Abstract
This study developed a kind of PEG-crosslinked O-carboxymethyl chitosan (O-CMC–PEG) with various PEG content for food packaging. The crosslinking agent of isocyanate-terminated PEG was firstly synthesized by a simple condensation reaction between PEG and excess diisocyanate, then the crosslink between O-carboxymethyl chitosan (O-CMC) and crosslinking agent occurred under mild conditions to produce O-CMC–PEG with a crosslinked structure linked by urea bonds. FT-IR and 1H NMR techniques were utilized to confirm the chemical structures of the crosslinking agent and O-CMC–PEGs. Extensive research was conducted to investigate the impact of the PEG content (or crosslinking degree) on the physicochemical characteristics of the casted O-CMC–PEG films. The results illuminated that crosslinking and components compatibility could improve their tensile features and water vapor barrier performance, while high PEG content played the inverse effects due to the microphase separation between PEG and O-CMC segments. The in vitro degradation rate and water sensitivity primarily depended on the crosslinking degree in comparison with the PEG content. Furthermore, caused by the remaining –NH2 groups of O-CMC, the films demonstrated antibacterial activity against Escherichia coli and Staphylococcus aureus. When the PEG content was 6% (medium crosslinking degree), the prepared O-CMC–PEG−6% film possessed optimal tensile features, high water resistance, appropriate degradation rate, low water vapor transmission rate and fine broad-spectrum antibacterial capacity, manifesting a great potential for application in food packaging to extend the shelf life.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Nowadays, the food safety problems caused by food contamination have become one of the most prominent public health problems around the world with the accelerated global food circulation. Approximately 30% of the global population experience serious health problems through consumption of food containing pathogens1. Furthermore, foods, especially fruits and vegetables, bring more security problems because they are perishable in the process of storage, transportation, and sale. Appropriate packaging material can maintain food quality and avoid possible contamination along the entire food supply chain2. Various petroleum-based packaging systems such as PP and PE have been widely used in our daily lives3,4, while these materials face a serious problem of environmental pollution because of their non-degradable nature5. Therefore, natural polymer materials have been considered as promising candidates to develop food packaging materials because of their non-toxicity, renewability, low cost, good biocompatibility, degradability, and high consumer acceptance6,7,8,9.
As a natural biopolymer material, chitosan (CS), the most abundant alkaline polysaccharide in nature10, has been extensively used in food, biomedicine, and other aspects due to its diverse bioactivities, such as biocompatibility, degradability, non-toxicity, and antibacterial activity11,12,13,14. As expected, CS has also drawn attention as an ideal environmental material regarding the replacement of petroleum-based materials15 and is becoming one of the key raw materials for preparing antibacterial packaging materials16,17. Despite the promise, strong intermolecular H-bonds existing in the crystalline structure of CS produced poor tensile properties18. Additionally, CS has limited solubility in water and most organic solvents, further restricting its application in packaging19,20,21. O-carboxymethyl chitosan (O-CMC), a derivative of CS, possesses similar chemical properties but offers improved water solubility, superior antibacterial activity, and enhanced chemical activity due to the introduction of the carboxymethyl group22,23,24,25. However, O-CMC has also drawbacks such as brittleness and weak gas permeability, which hinder its application in the field of food packaging26,27. Modification of O-CMC can improve the tensile properties, gas barrier properties, and so on, so considerable work has been carried out to promote its properties of O-CMC28,29.
Polyethylene glycol (PEG) is a biocompatible and non-toxic polyether that can dissolve in water and various organic solvents without undergoing hydrolysis30,31,32,33. The double-ended hydroxyl (–OH) structure of PEG allows for modifications with functional groups like carboxyl, hydroxyl, and amides34. As a result, PEG has been widely used as a modifier to enhance the properties of materials, including plasticity, hydrophilicity, and flexibility35. In a recent work36, we reported a class of monomethoxyl PEG grafted O-CMC films, which simultaneously exhibited excellent tensile properties, satisfactory water vapor barrier properties, and good broad-spectrum antibacterial activities. The nontoxic materials hold significant potential for edible food packaging. However, the application range of the composites was greatly limited by their high water solubility.
To solve the limitations of the above CS-based film materials, a novel food packaging material was designed with a simple strategy in this study. The condensation reaction between PEG and excess diisocyanate readily accomplished to produce NCO-terminated PEG (OCN–PEG–NCO), which was used as a crosslinking agent to react with O-CMC in water under mild conditions to produce PEG-modified O-CMC (O-CMC–PEG) with crosslinked structure linked by urea bonds. The influences of the PEG content (or crosslinking degree) on the physicochemical features (thermal properties, tensile properties, water sensitivity, water vapor barrier properties, degradability) of the casted O-CMC–PEG films were extensively investigated. In addition, the antibacterial performance of the composite film was evaluated.
Materials and methods
Materials
O-CMC (MW: 240 KDa, substitution degree: 90%; deacetylation degree: 90%) and PEG (Mn: 1000 g/mol, dried for 150 min at 100 °C under vacuum) were acquired from Sigma-Aldrich (Shanghai, China). Hexamethylene diisocyanate (HDI) and Sn(Oct)2 (purity > 95%) were purchased from Aladdin (Shanghai, China). Other reagents, including ethyl ether, and ethyl acetate (EA) (Macklin, Jinan, China) were of AR grade.
Synthesis of OCN–PEG–NCO
The method for synthesis of OCN–PEG–NCO was described in the previous literature37 and the reaction scheme is illustrated in Fig. 1a. To summarize, the PEG (0.02 mol), HDI (0.12 mol), and Sn(Oct)2 (0.3 wt%) were dissolved in 15 mL of EA in the presence of dry N2. The reaction was conducted at 60 °C for 6 h. Subsequently, the resulting mixture was precipitated in cold diethyl ether to remove the catalyst and unreacted HDI. The purification process was executed three times. After drying under vacuum, the viscid OCN–PEG–NCO was obtained.
Preparation of O-CMC–PEG Films
The reaction process can be observed in Fig. 1b. Typically, O-CMC was dissolved in deionized water under mechanical stirring at a temperature range of 2–4 °C to obtain a homogenous solution (0.1 g/mL). Then, the aqueous solution of OCN–PEG–NCO (0.2 g/mL) was introduced into the system. After rapid stirring, the mixture was gently transferred into a Teflon mold at the same temperature. The reaction was carried out in the mold at room temperature until the vanishing of –NCO absorption in the FT-IR spectrum (~ 2267 cm−1). Removal of solvent was achieved by volatilizing at 60 °C, resulting in the formation of O-CMC–PEG films (thickness: 0.10 ± 0.01 mm) which were thoroughly dried under vacuum. The basic formulations for O-CMC–PEG are provided in Table 1. The composite films with varying PEG content were labeled as O-CMC–PEG−X% (where X% represents the weight content of PEG in the films).
Measurements
FT-IR analyses were conducted on a NICOLET 6700 infrared spectrophotometer (USA) with a resolution of 4 cm−1. 1H NMR measurements were performed on a 400 MHz Bruker AVANCE II spectrometer (Germany). The microstructures of the film surfaces were observed with an SEM (Quanta 200, FEI, Holland).
The TGA 2950 instrument (TA, USA) was used to perform TGA with a ramp rate of 20 °C/min in the presence of N2. DSC analysis was conducted using a DSC2500 instrument (TA, USA) under N2 with a heating rate of 10 °C/min. Tensile testing was carried out on a UTM-0402 testing machine (Jijian Instruments, Chengde, China) following the standard testing procedure described in GB/T1040.3-2006.
Water vapor transmission rates (WVTR) were examined by the gravimetric method38. Typically, the sample films were cut into circular pieces and then were covered on the conical bottle containing anhydrous CaCl2, and placed in a relative humidity (RH = 30%, 50%, and 80%) incubator at 25 ± 1 °C. Then, the WVTR (g mm/ (m2·24 h)) of the samples was calculated by the change in the conical bottle quality after 24 h.
Water absorption (WA) measurement was performed in deionized water. The film samples were incubated in water at 25 ± 0.5 °C. At a predetermined period, the swollen samples were weighed after the excess water on the surface was gently wiped off with absorbent paper. The WA was calculated from the weight ratio of the swollen sample to the initial sample.
The degradation properties were executed according to the method in the published paper39. Briefly, the test samples were immersed in glass vials containing PBS (pH 7.4) and incubated at room temperature over 6 weeks. The mass loss percentages at specific time intervals were determined to evaluate the degradability. SEM was used to observe the surface morphologies of the lyophilized samples.
The antibacterial capacities of the film against Escherichia coli and Staphylococcus aureus were evaluated via an inhibition zone test40. In brief, the culture plate was first covered with a nutrient agar medium, and then the test bacteria (3 × 105–5 × 105 CFUs/mL) were spread on it. The sterilized film samples were positioned on the plate. After an incubation period of 24 h at room temperature, we measured the diameters of the inhibition zones to evaluate the antibacterial efficacy.
Results and discussion
Synthesis and characterization
The terminal –OH groups of PEG were end-capped with the –NCO groups to form the NCO–PEG–NCO linker without any byproducts. By using excess diisocyanate, the chain extension could be significantly limited. The chemical structure was analyzed by the FT-IR technique (Fig. 2c). In the spectrum, the broad absorption peak of the –OH groups in PEG (~ 3440 cm−1, Fig. 2a) disappeared41, accompanied by the presence of a new peak at 2266 cm−1 which vested in the typical absorption of –NCO groups. The peaks at 3332, 1717, and 1536 cm−1 should belong to the –NH–, amide, and C=O absorption in the newly formed urethane groups, respectively42. The analysis indicated that the terminal –OH groups of PEG were completely consumed and the –NCO groups were successfully introduced to the end of the PEG chain. Furthermore, the structure of OCN–PEG–NCO was confirmed by 1H NMR (Fig. 3). The chemical shifts at 4.85 ppm were attributed to the –NH– proton of urethane groups. The proton signals of urethane-linked methylene and repeat units (–OCH2CH2–) of PEG segments appeared at 4.22 and 3.63 ppm, respectively. Based on the molecular weight of PEG, the integral area of the proton peaks matched the chemical structure of OCN–PEG–NCO (Fig. 1), which further demonstrated no existence of a chain-extending byproduct.
For the reactivity of –NCO with –NH2 was much higher than that with –OH, the crosslinking reaction between O-CMC and OCN–PEG–NCO could be performed in water. A low temperature (2–4 °C) was used to reduce the reaction rate so that the reaction mixture could be easily transferred into the mold. The reaction endpoint could be monitored via the disappearance of the –NCO absorption in the FT-IR spectrum, and the composite films were produced by solvent evaporation. Due to the low solubility of the crosslinked O-CMC–PEG in water and organic solvents, their chemical structures were only characterized by FT-IR. The representative spectrum (O-CMC–PEG−6%) is shown in Fig. 2d. In the spectrum, the –NCO absorption at ~ 2266 cm−1 vanished completely, while two new strong peaks present at 1678 and 1533 cm−1 which vested in the H-bonded C=O and amide of the newly formed urea groups. The signals at 1571, 1413, and 1015 cm−1 belonged to the absorption of –COO− asymmetric stretching, –COO− symmetric stretching, and C–O–C vibration of saccharide ring from O-CMC (Fig. 2b), respectively. Meanwhile, the absorption peak belonging to ether C–O–C stretching at 1018 cm−1 of PEG (Fig. 2a) was retained. The broad absorption band at 3303 cm−1 was assigned to the –NH– absorption, which overlapped with the peak of –OH43. These results indicated that the terminal –NCO groups of OCN–PEG–NCO were completely reacted with –NH2 groups of O-CMC and the crosslinking structures linked by urea bonds were formed.
Microstructure
The microstructure of a composite film was closely with its tensile properties. The SEM images of the O-CMC–PEG film surfaces are presented in Fig. 4. Compared with the microstructure of O-CMC–PEG−3% (Fig. 4a), the film sample of O-CMC–PEG−6% (Fig. 4b) exhibited a smoother surface and better compatibility between O-CMC and PEG, while the rough surface and obvious microphase separation appeared in the O-CMC–PEG−9% and O-CMC–PEG−12% films which had higher PEG content (Fig. 4c,d). Although the crosslinking by urea bonds and hydrogen bonds could enhance the interface adhesion and improve component compatibility44, the large polarity difference between O-CMC and PEG still resulted in two distinct O-CMC-rich and PEG-rich phases when the PEG content was high. Thus, to obtain fine component compatibility and favorable tensile performance, the PEG content in the crosslinked O-CMC–PEG composites should be controlled within a certain range.
Thermal stability
Figure 5 shows the TGA and DTGA plots for O-CMC, PEG, and O-CMC–PEG films with various PEG content, and the corresponding data obtained for the plots are summarized in Table 2. Only one-step weight loss ranging from 343 to 432 °C with a peak temperature (Tp) of 402 °C was observed in the plot of PEG, while O-CMC exhibited 18.7% weight loss at 248–298 °C with a Tp of 279 °C and high residual weight (~ 46.8%) until the end of the test, which indicated that PEG had higher thermal stability in the relatively low-temperature region and lower thermal stability in the high-temperature region than O-CMC. After PEG was introduced into O-CMC to form crosslinked structures, the thermal degradation of prepared O-CMC–PEG films was mainly divided into two weight-loss stages with a small amount of moisture volatilization at ~ 100 °C. The first weight loss with the Tp−I at 254–258 °C belonged to the thermal dissociation of the O-CMC backbone. The second stage occurring at 397–407 °C (Tp−II) showed less weight loss, which mainly originated from the dissociation of PEG segments. The weight loss was slightly lower than the theoretical PEG content in the composites due to the decomposition of CMC at this temperature range. With the increase of PEG content, the Tp values of the film samples present a gradual increase, demonstrating that the high crosslinking degree could improve their thermal stability to some extent. In addition, the residual weight of composite films was approximately 40% at the end of the tests, which belonged to the heat-resistant salt existing in O-CMC. The above analysis illustrated that the O-CMC–PEG films had high thermal stability and could be used over a wide range of temperatures.
Thermal transition
Figure 6 demonstrates the DSC profiles of O-CMC powder and O-CMC–PEG films containing varying amounts of PEG, and the thermal transition values extracted from these thermograms are summarized in Table 3. No evident glass transition temperature (Tg) appeared in the O-CMC thermograms, which aligns with the findings of the previously published research45. On the other hand, a wide peak characterized by a melting temperature (Tm) of 136 °C and enthalpy change (ΔHm) of 52.0 J/g emerged, indicating the melting transition of the crystalline phase and suggesting the semicrystalline characteristics of O-CMC. The O-CMC–PEG films exhibited a Tg at approximately − 26 °C, indicating that the composites were rubbery state at ambient temperature. Compared with O-CMC, a broader endothermic peak with a much lower ΔHm value was present in the thermograms of O-CMC–PEG films, indicating a reduced crystallinity. When the PEG linker was introduced into O-CMC, the formed crosslinked structure restricted the chain motion and hindered the formation of crystalline domains46. Although the system was deemed partially miscible with immiscibility occurring in the amorphous phase47, it was noteworthy that the O-CMC–PEG−6% film exhibited the lowest ΔHm among the four samples, demonstrating superior component compatibility between O-CMC and PEG. This result was inconsistent with the microstructure analysis. Additionally, the Tm values of the endothermic peak steadily shifted to the lower temperature (Table 3) as the PEG content in the composites increased, which should be ascribed to the flexible nature of PEG.
Tensile properties
High flexibility and toughness were the essential requirements for packaging materials. The tensile curves of O-CMC–PEG films encompassing various PEG content are portrayed in Fig. 7, and the corresponding tensile parameters are summarized in Table 4. A conspicuously smooth yield point was presented in the curves, signifying that all films demonstrated an elastic deformation within the initial short section and plastic deformation subsequently exceeding the yield point. The augmentation of PEG content in the composites led to an escalation in strain at break, whereas the ultimate stress diminishes. The phenomenon could be attributed to the high flexibility of the PEG soft segments which promoted the conversion of the brittle O-CMC into an elastomer45. As the papers reported, a high crosslinking degree was conducive to improving the ultimate stress, but the microphase separation produced by the high PEG content played the opposite trend on the strain at break and ultimate stress41. The film sample of O-CMC–PEG−6% possessing superior component compatibility showed optimum tensile properties with strain at break of 202%, ultimate stress of 5.28 MPa, initial modulus of 30.5 MPa and fracture toughness of 8.89 MJ/m3, which was more suitable as a flexible packaging material.
Water absorption
Water sensitivity, which was strongly linked with the application range of packaging, was evaluated by measuring their WA. Figure 8 displays the WA profile of O-CMC–PEG films after immersion in water at room temperature for 3 h. WA of the films exhibited rapid growth in the initial stage and achieved equilibrium with small differences. It was noticed that the O-CMC–PEG−6% needed more time (~ 90 min) to reach the equilibrium WA than the other three samples (~ 60 min), which should be attributed to the homogeneous structure produced by crosslinking and high component compatibility. While with the increase of crosslinking degree in the composites (O-CMC–PEG−9% and O-CMC–PEG−12%), the high PEG content resulted in microphase separation, which generated free space to allow water molecules to easily permeate the materials48. Based on values of equilibrium WA, it could be found the water sensitivity of the composites mainly depended on the crosslinking degree, that is, the crosslinking was an effective strategy to improve their water resistance. The relatively high equilibrium WA (> 12%) was due to the high hydrophilicity of PEG and O-CMC components. Thus, it could be deduced that O-CMC–PEG composites with moderate PEG content and high crosslinking degree would possess better water resistance by adopting OCN–PEG–NCO with lower molecular weight as the crosslinking agent.
WVTR
Water vapor permeability was an important parameter for food packaging materials, and low WVTR could extend the shelf life of food49. Figure 9 displays the WVTR of the O-CMC–PEG films with various PEG content at RHs of 30%, 50% and 80%. For the samples with constant PEG content, the WVTR value exhibited a notable increase with the RH increasing from 30 to 80%, which was mainly attributed to the reduced humidity difference between the interior and exterior of the film. When the PEG content increased from 3% (O-CMC–PEG−3%) to 6% (O-CMC–PEG−6%), the WVTR values determined under the same RH showed a significant reduction. By enhancing the crosslinking degree, the miscibility between O-CMC and PEG was enhanced. As a result, the flexible PEG effectively occupied the gaps surrounding the O-CMC chains, thereby impeding the passage of water molecules and leading to a decreased WVTR. But for the O-CMC–PEG−9% and O-CMC–PEG−12% samples with relatively high crosslinking degrees, the WVTR presented a trend of sharp increase. The phenomenon should be due to the microphase separation caused by high PEG content in the samples, which offered convenient paths for the migration of water molecules. All the findings manifest that the WVTR of the composite films depended on both PEG content and crosslinking degree. The O-CMC–PEG−6% with suitable PEG content and medium crosslinking degree possessed minimum WVTR (< 100 g mm/(m2 24 h)) under different RH at 25 °C, meaning that the composite had good water vapor barrier performance and was suitable for food preservation, especially fruits and vegetables.
Degradation properties
The appropriate degradability of packaging materials was necessary for the avoidance of white pollution to the environment. Figure 10 shows the weight loss-based degradation behaviors of O-CMC–PEG films in PBS (pH 7.4) at room temperature. All the films displayed a slow degradation rate with less than 8% weight loss in the initial two weeks, followed by accelerated weight loss until the fragmentation of the samples. After initial degradation, the film surface became porous, which improved the water molecules entering the films and increased the hydrolytic degradation rate. With the PEG content increasing from 3 to 12% (O-CMC–PEG−3% ~ O-CMC–PEG−12%), the degradation rate of the composite film presented an obvious decrease. It was apparent that the degradation rate was mainly affected by the crosslinking degree in comparison with the PEG content and microphase separation. A similar tendency had been reported in crosslinked PVA/starch/citric acid composites50. From the results, it was inferred that the degradation rate of the O-CMC–PEG composites could be controlled by adjusting the crosslinking degree.
The morphological alterations on the film surface provided a direct indication of the degradation process. The lyophilized O-CMC–PEG−6% films at various degradation stages were observed by SEM, as illustrated in Fig. 11. After one week of degradation, the initially smooth film surface exhibited roughness (Fig. 11a). As the degradation time progressed, some cavities of various sizes emerged on the surface (Fig. 11b). By the 4.5 weeks of degradation, many large cavities were visible (Fig. 11c), signifying substantial mass loss.
Antibacterial activity
The antibacterial activities of O-CMC–PEG−6% film were performed using inhibition zone assays against Gram-negative (GN) E. coli and Gram-positive (GP) S. aureus, and the findings are presented in Fig. 12. Following a 24-h incubation period at 25 °C the inhibition zone diameter for E. coli was determined to be 13.2 ± 0.4 mm, while S. aureus exhibited a diameter of 17.5 ± 0.3 mm, which demonstrated a good broad-spectrum antibacterial activity. This effectiveness could be ascribed to the presence of residual –NH2 (or –NH3+) groups within the O-CMC–PEG composites. These groups possessed the capability to bind to the negatively charged surface of bacterial cells through electrostatic adsorption, leading to membrane damage, intracellular nutrient leakage, and ultimately cell death51. The antibacterial activity was much higher against GP bacteria than GN bacteria, which was ascribed to the bilayer cell membrane of GN bacteria52,53. The positive broad-spectrum antibacterial activity manifested that the O-CMC–PEG−6% films hold potential as antibacterial food packaging to prolong their shelf-life.
Conclusion
In the work, a simple strategy was developed to prepare the PEG-crosslinked O-CMC (O-CMC–PEG) for food packaging. The condensation reaction between –NCO groups of PEG linker and –NH2 groups of O-CMC was readily accomplished in water under mild conditions to produce the crosslinked structure linked by stable urea bonds. Extensive research was conducted to investigate the impact of the PEG content (or crosslinking degree) on the physicochemical characteristics of the casted O-CMC–PEG films. The findings illuminated that crosslinking and components compatibility could improve their tensile features and water vapor barrier performance, while high PEG content showed the inverse effects due to the microphase separation. In comparison with the PEG content and components compatibility, in vitro degradation rate and equilibrium WA mainly depended on the crosslinking degree in the composites. Furthermore, the films exhibited good antibacterial capacities against E. coli and S. aureus due to the residual –NH2 groups of O-CMC. When the PEG content was 6% (medium crosslinking degree), the prepared O-CMC–PEG−6% film possessed optimal tensile features (strain at break: 202%; ultimate stress: 5.28 MPa; initial modulus: 30.5 MPa; fracture toughness: 8.89 MJ/m3), relatively high water resistance (18.1% equilibrium WA), appropriate degradation rate (38.7% weight loss at 5.5 weeks degradation), low WVTR (77 g mm/(m2·24 h) at 50% RH) and fine broad-spectrum antibacterial capacity, manifesting a great potential for application in food packaging to extend the shelf life.
Data availability
The datasets used and/or analysed during the current study are available from the corresponding author on reasonable request.
References
Jung, S. et al. Multifunctional bio-nanocomposite coatings for perishable fruits. Adv. Mater. 32, 1908291 (2020).
Zhu, W. et al. Development of organic-inorganic hybrid antimicrobial materials by mechanical force and application for active packaging. Food Packag. Shelf 37, 101060 (2023).
Ji, H. S. & Jung, H. W. Effect of the multiple injection process on the structural and mechanical properties of PP impact copolymers focusing on the deformation of ethylene-propylene copolymer. Polym. Test. 124, 108051 (2023).
Srinivasa, P. C. & Tharanathan, R. N. Chitin/chitosan—safe, ecofriendly packaging materials with multiple potential uses. Food Rev. Int. 23, 53–72 (2007).
Pandey, S., Sharma, K. & Gundabala, V. Antimicrobial bio-inspired active packaging materials for shelf life and safety development: A review. Food Biosci. 48, 101730 (2022).
Sun, X. et al. Food spoilage, bioactive food fresh-keeping films and functional edible coatings: Research status, existing problems and development trend. Trends Food Sci. Technol. 119, 122–132 (2022).
Dorota, C. D. et al. Chitosan-based films with cannabis oil as a base material for wound dressing application. Sci. Rep. 12, 18658 (2022).
Tong, X. Q. et al. Recent advances in natural polymer-based drug delivery systems. React. Funct. Polym. 148, 104501 (2020).
George, A., Shah, P. A. & Shrivastav, P. S. Natural biodegradable polymers based nano-formulations for drug delivery: A review. Int. J. Pharmaceut. 561, 244–264 (2019).
Cai, M. et al. Multiple effects achieved with a single agent of O-carboxymethyl chitosan exhibiting cross-linking and antibacterial properties. Prog. Org. Coat. 175, 107345 (2023).
Geng, Y. et al. Recent advances in carboxymethyl chitosan-based materials for biomedical applications. Carbohyd. Polym. 305, 120555 (2023).
Wang, J. L. & Zhuang, S. T. Chitosan-based materials: Preparation, modification and application. J. Clean. Prod. 355, 131825 (2022).
Zhang, L., Zhang, Z., Chen, Y., Ma, X. & Xia, M. Chitosan and procyanidin composite films with high antioxidant activity and pH responsivity for cheese packaging. Food Chem. 338, 128013 (2021).
Harish, R. et al. Cytotoxicity assessment of chitosan coated CdS nanoparticles for bio-imaging applications. Appl. Surf. Sci. 499, 143817 (2019).
Wang, H., Qian, J. & Ding, F. Emerging chitosan-based films for food packaging applications. J. Agric. Food Chem. 66, 395–413 (2018).
Gomes, L. P. et al. Edible chitosan films and their nanosized counter parts exhibit antimicrobial activity and enhanced mechanical and barrier properties. Molecules 24, 127 (2019).
Campana, R., Casettari, L., Ciandrini, E., Illum, L. & Baffone, W. Chitosans inhibit the growth and the adhesion of Klebsiella pneumonia and Escherichia coli clinical isolates on urinary catheters. Int. J. Antimicrob. Agents 50, 135–141 (2017).
Bi, J., Tian, C., Zhang, G., Hao, H. & Hou, H. Novel procyanidins-loaded chitosan-graft-polyvinyl alcohol film with sustained antibacterial activity for food packaging. Food Chem. 365, 130534 (2021).
Wardana, A. A., Koga, A., Tanaka, F. & Tanaka, F. Antifungal features and properties of chitosan/sandalwood oil Pickering emulsion coating stabilized by appropriate cellulose nanofiber dosage for fresh fruit application. Sci. Rep. 11, 18412 (2021).
Potaś, J. et al. Multilayer films based on chitosan/pectin polyelectrolyte complexes as novel platforms for buccal administration of clotrimazole. Pharmaceutics 13, 1588 (2021).
Yang, Y. et al. Poly (lactic acid) fibers, yarns and fabrics: Manufacturing, properties and applications. Text. Res. J. 91, 1641–1669 (2020).
Geng, Y. et al. Recent advances in carboxymethyl chitosan-based materials for biomedical applications. Carbohyd. Polym. 305, 120555 (2023).
Haghighi, H., Licciardello, F., Fava, P., Siesler, H. W. & Pulvirenti, A. Recent advances on chitosan-based films for sustainable food packaging applications. Food Packaging Shelf 26, 100551 (2020).
Al-Tayyar, N. A., Youssef, A. M. & Al-Hindi, R. Antimicrobial food packaging based on sustainable bio-based materials for reducing foodborne pathogens: A review. Food Chem. 310, 125915 (2020).
Jayakumar, R. et al. Novel carboxymethyl derivatives of chitin and chitosan materials and their biomedical applications. Prog. Mater. Sci. 55, 675–709 (2010).
Adnan, S., Ranjha, N. M., Hanif, M. & Asghar, S. O-carboxymethylated chitosan: A promising tool with in-vivo anti-inflammatory and analgesic properties in albino rats. Int. J. Biol. Macromol. 156, 531–536 (2020).
Elsabee, M. Z. & Abdou, E. S. Chitosan based edible films and coatings: A review. Mater. Sci. Eng. C 33, 1819–1841 (2013).
Mo, Y. H. et al. Preparation and properties of a fast curing carboxymethyl chitosan hydrogel for skin care. Polym. Test. 113, 107667 (2022).
Huang, G., Cheng, L., Xiao, J. & Han, X. Preparation and characterization of O-carboxymethyl chitosan-sodium alginate polyelectrolyte complexes. Colloid Polym. Sci. 293, 401–407 (2015).
Xu, Q. et al. PEG modification enhances the in vivo stability of bioactive proteins immobilized on magnetic nanoparticles. Biotechnol. Lett. 42, 1407–1418 (2020).
Yin, S., Xia, Y., Jia, Q., Hou, Z. & Zhang, N. Preparation and properties of biomedical segmented polyurethanes based on poly(ether ester) and uniform-size diurethane diisocyanates. J. Biomat. Sci. Polym. E. 28, 119–138 (2017).
Knop, K., Hoogenboom, R., Fischer, D. & Schubert, U. S. Poly(ethylene glycol) in drug delivery: Pros and cons as well as potential alternatives. Angew. Chem. Int. Ed. 49, 6288–6308 (2010).
Dinc, C. Ö., Kibarer, G. & Güner, A. Solubility profiles of poly(ethylene glycol)/solvent systems. II. Comparison of thermodynamic parameters from viscosity measurements. J. Appl. Polym. Sci. 117, 1100–1119 (2010).
Liu, X., Xia, Y., Liu, L., Zhang, D. & Hou, Z. Synthesis of a novel biomedical poly (ester urethane) based on aliphatic uniform-size diisocyanate and the blood compatibility of PEG-grafted surfaces. J. Biomater. Appl. 32, 1329–1342 (2018).
Li, D., Ye, Y., Li, D., Li, X. & Mu, C. Biological properties of dialdehyde carboxymethyl cellulose crosslinked gelatin-PEG composite hydrogel fibers for wound dressings. Carbohyd. Polym. 137, 508–514 (2016).
Yang, B. et al. Preparation and properties of monomethoxyl polyethylene glycol grafted O-carboxymethyl chitosan for edible, fresh-keeping packaging materials. Food Packag. Shelf 33, 100874 (2022).
Bhalani, D. V. & Jewrajka, S. K. Fouling resistant amphiphilic poly(dimethylsiloxane)-linked-poly(ethyleneglycol) network on ultrafiltration poly(vinylidene fluoride) membrane and effect of spatial chain arrangement on separation of oil-water emulsions. J. Membr. Sci. 583, 278–291 (2019).
Duan, M. et al. Insights into electrospun pullulan-carboxymethyl chitosan/PEO core-shell nanofibers loaded with nanogels for food antibacterial packaging. Int. J. Biol. Macromol. 233, 123433 (2023).
Liu, Z. et al. Cross-linked poly(ester urethane)/starch composite films with high starch content as sustainable food-packaging materials: Influence of cross-link density. Int. J. Biol. Macromol. 256, 128441 (2024).
Lin, L., Liao, X., Surendhiran, D. & Cui, H. Y. Preparation of ε-polylysine/chitosan nanofifibers for food packaging against Salmonella on chicken. Food Packag. Shelf 17, 134–141 (2018).
Hou, Z., Zhang, H., Qu, W., Xu, Z. & Han, Z. Biomedical segmented polyurethanes based on polyethylene glycol, poly(ε-caprolactoneco-D, L-lactide), and diurethane diisocyanates with uniform hard segment: Synthesis and properties. Int. J. Polym. Mater. Polym. Biomater. 65, 947–956 (2016).
Lin, C. et al. Synthesis and properties of dynamic crosslinking polyurethane/PEG shape-stable phase change materials based on the Diels−Alder reaction. ACS Appl. Polym. Mater. 5, 4190–4198 (2023).
Cerrutti, B. M., Lamas, J. C., Campana-Filho, S. P. & Frollini, E. Carboxymethyl chitosan: Preparation and use in colloidal ceramic processing. J. Polym. Environ. 21, 816–825 (2013).
Taia, N. L., Adhikari, R., Shanks, R. & Adhikari, B. Flexible starch-polyurethane films: Physiochemical characteristics and hydrophobicity. Carbohyd. Polym. 163, 236–246 (2017).
Mourya, V. K., Inamdara, N. N. & Tiwari, A. Carboxymethyl chitosan and its applications. Adv. Mater. Lett. 1, 11–33 (2010).
Rahmani, S. & Barzegar, M. One-pot synthesis of dibenzaldehyde-terminated poly(ethylene glycol) for preparation of dynamic chitosan-based amphiphilic hydrogels. Polym. Bull. 78, 2887–2909 (2021).
Lewandowska, K. Miscibility and thermal stability of poly(vinyl alcohol)/chitosan mixtures. Thermochim. Acta 493, 42–48 (2009).
Cagnin, C., Simões, B. M., Yamashita, F., de Carvalho, G. M. & Grossmann, M. V. E. pH Sensitive phosphate crosslinked films of starch-carboxymethyl cellulose. Polym. Eng. Sci. 61, 388–396 (2021).
Liu, Z. et al. Dual-crosslinked starch-poly(ester urethane)-oligochitosan films with high starch content: Application as biodegradable food packaging. Food Packag. Shelf 37, 101064 (2023).
Das, A., Uppaluri, R. & Das, C. Feasibility of poly-vinyl alcohol/starch/glycerol/citric acid composite films for wound dressing applications. Int. J. Biol. Macromol. 131, 998–1007 (2019).
Wei, X. Y., Xia, W. & Zhou, T. Antibacterial activity and action mechanism of a novel chitosan oligosaccharide derivative against dominant spoilage bacteria isolated from shrimp Penaeus vannamei. Lett. Appl. Microbiol. 74, 268–276 (2022).
Thongsrikhem, N., Taokaew, S., Sriariyanun, M. & Kirdponpattara, S. Antibacterial activity in gelatin-bacterial cellulose composite film by thermally crosslinking with cinnamaldehyde towards food packaging application. Food Packag. Shelf 31, 100766 (2022).
Boyacioglu, S., Kodal, M. & Ozkoc, G. A comprehensive study on shape memory behavior of PEG plasticized PLA/TPU bio-blends. Eur. Polym. J. 122, 109372 (2020).
Acknowledgements
This research was financially supported by the Shandong Provincial Innovation Project for Science and Technology -Oriented Small and Medium Enterprises, China (no. 2023TSGC0276).
Author information
Authors and Affiliations
Contributions
B.Y.: Methodology, investigation, data curation, writing—original draft. B.L.: Methodology, investigation, data curation, writing—review and editing. Y.G.: Investigation, data curation, writing—original draft. J.W.: Investigation. G.L.: Investigation. H.Z.: Investigation. L.W.: Data curation. Z.H.: Project administration, funding acquisition, conceptualization, supervision, resources, writing—review and editing. All authors reviewed the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yang, B., Liu, B., Gao, Y. et al. PEG-crosslinked O-carboxymethyl chitosan films with degradability and antibacterial activity for food packaging. Sci Rep 14, 10825 (2024). https://doi.org/10.1038/s41598-024-61642-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-024-61642-x
- Springer Nature Limited