9H), 0.21 (s, 6H); 13C NMR (CDCl3, 125 MHz) δ 173.0, 167.4, 157.9, 144.3, 129.8, 120.6, 116.4, 74.2, 63.2, 62.9, 34.5, 34.4, 32.9, 32.8, 29.7, 29.6, 29.6, 29.6, 29.5, 25.9, 25.8, 25.8, 25.7, 25.5, 25.2, –4.2; HRMS (DART-TOF) m/z 535.3895 (C31H54O5Si + H+ requires 535.3819).
1,16-Dihydroxyhexadecan-6-yl (E)-3-(4-Hydroxyphenyl)acrylate (S11)
A solution of diol S9 (307 mg, 0.574 mmol) and over-reduced byproduct S10 (78 mg) in THF (13.3 mL) at 23 °C was treated with a 1 M solution of TBAF in THF (1.08 mL, 1.08 mmol). The resulting solution was stirred for 5 min. After 5 min, the reaction mixture was treated with 1 M HCl(aq) (10 mL) and extracted with EtOAc (3 × 10 mL). The combined organic layers were dried over Na2SO4, concentrated on a rotary evaporator, and purified by flash chromatography (SiO2, 80% EtOAc/Hexanes) to provide a clear, colorless oil containing the triol product (S11, 217 mg, 90%) and over-reduced byproduct (S12, 55 mg) as an inseparable mixture. For S11: 1H NMR (CDCl3, 500 MHz) δ 7.61 (d, J = 15.9 Hz, 1H), 7.41 (d, J = 8.7 Hz, 2H), 6.84 (d, J = 8.6, 2H), 6.47 (bs, 1H), 6.28 (d, J = 15.9 Hz, 1H), 5.01 (tt, J = 7.5, 5.0 Hz, 1H), 3.67–3.60 (m, 4H), 1.71–1.48 (m, 8H), 1.48–1.15 (m, 18H); 13C NMR (CDCl3, 125 MHz) δ 167.7, 158.3, 144.6, 130.1, 127.1, 116.1, 115.9, 74.3, 63.3, 62.9, 34.5, 34.4, 32.9, 32.6, 29.6, 29.6, 29.6, 29.5, 29.5, 25.8, 25.6, 25.4, 25.2; HRMS (DART-TOF) m/z 419.2881 (C25H40O5 – H+ requires 419.2798).
1,16-Dioxohexadecan-6-yl (E)-3-(4-Hydroxyphenyl)acrylate (25)
A solution of triol S11 (94.2 mg, 0.224 mmol) and over-reduced byproduct S12 (23.8 mg) in CH2Cl2 (2.56 mL) at 0 °C was treated sequentially with Et3N (1.30 mL) and a solution of SO3 ∙ py (267 mg, 1.68 mmol) in DMSO (1.77 mL). The resulting solution was stirred at 0 °C for 2.5 h. After 2.5 h, the reaction mixture was treated with 1 M HCl(aq) (5 mL) and extracted with EtOAc (3 × 5 mL). The combined organic layers were dried over Na2SO4, concentrated on a rotary evaporator, and purified by PTLC (SiO2, 50% EtOAc/Hexanes) to provide dialdehyde 25 as a clear, colorless oil (54.2 mg, 58%): 1H NMR (DMSO-d6, 500 MHz) δ 10.00 (s, 1H), 9.65 (dt, J = 3.2, 1.6 Hz, 2H), 7.57–7.52 (m, 3H), 6.79 (d, J = 8.7 Hz, 2H), 6.38 (d, J = 16.0 Hz, 1H), 4.93–4.88 (m, 1H), 2.43 (td, J = 7.2, 1.6 Hz, 2H), 2.39 (td, J = 7.3, 1.7 Hz, 2H), 1.58–1.47 (m, 8H), 1.33–1.24 (m, 14H); 13C NMR (CDCl3, 125 MHz) δ 203.4, 202.9, 167.5, 158.0, 144.5, 130.1, 127.3, 116.0, 116.0, 74.1, 44.0, 43.9, 34.4, 34.2, 29.6, 29.6, 29.4, 29.4, 29.3, 25.5, 25.1, 22.2, 22.1; IR (film) νmax 3347, 2926, 2854, 1704, 1603, 1585, 1514, 1261, 1164, 983, 832 cm−1; HRMS (DART-TOF) m/z 417.2740 (C25H36O5 + H+ requires 417.2641).
Sporopollenin-inspired polymer synthesis via crosslinking
To a solution of 5.00 wt% PVA in DMSO (1.00 mL, 1.14 mmol) was added an appropriate amount of dialdehyde (vide supra) to achieve the desired DOC at 23 °C. The suspension was heated to 60 °C in a sealed vial until complete dissolution of the dialdehyde was achieved (approx. 5 min). To this warm solution was added 0.10 mL of acid catalyst solution containing 7.50 v/v% AcOH and 2.50 v/v% H2SO4 in DMSO. The resulting solution was vigorously homogenized and poured into silicone molds. Curing of this solution at 55–60 °C at 760 torr for 90–120 min under an atmosphere of air, then at 40 °C at 250 torr for 72 h under an atmosphere of air provided crosslinked polymers which were subsequently washed by submerging sequentially in distilled H2O (10 min), sat. NaHCO3(aq) (10 min), and distilled H2O again (2 h). Drying of the resultant materials under ambient conditions for 24 h provided sporopollenin-inspired polymers which were utilized, without further treatment, for chemical, physical, and thermal analyses.
Solvolysis studies
One disk of sporopollenin-inspired polymer (vide supra) of known mass was placed in 10 mL of solvent and allowed to shake (150 rpm) at 23 °C for 24 h. The polymer disk was then dried at 40 °C and 250 torr for 24 h unless otherwise noted, allowed to equilibrate under ambient conditions for 24 h, then weighed to determine total mass loss during solvolysis. All observed mass losses, with the exception of the conc. H2SO4 sample, are below the mass fraction attributed to volatile low molecular weight compounds (i.e., residual solvent) in the starting samples as observed by TGA (vide infra).
Degradative thioacidolysis/liquid chromatography-high resolution mass spectrometry (DT/LC-HRMS)
A suspension of authentic sporopollenin or synthetic sporopollenin analogue (4.0 mg) in dry 1,4-dioxane (9.0 mL) was treated sequentially with ethane thiol (1.0 mL, 14 mmol) and >46.5% boron trifluoride diethyl etherate (0.25 mL, 0.05 mmol) at 23 °C. The resulting suspension was sealed and heated to 100 °C for 4 h. After 4 h, the reaction mixture was cooled to 23 °C, treated dropwise with sat. NaHCO3(aq) to achieve a pH of approximately 4, and extracted with CHCl3 (3 × 5 mL). The combined organic layers were dried over Na2SO4 and concentrated under a stream of nitrogen. The crude product was dissolved in CHCl3, filtered, and submitted for LC-HRMS analysis35.
Durometer hardness
Durometer hardness measurements were conducted by Element Materials Technology in accordance with ASTM D2240 (excepting sample geometry) with conditioning at laboratory conditions of 23 ± 2 °C and 50 ± 10% relative humidity. Samples were disks approximately 1.4 mm in thickness and 3.5 mm in diameter. Due to the small sample size, one reading was taken from each individual sample. Hardness reported on the Shore D scale.
Compression testing
Compression testing was conducted in triplicate according to the following procedure: We fabricated the testing samples in a disk shape with a diameter D of around 3.7 mm and a thickness H of around 1.6 mm. The disk-shaped sample was compressed using a mechanical tester from Zwick/Roell company up to its nominal strain of 80% and subsequently unloaded to its original state. The loading speed was set as 1 mm/min. The measured nominal stress s versus nominal strain ε of the sample can be calculated via s = F/A and ε = ∆/H, where F is the measured force, A = πD2/4 is the cross-sectional area of the sample with D as the diameter of the sample, ∆ is the loading displacement, and H is the thickness of the sample. The elastic modulus of the sample was calculated via E = ds/dε|ε=0). The hysteresis ratio was calculated by \(h={\int }_{0}^{{\varepsilon }_{{\max }}}{sd}\varepsilon\), where εmax is the maximum nominal strain during the cyclic compressive loading.
Tensile testing
Tensile testing was conducted in triplicate according to the following procedure: We fabricated the testing samples in a strip shape with a width W of around 8.6 mm, a thickness T of around 1.6 mm, and a height H of around 10 mm. A monotonic tensile load was applied on the strip-shaped sample using a mechanical tester from Zwick/Roell company up to the rupture of the sample. The loading speed was set as 1 mm/min. The measured nominal stress s versus nominal strain ε of the sample can be calculated via s = F/A and ε = ∆/H, where F is the measured force, A = WT is the cross-sectional area of the sample with W as the width of the sample and T as the thickness of the sample, ∆ is the loading displacement, and H is the height of the sample. We also performed a cyclic tensile loading on the sample at the same loading speed of 1 mm/min, measuring its hysteresis at various applied strains under tensile loading.
Swelling ratio
The measurement of swelling ratio was conducted in triplicate according to the following procedure: We fabricated the testing samples in a disc shape with a diameter D of around 3.7 mm and a thickness H of around 1.6 mm. Both the volume and weight of the sample were measured before and after immersing in a deionized water, measuring the volume swelling ratios and the weight swelling ratios, respectively.
Thermogravimetric analysis (TGA)
Thermogravimetric analysis was conducted in triplicate by Element Materials Technology in accordance with Element New Berlin Procedure PA-04 with all polymer samples disclosed herein. Samples were heated from 20 °C to 650 °C at a rate of 20 °C/min under an atmosphere of nitrogen, cooled to 500 °C, exposed to air, then heated to 800 °C at a rate of 20 °C/min. Three mass loss events were observed. The first, observed at 184–236 °C in nitrogen, corresponds to evolution of loss of low molecular weight (i.e., solvents). The second, observed at 440–464 °C in nitrogen, corresponds to decomposition of the base polymer. The third, observed at 519–540 °C in air, corresponds to combustion which left behind a particulate carbonaceous residue.
Differential scanning calorimetry (DSC)
Differential scanning calorimetry was conducted in triplicate by Element Materials Technology in accordance with Element New Berlin Procedure PA-06 with synthetic sporopollenin analogue 15. A three-step methodology was employed in which samples were heated from –60 °C to 275 °C, control cooled to –60 °C, then heated to 300 °C under an atmosphere of nitrogen. No significant thermal features were observed below 110 °C. Above 110 °C, volatilization of residual low molecular weight compounds (i.e., solvents, observed via TGA) interfered with observations. Subsequent modulated DSC focused below 110 °C was performed by heating samples from –60 °C to 110 °C at an underlying heating rate of 3 °C/min which was modulated ±1 °C every 60 s.
Data availability
Additional experimental details including: supplementary methods, Supplementary Notes, Supplementary Tables S1–S9, and Supplementary Figs. S1–S62 are available in the Supplementary Information. The raw data that support the findings of this study are available from the corresponding author upon reasonable request. Correspondence and request for materials should be addressed to J.-K.W.
References
Zetzsche, F. & Kälin, O. Untersuchungen über die membran der sporen und pollen V. 4. Zur autoxydation der sporopollenine. Helv. Chem. Acta 14, 517 (1931).
Zetzsche, F. & Vicari, H. Untersuchungen über die membran der sporen und pollen IV. 3. fossiles sporopollenin aus dem tasmanit und der moskauer braunkohle. Helv. Chem. Acta 14, 62 (1931).
Braconnot, H. Recherches chimique sur le pollen du typha latifolia, Lin. Famille d. typhacees. Ann. Chim. Phys. 2, 91 (1829).
John, J. F. Ueber den befruchtungsstaub, nebst einer analyse des tulpenpollens. J. Chem. Phys. 12, 244 (1814).
Mackenzie, G., Boa, A. N., Diego-Taboada, A., Atkin, S. L. & Sathyapalan, T. Sporopollenin, the least known yet toughest natural biopolymer. Front. Mater. 2, 66 (2015).
Brooks, J. & Shaw, G. Sporopollenin: A review of its chemistry, palaeochemistry and geochemistry. Grana 17, 91 (1978).
Ariizumi, T. & Toriyama, K. Genetic regulation of sporopollenin synthesis and pollen exine development. Ann. Rev. Plant Biol. 62, 437 (2011).
Pacini, E., Guarnieri, M. & Nepi, M. Pollen carbohydrates and water content during development, presentation, and dispersal: a short review. Protoplasma 288, 73 (2006).
Qu, Z. & Meredith, J. C. The atypically high modulus of pollen exine. J. R. Soc. Interface 15, 20180533 (2018).
Montgomery, W., Potiszil, C., Watson, J. S. & Sephton, M. A. Sporopollenin, a natural copolymer, is robust under high hydrostatic pressure. Macromol. Chem. Phys. 217, 2494 (2016).
Southworth, D. Solubility of pollen exines. Am. J. Bot. 61, 36 (1974).
Shaw, G. et al. The use of modified sporopollenin from Lycopodium clavatum as a novel ion- or ligand-exchange medium. React. Polym. Ion-. Exchangers Sorbents 9, 211 (1988).
Barrier, S. et al. Access to a primary aminosporopollenin solid support from plant spores. Green. Chem. 12, 234 (2010).
Archibald, S. J. et al. How does iron interact with sporopollenin exine capsules? An X-ray absorption study including microfocus XANES and XRF imaging. J. Mater. Chem. B 2, 945 (2014).
Mackenzie, G. & Shaw, G. Sporopollenin. A novel, naturally occurring support for solid phase peptide synthesis. Int. J. Peptide Protein Res. 15, 298 (1980).
Sahin, M., Gubbuk, I. H. & Kocak, N. Synthesis and characterization of sporopollenin-supported schiff bases and ruthenium(III) sorption studies. J. Inorg. Organomet. Polym. Mater. 22, 1279 (2012).
de Souza, S. P. et al. Sporopollenin as an efficient green support for covalent immobilization of a lipase. Catal. Sci. Technol. 5, 3130 (2015).
Keleş, M. Preparation of heterogeneous palladium catalysts supported on sporopollenin for heck coupling reactions. Synth. React. Inorg., Met. -Org., Nano-Met. Chem. 43, 575 (2013).
Yilmaz, E. Enantioselective enzymatic hydrolysis of racemic drugs by encapsulation in sol-gel magnetic sporopollenin. Bioprocess Biosyst. Eng. 35, 493 (2012).
Yaacob, S. F. F. S. et al. Synthesis and characterizations of magnetic bio-material sporopollenin for the removal of oil from aqueous environment. Ind. Crops Prod. 124, 442 (2018).
Atwe, S. U., Ma, Y. & Gill, H. S. Pollen grains for oral vaccination. J. Control. Release 194, 45 (2014).
Barrier, S. et al. Viability of plant spore exine capsules for microencapsulation. J. Mater. Chem. 21, 975 (2011).
Diego-Taboada, A. et al. Protein free microcapsules obtained from plant spores as a model for drug delivery: ibuprofen encapsulation, release and taste masking. J. Mater. Chem. B 1, 707 (2013).
Lorch, M. et al. MRI contrast agent delivery using spore capsules: controlled release in blood plasma. Chem. Commun. 42, 6442 (2009).
Beckett, S. T., Atkin, S. L. & Mackenzie, G. Dosage form comprising an exine coating of sporopollenin or derivatized sporopollenin. World Patent Number: WO/2005/000280. US07608270 (27 October 2009).
Sporomex Ltd., sporomex.co.uk.
Hamad, S. A., Dyab, A. F. K., Stoyanov, S. D. & Paunov, V. N. Encapsulation of living cells into sporopollenin microcapsules. J. Mater. Chem. 21, 18018 (2011).
Lutzke, A., Morey, K. J., Medford, J. I. & Kipper, M. J. Detailed characterization of Pinus ponderosa sporopollenin by infrared spectroscopy. Phytochemistry 170, 112195 (2020).
Guilford, W. J., Schneider, D. M., Labovitz, J. & Opella, S. J. High resolution solid state 13C NMR spectroscopy of sporopollenins from different plant taxa. Plant Physiol. 86, 134 (1988).
Depciuch, J., Kasprzyk, I., Roga, E. & Parlinska-Wojtan, M. Analysis of morphological and molecular composition changes in allergenic Artemisia vulgaris L. pollen under traffic pollution using SEM and FTIR spectroscopy. Environ. Sci. Pollut. Res. 23, 23203 (2016).
Depciuch, J., Kasprzyk, I., Sadik, O. & Parlinska-Wojtan, M. FTIR analysis of molecular composition changes in hazel pollen from unpolluted and urbanized areas. Aerobiologia 33, 1 (2017).
Jardine, P. E., Fraser, W. T., Lomax, B. H. & Gosling, W. D. The impact of oxidation on spore and pollen chemistry. J. Micropalaeontol. 34, 139 (2015).
Mikhael, A. et al. Demystifying and unravelling the molecular structure of the biopolymer sporopollenin. Rapid Commun. Mass Spectrom. 34, e8740 (2020).
Ahlers, F., Thom, I., Lambert, J., Kuckuk, R. & Wiemann, R. 1H NMR analysis of sporopollenin from Typha Angustifolia. Phytochemistry 50, 1095 (1999).
Li, F.-S., Phyo, P., Jacobowitz, J., Hong, M. & Weng, J.-K. The molecular structure of plant sporopollenin. Nat. Plants 5, 41 (2019).
Rudra, R., Kumar, V. & Kundu, P. P. Acid catalyzed cross-linking of poly vinyl alcohol (PVA) by glutaraldehyde: effect of crosslink density on the characteristics of PVA membranes used in single chambered microbial fuel cells. RSC Adv. 5, 83436 (2015).
Philipp, W. H. & Hzu, L.-C. Three methods for in situ cross-linking of polyvinyl alcohol films for application as ion-conducting membranes in potassium hydroxide electrolyte. NASA Technical Paper 1407, (1979).
Kumeta, K., Nagashima, I., Matsui, S. & Mizoguchi, K. Crosslinking of Poly(vinyl alcohol) via Bis(β-hydroxyethyl) sulfone. Polym. J. 36, 472 (2004).
Piluso, P., Boisson, F. D.-C., Bounor-Legaré, V. & Espuche, E. Acetalization of poly(vinyl alcohol) by a fatty aldehyde in water medium: Model study, kinetics, and structure analysis. J. Polym. Sci., Part A: Polym. Chem. 56, 661 (2018).
Ahmad, A. L., Yusuf, N. M. & Ooi, B. S. Preparation and modification of poly(vinyl) alcohol membrane: Effect of crosslinking time towards its morphology. Desalination 287, 35 (2012).
Figueiredo, K. C. S., Alves, T. L. M. & Borges, C. P. Poly(vinyl alcohol) films crosslinked by glutaraldehyde under mild conditions. J. Appl. Polym. Sci. 111, 3074 (2009).
Gadhave, R. V., Mahanwar, P. A. & Gadekar, P. T. Study of cross-linking between boric acid and different bypes of polyvinyl alcohol adhesive. Open J. Polym. Chem. 9, 76 (2019).
Roels, J. & Metz, P. Oxidation of α,ω-Diols using the Dess-Martin periodinane. Synlett. 6, 789 (2001).
Deguchi, Y., Kono, M., Koizumi, Y., Izato, Y. & Miyake, A. Study on autocatalytic decomposition of dimethyl sulfoxide (DMSO). Org. Process Res. Dev. 24, 1614 (2020).
Yang, Q. et al. Potential explosion hazards associated with the autocatalytic decomposition of dimethyl sulfoxide and its mixtures. Org. Process Res. Dev. 24, 916 (2020).
Song, Y.–Y. et al. First total synthesis of (+)-broussonetine W: glycosidase inhibition of a natural product & analogs. Org. Biomol. Chem. 14, 5157 (2016).
Baeyer, A. & Villiger, V. Einwirkung des caro’schen reagens auf ketone. Ber. Dtsch. Chem. Ges. 32, 3625 (1899).
Baeyer, A. & Villiger, V. Ueber die einwirkung des caro’schen reagens aug ketone. Ber. Dtsch. Chem. Ges. 33, 858 (1900).
Neises, B. & Steglich, W. Simple method for the esterification of carboxylic acids. Angew. Chem. Int. Ed. 17, 522 (1978).
Brandt, D. R., Pannone, K. M., Romano, J. J. & Casillas, E. G. The synthetic preparation of naturally-occuring aromatase inhibitors, morachalcone A, isogemichalcone B, and isogemichalcone C. Tetrahedron 69, 9994 (2013).
Liu, S. X. et al. Inhibitory effect of 4,4’-dihydroxy-α-truxillic acid derivatives on NO production in lipopolysaccharide-induced RAW 264.7 macrophages and exploration of structure-activity relationships. Bioorg. Med. Chem. Lett. 23, 2207 (2013).
Kim, S. S. & Douglas, C. J. Sporopollenin monomer biosynthesis in Arabidopsis. J. Plant Biol. 56, 1 (2013).
Aarts, M. G. et al. The Arabidopsis MALE STERILITY 2 protein shares similarity with reductases in elongation/condensation complexes. Plant J. 12, 615 (1997).
Souza, C. et al. Genome-wide analysis of a land plant-specific acyl:coenzymeA synthetase (ACS) gene family in Arabidopsis, poplar, rice, and Physcomitrella. N. Phytol. 179, 987 (2008).
Dobritsa, A. A. et al. LAP5 and LAP6 encode anther-specific proteins with similarity to chalcone synthase essential for pollen exine development in Arabidopsis. Plant Physiol. 153, 937 (2010).
Kim, S. S. et al. LAP6/POLYKETIDE SYNTHASE A and LAP5/POLYKETIDE SYNTHASE B encode hydroxyalkyl α-pyrone synthases required for pollen development and sporopollenin biosynthesis in Arabidopsis thaliana. Plant Cell 22, 4045 (2010).
Tang, L. K., Chu, H., Yip, W. K., Yeung, E. C. & Lo, C. An anther-specific dihydroflavonol 4-reductase-like gene (DLR1) is essential for male fertility in Arabidopsis. N. Phytol. 181, 576 (2009).
Grienenberger, E. et al. Analysis of TETRAKETIDE α-PYRONE REDUCTASE function in Arabidopsis thaliana reveals a previously unknown, but conserved, biochemical pathway in sporopollenin monomer biosynthesis. Plant Cell 22, 4067 (2010).
Dobritsa, A. A. et al. LAP3, a novel plant protein required for pollen development, is essential for proper exine formation. Sex. Plant Reprod. 22, 167 (2009).
Morant, M. et al. CYP703 is an ancient cytochrome P450 in land plants catalyzing in-chain hydroxylation of lauric acid to provide building blocks for sporopollenin synthesis in pollen. Plant Cell 19, 1473 (2007).
Dobritsa, A. A. et al. CYP704B1 is a long-chain fatty acid ω-hydroxylase essential for sporopollenin synthesis in pollen of Arabidopsis. Plant Physiol. 151, 574 (2009).
Reif, B., Ashbrook, S. E., Emsley, L. & Hong, M. Solid-state NMR spectroscopy. Nat. Rev. Methods Primers 1, 2 (2021).
Braun, D., Böhringer, B. & Eidam, N. ATR-FTIR spectroscopy as a tool for studies of polymer-polymer miscibility. Polym. Bull. 21, 63 (1989).
Mukherjee, S. & Gowen, A. A review of recent trends in polymer characterization using non-destructive vibrational spectroscopic modalities and chemical imaging. Anal. Chim. Acta 895, 12 (2015).
Alwardt, T. L. An investigation of recycled high density polyethylene reinforced with short glass fibers. Ph.D. Dissertation, Eastern Illinois University, Charleston, IL, 1994.
Rubinstein, M. & Colby, R. H. Polymer physics. Vol. 23. Oxford University Press New York, 2003.
Rutenberg, R., Golden, G., Cohen, Y., Kleiman, M. & Poverenov, E. Investigation of substituent effect in modified nature-sourced polymers: rational side chain engineering to control yield, design, and properties. ACS Omega 3, 12841 (2018).
Mangaleswaran, S. & Argade, N. P. A facile synthesis of naturally occuring aminopeptidase inhibitor tyromycin A. J. Org. Chem. 66, 5259 (2001).
Ziffle, V. E., Cheng, P. & Clive, D. L. J. Conversion of 1,4-Diketones into para-Disubstituted Benzenes. J. Org. Chem. 75, 8024 (2010).
Degani, I. & Fochi, R. Pentatomic heteroaromatic cations. Part V. A convenient general method for the preparation of aldehydes from acyl chlorides via 2-substituted 1,3-benzoxathiolylium tetrafluoroborates. J. Chem. Soc. Perkin Trans. 1, 323 (1976).
Guillonneau, L., Taddei, D. & Moody, C. J. Synthesis of the reported structure of the bisbenzoquinone lanciaquinone, isolated from Maesa lanceolata. Org. Lett. 10, 4505 (2008).
Takezawa, E., Sakaguchi, S. & Ishii, Y. Oxidative cleavage of vic-diols to aldehydes with dioxygen catalyzed by Ru(PPh3)3Cl2 on active carbon. Org. Lett. 1, 713 (1999).
Acknowledgements
This work was supported by the Grantham Foundation (J.-K.W.). We thank Dr. Walter Massefski, Dr. Bruce Adams, Dr. Mohan Kumar, and John Grimes for assistance with NMR spectroscopy and DART-TOF spectrometry, Tenzin Kunchok for assistance with mass spectrometry, and the MIT Institute for Soldier Nanotechnologies for access to material characterization instrumentation.
Author information
Authors and Affiliations
Contributions
C.M.G. and J.-K.W. designed the research. C.M.G. designed and executed the synthesis of simplified and synthetic crosslinkers, their polymerization with polyvinyl alcohol, and the spectroscopic and degradative spectrometric characterization thereof. F.-S.L. assisted with various aspects of polymer characterization. C.M.G., S.L., and J.N. mechanically characterized the polymers under the supervision of X.Z. All authors interpreted the results and contributed to the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Communications Chemistry thanks Kousuke Tsuchiya and Qunfeng Cheng for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Glinkerman, C.M., Lin, S., Ni, J. et al. Sporopollenin-inspired design and synthesis of robust polymeric materials. Commun Chem 5, 110 (2022). https://doi.org/10.1038/s42004-022-00729-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s42004-022-00729-w
- Springer Nature Limited