Abstract
Cotton fiber is the most commonly used fabric in textiles and clothing. As compared to inorganic materials like foam, sponge and paper, cotton fibers boast higher levels of flexibility and toughness, which makes it more durable and be better integrated with clothes. In this study, a conductive cotton fiber material modified by reduced graphene oxide (rGO) was prepared, and applied in pressure sensor. The highest sensitivity of the pressure sensor constructed is 0.21 kPa−1, and the pressure range covers up to 500 kPa, which demonstrates a combination of fine sensitivity and broader pressure range. The pressure sensor developed in this study demonstrates great performance in real-time monitoring of human physiological signals like pulse, breath rate and speech recognition, boasting great application value in wearable electronics and smart clothing.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
With the rapid development of robotics technology and wearable electronics in recent years, flexible pressure sensors widely applied in e-skins and wearable devices have come under the spotlight of a great number of researchers1,2,3,4,5,6,7,8,9,10,11. A variety of pressure sensors have appeared with different flexible materials. In these sensors, organic polymers like PDMS12,13,14, rubber2, P(VDF-TrFE)15,16 are commonly used materials owing to their natural flexibility and transparency. Meanwhile, inorganic materials like foam17,18,19, sponge20,21, paper6 and textiles22,23 serve as active materials for flexible pressure sensors due to their high-efficiency, low cost, and the fact that they can be easily manufactured. As is commonly known, most of our clothes are made of cotton fibers. Compared with inorganic materials mentioned above, cotton fiber based material boasts higher levels of flexibility and toughness, which makes it durable and the most commonly wearable material. In previous studies, functionalized cotton textiles have been employed as a wearable platform in many applications24,25,26,27.
Recently, owing to its advantageous features, the unique three-dimensional (3D) microstructure based devices have been widely studied28,29. Lou et al. reported an rGO wrapped P(VDF-TrFE) 3D nanofibers based pressure sensor, whose measuring sensitivity was 15.6 kPa−1 and the detection limit was as low as 1.2 Pa30. Pan et al. fabricated an ultra-sensitive pressure sensor based on 3D hollow-sphere microstructure polypyrrole film, whose measuring sensitivity reached 133.1 kPa−1 and detection limit was below 1 Pa28. The 3D porous or networks structure forms a 3D conducting path to produce sensitive response to external pressure. The cotton fibers can form a 3D-network microstructure, and cotton is the most commonly used material in textile production, which facilitates its integration with clothes and wearable devices. In this study, by virtue of a simple dipping and annealing process, a conductive cotton fibers material modified by rGO nanosheets was prepared and then used to fabricate a novel flexible pressure sensor. The pressure sensor proposed in this study can be easily fabricated and highly sensitive (0.21 kPa−1 in 0–2 kPa and 0.0368 kPa−1 in 2–20 kPa) with a broad pressure range spanning up to 500 kPa (see Supporting Information). The response to loading-unloading cycles of external pressures show good reproducibility and stability. The detection of human physiologic signals (such as wrist pulse and respiration rate) was achieved by virtue of high signal-to-noise ratio (SNR). These results show that the pressure sensor based on rGO modified cotton proposed in this study boasts great potential in application in wearable electronics especially in smart clothing.
Ressults and Discussion
Similar to graphene membranes, the rGO nanosheets are ultrathin and mechanically flexible, which allows them to conformally adhere to the surfaces of the cotton fibers. As shown in Fig. 1a,b, to obtain conductive cotton material, 2 mg/mL GO solution with dispersed GO sheets in aqueous solution was prepared. Subsequently, the degreasing cotton usually applied in laboratory was cut into small pieces and immersed in the GO solution for 12 h. The cotton pieces immersed in GO solution were then annealed in furnace at 250 °C for 5 h, under nitrogen protection. Thus the conductive cotton material was obtained. After being connected to copper electrodes and packaged with polyimide tape, the pressure sensor was constructed. Figure 1c,d show scanning electron microscopy (SEM) results of the rGO wrapped cotton, from which it can be clearly seen that the morphology of 3D porous networks and the cotton fibers were wrapped by the rGO sheets.
The full range (0–500 kPa) response properties of the conductive cotton based pressure sensor is shown in Fig. 2a, and the low pressure (0–2 kPa) response properties are shown in Fig. 2b. A testing platform was constructed, including a Shimadzu AGS-X mechanical testing machine and a Keithley 34410A digital multimeter, to study the performance of the pressure sensor developed in the present study. The sensitivity is defined as:
where ΔR represents the relative change of resistance value under pressure, R represents the resistance value when the pressure is implemented, R0 represents initial resistance value, and δP represents the variation of the applied pressure. As shown in Fig. 2a, the sensitivities of three different cotton based pressure sensors (g1, g2 and g3) were calculated with S1 indicating middle pressure range (0–20 kPa) and S2 indicating the high pressure range (100–500 kPa). Additionally, the sensitivities S3 are high in the very low range (0–2 kPa) of the sensors, and the linearity is also excellent, as shown in Fig. 2b. Figure 2c schematically demonstrates the working mechanism of the rGO modified cotton based pressure sensor. The SEM images in Fig. 1c,d above show the morphology of the 3D porous networks of the rGO wrapping cotton, suggesting there are a number of air gaps and overlapping in the networks structure of cotton. The rGO modified cotton based pressure sensor acts as a resistive pressure sensor. When the pressure is applied, air gaps reduce and overlapping in the cotton fibers increase, then the contact sites between the rGO nanosheets increase, and the resistance value of the sensor decreases.
Because there is no fixed shape in cotton fiber, the values of weight are used to differentiate the three samples. The weight of conductive cotton in g1, g2 and g3 sensors was measured by an electronic balance (LT1002E, with the accuracy of 0.01 g) and results were 0.08 g, 0.12 g and 0.14 g, respectively. The pressure sensors have a wide detection range and high sensitivity, and the sensitivities decline with the increase of the pressures. The performance of the conductive cotton pressure sensors varies with weight. As shown in Fig. 2a,b, when the weight of the conductive cotton increases, the sensitivity of the constructed sensors increases in the middle range and decreases in the high range. The 3D networks structure of cotton plays a key role in the excellent performance of the conductive cotton pressure sensor. This unique structure offers 3D conducting path, more air gaps and more contact sites than layer-structured materials like paper, which endows the graphene cotton based pressure sensor with a high sensitivity. Meanwhile, the 3D construction and high levels of flexibility of cotton fibers allow sensing material to withstand large loading, which endows the cotton based pressure sensor with an extremely wide detection range. The porous structure and air gaps lead to poor contact among the conducting material (rGO nanosheets) when there is no pressure, indicating that the pressure sensor has a high initial resistance. When a small pressure is applied, air gaps become smaller and the resistance of the graphene cotton based pressure sensor decreases sharply. There are more air gaps for the graphene cotton with greater weight and thickness. Therefore, the resistance of the sensor g3 decreases more quickly in the low pressure range, and g3 is more sensitive in the low pressure range of 0–20 kPa (0.21 kPa−1 in 0–2 kPa and 0.0368 kPa−1 in 2–20 kPa). Otherwise, when the applied pressure continuously increases, air gaps will disappear and the resistance of the graphene cotton based pressure sensor will decrease slowly. The sensor g1 is more sensitive in the high pressure range of 100–500 kPa and its value is 3.5 × 10−4 kPa−1.
The stability and repeatability are significant indicators for the performance of pressure sensors. Hence, a test was performed to detect the responses of the conductive cotton based pressure sensor under different loadings. As shown in Fig. 2d, the responses of pressure sensors to different pressures are stable and noise-free. The resistance of the sensor under middle pressure from 2 kPa to 20kPa changes more significantly than that under high pressure from 20 kPa to 100 kPa. Further, the long-time stability of the graphene cotton based pressure sensor was also tested. Figure 2e shows how the relative resistance of five different sensor samples g1a-g1e with the same weight of 0.08 g changes with pressure from 0 to 500 kPa. The response performance of each sample is diverse, but the error is small and the sensitivities of the pressure sensors with their weight controlled only fluctuate within a certain range. Figure 2f,g show the repeatability responses of the pressure sensor g2 under pressure 20 kPa and 200 kPa in 500 loading-unloading cycles, it can be seen that the variation of relative resistance is almost constant throughout the cycling, except a slight increase in the initial resistance value. Figure 2h shows a local magnification of the repeatability response of g2 in 500 repetitive cycles under pressure of 200 kPa, the level of consistency of the response curve is good. These results confirm that the pressure sensors proposed in this study can maintain stability under repetitive loadings.
Furthermore, the response-recover properties of the pressure sensor were tested. Figure 3a shows a single response and recovery curve of sensor g3 with good reproducibility under the pressure of 2 kPa. According to Fig. 3,c, the response time and recovery time of the cotton based pressure sensor are 1200 ms and 137 ms, respectively. It turns out that the response-recovery time can change drastically under higher pressure. Figure 3d shows a single response and recovery curve of sensor g3 under the pressure of 500 kPa. As shown in Fig. 3e,f, the response time and recovery time of the pressure sensor are 681 ms and 427 ms, respectively. In addition, the response time is almost halved under high pressure, which may be attributed to the fact that larger deformation occurred in the conductive cotton when higher pressure was applied. And the recovery time increases to a certain extent under higher pressure as well, which leads to more recovery time for larger deformation. Also, as the cotton fiber has no fixed shape and errors exist in manual operation of different batches of annealing and packaging processes, the properties of the pressure sensors vary in different sensor samples, as shown in Fig. 2e. These results indicate good static and dynamic performance of the graphene cotton based pressure sensors proposed in this study, which well lends itself to human motion monitoring.
The real-time detection of human physiological signals is growingly prevalent in medical clinical diagnosis and human-computer interfaces. The conductive cotton based pressure sensor proposed in this study is attached to human wrists by tapes to realize the real-time monitoring of human pulse, as shown in Fig. 4a,d. Our testers included a boy (subject A, 25 years old, 185 cm height, 63 kg weight) and a girl (subject B, 23 years old, 158 cm height, 47.5 kg weight). According to the results shown in Fig. 4b,e, the pulse rates of subjects A and B are 64 bpm (beats per minute) and 70 bpm, respectively. Pulse beats of the boy are initially strong and then slightly slower, and pulse of the girl is initially weak and then slightly faster. The diastole region31 can be clearly seen in Fig. 4b,c, as marked in the pictures. For further comparison, the electrocardiography (ECG) examination was implemented for subjects A and B, the results show that the heart rates of subjects A and B are 65 bpm and 67 bpm, respectively (shown in Fig. S3a–c). As is commonly known, the heart rate and pulse rate are the same in a normal person. The results of our wrist pulse test by the cotton based pressure sensor are almost identical to those of ECG, which demonstrates the reliability of our wrist pulse test. Furthermore, the wrist pulse and respiratory rate of subject A were detected after he had ran for 5 min (for a distance of about 1.2 km), as shown in Fig. 4b,f. Because the boy’ body is very healthy, his heart rate recovered very fast after the run, so almost no change happened to his pulse rate, but his pulse amplitude increased significantly compared to the amplitude before running. Compared to heart rate, breath recovered more slowly, the boy’s respiration rate was ~30 times/min when he rested in sitting positions 5 min after running. And until 10 min after running, the boy’s breath returned to normal level (~16 times/min). The phenomenon observed in the experimental results are consistent with clinical medical knowledge. These experiments show the excellent performance of graphene cotton based pressure sensor in real-time monitoring of the physiological status of human bodies.
The pressure sensor proposed in this study is also promising in speech recognition. The pressure sensor was attached to the throat of subject A by tapes, as shown in Fig. 5a. The muscle movements of the tester were detected while he spoke. Figure 5b–d show how the curves of resistance changed with time when the tester articulated different sentences, like “I am a student”, “What are you doing” and some Chinese words. Results indicate that the waveforms corresponding to different sentences are significantly different, and the difference in the pronunciation of each word is obvious and can be easily captured in the curves. And the reproducibility of the curves is good (shown in Fig. S4a,b). The results demonstrate that with high sensitivity and good reliability, the conductive cotton based pressure sensor can be well applied in speech recognition and other fields like human-computer interaction.
Conclusion
In this study, the graphene modified conductive cotton was fabricated and applied in pressure detection. The rGO modified cotton based pressure sensor has a high sensitivity of 0.21 kPa−1 in a wide pressure range of up to 500 kPa. It also boasts good repeatability and stability. It demonstrates excellent performance in the detection of pulse, breath rate and muscle movement. The outstanding performance of the pressure sensor is attributed to the 3D porous networks structure of the cotton fibers. To sum up, the rGO modified cotton based pressure sensor proposed in this study have great promise in application of wearable devices especially in smart clothing.
Methods
Fabrication of rGO-cotton based pressure sensor
Absorbent cotton usually used in labs was cut into small pieces, and then immersed in 2 mg/mL graphene oxide (GO) aqueous solution for 12 h to make sure it was fully soaked by the solution. Subsequently, the cotton was put into chemical vapor deposition (CVD) furnace under 250 °C for 5 h, to reduce the GO dopant into rGO under nitrogen protection. The rGO cotton was not taken out until it was cooled down to room temperature within the furnace. Then the rGO cotton was sandwiched between the copper tapes as electrodes, and fixed by silver paste. The dimension of the top electrode was 1 cm × 1 cm. Finally, the cotton-based pressure sensor was packaged by polyimide tapes.
Monitoring of human physiologic signals
The cotton-based pressure sensor was stuck to the wrists of subject A and B to detect their pulse, and stuck to the throat of subject A to detect his muscle movements while he was speaking. Resistance of the pressure sensor was measured by a Keithley 34410A digital multimeter throughout all the experiments. Informed consent to participation in the study and publication of identified information/images in an online open-access publication was obtained from all subjects prior to their enrollment in the study. This research was approved by the Ethics Committee of Xi’an Jiaotong University. All the experiments that were conducted on human wrists and necks in this study were performed in accordance with guidelines and regulations. No other human subjects were involved in our experiments or manuscript.
References
Someya, T. et al. A Large-Area, Flexible Pressure Sensor Matrix with Organic Field-Effect Transistors for Artificial Skin Applications. Proceedings of the National Academy of Sciences of the United States of America 101, 9966–9970 (2004).
Mannsfeld, S. C. B. et al. Highly sensitive flexible pressure sensors with microstructured rubber dielectric layers. Nature Materials 9, 859–864 (2010).
Wang, C. et al. User-interactive electronic skin for instantaneous pressure visualization. Nature Materials 12, 899–904 (2013).
Schwartz, G. et al. Flexible polymer transistors with high pressure sensitivity for application in electronic skin and health monitoring. Nature Communications 4, 1859 (2013).
Hou, C., Wang, H., Zhang, Q., Li, Y. & Zhu, M. Highly conductive, flexible, and compressible all-graphene passive electronic skin for sensing human touch. Advanced Materials 26, 5018–5024 (2014).
Gong, S. et al. A wearable and highly sensitive pressure sensor with ultrathin gold nanowires. Nature Communications 5, 3132 (2014).
Zang, Y. et al. Flexible suspended gate organic thin-film transistors for ultra-sensitive pressure detection. Nature Communications 6, 6269 (2015).
Wang, X. et al. Dynamic pressure mapping of personalized handwriting by a flexible sensor matrix based on the mechanoluminescence process. Advanced Materials 27, 2324–2331 (2015).
Zang, Y., Zhang, F., Di, C. & Zhu, D. Advances of flexible pressure sensors toward artificial intelligence and health care applications. Materials Horizons 2, 25–59 (2014).
Su, B., Gong, S., Ma, Z., Yap, L. W. & Cheng, W. Mimosa-inspired design of a flexible pressure sensor with touch sensitivity. Small 11, 1885–1885 (2015).
Wang, J. et al. A highly sensitive and flexible pressure sensor with electrodes and elastomeric interlayer containing silver nanowires. Nanoscale 7, 2926–2932 (2015).
Wang, X., Gu, Y., Xiong, Z., Cui, Z. & Zhang, T. Silk-Molded Flexible, Ultrasensitive, and Highly Stable Electronic Skin for Monitoring Human Physiological Signals. Advanced Materials 26, 1336–1342 (2014).
Lipomi, D. J. et al. Skin-like pressure and strain sensors based on transparent elastic films of carbon nanotubes. Nature Nanotechnology 6, 788–792 (2011).
Choong, C. L. et al. Highly Stretchable Resistive Pressure Sensors Using a Conductive Elastomeric Composite on a Micropyramid Array. Advanced Materials 26, 3451–3458 (2014).
Sharma, T., Je, S. S., Gill, B. & Zhang, J. X. J. Patterning piezoelectric thin film PVDF–TrFE based pressure sensor for catheter application. Sensors & Actuators A Physical 177, 87–92 (2012).
Persano, L. et al. High performance piezoelectric devices based on aligned arrays of nanofibers of poly(vinylidenefluoride-co-trifluoroethylene). Nature Communications 4, 1633 (2013).
Pang, Y. et al. A Flexible, Highly Sensitive and Wearable Pressure and Strain Sensors with Graphene Porous Network Structure. Acs Applied Materials & Interfaces 8 (2016).
Tian, H. et al. A Graphene-Based Resistive Pressure Sensor with Record-High Sensitivity in a Wide Pressure Range. Sci Rep 5, 8603 (2015).
Tolvanen, J., Hannu, J. & Jantunen, H. Hybrid foam pressure sensor utilising piezoresistive and capacitive sensing mechanisms. IEEE Sensors Journal PP, 1–1 (2017).
Han, J. W., Kim, B. S., Li, J. & Meyyappan, M. Flexible, compressible, hydrophobic, floatable, and conductive carbon nanotube-polymer sponge. Applied Physics Letters 102, 1307 (2013).
Yao, H. B. et al. A Flexible and Highly Pressure‐Sensitive Graphene–Polyurethane Sponge Based on Fractured Microstructure Design. Advanced Materials 25, 6691–6691 (2013).
Lee, J. et al. Conductive Fiber-Based Ultrasensitive Textile Pressure Sensor for Wearable Electronics. Advanced Materials 27, 2433–2439 (2015).
Wang, D., Li, D., Zhao, M., Xu, Y. & Wei, Q. Multifunctional wearable smart device based on conductive reduced graphene oxide /polyester fabric. Applied Surface Science (2018).
Hu, L. et al. Stretchable, Porous, and Conductive Energy Textiles. Nano Letters 10, 708–714 (2010).
Yu, G. et al. Solution-processed graphene/MnO2 nanostructured textiles for high-performance electrochemical capacitors. Nano Letters 11, 2905–2911 (2011).
Bao, L. & Li, X. Towards textile energy storage from cotton T-shirts. Advanced Materials 24, 3246–3252 (2012).
Souri, H. & Bhattacharyya, D. Highly Stretchable Multifunctional Wearable Devices Based on Conductive Cotton and Wool Fabrics. Acs Applied Materials & Interfaces (2018).
Pan, L. et al. An ultra-sensitive resistive pressure sensor based on hollow-sphere microstructure induced elasticity in conducting polymer film. Nature Communications 5, 3002 (2014).
Zhong, W. et al. A nanofiber based artificial electronic skin with high pressure sensitivity and 3D conformability. Nanoscale 8, 12105 (2016).
Lou, Z., Chen, S., Wang, L., Jiang, K. & Shen, G. An ultra-sensitive and rapid response speed graphene pressure sensors for electronic skin and health monitoring. Nano Energy 23, 7–14 (2016).
Nichols, W. W. Clinical measurement of arterial stiffness obtained from noninvasive pressure waveforms. American Journal of Hypertension 18, 3–10 (2005).
Acknowledgements
This work was supported in part by the National Key R&D Program of China under grant No. 2016YFB1200100, the National Natural Science Foundation of China (51875449, 51890884, 51421004, 91748207), the Key Research and Development Project of Shaanxi Province (2018ZDXM-GM-103), the Fundamental Research Funds for the Central Universities (Grant No. xjj2017165), and the 973 Program (2015CB057402).
Author information
Authors and Affiliations
Contributions
P.L. accomplished the experiments, processed the data and wrote the manuscript; M.-Z.Y. and Z.L. assisted in the experiments and data processing; L.-B.Z. and Z.-D.J. conceived the experiments, organized and supervised the project; X.-Y.Z. and Y.-L.Z. modified the manuscript. All authors discussed and commented on the methods and results and contributed to the paper’s final version.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, P., Zhao, L., Jiang, Z. et al. A wearable and sensitive graphene-cotton based pressure sensor for human physiological signals monitoring. Sci Rep 9, 14457 (2019). https://doi.org/10.1038/s41598-019-50997-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-50997-1
- Springer Nature Limited
This article is cited by
-
Graphene-based nanotechnology in the Internet of Things: a mini review
Discover Nano (2024)
-
MoS2 nanoflowers and PEDOT:PSS nanocomposite enabling wearable dual-mode pressure sensors
Science China Technological Sciences (2024)
-
End-to-end design of wearable sensors
Nature Reviews Materials (2022)
-
Carbonization fabrication of a piezoresistive sensor with improved sensitivity via Ni decoration of carbonized cotton fibers
Science China Technological Sciences (2022)
-
Macroporous and free-shape reduced graphene oxide paper as sensitive wearable pressure and strain sensors
Applied Physics A (2022)