Abstract
Copper Zinc Tin Sulphide (CZTS) is a propitious semiconductor for active absorber material in thin-film solar cells (SCs). Here, SC architecture comprising FTO/ZnS/CZTS/variable HTLs/Au is discussed. Fluorine-doped tin oxide (FTO) and gold (Au) are used as front and back contacts, respectively. Zinc sulphide (ZnS) is used as an active electron transport layer (ETL), while different Cu-based materials (Cu2O, CuO, CuI, and CuSCN) are used as hole transport layers (HTL). A one-dimensional solar cell capacitance simulator (SCAPS-1D) is utilized to simulate the SC structure. Among different Cu-based HTLs, Cu2O is preferred as a potential candidate for high cell performance of CZTS-based SC. The effects of various layer parameters such as thickness, doping density, and carrier concentrations, electron affinity of HTL and absorber, respectively, are also discussed. After optimization of the device, variation of operating temperature and the effect of series and shunt resistance are also taken into consideration. The optimized results of thickness and acceptor concentration (NA) of absorber material are 1.5 µm and approx. 1.0 × 1019 cm−3, respectively. In addition, the function of HTL (with and without) in the designed SC structure is also studied. Capacitance–voltage (C–V) characteristics are also discussed to get an insight of built-in potential. We have achieved cell performances viz. efficiency = 31.86%, short circuit current density = 32.05 mA/cm2, open circuit voltage = 1.19 V, and fill factor = 83.37%.
Similar content being viewed by others
Introduction
With the growing population, there has been a great demand for energy, which is mostly fulfilled by using fossil fuels, but solar energy is considered the need of the future due to its various advantages1. Fossil fuel is going to deplete one day, but solar energy is entirely renewable and, at no cost, can supply an infinite amount of energy2. The dependence on solar energy is growing as a result of new research developments that can enhance its efficiency. In our country, various electrification programmes of the government have been in operation, which highlights the importance of solar power3. Among the most essential aspects of any country's advancement and prosperity is energy. When talking about sustainable energy, we have to replace the existing sources with renewable energy supply. The regular and never-ending use of fossil fuels has already led to many problems such as pollution, global warming, health issues, and so on4. Therefore, with the ongoing high demand for energy and environmental concerns, researchers have focused on alternative sources (solar energy) that can meet our energy demand and also not contaminate our environment5.
CIGS (copper indium gallium (di)selenide) and CdTe SCs dominate the market for thin-film technologies. However, cadmium (Cd) and tellurium (Te) are poisonous6 and with the availability of rare elements such as indium (In) and gallium (Ga), the need of the hour is to look for non-toxic and earth-abundant materials that can suitably replace the existing ones with desired characteristics. CZTS is an extrinsic p-type semiconductor known for its ease of preparation due to the availability of its constituent components (copper, zinc, tin, and sulphur)7,8,9,10. CZTS mainly exist in kesterite form as it is more stable11,12. CZTS is ecologically beneficial due to the quantity of harmless elements. Apart from that, CZTS offers strong electrical and optical properties along with excellent stability, making it a more profound material for PV devices13,14. CZTS has gained attention across the scientific community due to its promising optoelectronic properties, including high hole mobility, an adjustable bandgap, and earth-abundant elements15,16. However, due to poor open circuit voltage (Voc), CZTS-based SCs have a deficit in higher conversion efficiency12.
Various works have been reported that show that CZTS is the best material for thin-film SCs. It has been observed that the CZTS-based SC with zinc telluride (ZnTe) as a buffer layer revealed an impressive power conversion efficiency (PCE) of 23.47% with the SC structure Mo/CZTS/ZnTe/ZnO/ZnO:Al17. In another study, TiO2 was used as ETL, and the tin perovskite CH3NH3SnI3 (MASnI3) acted as an absorber layer (FTO/TiO2/CH3NH3SnI3/CZTS/Au). They obtained short circuit current density (JSC) = 31.66 mA/cm2, open circuit voltage (VOC) = 0.96 V, fill factor (FF) = 67%, and efficiency = 20.28%18. Dey et al.19 measured SC performance on i-ZnO, InSe, and CZTS simulation structures and found it to be 16.30%. In this structure, CZTS and InSe served as absorber layers and buffer layers, respectively. A new device structure (FTO/ZnO/CdS/CZTS/CZTSe/Mo) is reported by Rana et al. in 2021. In the reported structure, CZTS and CdS were taken as a absorber and buffer layers, respectively. The cell performances were analysed against thickness variations, carrier concentrations, and defect densities (Nt) and found an overall conversion efficiency of 22.03%20. The architecture (MO/CZTS/CdS/ZnO/FTO) was studied by Zyoud et al. in 2021 and has a PCE of 27.72%, including a poor value of Voc of 0.64V21. However, Benzetta et al. tried to replace CdS with ZnS and introduced an alternative layer in CZTS-based SC known as a back surface field (BSF), which attains an efficiency of 14.14% and an improved Voc of 0.89 V12.
Therefore, the current work focuses on copper-based (p-type) inorganic semiconductors as a viable HTL to address the issue of low VOC and improve the efficiency of CZTS-based SCs. High-hole mobility, high conductivity, great optical transmittance, low cost, and eco-friendliness of copper-based semiconductors enable them to be projected as HTL in SCs22,23. Therefore, due to their meritorious properties, CuO, Cu2O, CuI, and CuSCN are introduced as different HTLs in our designed SC.
In this study, we have discussed the CZTS-based SC structure comprising FTO/ZnS/CZTS/Cu-based HTLs/Au. In which FTO metal work function (4.4 eV) is used as a front contact, ZnS as an ETL, CZTS as an absorber layer, copper-based materials as HTL, and gold (Au) metal work function (5.1 eV) as a back contact. Generally, CdS is used with CZTS. However, in the present study, CdS is replaced by ZnS due to its toxicity. The effect of thickness variation and acceptor concentrations is calculated for the absorber and HTL. In addition, variations of defect density and electron affinity of the absorber and HTL are studied, respectively. Further, the influence of operating temperature, shunt, and series resistances is well examined for the optimised structure. The capacitance–voltage (C-V) characteristic is also considered to gain an in-depth understanding of junctions. The computed SC performances of the suggested SC structure include an efficiency of 31.86%, FF of 83.37%, JSC of 32.05 mA/cm2, and VOC of 1.19 V. In addition, we have also studied the role of HTL (with and without) in the discussed structure.
The commercialization of solar cells could possibly be accelerated by CZTS-based solar cells. CZTS is a non-hazardous, ecologically safe semiconductor that exhibits encouraging PCE but is constrained by its low VOC. Therefore, relevant HTMs have been included in numerous studies to boost VOC. Thus, this work explores the use of several copper-based HTLs to enhance the efficiency of CZTS-based solar cells. Cu-based HTLs were previously known to be low-cost, non-toxic, highly heat- and chemical-resistant materials with good charge carrier mobility. The improvement in PCE was made possible by optimizing a number of solar cell properties. Cu2O is therefore established to be an appropriate HTL for CZTS-based solar cells with good band alignment and an efficiency of 31.86%.
Materials and methods
Device design and numerical simulation study
The investigation of SC's photovoltaic (PV) properties through manufacture requires both time and money. Thus, one of the crucial aspects in analysing their PV properties is numerical design and modelling of SC architecture. With the various input material parameters and the modelling process, any solar structure may be designed. They also allow us to study the performance of the SC application by changing the material's characteristics. We can quickly understand the SC device behaviour from the simulation results, which helps us to realize the indicated SC restrictions. Additionally, the software's validity is shown in Table 1 by the fact that SCAPS simulated results closely match with the experimental results.
In this study, SCAPS-1D (version 3.3.10), a 1-D simulation of solar cell capacitance, is employed. Prof. Marc Bargeman et al. at the Department of Electronics and Information Systems at the University of Gent in Belgium developed this software23. It is utilized in SC modelling, numerical analysis, and the investigation of solar structure characteristics. SCAPS-1D uses stability, Poisson, and semiconductor equations to solve them in order to describe the in-depth analysis of the SC structure27. A numerical simulation study of solar cells provides us a better insight of various material properties, which is used during the fabrication of the SCs4,28. A thorough study of simulated results enables researchers to sustainable and more efficient way to manufacture low cost and high efficient PV devices29.
Table 2 lists the electrical properties of different materials that were employed in this simulation, including the mobility of electrons and holes, relative permittivity, electron affinities, effective density of states (DOSs) in the valence band and conduction band, and acceptor and donor densities30,31. The material properties of various Cu-based HTLs are shown in Table 332,33.
The designed CZTS-based solar cell structures (FTO/ZnS/CZTS/Cu-based HTLs/Au) is shown in Fig. 1. The simulation is performed at 300 K, and the under AM 1.5 G solar spectrum. It is well known that the absorption coefficient for CZTS absorber layer should be more than 104 cm−1. It is clear from Fig. 2 that the absorption coefficient for CZTS is ranged above 104 cm−1 which confirmed good an absorption characteristics of absorber material for photovoltaic cell.
Results and discussion
Selection of appropriate HTL for SC
In this study, various Cu-based materials have been proposed as the HTL for a CZTS-based SC. Initially, the simulation process is performed for different HTLs (CuO, Cu2O, CuI, and CuSCN). The thickness of different active layers likewise electron transport, various hole transport and absorber materials, are taken to be 50 nm, 50 nm, and 500 nm, correspondingly. Figure 3a and b show the energy band diagram and energy band alignment of the SC using various Cu-based materials as HTL.
As energy band alignment governs the movement of photo-generated charge carriers, which regulates the PV performance of the designed SC22. Table 4 shows the calculated valence band offsets (VBO) for each HTL with respect to the CZTS absorber layer, using Eq. (1)35;
where, \({\chi }_{HTL}\), \({\chi }_{abs}\) are electron affinities of HTL and absorber layer, respectively. \({E}_{{g}_{HTL}}\), \({E}_{{g}_{abs}}\) are the energy band gap values of HTL and absorber layer, respectively.
From Table 4, it can be observed that the VBO for Cu2O, CuI, and CuSCN is negative but the VBO for CuO is positive. A positive VBO means it will form a spike close to the interface of absorber/HTL, which hinders the motion of hole charge carriers12,36. However, a negative VBO forms an energy cliff close to the interface of absorber/HTL, which promotes the motion of hole charge carriers. The formation of cliffs and spikes at the absorber/HTL edge alters the efficiency of the designed SC36. This can be observed in Table 5, Cu2O with a small negative VBO (− 0.13 eV) attains the maximum efficiency with respect to other Cu-based HTLs.
From Table 5, it can be observed that Cu2O, CuI, and CuSCN have the same Voc and Jsc. Cu2O, on the other hand, has a quiet higher fill factor, and efficiency enhanced to 25.01%. The higher efficiency may be inferred from Fig. 4a and b, which display the generation rates across the device and the distribution of the electric field at the CZTS/HTLs interface, respectively. The generation rates for Cu2O and CuSCN are almost similar. However, the relatively reduced production rates for CuI and CuO result in low efficiency. Additionally, Fig. 4b shows the distribution of the electric field at the CZTS/HTLs contact. Despite its modest generation rates, the CuI exhibits the largest electric field, which further contributes to its excellent efficiency. However, since both Cu2O and CuSCN have essentially identical electric fields, less recombination occurs at the contact. CuO, on the other hand, has a lowered electric field that permits the migration of a minority electron towards the HTL, which promotes recombination and results in poor efficiency37. Figure 4c and d show the I–V and QE curves for different HTLs, which illustrate the fact that the QE responses of each HTL are similar. Thus, considering the efficiency, FF Cu2O has been taken as the HTL in further studies.
Impact of HTL thickness on the performance of SC
Proper thickness of HTL plays a crucial role in shaping high performance of the SC. The best HTL is the one that reduces electrical resistance and recombination setbacks, which further aids in boosting the SC's performance. Thickness of Cu2O material in designed SC structure is varied in the range of 0.02–0.12 μm. The thickness of Cu2O shows insignificant effect on the SC’s performance, as shown in Fig. 5a–d. However, Cu2O plays an active role in transporting the hole to the counter electrode owing to the making an energy cliff near the interface’s HTL/absorber. Thereby, the thickness of HTL is taken to be 50 nm for the optimized device structure.
Impact of HTL doping density on the performance of SC
HTLs doping density controls SC performance by changing the electric field intensity at the HTL/absorber interface. An increase in electric field leads to a greater separation of electron–hole pairs and thus an increase in efficiency. Here, the acceptor density of HTL varies in between the range 1013–1021 per cm3. Figure 6a–d illustrate that increasing the acceptor concentration of Cu2O from 1 × 1013 per cm3 to 1 × 1021 per cm3 have no significant effect on the performance of SC. There are insignificant changes on Voc and Jsc as represented in Figure 6b and c, respectively. However, we observed that there is a small change in efficiency from 24.14% to 25.14% (Fig. 6a) and FF from 81.61 to 82.86% (Fig. 6d). As we increase the doping concentration, charge carrier separation is increased and then the cell performances are also increased. The optimized result for acceptor concentration of Cu2O is considered 1 × 1019 per cm3.
Impact of HTL electron affinity on the SC performance
Electron affinity governs the contact conditions of the designed solar cell. A band offset is created when the electron affinities of the various layers differ, in the case of HTL, this is a valence band offset. In the present study, the impact of various HTL’s electron affinity is also studied on the SC performance parameters. The variation of Cu2O electron affinity has been performed considering that the bandgap of Cu2O be same (i.e. 2.17 eV). This will aid in selecting the best possible hole transport material with the proper band alignment for CZTS. Here, electron affinity is changes in between 2.8 and 3.4 eV, as shown in Fig. 7a–d. As the electron affinity increases from 2.8 to 3.4 eV, the Voc usually increases and then begins to decrease after the electron affinity of 3.4 eV (Fig. 7b).
Figure 7c indicates that the Jsc is unaffected by changing electron affinity of HTL. Moreover, at electron affinities between 2.8 and 3.2 eV, the FF increases from 71 to 83% and then begins to drop after 3.2 eV (Fig. 7d). The same variation can be seen in Fig. 7a, where efficiency improves from 19.71 to 25.09% for affinities ranging from 2.8 to 3.4 eV before abruptly decreasing after 3.4 eV. The VBO will vary from − 0.53 to + 0.47 eV for electron affinities of 2.8 eV and 3.8 eV, respectively. At lower electron affinity the VBO becomes more negative, further forming the larger energy cliff. Further, the larger energy cliff will result in enhanced recombination probability at the HTL/CZTS interface38. Similarly, greater electron affinity will result in a higher positive VBO, creating a larger energy spike and increasing the chance of recombination. The increase in Voc, FF and efficiency with the HTL electron affinity of lower than 3.4 eV may be ascribed due to the minimization of recombination probability at the interface of HTL/CZTS, as manifested in Fig. 7. Additionally, as illustrated in Fig. 8, the impact of the HTL bandgap and electron affinity on efficiency is also examined. Therefore, it can be manifested from Fig. 8 that materials with bandgap over 2 eV and electron affinities in the range of 3.2–3.4 eV will be the most suitable HTL for this SC structure. Thus, to enhance the PV properties of the designed SC, the electron affinity of HTL is considered to be 3.2 eV.
Impact of defect density of CZTS/ZnS and CZTS/Cu2O interface
Take into account that the incident photons must pass through the ETL/absorber interface before reaching the absorber layer. Exposure to extreme heat, light, oxygen, and humidity aggravates interface flaws, further impairing device performance. So, it's impossible to completely rule out the possibility of interface flaws39,40. Thus, to study the impact of CZTS/ZnS and CZTS/Cu2O interface defects, the defect density was varied from 1010 to 1016 cm−2. Figure 9a–d show the effect of defect density at the CZTS/ZnS and CZTS/Cu2O interfaces. It can be observed that the Voc, Jsc, and FF remain almost constant up to 1013 cm−2 for both ETL and HTL. However, Voc, Jsc, and FF degrade drastically after 1013 cm−2. This drastic decrease in solar cell parameters is due to increased recombination at higher defect densities. However, the results show that at the Cu2O/CZTS interface, the density of interface traps has a significantly greater impact on the overall performance than at the ZnS/CZTS interface. The reason for this is that the electric field developed at the interface is reduced, which promotes greater recombination. Accordingly, the interfacial defect density is taken to be 1012 cm−2 for both ZnS and Cu2O interfaces.
Optimization of CZTS absorber layer
The thickness absorber material has a crucial effect on efficiency of the SC device. Light absorption and charge transfer are accomplished by the absorber layer. As a result, optimizing the absorber material is critical for improving SC performance. The change of doping density, thickness, and defect density is investigated here.
Impact of CZTS absorber layer thickness on the performance of SC
Figure 10a–d show the thickness of absorber material varies in the range between 0.2 and 1.8 µm. The rise in charge carrier recombination owing to the escalation in dark saturation current leads to a slight decrement in the Voc (Fig. 10b). Efficiency Voc, and Jsc, increases until 1.4 µm and then get saturated. As absorber material thickness reduces, the electrons and holes combine quickly, thereby increasing the rate of recombination. The rise in absorber thickness gives ample space for an increase in the number of photons to be absorbed, thus increasing the Jsc, (Fig. 10c). Further, the FF also rises with increasing thickness. We observe a SC efficiency of 27.33% at the optimum absorber thickness (1.5 µm).
Impact of absorber (CZTS) doping density on the SC performance
The acceptor concentration of absorber material varies in between 1012 and 1022 per cm3. It can be noticed from Fig. 11a–d that when the acceptor concentration of CZTS increases efficiency, Voc, and FF increases. However, Jsc remains constant and decreases when doping concentration goes beyond 1 × 1020 per cm3. This is because high doping concentration decreases the depletion region and charge carrier mobility which leads to increase in holes and electrons recombining and decreasing the chance of capturing electrons produced by photons. Voc increases on increasing acceptor concentration. The device saturation current increases lead to increase in Voc. The efficiency increases from 23 to 29% as absorber material’s acceptor concentration are varies in between 1012 and 1022 per cm3. The optimum value of acceptor concentration for CZTS layer is taken as ~ 1019 per cm3. Columbic traps will be created by extremely high doping, which will increase recombination41.
Impact of absorber layer (CZTS) defect density on the SC performance
The impurities and defects are unavoidable during the manufacturing processes of SCs. Thus, to get a detailed overview of our designed CZTS-based SC, the defects are being introduced in absorber layers during simulation. The defects in absorber layer significantly affect the PCE of SCs. The Shockley–Read–Hall (SRH) recombination dominates due the existence of defects. The recombination increases owing to the existence of defects42. Higher defect density reduces the carrier lifetime and carrier diffusion length of the charge carriers generated due to absorption of photon30,35,43. Acceptor concentration of absorber materials varies in the range of 1013–1019 per cm3, can be seen in Fig. 12a–d. The Voc falls sharply from 1.36 to 0.62 V, due to the increase in recombination at higher defect density, as revealed in Fig. 12b. In addition, Fig. 12c depicts that the Jsc remains constant up to 1017 cm−3 and shows a sudden decrease from 29.2 to 19.2 mA/cm2 at higher defect density. Consequently, the FF decreases from 82.44 to 52.06%. Besides, The SC's efficiency drops dramatically from 32.43 to 6.28% as a result of an increase in resistance and recombination, as shown ion Fig. 12a. Thus, the optimum defect concentration of 1015 per cm3 is set for the simulation.
Impact of shunt and series resistances on the SC performance
Resistivity is an intrinsic property of any material. Hence, the shunt and series resistances are considered during the optimization of designed SC. shunt (Rsh) and Series (Rs) resistances are attributed to contacts between layers and defects of materials, respectively44,45,46. Here, the Shunt and series resistances have been varied from 2 to 16 Ω cm2 and 500 to 3000 Ω cm2, respectively, as shown in Fig. 13a–d. It can be observed from Fig. 13b and c that there is a negligible effect of shunt and series resistance on Jsc and Voc, respectively. Furthermore, the increasing series resistance advances the decrease in FF and efficiency from 79.49 to 50.15% and 30.32 to 18.82%, respectively. On the contrary, the increasing shunt resistance gives rise to FF and efficiency, which increase from 78.82 to 83.55% and 30.03 to 31.92%, respectively. This may be ascribed to the decline the value of leakage current in the designed SC. Thus, the optimum value of series and shunt resistance is manifested in the range of 0–4 Ω cm2 and 2500–3000 Ω cm2, correspondingly.
Impact of operating temperature on the device performance
The operating temperature of an SC device affects its performance. The hole, electron mobilities and material carrier concentration are impressed with higher operating temperature of the PV device, which leads to lower efficiency47. The operating temperature is measured in between of 290–350 K and the resulting outcomes are shown in Fig. 14a–d. Figure 14b indicates that the increase in operating temperature leads to decline the Voc. The Voc decreases because the temperature’s rise leads to a shrinkage in the bandgap of the absorber36. The Jsc is unaffected by varying temperatures. Figure 14d shows that the FF increases with increasing temperature, indicating that there is an increment in the power output of the device. However, there is a minor drop in efficiency (Fig. 14a) from 32.09 to 30.88%. Because of the high temperature, the holes and electrons combine faster before reaching the depletion area, leading to a decrease in device efficiency48. Therefore, the designed CZTS-based SC is highly stable at higher temperatures. Thus, the optimum operating temperature is chosen to be 300 K.
Optimized result and I–V curve
After considering all the optimization parameters, the optimized values for different material parameters are tabulated in Table 6.
In addition to that the SC parameters with and without HTL is also shown in Table 6. The role of HTL (Cu2O) in the proposed structure of CZTS based SC. Figure 15a represents the J–V and QE curve of CZTS-based SC with HTL (FTO/ZnS/CZTS/Cu2O/Au) and without HTL (FTO/ZnS/CZTS/Au). It can be manifested from Table 7 that the FF and efficiency are enhanced after the introduction of Cu2O as HTL. At optimized device parameters the efficiency with and without HTL is found to be 31.86% and 21.17%, respectively. This is because of the interfacial recombination of charge carriers between CZTS and back contact metal (gold)37. Figure 15b shows a sharp decrease in QE response beyond 885 nm, confirming the band gap of CZTS, which is 1.4 eV. It is also evident that the QE response of SC using Cu2O as HTL is higher than the QE response of solar cells without HTL. This difference in QE response can be attributed to the generation of a back surface field after the incorporation of HTL38,49. CZTS can act both as absorber and p-type layer. After adding another p-type layer (Cu2O) the performance of SC improves. So, Cu2O as HTL is required for better performance of the proposed SC.
Capacitance–voltage (C–V) for the optimized structure
Apart from the J–V curve, C–V is one of the most important parameters to study to get a better insight of the built-in potential (Vbi) of the proposed SC heterostructure. In addition to that the doping density can also be calculated using the C-V curve, by using the equations43
here, ε0is permittivity of free space (8.85 × 10–14 F cm−1), Na and q are doping density (in per cm3) and charge on electron (1.6 × 10−19C). εs, A, C and V are relative dielectric constant (refer Table 2), area of SC (in square-cm), capacitance, and applied potential respectively.
Figure 16 indicates the graph between 1/C2 vs. V. We have calculated built-in potential (Vbi) from the intercept of the graph. The Vbi is found to be 1.3 V for the CZTS-based SC. The improved efficiency of the SC is owing to large Vbi, which enhances the separation of charge carriers. Further, the doping density (NA) is calculated by using Eq. (2) and found the value to be approx. 1 × 1019 cm−3. The calculated value of doping density is nearly the optimized doping density of CZTS material (Table 2).
Conclusions
The suggested structure, which consists of FTO/ZnS/CZTS/Cu2O/Au, is simulated using the SCAPS-1D programme. It has been noticed that the SC's efficiency may improve by selecting the optimum value thickness and charge carrier concentration for absorber material and HTL. The optimized thickness of absorber, HTL is 1.5 µm and 0.05 µm, respectively, and optimized doping concentration is 1.0 × 1019 per cm3 for both absorber and HTL. We achieved excellent results such as efficiency ~ 31.86%, Jsc ~ 32.05 mA cm−2, Voc ~ 1.19 V and the FF ~ 83.37%. The calculated doping density ~ 1 × 1019 cm−3 is similar to the optimized doping density of CZTS material. We observed built-in potential 1.3 V for the CZTS-based SC. The outcomes showed that the thin layer of ZnS may be used in the creation of SCs and offers a potential alternative for the commonly employed hazardous CdS as ETL. Sustainable development may be facilitated by the use of low-cost, non-toxic, and plentiful CZTS.
Data availability
Data and materials for this study are available and will be provided to the journal upon request.
References
Kannan, N. & Vakeesan, D. Solar energy for future world: A review. Renew. Sustain. Energy Rev. 62, 1092–1105 (2016).
Shaikh, M. R. S. A review paper on electricity generation from solar energy. Int. J. Res. Appl. Sci. Eng. Technol. 9, 1884–1889 (2017).
Srivastava, S. P. & Srivastava, S. P. Solar energy and its future role in Indian economy. Int. J. Environ. Sci. Dev. Monit. 4, 81–88 (2013).
Ouslimane, T., Et-taya, L., Elmaimouni, L. & Benami, A. Impact of absorber layer thickness, defect density, and operating temperature on the performance of MAPbI3 solar cells based on ZnO electron transporting material. Heliyon 7, e06379 (2021).
Periyamayan, N. & Swamikannan, D. Role of solar power in environmental protection in India. Int. J. Emergy Tech. Innov. Res. 6, 418–422 (2020).
Khattak, Y. H. et al. Efficiency enhancement of novel CNTS/ZnS/Zn (O, S) thin film solar cell. Optik. 171, 453–462 (2018).
Adewoyin, A. D., Olopade, M. A. & Chendo, M. Enhancement of the conversion efficiency of Cu2ZnSnS4 thin film solar cell through the optimization of some device parameters. Optik 133, 122–131 (2017).
Boutebakh, F. Z., Zeggar, M. L., Attaf, N. & Aida, M. S. Electrical properties and back contact study of CZTS/ZnS heterojunction. Optik 144, 180–190 (2017).
Ananthakumar, S., Ram Kumar, J. & Moorthy Babu, S. Synthesis of Cu2ZnSnSe4 hierarchical nanostructures by colloidal method. Optik 127, 10360–10365 (2016).
Benchikhi, M. et al. Low-temperature molten salt synthesis and characterization of Cu2ZnSnS4 ultrafine powders. Optik 138, 568–572 (2017).
Suryawanshi, M. P. et al. CZTS based thin film solar cells: A status review. Mater. Technol. 28, 98–109 (2013).
Benzetta, A. E. H., Abderrezek, M. & Djeghlal, M. E. A comparative study on generation and recombination process of kesterite CZTS based thin film solar cells for different designs. Optik 219, 165300 (2020).
Zyoud, S. H. et al. Numerical modeling of high conversion efficiency FTO/ZnO/CdS/CZTS/MO thin film-based solar cells: Using SCAPS-1D software. Crystals 11, 1468 (2021).
Latrous, A. R., Mahamdi, R., Touafek, B. N. & Pasquinelli, M. Performance enhancement in CZTS solar cells by SCAPS-1D software. Int. J. Thin Film Sci. Technol. 10, 59–65 (2021).
Bade, B. R. et al. Investigations of the structural, optoelectronic and band alignment properties of Cu2ZnSnS4 prepared by hot-injection method towards low-cost photovoltaic applications. J. Alloys Compd. 854, 157093 (2021).
Xu, H. et al. Perovskite solar cells enhancement by CZTS based hole transport layer. Surf. Interfaces 33, 102187 (2022).
Prakash, B. et al. Solution-processed CZTS thin films and its simulation study for solar cell applications with ZnTe as the buffer layer. Environ. Sci. Pollut. Res. 1, 1–11 (2022).
Piñón Reyes, A. C. et al. Study of a lead-free perovskite solar cell using CZTS as HTL to achieve a 20% PCE by SCAPS-1D simulation. Micromachines 12, 1508 (2021).
Dey, M. et al. Design of ultra-Thin CZTS solar cells with Indium selenide as buffer layer. in 2017 International Conference on Electrical, Computer and Communication Engineering (ECCE) 946–950 (IEEE, 2017).
Rana, M. S., Islam, M. M. & Julkarnain, M. Enhancement in efficiency of CZTS solar cell by using CZTSe BSF layer. Sol. Energy 226, 272–287 (2021).
Arumugam, G. M. et al. Inorganic hole transport layers in inverted perovskite solar cells: A review. Nano Sel. 2, 1081–1116 (2021).
Hossain, M. I., Alharbi, F. H. & Tabet, N. Copper oxide as inorganic hole transport material for lead halide perovskite based solar cells. Sol. Energy 120, 370–380 (2015).
Burgelman, M., Decock, K., Khelifi, S. & Abass, A. Advanced electrical simulation of thin film solar cells. Thin Solid Films 535, 296–301 (2013).
Ganem, H. T. & Saleh, A. N. Enhancement of the efficiency of the CZTS/Cds/Zno/ITO solar cell by back reflection and buffer layers using SCAPS-1D. Iraqi J. Sci. 11, 1144–1157 (2021).
Haddout, A., Raidou, A. & Fahoume, M. A review on the numerical modeling of CdS/CZTS-based solar cells. Appl. Phys. A 125, 1–16 (2019).
Djinkwi Wanda, M., Ouédraogo, S., Tchoffo, F., Zougmoré, F. & Ndjaka, J. M. B. Numerical investigations and analysis of Cu2ZnSnS4 based solar cells by SCAPS-1D. Int. J. Photoenergy 2016, 1–9 (2016).
Burgelman, M., Decock, K., Niemegeers, A., Verschraegen, J. & Degrave, S. SCAPS manual. February (2016).
Osman, B., Abdolkader, T. & Ahmed, I. A review of perovskite solar cells. Int. J. Mater. Technol. Innov. https://doi.org/10.21608/ijmti.2021.78369.1032 (2021).
Huang, S., Rui, Z., Chi, D. & Bao, D. Influence of defect states on the performances of planar tin halide perovskite solar cells. J. Semicond. 40, 032201 (2019).
Nalianya, M. A. et al. Numerical study of lead free CsSn0.5Ge0.5I3 perovskite solar cell by SCAPS-1D. Optik 248, 168060 (2021).
Abdelaziz, S., Zekry, A., Shaker, A. & Abouelatta, M. Investigation of lead-free MASnI3-MASnIBr2 tandem solar cell: Numerical simulation. Opt. Mater. 123, 111893 (2022).
Kanoun, A.-A., Kanoun, M. B., Merad, A. E. & Goumri-Said, S. Toward development of high-performance perovskite solar cells based on CH3NH3GeI3 using computational approach. Sol. Energy 182, 237–244 (2019).
Tara, A., Bharti, V., Sharma, S. & Gupta, R. Device simulation of FASnI3 based perovskite solar cell with Zn(O0.3, S0.7) as electron transport layer using SCAPS-1D. Opt. Mater. 119, 111362 (2021).
Ahmmed, S. et al. CuO based solar cell with V2O5 BSF layer: Theoretical validation of experimental data. Superlattices Microstruct. 151, 106830 (2021).
Abdelaziz, S., Zekry, A., Shaker, A. & Abouelatta, M. Investigating the performance of formamidinium tin-based perovskite solar cell by SCAPS device simulation. Opt. Mater. 101, 109738 (2020).
He, Y., Xu, L., Yang, C., Guo, X. & Li, S. Design and numerical investigation of a lead-free inorganic layered double perovskite CS4CuSb2Cl12 Nanocrystal Solar Cell by SCAPS-1D. Nanomaterials 11, 2321 (2021).
Rahman, S. & Ahmed, S. R. A. Photovoltaic performance enhancement in CdTe thin-film heterojunction solar cell with Sb2S3 as hole transport layer. Sol. Energy 230, 605–617 (2021).
Sunny, A. & Ahmed, S. R. A. Numerical simulation and performance evaluation of highly efficient Sb2Se3 solar cell with tin sulfide as hole transport layer. Phys. Status Solidi 258, 2000630 (2021).
Singh, N. K., Agarwal, A. & Kanumuri, T. Performance enhancement of environmental friendly Ge-based perovskite solar cell with Zn3P2 and SnS2 as charge transport layer materials. Energy Technol. 10, 2100782 (2022).
Rahmoune, A. & Babahani, O. Numerical analysis of Al/Gr/ETL/MoS2/Sb2S3/Ni solar cell using non-toxic In2S3/SnS2/ZnSe electron transport layer. Optik 283, 170875 (2023).
Gamal, N., Sedky, S. H., Shaker, A. & Fedawy, M. Design of lead-free perovskite solar cell using Zn1-Mg O as ETL: SCAPS device simulation. Optik. 242, 167306 (2021).
Jäger, K.-D., Isabella, O., Smets, A. H. M., van Swaaij, R. A. & Zeman, M. Solar Energy: Fundamentals, Technology and Systems (UIT, 2016).
Basak, A. & Singh, U. P. Numerical modelling and analysis of earth abundant Sb2S3 and Sb2Se3 based solar cells using SCAPS-1D. Sol. Energy Mater. Sol. Cells 230, 111184 (2021).
Green, M. A. Silicon solar cells: Evolution, high-efficiency design and efficiency enhancements. Semicond. Sci. Technol. 8, 1 (1993).
Mundhaas, N. et al. Series resistance measurements of perovskite solar cells using Jsc-Voc measurements. Sol. RRL 3, 1800378 (2019).
Dhass, A. D., Natarajan, E. & Ponnusamy, L. Emerging trends in electrical engineering and energy management (ICETEEEM). in 2012 International Conference on 382–386 (2012).
Nakada, T. & Mizutani, M. 18% efficiency Cd-free Cu (In, Ga) Se2 thin-film solar cells fabricated using chemical bath deposition (CBD)-ZnS buffer layers. Jpn. J. Appl. Phys. 41, L165 (2002).
Sadek, M. S. I. Performance study of CZTS solar cell by optimizing buffer layer materials (ZnS and SnS) using AMPS-1D simulation. SEU J. Sci. Eng 13, 30–35 (2019).
Maiti, A., Chatterjee, S. & Pal, A. J. Sulfur-vacancy passivation in solution-processed Sb2S3 thin films: Influence on photovoltaic interfaces. ACS Appl. Energy Mater. 3, 810–821 (2019).
Acknowledgements
The SCAPS-1D simulation software was provided by Dr. Marc Bargeman, University of Gent, Belgium, and is gratefully acknowledged by the authors. This study was partly supported by the Research Center for the Smart Energy Technologies, Toyota Technological Institute, Nagoya, Japan.
Funding
The authors affirm that they did not accept any money, grants, or other assistance in the preparation of this manuscript.
Author information
Authors and Affiliations
Contributions
R.R., N. A. and M. N. T. collected datas and prepared a draft of the manuscript. N.S. and A.K.S. jointly reviewed the draft and validated the datas. M.Y. and L.C. editing the manuscript and finally R.N.T reviewed and edited the original draft of the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ranjan, R., Anand, N., Tripathi, M.N. et al. SCAPS study on the effect of various hole transport layer on highly efficient 31.86% eco-friendly CZTS based solar cell. Sci Rep 13, 18411 (2023). https://doi.org/10.1038/s41598-023-44845-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-44845-6
- Springer Nature Limited