Abstract
In this study, nickel hydroxide nanoparticles (NPs) decorated with nitrogen doped multiwalled carbon nanotubes (N-MWCNT) hybrid composite was synthesized by thermal reduction process in the presence of cetyl ammonium bromide (CTAB) and urea. The as-synthesized Ni(OH)2@N-MWCNT hybrid composite was characterized by FTIR, Raman, XRD, BET, BJH and FE-TEM analyses. These prepared porous carbon hybrid composite materials possessed high specific surface area and sheet like morphology useful for active electrode materials. The maximum specific capacitance of Ni(OH)2@N-MWCNT hybrid nanocomposite in the two electrode system showed 350 Fg−1 at 0.5 A/g,energy density ~43.75 Wkg−1 and corresponds to power density 1500 W kg−1 with excellent capacity retention after 5000 cycles. The results suggest that the prepared two-dimensional hybrid composite is a promising electrode material for electrochemical energy storage applications.
Similar content being viewed by others
Introduction
Supercapacitors or ultra-capacitors are energy storage devices that have higher power density and better cyclic stability than conventional batteries. They are used as the most promising electrochemical energy storage devices with potential to eventually replace batteries for high-performance energy storage applications. Hybrid composites have been widely utilized in portable electronics, hybrid vehicles and backup energy systems for high-performance applications1,2,3. Based on energy storage mechanisms and properties, the supercapacitors can be classified into electric double layer (EDLCs) and pseudocapacitors4,5,6. In EDLCs, the electrodes generally consist of various forms of carbon, including activated carbons, carbon nanotubes, graphene and porous materials for supercapacitors7,8,9. Redox capacitors or pseudocapacitors employ transition metal oxides or conducting polymer as electrode materials.
In EDLCs, the energy storage mechanism involves electrostatic accumulation of charges at electrode-electrolyte interface between the electrode and ionic charges in the electrical double layer. However, in pseudo capacitors, stored energy is released in presence of reversible redox reactions or faradaic reactions occurring in electroactive materials. In addition, in EDLCs, capacitance is originated from a collection of charges at the electrode-electrolyte interface. To increase electrical conductivity and achieve high storage capacity, specific surface area and pore sizes are very important in EDLCs. Various graphene and carbon nanotubes structured composites have been widely used for electrochemical energy storage applications7,8,9.
The currently, recent developments of asymmetric supercapacitor is mainly focused on synthesis, properties, and performances of the state of the art materials for anode and cathodes in the supercapacitor applications. Mainly, the carbon-based materials such as porous carbon, activated carbon, carbon nanotubes, graphene, and graphene oxide materials are generally used for negative electrodes due to their high surface area and electrostatic charge-storage mechanisms at electrode/electrolyte interfaces. In particular, the pseudo capacitance of some metal oxides and nitrides have also been utilized as anode materials. The positive electrode containing the pseudocapacitive behaviours metal oxides and include carbonaceous materials. In addition, the electrode materials are design in the various nanostructured morphology of nanospheres, nanosheets, nanorods, nanowires, and nanoribbons. Recently, the studied two-dimensional materials such as transition metal dichalcogenides and transition-metal carbides for used in the current filed of supercapacitor applications10.
The asymmetric supercapacitors are an effective approach for extending the operating voltage window of the powder sources for supercapacitor and battery applications. These supercapacitor generally consists of a battery-type Faradic electrode (used as cathode) as an energy source and a capacitor-type electrode (anode) is a power source. Therefore, the asymmetric technology is expected to achieve an increased energy density and high cell voltage and improving the capacitance of cathode and anode materials have been widely studied. The carbon based materials are frequently used as anode in asymmetric supercapacitors. Because of the lower specific capacitance of carbon materials severely limits the energy density for supercapacitor for two electrodes. Metal oxide based anodes with nanostructures, such as MnO2, NiO, Co3O4, and Fe2O3, are promising electrode materials for asymmetric supercapacitors because of their high specific capacitance, two or three times higher than that of carbon/graphite-based materials11.
Based on these asymmetric electrode properties, the carbon nanotubes (CNTs) and reduced graphene oxide materials have also attracted significant attention in the field of biosensor, supercapacitor and electro catalytic applications due to their inherent potential properties of chemical stability, conductivity, flexibility, excellent catalytic activity and fast electron transfer reactions12,13,14,15. To improve the conducting property and surface area of MWCNT, nitrogen (N) was doped into the carbon matrix of MWCNT in the present investigation. Such N-doped process is very important for new generation of metal-free catalysts for electrochemical reactions. Nitrogen valence electrons are incorporated to the graphitic plane while π-electrons are generated in the carbon surface16. This may be due to π-electrons generation together with significant difference in electronegativity between nitrogen and carbon atoms. Therefore, the carbon-based materials contains unique properties such as high surface energy and polarization effect. N-doping can also improve both reactivity and electro catalytic performance of carbon materials. Therefore, in-situ doping involves direct incorporation of N atoms into carbon materials during the synthesis process in the presence of suitable catalyst.
Nickel oxide (NiO) is an important transition metal oxide that has attracted great interest due to its extensive applications in fields of catalysis, sensors and renewable energy sources14,15,16. A plenty of studies have been investigated the active electrode materials used like CuO, NiO, MnO2, Co(OH)2 and Ni(OH)2 for supercapacitors16,17,18,19,20,21,22. Amongst, nickel hydroxide, Ni(OH)2 materials have paid great attention due to their widely potential applications in alkaline rechargeable batteries, portable electronics and electric vehicles2. Further, it contains α and β phases. The crystalline β-Ni(OH)2 electrodes have been widely used for electrochemical applications due to their higher stacking density and stability when compared to α-Ni(OH)2. Numerous electrochemical studies have been reported the Ni(OH)2 electrodes on various carbon materials shows an improved electrochemical performance with excellent cyclic stability23,24,25,26. Electrochemical properties of Ni(OH)2/CNTs hybrid composite could be improved the specific capacitance and cyclic stability in presence of strong electrolyte like KOH at different concentrations. The electrochemical properties of Ni(OH)2/CNTs composite shows various specific capacitances and excellent stability of electroactive carbon materials have been shown27. Additionally, Ni (OH)2/MWCNTs hybrid nanocomposite can provide one-dimensional (1D) nanostructure owing to its high specific capacitance and excellent cycling stability and unusual electrical conducting properties.
Based on previous studies28,29, hybrid nanocomposites with different morphology based electrode materials have been synthesized for high-performance supercapacitors with excellent cyclic stability. In the present study, nanostructured nickel hydroxide oxide decorated N-MWCNT hybrid composite electrodes were synthesized and characterized for utilization in high performance supercapacitors for the first time. Systematic morphology and structural analyses revealed that the prepared hybrid electrode possessed high surface area with uniform pore size. Electrochemical properties of Ni(OH)2 @N-MWCNT hybrid composite (two and three) electrodes are displayed a high specific capacitance of two electrode is ~350 Fg−1 at 0.5 A/g and the detailed analyses are discussed below.
Results and Discussion
Structural results of the hybrid composite
The Schematic illustration of step by step synthesis of Ni(OH)2@N-MWCNT hybrid electrode is demonstrated in Fig. 1. The various structural interactions and complexation properties between N-MWCNT and Ni(OH)2 of the hybrid composite were analyzed through FTIR spectroscopy. The hybrid composite results are displayed in Fig. 2a. A broad band was observed at ~3495 cm−1. It could be represented to the stretching frequency of Ni(OH)2 present in the hydrogen bonded hydroxyl groups. The peaks appeared at 2844–2909 cm−1, indicating CH2 stretching mode from CTAB surfactant and other important functional modes such as C=O, C-H bending, C-O stretching, C-O-C stretching observed at 1631, 1476, 1357 and 1162 cm−1 respectively. There was a strong vibrational band in the region between 650 and 550 cm−1, especially at 598 cm−1 corresponding to Ni-O bond of Ni(OH)2. These results strongly suggest the presence of (NiOH)2 in the hybrid composite structure. The hybrid composite results also further confirmed that (NiOH)2 bonded to N-doped MWCNT surface in presence of CTAB surfactant and results compared to previous reports28,30.
Raman spectra of hybrid composite are shown in Fig. 2b. There were two prominent peaks at 1287 cm−1 and 1604 cm−1 represent that the D and G peaks from N-doped MWCNT, respectively. Generally, the G band indicates in-plane bond stretching motion of carbon (C, sp2) atoms of (E2g phonons). In addition, the peaks position of 2575 cm−1 (D’) and 2873 (2D) were also present in the hybrid nanostructure. The strong D band represents a large number of defects of N-doped MWCNT which is due to the reduction process of MWCNT. The intensity ratio of D and G peaks can be used to calculate disorder behaviours of carbon materials in sp2 domains31. The peak intensity of D and G are roughly calculated as (ID/IG = 1.08) represent that the large number of defects in the N-MWCNT surface. The peaks position at 3491 cm−1 and 2903 cm−1 are characteristic peaks of β-Ni(OH)2. These Raman spectral results confirmed that Ni(OH)2 was successfully anchored onto the surface of N-MWCNT.
Figure 2c represents XRD pattern of Ni(OH)2@N-MWCNT hybrid composite. Diffraction peaks at 6.94°, 12.34°, 17.10°, 18.08°, 21.04°, 24.03°, 25.82°, 29.12°, 31.11°, 33.10°, 35.92°, 40.0°, 51.42° and 59.63° corresponded to (001), (003), (002), (006), and (110) planes of Ni(OH)2@N-MWCNT surface confirmed by using standard JSPDS data (Card No. 14-0117).
All diffraction peaks showed hexagonal structure of Ni(OH)2. There was no impurity in the hybrid composite. Therefore, the XRD peaks proved that thermal reduction process played an important role in improving the crystalline nature, consistent with previous reports31,32,33.
Surface chemical compositions of Ni(OH)2@N-MWCNT hybrid composite was analyzed by XPS. The XPS spectral results ranging from 0 to 1200 eV are shown in Fig. 3. Peaks at 855.65 and 872.90 eV indicates to Ni 2p3/2 and Ni 2p1/2 energy levels, respectively. Its corresponding fitting plot is represented in Fig. 4(a). Energy spin-energy separation of ~17.20 eV represented the characteristic of Ni(OH)2 phase and further confirmed with a previous report32. In addition, O1s peaks at 532.12 eV are associated with bound hydroxide groups (OH), carbon (284.34 eV) and nitrogen (402–406 eV) (Fig. 4(b)) present in the hybrid composite structure confirmed the bonding between Ni (OH)2 and n-doped MWCNT surface.
Surface and morphological properties
Figure 5 shows nitrogen adsorption/desorption isotherms of Ni(OH)2@N-MWCNT hybrid composite samples at 77 K and analyzed by mesoporous materials. BET surface area of the hybrid composite was ~250 m2 g−1, then that of pristine nickel hybrid oxides (~108 m2 g−1)34,35. Pore size distribution of the hybrid composite showed very thin microspores and mesoporous of 0.5 to ~2.5 nm and macrospores below the ~200 nm. The hybrid composite showed a wide pore size distribution with particle size of ~1.5–20 nm. These mesopores and macropores of hybrid composite can facilitate the migration of K+ and OH− ions and enhanced the specific capacitance and cyclic stability in the electrochemical reactions36.
Morphology and structure of Ni (OH)2 @ N-MWCNT hybrid composite results were then studied by FE-TEM analysis. In these results (Fig. 6) of hybrid composite showed nanosheets like structure. The Ni(OH)2 nanoparticles are densely decorated over the surface of N-MWNT. In certain areas, aggregated nanoparticles are occurred, this may be due to mixing of N-MWCNT and Ni(OH)2. The SAED patterns corresponds to (003), (006), (110) and (002) patterns of Ni(OH)2 are observed in the hybrid composite and also consistent with previous reports37.
Electrochemical properties of the hybrid composite
Electrochemical properties of pristine nickel oxide, nickel hydroxides, carbon materials and metal oxides for supercapacitor applications have been widely reported in previous studies37,38,39. The metal oxides and metal hydroxides previous reports very clearly showed that the specific capacitance and cyclic stability increases due to various surface morphologies present in the hybrid composite38,40. In the present study, electrochemical properties of Ni(OH)2@N-MWCMT hybrid composite was studied in the presence of 6 M KOH as electrolyte. Figure 7 shows CV profiles of Ni (OH)2 @N-MWCNT hybrid composite at different scan rates (20 to100 mV/s) in the range of potential −0.2 to 0.8 V. The shape of CV loops for the hybrid composite electrode was close to a rectangular shape, indicating double layer capacity behaviour. The electrode showed a higher current density response than MWCNT, indicating its good charge storage performance. These results indicate that the overall capacitance of the electrode is increased because of Ni(OH)2@N-MWCNT hybrid composite. Figure 7c shows results of galvanostatic charge–discharge tests of the electrode at different current densities form 3 to 6 A g−1. Therefore, the hybrid composite showed a linear triangular-shaped curve, indicating a double-layer capacitive behaviour. Figure 7c shows specific capacitance versus current density plot. The hybrid composite showed specific capacitances of ~615, 560, 500 and 380 F·g−1 at different current densities from 3 to 6 A g−1, respectively. The specific capacitance decreased when the applied current increased due to limited movement of electrolyte ions through electrodes. The composite exhibited higher capacitance (~615 F·g−1) than pristine MWNT due to decoration of nickel hydroxides onto the surface of N-MWNT which effectively prevented agglomeration of MWNT. This may be due to increasing the ion transport and improving the EDLC behaviour of the electrode materials. Moreover, the composite showed capacitance of 380 F·g−1 when increases to 6 A·g−1, indicating its excellent rate capability. The electrode showed only 10% capacitance loss after 5000 cycles at 3 A·g−1, indicating its outstanding long-time stability. This might be due to its strong interaction with nickel hydroxides and N-MWCNT’s rapid electron transfer and charge separation as well as its excellent conductive nature.
Typical Nyquist plots of Ni(OH)2 @N-MWCNT hybrid composite electrode are shown in Fig. 7f. The plot consisted of a semicircle at high frequency region (0.1 Hz to 100 Hz). The internal resistance of the hybrid composite electrode in an open circuit condition was evaluated. In the high-to-medium frequency region, one semicircle was related to faradic reactions and charge transfer in the electrochemical reaction41,42,43,44,45. The charge transfer resistance was found to be 3.2 Ω and 15 Ω respectively, before and after cycling process which demonstrating the stable electrochemical performance nature of the prepared electrode material. Consequently, the low ESR value (straight line) in the low-frequency region might be due to incorporation of hybrid composite which enhanced electrochemical properties of N-MWCNT surface46,47,48,49.
Cyclic stability is an important factor for electrode performance of supercapacitor in the electrochemical reaction via three-electrode system. As shown in Fig. 7b, the stability of hybrid composite as an electrode material was studied by repeating continuous galvanic-charge discharge (GCD) of 3 A g−1 for 5000 cycles. The GCD cycles of the hybrid composite electrode retained about ~90% of its initial specific capacitance after 5000 cycles, demonstrating its excellent cyclic stability. The high capacitance retention implies that the hybrid composite electrode is a suitable material for high performance energy storage devices.
In addition, the flexible solid state asymmetric supercapacitor device used to study the Ni(OH)2 @N-MWCNT hybrid composite electrode for practical applications. Ni(OH)2 @N-MWCNT hybrid composite asymmetric results are shown in Fig. 8(a–e). The CV curves in the potential window between 0 and 1.2 V at different scan rates are displayed in the Fig. 8(a). When the scan rates increase from 10 to 100 mV s−1, the shapes of CV curves are similar which indicating the good rate capability of the prepared electrodes. The electrochemical properties of the as-prepared ASC device was further evaluated by GCD tests at different current densities of 0.5 to 5 A/g, as shown in Fig. 8(b). The specific capacitance of the Ni(OH)2 @N-MWCNT hybrid composite ASC device can be calculated based on the loading mass of the active materials (Fig. 8(c)). The specific capacitances are found to be ~350, 315, 282, 240, 210, 160 and 140 F g−1 at the current densities of 0.5,1, 1.5, 2, 3, 4 and 5 A g−1 respectively, and retains 90% of its initial capacitance after 5000 cycles at a current of 0.5 A g−1. Figure 8(d) shows the Ragone plots that compares the power density and energy density50,51. It is quite observed from the Fig. 8(d) that the ASC shows the maximum energy density of ~43.75 Wh kg−1 with a power density of 1500 W kg−1 at 0.5 A g−1. Its relative nyquist impedance plot is provided in Fig. 8(e). In this asymmetric electrode device even at high current density of 5 A g−1, the energy density maintains at 17.50 Wh kg−1 at a power density of 3500 W kg−1 which suggests that the prepared composite electrodes could be utilized as a prime candidate in conventional electrochemical energy storage devices.
Conclusions
In summary, Ni(OH)2@N-MWCNT hybrid composite was successfully synthesized via thermal reduction process. In this process, CTAB was an important surfactant to avoid agglomeration of nickel hydroxide particles. XRD diffraction peaks were proved to be hexagonal phase of β-Ni (OH)2. There was no impurity in the hybrid composite. BET surface area of the hybrid composite was ~250 m2 g−1, greater than pristine Ni(OH)2 sample (~108 m2 g−1). The hybrid composite showed wide pore size distribution with particle size of ~1.5–20 nm. The specific capacitance of the Ni(OH)2 @N-MWCNT hybrid composite showed the maximum specific capacitance of ~350 F g−1 at 0.5 A g−1 and retains 90% of initial capacitance after 5000 cycles. This can facilitate the migration of ions in presence of 6 M KOH electrolyte during the charge/discharge process. After 5000 cycles, only 10% of its initial capacitance was lost, demonstrating its good cyclic stability which in turn favors the way to utilize as potential candidate in high performance supercapacitors.
Materials and Methods
All chemicals and reagents were used without any distillation process. Multiwalled carbon nanotubes (MWCNT-CMP-310F, Size 10–20 nm) were purchased from Lijiang Nanotech Co. Ltd, South Korea. Nickel nitrate Ni(NO3)2·6H2O, potassium permanganate (KmnO4), urea (Sigma-Aldrich, 98%), cetyltriemthyl ammonium bromide (CTAB), Sulfuric acid (H2SO4,), ammonium hydroxide (NH4OH), potassium hydroxide (KOH), polytetrafluorethylene (PTFE), Poly vinyl alcohol (PVA)MW = 77,000 were collected from Aldrich chemical company, South Korea.
Synthesis of nitrogen doped N-MWCNT
Typical synthetic methods used to dope MWCNT materials with N include high-temperature arc-discharge process, CVD, solvothermal process (200–300 °C) and laser ablation methods were reported in detail52,53,54. Based on the thermal reduction chemical process of MWCNT synthesis as follows. MWCNT (3 g) was dispersed in DI water followed by well sonication for 2 h. The reaction solution was then added with 20 ml of ammonia and 1.2 g of urea followed by continuous stirring at 95 °C for 10 h. The resultant product of N-doped MWCNT was calcined at 350 °C for 8 h. Samples were then collected for further study.
Synthesis of Ni (OH)2@N-MWCNT decorated hybrid composite
N-MWCNT (0.25 g) was taken in to 500 ml beaker and required 100 ml of distilled water then continuously stirred for 1 h at 95 °C. Stoichiometric amounts of Ni(NO3)2·6H2O (0.74 g), cetyl ammonium bromide (1 g) and urea (0.9 g) were then added into the MWCNT solution and stirred at 95 °C. Initially, the solution became turbid due to formation of Ni(OH)2 which was dissolved by addition of surfactant. Afterwards, the resulting transparent solution was kept under vacuum in a vacuum oven at 95 °C for 12 h. The resulting composite material was purified by ethanol followed by calcination at 450 °C for 8 h. Finally, hybrid composite samples were collected and stored in a desiccator to prevent moisture effect.
Materials characterization
Ni(OH)2 @N-MWCNT hybrid composites were characterized by FTIR and RM200 confocal Raman spectro microscopy scanned in the range of 100 to 400 cm−1 in the presence of He and Ni laser beam source. XRD pattern of hybrid composite was studied using Rigaku Rotaflex (RU-200B) X-ray diffractometry in presence of Cu Kα radiation source. Morphology of the electrode was characterized by FE-TEM analysis using JEM-2010F (Hitachi S-4800, Japan). XPS analysis of hybrid composite was performed using XPS, ESCALAB 250Xi (Thermo Fisher Scientific, USA) in the presence of Al Kα radiation. Electrochemical properties of the hybrid composite were evaluated with CHI 760D (CH instrument Inc.). CV experiments were performed with the three-electrode system in the presence of 6 M KOH as strong electrolyte solution. In these experiments, the potential ranged from −0.8 to 0.2 SCE at a series of scan rates (20 to 100 mV/s). GCD curves occurred at various current densities (3, 4, 5 and 6 A/g) in the range of potential (−0.8 to 0.2). EIS analysis was characterized by using the experimental range of 0.1 Hz to 100 KHz and referring to open circuit potential. The electrochemical properties of the asymmetric cells were studied through cyclic voltammetry (CV), GCD, and EIS analyses via (VersaSTAT3 electrochemical workstation, Princeton, USA). The two-electrode system configured as counter electrode is connected together with reference electrode at same terminal.
Electrode preparation
A conventional three-electrode system (CHI 760D, CH instrument Inc.) was used to characterize Ni(OH)2 @N-MWCNT hybrid composites in presence of 6 M KOH electrolyte solution. In this experiment, active material as a working, Pt wire utilize (counter) and reference electrodes (Ag/AgCl) for CV analysis. These working electrodes were fabricated by coating Ni wire electrode with 75 wt% active materials, 20 wt% conductive agent (carbon black) and 5 wt% polyvinylidene fluoride (PVDF) using N-methylpyrrolidone (NMP) as solvent. Electrochemical performance of the prepared hybrid composite was determined using cyclic voltammetry (CV) (20–100 mV/s), galvanostatic charge-discharge (GCD) (3 to 6 A g−1) and electrochemical impedance spectroscopy (EIS) measurements (0.1 Hz to 100 KHz). Results are discussed in the following sections.
The asymmetric device were fabricated as following methods: Ni(OH)2 @N-MWCNT hybrid composites electrodes were placed in the parallel and calculated 500 μm apart, then fixed with tape and inserted into a glass tube complete with 6 M KOH electrolyte. The KIMTECH paper was soaked in 6 M KOH solution and acted as the separator. The two electrodes were prepared by using a hybrid composite, conductive carbon black, and PTFE in the mass ratio of 85:10:5. The obtained slurry was then coated onto carbon fiber paper (with an active area of exactly 1 cm2) and dried at 90 °C for 30 min. The mass of hybrid composite electrodes E1 and E2 was 14 mg and 10 mg, respectively.
References
Miller, J. R. et al. Graphene Double-Layer Capacitor with ac Line-Filtering Performance. Science (80-.). 329, 1637–1639 (2010).
Wang, H., Casalongue, H. S., Liang, Y. & Dai, H. Ni(OH)2 Nanoplates Grown on Graphene as Advanced Electrochemical Pseudocapacitor Materials. J. Am. Chem. Soc. 132, 7472–7477 (2010).
Wang, G., Zhang, L. & Zhang, J. A review of electrode materials for electrochemical supercapacitors. Chem. Soc. Rev. 41, 797–828 (2012).
Emmenegger, C. et al. Investigation of electrochemical double-layer (ECDL) capacitors electrodes based on carbon nanotubes and activated carbon materials. J. Power Sources 124, 321–329 (2003).
Ferrero, G. A., Fuertes, A. B. & Sevilla, M. N-doped microporous carbon microspheres for high volumetric performance supercapacitors. Electrochim. Acta 168, 320–329 (2015).
Le, Q., Wang, T., Zhu, S., Zhang, J. & Zhang, Y. Facile synthesis of carbon sphere@Ni(OH) 2 and derivatives for high-performance supercapacitors. Funct. Mater. Lett. 09, 1642002 (2016).
Arul, N. S. & Han, J. I. Enhanced pseudocapacitance of NiSe2/Ni(OH)2 nanocomposites for supercapacitor electrode. Mater. Lett. 234, 87–91 (2019).
Zhang, Y. X. et al. Hierarchical NiO moss decorated diatomites via facile and templated method for high performance supercapacitors. Mater. Lett. 120, 263–266 (2014).
Kirubasankar, B., Palanisamy, P., Arunachalam, S., Murugadoss, V. & Angaiah, S. 2D MoSe2-Ni(OH)2 nanohybrid as an efficient electrode material with high rate capability for asymmetric supercapacitor applications. Chem. Eng. J. 355, 881–890 (2019).
Xu, Y. et al. Holey graphene frameworks for highly efficient capacitive energy storage. Nat. Commun. 5, 4554 (2014).
Zhi, M., Xiang, C., Li, J., Li, M. & Wu, N. Nanostructured carbon–metal oxide composite electrodes for supercapacitors: a review. Nanoscale 5, 72–88 (2013).
Vijayakumar, S., Nagamuthu, S. & Muralidharan, G. Supercapacitor Studies on NiO Nanoflakes Synthesized Through a Microwave Route. ACS Appl. Mater. Interfaces 5, 2188–2196 (2013).
Saravanakumar, B., Purushothaman, K. K. & Muralidharan, G. Interconnected V2O5 Nanoporous Network for High-Performance Supercapacitors. ACS Appl. Mater. Interfaces 4, 4484–4490 (2012).
Wu, G. et al. High-performance Supercapacitors Based on Electrochemical-induced Vertical-aligned Carbon Nanotubes and Polyaniline Nanocomposite Electrodes. Sci. Rep. 7, 43676 (2017).
Cao, P., Wang, L., Xu, Y., Fu, Y. & Ma, X. Facile hydrothermal synthesis of mesoporous nickel oxide/reduced graphene oxide composites for high performance electrochemical supercapacitor. Electrochim. Acta 157, 359–368 (2015).
Liao, Q., Li, N., Jin, S., Yang, G. & Wang, C. All-Solid-State Symmetric Supercapacitor Based on Co3O4 Nanoparticles on Vertically Aligned Graphene. ACS Nano 9, 5310–5317 (2015).
Ding, S. et al. Controlled synthesis of hierarchical NiO nanosheet hollow spheres with enhanced supercapacitive performance. J. Mater. Chem. 21, 6602 (2011).
Sun, X., Wang, G., Hwang, J.-Y. & Lian, J. Porous nickel oxide nano-sheets for high performance pseudocapacitance materials. J. Mater. Chem. 21, 16581 (2011).
Ramesh, S., Haldorai, Y., Sivasamy, A. & Kim, H. S. Nanostructured Co3O4/nitrogen doped carbon nanotube composites for high-performance supercapacitors. Mater. Lett. 206, 39–43 (2017).
Jiang, Y. et al. A facile hydrothermal synthesis of graphene porous NiO nanocomposite and its application in electrochemical capacitors. Electrochim. Acta 91, 173–178 (2013).
Ke, Q. et al. Surface-Charge-Mediated Formation of H-TiO 2 @Ni(OH) 2 Heterostructures for High-Performance Supercapacitors. Adv. Mater. 29, 1604164 (2017).
Vijayakumar, S. & Muralidharan, G. Electrochemical supercapacitor behaviour of α-Ni(OH)2 nanoparticles synthesized via green chemistry route. J. Electroanal. Chem. 727, 53–58 (2014).
Huang, Q. et al. Nickel hydroxide/activated carbon composite electrodes for electrochemical capacitors. J. Power Sources 164, 425–429 (2007).
Wang, D.-W., Li, F. & Cheng, H.-M. Hierarchical porous nickel oxide and carbon as electrode materials for asymmetric supercapacitor. J. Power Sources 185, 1563–1568 (2008).
Zhang, H. et al. One-Step Electrophoretic Deposition of Reduced Graphene Oxide and Ni(OH) 2 Composite Films for Controlled Syntheses Supercapacitor Electrodes. J. Phys. Chem. B 117, 1616–1627 (2013).
Ji, J. et al. Nanoporous Ni(OH) 2 Thin Film on 3D Ultrathin-Graphite Foam for Asymmetric Supercapacitor. ACS Nano 7, 6237–6243 (2013).
Li, F. et al. Reduction of Graphene Oxide with Ni Powder for the Preparation of Ni(OH)<SUB>2</SUB>/Reduced Graphene Oxide Hybrid Electrodes for Supercapacitors. Sci. Adv. Mater. 7, 269–277 (2015).
Ramesh, S., Vikraman, D., Kim, H.-S., Kim, H. S. & Kim, J.-H. Electrochemical performance of MWCNT/GO/NiCo2O4 decorated hybrid nanocomposite for supercapacitor electrode materials. J. Alloys Compd. 765, 369–379 (2018).
Yun, J., Kim, D., Lee, G. & Ha, J. S. All-solid-state flexible micro-supercapacitor arrays with patterned graphene/MWNT electrodes. Carbon N. Y. 79, 156–164 (2014).
Yang, Z. et al. Recent Advancement of Nanostructured Carbon for Energy Applications. Chem. Rev. 115, 5159–5223 (2015).
Wang, Y. et al. High-Performance Flexible Solid-State Carbon Cloth Supercapacitors Based on Highly Processible N-Graphene Doped Polyacrylic Acid/Polyaniline Composites. Sci. Rep. 6, 12883 (2016).
Lee, J. W., Ko, J. M. & Kim, J.-D. Hierarchical Microspheres Based on α-Ni(OH) 2 Nanosheets Intercalated with Different Anions: Synthesis, Anion Exchange, and Effect of Intercalated Anions on Electrochemical Capacitance. J. Phys. Chem. C 115, 19445–19454 (2011).
Hyder, M. N. et al. Layer-by-Layer Assembled Polyaniline Nanofiber/Multiwall Carbon Nanotube Thin Film Electrodes for High-Power and High-Energy Storage Applications. ACS Nano 5, 8552–8561 (2011).
Zhu, G. et al. Polymer guided synthesis of Ni(OH)2 with hierarchical structure and their application as the precursor for sensing materials. CrystEngComm 15, 9189 (2013).
Trung, N. B. et al. Facile synthesis of three-dimensional graphene/nickel oxide nanoparticles composites for high performance supercapacitor electrodes. Chem. Eng. J. 264, 603–609 (2015).
Ganesh, V., Pitchumani, S. & Lakshminarayanan, V. New symmetric and asymmetric supercapacitors based on high surface area porous nickel and activated carbon. J. Power Sources 158, 1523–1532 (2006).
Wu, M.-S. & Hsieh, H.-H. Nickel oxide/hydroxide nanoplatelets synthesized by chemical precipitation for electrochemical capacitors. Electrochim. Acta 53, 3427–3435 (2008).
Lee, J. Y., Liang, K., An, K. H. & Lee, Y. H. Nickel oxide/carbon nanotubes nanocomposite for electrochemical capacitance. Synth. Met. 150, 153–157 (2005).
Cheng, J., Cao, G.-P. & Yang, Y.-S. Characterization of sol–gel-derived NiOx xerogels as supercapacitors. J. Power Sources 159, 734–741 (2006).
Chen, H., Zhou, M., Wang, Z., Zhao, S. & Guan, S. Rich nitrogen-doped ordered mesoporous phenolic resin-based carbon for supercapacitors. Electrochim. Acta 148, 187–194 (2014).
Zheng, Y., Ding, H. & Zhang, M. Preparation and electrochemical properties of nickel oxide as a supercapacitor electrode material. Mater. Res. Bull. 44, 403–407 (2009).
Liang, K., Tang, X. & Hu, W. High-performance three-dimensional nanoporous NiO film as a supercapacitor electrode. J. Mater. Chem. 22, 11062 (2012).
Fan, L., Tang, L., Gong, H., Yao, Z. & Guo, R. Carbon-nanoparticles encapsulated in hollow nickel oxides for supercapacitor application. J. Mater. Chem. 22, 16376 (2012).
He, X. et al. Hierarchical FeCo2O4@NiCo layered double hydroxide core/shell nanowires for high performance flexible all-solid-state asymmetric supercapacitors. Chem. Eng. J. 334, 1573–1583 (2018).
Bittencourt, C. et al. Decorating carbon nanotubes with nickel nanoparticles. Chem. Phys. Lett. 436, 368–372 (2007).
He, X. et al. High-performance all-solid-state asymmetrical supercapacitors based on petal-like NiCo2S4/Polyaniline nanosheets. Chem. Eng. J. 325, 134–143 (2017).
Xing, W., Li, F., Yan, Z. & Lu, G. Q. Synthesis and electrochemical properties of mesoporous nickel oxide. J. Power Sources 134, 324–330 (2004).
Duraisamy, N. et al. Investigation on structural and electrochemical properties of binder free nanostructured nickel oxide thin film. Mater. Lett. 161, 694–697 (2015).
Ge, D. et al. Foldable supercapacitors from triple networks of macroporous cellulose fibers, single-walled carbon nanotubes and polyaniline nanoribbons. Nano Energy 11, 568–578 (2015).
Zhao, Y. et al. Hierarchical NiCo2S4@CoMoO4 core-shell heterostructures nanowire arrays as advanced electrodes for flexible all-solid-state asymmetric supercapacitors. Appl. Surf. Sci. 453, 73–82 (2018).
Zhao, Y. et al. A flexible all-solid-state asymmetric supercapacitors based on hierarchical carbon cloth@CoMoO4@NiCo layered double hydroxide core-shell heterostructures. Chem. Eng. J. 352, 29–38 (2018).
Ramesh, S., Kathalingam, A., Karuppasamy, K., Kim, H.-S. & Kim, H. S. Nanostructured CuO/Co2O4@ nitrogen doped MWCNT hybrid composite electrode for high-performance supercapacitors. Compos. Part B Eng. 166, 74–85 (2019).
Mo, Z., Liao, S., Zheng, Y. & Fu, Z. Preparation of nitrogen-doped carbon nanotube arrays and their catalysis towards cathodic oxygen reduction in acidic and alkaline media. Carbon N. Y. 50, 2620–2627 (2012).
Szabó, A. et al. Synthesis Methods of Carbon Nanotubes and Related Materials. Materials (Basel). 3, 3092–3140 (2010).
Acknowledgements
This research was fully supported by Basic Science Research Program through National Research Foundation (NRF-2017R1D1A1B03028368), under the Ministry of Education, and Institute for Information & communications Technology Promotion (IITP) grant funded by the Korea government (MSIP) (No. R75201600050001002) and also supported under the framework of 2017 international cooperation program (GRDC- INHA IST-NASA Joint Research Center) through National Research Foundation by Ministry of Science and ICT of Korea (Grant No: 2017K1A4A3013662).
Author information
Authors and Affiliations
Contributions
S.R., K.K. and H.S.K. design the project and the experiments. S.R. and K.K. carried out the experiments. All authors S.R., K.K., H.M.Y., J.-J.L., H.-S.K., H.S.K. and J.-H.K. involved to the characterization of the materials and the discussions prominent up to the writing of the manuscript. S.R. and H.S.K. took part in the main discussions that led to the final manuscript; all authors read and finalized the final manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ramesh, S., Karuppasamy, K., Yadav, H.M. et al. Ni(OH)2-decorated nitrogen doped MWCNT nanosheets as an efficient electrode for high performance supercapacitors. Sci Rep 9, 6034 (2019). https://doi.org/10.1038/s41598-019-42281-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-42281-z
- Springer Nature Limited
This article is cited by
-
Durable superhydrophobic/superoleophilic melamine foam based on biomass-derived porous carbon and multi-walled carbon nanotube for oil/water separation
Scientific Reports (2023)
-
Advances in Supercapacitor Development: Materials, Processes, and Applications
Journal of Electronic Materials (2023)
-
Magnetic patterning of Co/Ni layered systems by plasma oxidation
Scientific Reports (2022)
-
Photoelectrochemical reduction of dissolved carbon dioxide over Ni(OH)2 into organic oxygenates
Journal of the Iranian Chemical Society (2021)
-
Porous materials of nitrogen doped graphene oxide@SnO2 electrode for capable supercapacitor application
Scientific Reports (2019)