Abstract
Calcium fluoride (CaF2) crystals is a kind of important optical material for ultraviolet (UV) and deep-ultraviolet (DUV) lithography and high-power laser-related applications. However, its laser-induced damage threshold (LIDT) directly affects the laser power, so that the above-mentioned applications could be limited. Therefore, the research on the damage characteristics and laser damage resistance of CaF2 crystals is urgent. A 3D Finite-Difference Time-Domain (FDTD) method with Maxwell spinor equation is used, and the results show that the electric field intensity of rear surface is larger than that of front surface, which causes a lower threshold and is consistent with the experimental observations. And a thermo-mechanical coupled finite element model (FEM) of CaF2 with Ce2O3 impurities, which are introduced by polishing process, has semiquantitatively described the damage mechanism of CaF2 by 248 nm-excimer laser.
Similar content being viewed by others
Introduction
Due to the large band gap energy (12.1 eV), high transmission at UV range, very low value of nonlinear refractive index, good optical isotropy and excellent chemical stability1,2,3,4,5, CaF2 optical window materials have been widely used. The results of surface damage of different types of CaF2 materials induced by different laser parameters showed that the damage behavior was closely dependent on the materials characteristics as well as laser parameters6,7,8,9,10,11,12,13.
Among the works of ultraviolet excimer laser damage of ultraviolet windows, fused silica has been reported mostly14,15,16,17,18,19,20,21,22,23,24. In contrast, the reports on fluoride windows are relatively few, and most of the studies were just focused on the damage of fluoride films. Only a few reports are limited to the laser damage of single fluoride windows at 1064 nm wavelength25, and most of them were concerned with the damage caused by the fundamental 1064 nm laser and triple frequency 355 nm ultraviolet laser. There are few publications about the damage caused by shorter wavelength excimer laser, such as 248 nm laser. Because ultraviolet excimer lasers present favorable characteristics such as high photon energy, high coupling efficiency as well as high peak power26,27,28,29,30, they are expected to be widely used in precision laser machining and military area. This research will provide great significance in deeply understanding the interaction between ultraviolet laser and material, offer important reference in laser precision machining and laser attack-defense field, and also provide theoretical basis for the anti-laser damage ability of optical components.
Based on the self-developed PLD-50 excimer laser, a set of LIDT testing system was established. The CaF2 samples were divided into 2 groups, one group was highly polished, and the other one was roughly polished. First, the structural defects from polishing the CaF2 crystal were characterized with fluorescence spectroscopy.
Second, the samples were irradiated in a 1-on-1 mode with increasing energy density. Afterwards, the surface fragmentation and damage characteristics of CaF2 crystals were analyzed via dark field microscopy. From the experimental results, 2 phenomena were found: (1) the damage threshold of the rear surface of the optical window material is lower than that of the front surface, and (2) the LIDT of highly polished samples is higher than that of roughly polished samples regardless of incident surface or rear surface. The zero-damage thresholds were found from linear fits of the experimental data.
Third, electro-magnetic FDTD and thermo-mechanical FEA simulations were performed to replicate the findings and to get a deeper understanding of the damage process. The lower damage threshold of the rear surface compared to the incident surface is consistent with the FDTD simulation and the approximate value of the damage threshold could be reproduced with a thermo-mechanical FEA simulation. However, the effect that the damage threshold for the rear surface is lower for a roughly polished compared to a highly polished incident surface could not be replicated with the presented simulation schemes.
Damage tests on CaF2 samples
In this paper, when the CaF2 samples changes significantly and irreversibly, it is considered to be damaged. In order to reduce the measurement errors, 10 damage points are selected for the same laser fluence, and the damage probability is defined as N_damage/N_total. The zero-probability damage is used as the criterion to measure the LIDT. The damage morphology of the samples was observed and analyzed by optical microscope.
In the polishing process of CaF2, some physical loads caused by the polishing particles will result in brittle fracture removal, thus brittle defects such as scratches, digs and microcracks will occur on the surface of CaF2. These fragmentation defects can induce local modulation of light field during laser irradiation, enhance absorption and also reduce the mechanical strength of component surface. Therefore, these defects are generally considered as a low threshold damage-inducing precursor widely existing on component surface. In this paper, we use dark-field imaging of optical microscopy to characterize the surface fragmentation defects of CaF2. In dark-field imaging, the light reflected by the reflecting collector will project on the sample. Due to its great inclination angle, the reflected light cannot enter the objective lens if the sample is a polished mirror, so that only a dark patch can be seen in the eyepiece tube. Figure 1 shows the defects distribution images in dark field of CaF2 samples with two different polishing levels. It can be seen that the surface defects of different samples have distinct distribution characteristics under the influence of polishing level. Obvious distribution of defects, mainly scratches and digs, can be seen in roughly polished samples. While in the highly polished samples, scratch is the main defect form, and dig defect is markedly reduced.
The surface damage curves (linear fitting) of highly polished and roughly polished samples show, reported in Fig. 2, that damage probability increases with the laser fluence. And the LIDT of highly polished CaF2 samples, which is 6.1 J/cm2, is higher than that of roughly polished samples (5.6 J/cm2). By comparing Fig. 2a,b, it can be seen that the LIDT difference between front and rear surfaces of highly polished samples (1.5 J/cm2) are much smaller than that of roughly polished samples (4.5 J/cm2). What is more, no matter in which sample, the LIDT of rear surface is higher than that of incident surface. And it is worth noting that the polishing levels of the incident surfaces are different, while the rear ones are the same. So the experimental results tells that the polishing level of the incident surface has little influence on the LIDT of the incident surface (6.1 → 5.6 J/cm2), but has a great influence on that of the rear surface (5.6 → 1.1 J/cm2).
Figure 3 shows the rear surface damage morphology of the samples after roughly polished with different laser fluences. The results show that when the laser fluence is 1.4 J/cm2, small damage points appear initially. As the laser fluence increases, the damage area gets bigger. With further increase of the laser fluence a partial or complete peeling of the surface layer occurs.
Analysis of lower damage threshold on rear surface of CaF2 by 3D-FDTD
In the process of laser irradiation, defects on the surface of the sample with the size of laser wavelength level will cause uneven light field distribution in the sample. Many researchers have done a lot of work in theory on the problem of laser induced damage, especially some of them have used finite-difference time-domain (FDTD) method to calculate the light field distribution near the defects. However, the most used is simplified 2D models31,32. In practical situation, because of the spatial complexity of defects, 3D-FDTD can better reflect the light field distribution.
The FDTD method is one of the simplest full-wave techniques which can accurately solve a wide range of complicated problems in electromagnetics. However, it generally consumes large computing resources. In other words, it may require a large amount of memory and computation time. The FDTD method uses finite differences as approximations to both the spatial and temporal derivatives that appear in Maxwell’s equations (specifically Ampere’s and Faraday’s laws). The spatial arrangement of each electric field (EF) node and magnetic field (MF) node in FDTD is shown in Fig. 4, which is the famous Yee’s cell33. It can be seen from the graph that each MF component is surrounded by four EF components; similarly, each EF component is surrounded by four MF components. According to theoretical calculation and test, this sort of spatial sampling method of electromagnetic field components satisfies both Faraday’s law of electromagnetic induction and Ampere’s circuital law. Moreover, the spatial distribution of electromagnetic field components is also applicable to the differential discretization of Maxwell equation, so as to accurately show the propagation rules of electromagnetic field. In addition, the EF and MF are calculated alternately in time order, and the time intervals are half time steps different from each other. After the Maxwell curl equation is discretized, the explicit difference equation can be formed, so it can be solved iteratively on the time axis without matrix inversion, when the initial value and boundary conditions of a specific electromagnetic field problem are given. The Maxwell curl equations34 are
where E is the intensity of the EF (V/m), D is the dielectric flux density (C/m2), H is the intensity of the MF (A/m), B is the magnetic flux density (Wb/m2), J is the electric current density (A/m2), Jm is the magnetic current density (V/m2). And the constitutive equations are
where ε is the dielectric coefficient (F/m), μ is the magnetic permeability (H/m), σ is the conductivity (S/m), σm is the magnetoconductivity (O/m). When calculating scattering problems with FDTD, the computational region is usually divided into the total field area and the scattering field area. Absorption boundary conditions are set outside the scattering field, and a perfectly matched layer (PML) is used. By setting a special dielectric layer at the truncated boundary of the FDTD region, the impedance of the dielectric layer matches that of the adjacent dielectric perfectly, so the incident wave will pass into the PML through the interface without reflection. Because PML is a lossy medium, the transmitted wave entering PML will decay rapidly. Additionally, differ from two-dimensional case, the edges of the total field boundary should also be treated with corresponding boundary treatment.
The relative dielectric constant of CaF2 samples used in this research is 6.81. The incident beam can be regarded as a plane wave with a TM mode (The longitudinal component of the magnetic field is zero, while the longitudinal component of the electric field is not zero) with a wavelength of 248 nm. Suppose that the EF amplitude of the incident wave is 1.0 V/m and its incident direction is along the Z-axis, the front and the rear surfaces of CaF2 are parallel to the XOY plane. We consider the defect area to be a vacuum cuboid with a length of 2λ, a width of 2λ, and a height of 3λ. And its position is on the middle of the front surface. The 3D model is shown in Fig. 5. The size of the defect in the two cases is the same. The mesh size is taken as δ = λ/12 = 20.67 nm. In order to save computing resources and make the sample size an integral multiple of δ, we take a part of the CaF2 sample as the computational domain. The total field area is set as −6δ~81δ, −6δ~389δ, −16δ~123δ, and the target area is set as 0~72δ, 0~380δ, 0~104δ. The defect area of front surface is 24δ~48δ, 178δ~202δ, 0~36δ, and the defect area of rear surface is 24δ~48δ, 178δ~202δ, 68δ~104δ. The calculation iterations is 1000.
The relevant 3D-FDTD results are shown in Figs. 6–9. In Fig. 6, the plane of x = 28δ, which is central cross-section of the defect, is selected because the light field on this plane is most obviously modulated by the defect. Since the incident wave is TM mode, all the calculation results of the EF are components in the X direction, i.e., Ex. Figure 6(a) is the case of defect on the front surface of CaF2 (Z = 0 is the incident/front surface). We can see that the EF intensity near the defect is obviously modulated, and the EF distribution near the rear surface changes to some extent. Except for the area from the defect to the rear surface (148δ < Y < 230δ, 36 < Z < 104δ), the EF intensity does not change significantly. The case of defect on the rear surface is shown in Fig. 6(b). The EF distribution near the defect is obviously affected, and the EF intensity near the rear surface is also greatly increased. The above phenomenon can be explained as follows:
For the case of the defect on the front surface. Because of the defect (especially for the size of 2λ × 2λ × 3λ), the scattering of the transmitted laser wave occurs. An obvious standing wave is formed in front of the defect. As a result, behind the defect, the mode of laser is no longer the basic mode of a TE mode, but the superposition and coupling of multiple modes. When the defect is on the rear surface, the situation is similar because the defect has a depth of 3λ.
Also, the distribution of the EF in the XOY plane is investigated. As a reference, EF intensity distribution of XOY cross-section without defect is shown in Fig. 7. The electric field along Y-axis when X = 36δ is evenly distributed between 0.6 V/m and 0.9 V/m. Then, by comparing Figs. 8 and 9, the EF intensity varies with the location of the defect. It can be seen that the EF intensity on the rear surface (Figs. 8c,d and 9c,d) is more or less greater than that near the front surface (Figs. 8a,b and 9a,b) in the range of about 24δ < X < 48δ, which is consistent with the results of Fig. 2.
However, these are just two special XOY planes. To better illustrate the problem, the difference of EF intensity between front and rear surfaces in two cases are drawn in Fig. 10. The positive value means the EF intensity of rear surface is larger than that of front surface with the same x, y coordinate. It is obvious that the sum of EF intensity difference between front and rear surfaces is far more than zero (5884.3 V/m for the case of defect on the front surface and 7663.1 V/m for the case of defect on the rear surface). And the numbers of pairs of nodes (the corresponding points on front and rear surface, which have the same X, Y coordinate values, but different Z coordinate values) with their EF intensity difference above zero are 6271 (66.01%) and 5514 (58.04%), respectively.
The essence of light is electromagnetic wave, so analyzing the distribution of electromagnetic field in target materials, in certain degree, can reflect the coupling intensity of laser power in materials. However, the distribution of electromagnetic field in target materials is not enough to explain the damage mechanism, namely, the value of damage threshold, it can only analyze the problems of transmission and distribution of electromagnetic fields. As a result, in this paper, the FDTD was used to analyze the relative value of electric fields of the front and rear surface. The comparison result can show which surface couples more energy of the laser, in other words, the surface which couples more energy of laser will have a low damage threshold.
The explanation of the FDTD simulation results is interference. Here the incident wave is added to the reflected waves of the incident surface and the rear surface of CaF2 which would cause higher field strength and higher energy density via constructive interference. However, because this happens in air (which cannot get damaged) at the incident surface and inside the material at the rear surface, the rear surface gets damaged at lower energies.
We assume that the electric field strength on the rear Er is enhanced by a factor A due to reflection when compared to the incident E-field Ei.
The electric field on the front Ef is assumed to be equal to the incident field Ei
We also assume that there is a damage threshold E-Field ED, which represents the field strength just before the material gets damaged. We now irradiate with an incident E-Field Ei1, which causes a damage threshold E-field to appear on the rear:
Now we irradiate with an incident E-field Ei2 which causes damage threshold E-field to appear on the front.
Now we divide Eq. (6) by Eq. (7),
where Ef = Er = ED, and
Now we square it and
where I is the laser intensity, which is square of E-field. From Fig. 2 we know Ii2 corresponds to the LIDT of front surface, and Ii1 corresponds to the LIDT of rear surface. Here, we take the values in the highly polished case, that is, Ii2 is 6.1 J/cm2 and Ii1 is 4.6 J/cm2.
Simulation results in Fig. 10 could successfully replicate the finding. \(\frac{{{\rm{E}}}_{r}^{2}}{{E}_{i}^{2}}\) values are obtained by calculating the ratio of electric field strength of the corresponding nodes (the corresponding points on front and rear surface, which have the same X, Y coordinate values, but different Z coordinate values), and then square them. Figure 10a,b are the cases that the defect is on the front surface and the rear surface respectively. It can be seen that average and standard deviation values of A2 are 1.3217, 1.381 and 0.3826, 0.3346 in 2 cases, and 1.326 lies in that range.
With the coupling of the laser power, electromagnetic energy is converted into heat and mechanical energy, which are the direct reasons of damaging. So in the next FEA part, the laser is regarded as a kind of heat source. Through analyzing the heat and force effect of the physical process, the value of damage threshold can be predicted.
Thermo-mechanical coupling FEA model of laser induced damage to CaF2
Figure 11 shows the photoluminescence spectrum of CaF2 samples. A 250 nm-wavelength Xe lamp is used as excitation source, and the detection spectrum ranges from 300 to 800 nm. It can be seen that the luminescence signal in highly polished sample is rather weak, with only a weak peak at 501 nm, while in roughly polished sample there are four emission peaks at 326 nm, 346 nm, 424 nm, and 501 nm. From the peak wavelength and spectral bandwidth of emission peaks, it can be confirmed that 326 and 346 nm emission are originated from 4f → 5d transition emission of Ce3+, and 424 nm emission is originated from 4f → 5d transition emission of Eu2+. However, 501 nm emission was unclear. This indicates that roughly polished samples contain trace impurity ions. Comparatively, the impurity content in highly polished samples is very low. It should be noted that The purpose of polishing is to minimize the content of impurities on the surface, but no residue at all is impossible. From Fig. 1a, some bright spots (impurity particles or dig defect) still can be seen.
In order to calculate the temperature and stress fields of CaF2 irradiated by 248 nm laser, the theoretical model is established and shown in Fig. 12 (2D crosssection of the model). The laser focus is on the CaF2 surface, and the duration of the pulse is τ = 20 ns. The CaF2 sample is disc-shaped, and the laser is vertically incident to the surface of the sample (Z = 0), the center of the laser beam is concentric with the sample center. In order to save computing resources, we take a part of the CaF2 sample as the computational domain. The radius and thickness of the CaF2 model are R = 2 mm and h = 1 mm, respectively. And the Ce2O3 impurity particle is a ri = 300 nm sphere, its spherical center is 1μm away from the incident surface of the laser. Figure 13 shows the energy distribution of the KrF laser spot by a beam quality analyzer. It shows that the output laser is a flat-topped beam, and the energy distribution is similar to uniform distribution, which is different from the Gaussian distribution of general lasers. Therefore, in this paper, the temporal distribution of the laser beam is assumed as a step function and the peak power density I0 is uniform in pulse duration.
The absorbed energy in CaF2 can be expressed by the heat conduction equation30,
where Eqs. (12) and (13) are the boundary and initial conditions, respectively. Cp, ρ, and k are isobarically heat capacity, density, and thermal conductivity, respectively. T0 = 293 K is an initial temperature, Q(r, z, t) is the heat source, which can be shown as:
where α is the absorption coefficient of the material and Rs is the surface reflectance of CaF2. I(r, t) is the incident laser intensity, which can be written as:
where I0 is the peak power density of the incident laser. f(r) and g(t) are the spatial and temporal distribution functions of the laser, respectively, and they can be described as follows:
where RL is the beam radius and τ is the pulse duration. In this paper, the effect of thermal radiation and thermal convection can be ignored since the duration of the laser pulse is very short.
Related parameters of CaF2 and Ce2O3 are listed in Tables 1 and 2. The transmission of the umcoated CaF2 sample at 248 nm is Rs = 92.28%35. In the analysis model, because CaF2 is the window of 248 nm, we consider that 92.28% laser influece is absorbed by the Ce2O3 particle.
In this paper, due to the extremely short time scale, we consider that the melting damage occurs when the incident surface of the CaF2 sample reaches its melting point. Figure 14 shows the maximum temperature on incident surface of the CaF2 sample with different laser fluences. It can be seen that the maximum temperature of incident surface just reaches the melting point of 1635K when the laser fluence is 5.92 J/cm2 (Fig. 15), and the melting damage will occur in the laser spot area. So 5.92 J/cm2 is the melting damage threshold of CaF2. However, the corresponding maximum thermal-stress at 5.92 J/cm2 is 1.044 GPa (Fig. 16), which is far more than the compressive strength of CaF2 (300 MPa). So, it is obvious that the compressive stress damage occurs before the melting damage.
Figure 17 shows the thermal-stress distribution between the incident surface and Ce2O3 particle with laser fluence of 3.74 J/cm2. And Figs. 18 and 19 show the maximum stress value and the stress distribution along r-axis at different time, respectively. It can be seen that the compressive stress at the spot center just reaches the compressive strength (300 MPa) at 20 ns, so the compressive stress damage on the surface exactly occurs. However, compared with the experimental results, the calculated stress damage threshold (3.74 J/cm2) is between the measurements of rear surface with roughly polished (1.1 J/cm2) and highly polished (4.6 J/cm2). Through analysis, the reason is (1) in roughly polished condition, the distribution density of Ce2O3 particles is larger than the calculation model, while in highly polished condition, the distribution density of Ce2O3 particles is smaller than the calculation model; (2) there are some other impurities like EuOx in the CaF2 samples, and the parameters are not reported.
Conclusions
To summarize, laser-driven surface damage and material failure behavior of CaF2 crystal under ultraviolet laser beam irradiation have been systematically studied. Experimental research on damage in CaF2 irradiated by a 248 nm/20 ns KrF excimer laser is carried out. The 3D-FDTD simulation could successfully replicate the finding that the rear surface is always damaged before incident surface by showing that the laser intensity (square of electric field strength) on the rear is always approximately 1.3–1.4 times higher than that on the front (from Fig. 10, the ratios are 1.3217 and 1.381, respectively). The phenomenon that the rear surface always gets damaged at lower energies, when the front surface is roughly polished compared to highly polished, could not be reproduced. This might be achievable with an increase in the computational grid to the width of the sample window. Because in the present simulation we are still in the near field.
In addition, this paper essentially establishes the theoretical model of nanosecond laser damage to optical window materials by FEA method. Due to the unknown distribution density of Ce2O3 in CaF2, the analytical results are somewhat different from the experimental results. However, the presented model could successfully reproduce the order of magnitude of the laser induced damage threshold.
Methods
Laser system and samples
The experimental optical path of CaF2 windows damaged by 248 nm KrF ultraviolet laser is shown in Fig. 20. The laser source is a 248 nm KrF excimer laser, which was produced by Anhui Institute of Optics and Fine Mechanics, Chinese Academy of Sciences. It can emit high-quality pulsed laser beams with adjustable frequency (1 Hz to 50 Hz), and pulse width is 20 ns, and its single pulse energy can be adjusted in the range of 0mJ to 550mJ. An OPHIR L30A-10MM energy meter is used to monitor the pulse energy. The CaF2 window samples with both surfaces polished is 30 × 30 × 3 mm in size. “1-on-1” mode is adopted in the experiment, i.e., each position on the sample is allowed no more than one pulse shot on it.
Materials
Commercially available CaF2 (Beijing Scitlion Technology Corp., LTD.) was used in this study. And the polishing of samples is also done by Beijing Scitlion Technology Corp., LTD.
Numerical simulations
The EF distribution in CaF2 samples when the defect is on the incident surface and rear surface is calculated by FDTD Solutions. And the temperature and thermal-stress distribution in CaF2 samples with Ce2O3 particle after irradiation by 248 nm KrF laser are calculated using COMSOL Multiphysics.
References
Klein, C. A. Materials for high-energy laser windows: oxyfluoride glass vs. fusion-cast CaF2. Proc. SPIE 5786, 280–295 (2005).
Sakuragi, S. Evaluation of high-quality CaF2 single crystals for ultraviolet laser applications. Proc. SPIE 5647, 314–321 (2005).
Jeffrey, T. K., Qiao, L. & William, R. R. Improvements in CaF2 material properties for next-generation microlithography applications. Proc. SPIE 5377, 1735–1739 (2004).
Mouchovski, J. T., Temelkov, K. A., Vuchkov, N. K. & Sabotinov, N. V. Laser grade CaF2 with controllable properties: growing conditions and structural imperfection,. J. Phys. D. Appl. Phys. 40, 7682–7686 (2007).
Yanagi, H. et al. Properties of large CaF2 crystals grown by CZ method for lens materials. Proc. SPIE 5377, 1886–1893 (2004).
Bauer, M. et al. Exterior surface damage of calcium fluoride outcoupling mirrors for DUV lasers. Opt. Express 17, 8253–8263 (2009).
Reif, J., Petzoldt, S., Elg, A. P. & Matthias, E. The role of defects in laser surface damage thresholds of fluoride crystals. Appl. Phys. A 49, 199–204 (1989).
Gogoll, S., Stenzel, E., Reichling, M., Johansen, H. & Matthias, E. Laser damage of CaF2 (111) surfaces at 248 nm. Appl. Surf. Sci. 96–98, 332–340 (1996).
Bozlee, B. J., Exarhos, G. J. & Teel, R. W. Spectroscopic studies of pulsed-laser-induced damage sites in heated CaF2. crystals, Proc. SPIE 3578, 533–543 (1999).
Liberman, V., Rothschild, M., Palmacci, S. T., Efremow, N. N. & Sedlacek, J. H. C. Accelerated damage to blank and antireflectance-coated CaF2 surfaces under 157 nm laser irradiation. Proc. SPIE 5040, 1631–1638 (2003).
Kirkpatrick, S., Walsh, M., Svrluga, R. & Thomas, M. Improved laser damage threshold performance of calcium fluoride optical surfaces via Accelerated Neutral Atom Beam (ANAB) processing. Proc. SPIE 9632, 96321Y (2015).
Wang, J., Cox, G. P., D’Lallo, M. J., Vankerkhove, S. & Oudard, J. F. Laser-induced damage of F-SiO2 protected fluoride-based AR coatings on subsurface-damage-free CaF2 at 193 nm. Proc. SPIE 10014, 100140A (2016).
Takazawa, A., Sakuragi, S., Tanaka, Y., Yamada, K. & Wada, S. Long-term damage test of CaF2 optical window under irradiation of 4ω Nd:YAG laser. Jpn. J. Appl. Phys. 43, 644–645 (2004).
Smith, A. V. & Do, B. T. Bulk and surface laser damage of silica by picosecond and nanosecond pulses at 1064 nm. Appl. Opt. 47, 4812–4832 (2008).
Carr, C. W., Bude, J. D. & DeMange, P. Laser-supported solid-state absorption fronts in silica. Phys. Rev. B 82, 184304 (2010).
Natoli, J. Y., Bertussi, B. & Commandre, M. Effect of multiple laser irradiations on silica at 1064 and 355 nm. Opt. Let. 30, 1315–1317 (2005).
Demos, S. G., Negres, R. A., Raman, R. N., Rubenchik, A. M. & Feit, M. D. Material response during nanosecond laser induced breakdown inside of the exit surface of fused silica. Laser &Photonics Reviews 7, 444–452 (2013).
Raman, R. N., Negres, R. A. & Demos, S. G. Time-resolved microscope system to image material response following localized laser energy deposition: exit surface damage in fused silica as a case example. Opt. Eng. 50, 13602 (2011).
Raman, R. N., Negres, R. A. & Demos, S. G. Kinetics of ejected particles during breakdown in fused silica by nanosecond laser pulses. Appl. Phys. Lett. 98, 51901 (2011).
Zhou, Q. et al. Ultra-fast diagnosis of shock waves and plasma at front and rear surfaces in the bulk of fused silica induced by an Nd:YAG pulse laser. Chin. Opt. Lett. 14, 51402 (2016).
Shen, C., Cheng, X. A., Xu, Z. J., Wei, K. & Jiang, T. Observation of particle ejection behavior following laser-induced breakdown on the rear surface of a sodium chloride optical window. Opt. Eng. 56, 011009 (2017).
Stevens-Kalceff, M. A., Stesmans, A. & Wong, J. Defects induced in fused silica by high fluence ultraviolet laser pulses at 355 nm. Appl. Phys. Lett. 80, 758 (2002).
Raman, R. N., Negres, R. A. & Demos, S. G. Kinetics of ejected particles during breakdown in fused silica by nanosecond laser pulses. Appl. Phys. Lett. 98, 51901 (2011).
Demos, S. G. et al. Mechanisms governing the interaction of metallic particles with nanosecond laser pulses. Opt. Expr. 24, 7792–7815 (2016).
Demos, S. G. et al. Relaxation dynamics of nanosecond laser superheated material in dielectrics. Optica 2, 765–772 (2015).
Basting, D. & Marowsky, G. Excimer Laser Technology. Springer, Berlin, (2005).
Smiley, V. N. Review of high power excimer lasers. Proc. SPIE 1225, 2–22 (1990).
Zhang, H. B., Yuan, Z. J., Zhou, J. & Wei, Y. R. Effects of prism beam expander and slits on excimer laser linewidth narrowing modules. Chin. Opt. Lett. 11, 041405 (2013).
Wang, X. S., Yu, Y. S., Wang, Q. S. & Fang, X. D. A discharge-pumped KrF excimer laser with high efficiency. Chin. J. of Las. 38, 0102001 (2011).
Wang, X., Shao, J. Z., Li, H., Nie, J. S. & Fang, X. D. Analysis of damage threshold of K9 glass irradiated by 248nm KrF excimer laser. Opt. Eng. 55, 027102 (2016).
Wong, P. B. et al. A three-wave FDTD approach to surface scattering with application to remote sensing of geophysical surfaces. IEEE Trans. Ant. and Prop. 44, 504–514 (1996).
Deford, J. E. Modeling of electric field enhancement at nodular defects in dielectric mirror coating. Proc. SPIE 1578, 166–173 (1992).
Liu, J., Brio, M., Moloney & Jerome, V. A diagonal split-cell model for the overlapping Yee FDTD method. Acta Math. Sci. Ser. B 29, 1670–1676 (2009).
Elsherbeni, A. & Demir, V. The Finite-Difference Time-Domain Method in Electromagnetics: with MATLAB. Raleigh, NC: SciTech Publishers, 2006.
https://www.thorlabschina.cn/NewGroupPage9.cfm?ObjectGroup_ID=3978.
Li, C., Kang, X., Han, W., Zheng, W. & Su, L. Nanosecond laser-induced surface damage and material failure mechanism of single crystal CaF2 (111) at 355nm. App. Surf. Sci. 480, 1070–1077 (2019).
Acknowledgements
This work was supported by the Anhui Province Natural Science Foundation (Project No. 1908085MF222), Foundation of the State Key Laboratory of Pulsed Power Laser Technology (Project No. SKL2019ZR04) and Foundation of National University of Defense Technology (Project No. ZK19-15). The authors would like to express their gratitude to Prof. Xiaoquan Sun from the State Key Laboratory of Pulsed Power Laser Technology and Prof. Xiaodong Fang and Prof. Jingzhen Shao from Hefei institutes of Physical Science, Chinese Academy of Sciences for their assistance in the discussion and experiments.
Author information
Authors and Affiliations
Contributions
X. Li and X. Wang contributed to the original idea. X. Wang supervised the project. X. Li performed the experiments and prepared the main manuscript. X.A. Dou, H. Zhu and Y. Hu contributed to data analysis and language improvement.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, X., Dou, Xa., Zhu, H. et al. Nanosecond laser-induced surface damage and its mechanism of CaF2 optical window at 248 nm KrF excimer laser. Sci Rep 10, 5550 (2020). https://doi.org/10.1038/s41598-020-62469-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-62469-y
- Springer Nature Limited