Abstract
The development of a fast semiconductor laser is required for the realization of next-generation telecommunication applications. Since lasers operating on quantum dot ground state transitions exhibit only limited gain due to the saturation effect, we investigate lasing from excited states and compare its corresponding static and dynamic behavior to the one from the ground state. InAs quantum dots (QDs) grown in dot-in-well (DWELL) structures allowed to obtain light emission from ground and three excited states in a spectral range of 1.0–1.3 μm. This emission was coupled to whispering gallery modes (WGMs) of a 6 μm microdisk resonator and studied at room temperature by steady-state and time-resolved micro-photoluminescence. We demonstrate a cascade development of lasing arising from the ladder of quantum dot states, and compare the lasing behavior of ground and excited state emission. While the lasing threshold is being increased from the ground state to the highest excited state, the dynamic behavior is improved: turn-on times and lifetimes of WGMs become shorter paving the way towards high frequency direct driven microlasers.
Similar content being viewed by others
Introduction
The current interest in modern nanophotonics has motivated numerous studies of microcavity lasers based on microdisks and microrings1. Cavities with rotational symmetry support high-quality factor (Q) whispering gallery modes (WGMs) and exhibit advantages such as low threshold, small foot-print, small mode volume, and control of in-plane emission wavelength by the cavity diameter2,3. In WGMs, the mode fields are concentrated within several hundreds of nanometers from the disk’s edge and allow for efficient coupling with emitters placed there. Self-organized InGaAs quantum dots (QDs) formed in a GaAs matrix and emitting in the near infrared (NIR) region are very attractive for high-speed telecom applications4,5. Such QDs cause strong carrier localization that provides high temperature stability, elevated operating temperatures, and high signal-to-noise ratios6. This is of special interest for nanophotonic applications to avoid increased carrier recombination at the surfaces of small resonators. However, the optical gain from the ground state (GS) transition in QDs is limited due to the finite number of carriers in the QD ground state (two electrons on an s-like level). The problem of gain saturation can be overcome by the employment of excited states (ES). While the lasing at WGMs from GS transitions in QD cavities were theoretically and experimentally thoroughly investigated7,8,9,10,11,12, the lasing from ES in a QD laser microcavity has not yet been well studied. This is partly due to the fact that it is quite difficult to obtain large defect-free QDs with a well-defined set (ladder) of optical transitions.
Lasing dynamics is a decisive characteristic of cavity lasers for telecom applications and especially the turn-on dynamics is important for high data rate transmission13. Nevertheless, up to now the dynamics of WGMs in microdisks of small diameters was not sufficiently investigated. The temporal response of QD microdisk lasers characterized by a turn-on delay time and the radiative lifetime is hardly known. Gain-switched QD lasers show a fast dynamical response, which is characterized by the turn-on delay time, as well as damped relaxation oscillations14. Nevertheless, the explanation of the underlying dynamical processes is still under discussion.
In this work, we investigate lasing in microdisks, 6 μm in diameter, with a dot-in-well (DWELL) structure as active medium. The direct deposition of InGaAs quantum wells (QWs) on InAs QDs allowed growing large-scale defect-free QDs with a set of states ranging from GS (transition at 1.3 μm) up to the third excited state (ES3) with an emission peak near 1 μm. Thus, we achieve two goals simultaneously: a lasing wavelength of 1.3 μm that is relevant for telecom and the presence of several excited states in the QDs, which allows us to make a direct comparison of lasing on different QD states. Applying steady-state and time-resolved micro-photoluminescence measurements we investigate the spectral distribution as well as the dynamic behavior of the stimulated emission in this system. We present a complementary study on the kinetics of a complex QD band structure, and for practical applications, i.e. telecom lasers on excited states, the entire scheme can be shifted to lower energies by varying the QD size.
The paper is organized as follows: after the description of methods used in this study, we present steady-state and time-resolved luminescence of the unprocessed epitaxial substrate, which leads to the cascade model of the carrier relaxation in the QDs. Then we show the coupling of the QD emission to the WGMs of a microdisk fabricated on the substrate. Next, we present a static lasing in the microdisk, which allows obtaining Q-factors and threshold powers for lasing on different QD optical transitions. And in the last section, we discuss the lasing dynamics of the microdisk and identify the maximum modulation frequency and damping factor of the laser.
Methods
Sample preparation
Epitaxial structures were grown by molecular beam epitaxy on a semi-insulating GaAs (100) substrate. The active region comprised five layers of DWELL (In0.15Ga0.85As QWs deposited directly on InAs QDs) separated by 35 nm GaAs spacers. This active area was surrounded on both sides by 20 nm thick Al0.3Ga0.7As barriers and placed in the middle of a 330 nm thick GaAs waveguide layer grown on top of a 450 nm Al0.98Ga0.02As cladding layer.
Microdisks of a 6 μm diameter were fabricated using photolithography and reactive ion etching. After that, the 450 nm thick Al0.98Ga0.02As layer was transformed into (AlGa)xOy layer by a selective oxidation process to ensure the optical confinement from the substrate side. A schematic cross-section (a) and scanning electron microscope image of the grown structure (b) are shown in Fig. 1. The lateral density of QDs in each layer of 3.5 × 1010 cm−2 has been determined from plan-view TEM data (not shown). Thus, the total number of QDs in the disk is N0 = 5 × 104.
Micro-photoluminescence
The single microdisks under investigation were characterized by micro-photoluminescence (μPL) at ambient temperature. To prevent heating, the sample was attached to a Peltier element. An exciting laser spot was focused on the microdisk’s surface by a 100× microscope objective (Mitutoyo, M Plan APO NIR HR) with a numerical aperture NA = 0.7. Both steady-state PL (CWμPL) for light-in/light-out measurements and time-resolved PL (TRμPL) for the study of the dynamics were carried out in a back-scattering geometry, i.e. emitted light was collected from the disk plane by the same objective (normal incidence) and directed by mirror optics into a grating monochromator.
CWμPL was excited by the second harmonic of a cw-operating YAG:Nd laser with a wavelength of 532 nm. The static lasing behavior of the WGMs (light-in/light-out dependence) was investigated by measuring the PL spectra as a function of pump power. For this, a set of neutral density filters with a 0.1-optical density step was used to adjust the excitation power. We consider light-in power on disk, i.e. power brought to the active DWELL area without taking into account reflection losses and internal losses in the disk. Collected PL light was focused on the entrance slit of a 0.5-m grating monochromator (Acton Research SP-2500) and detected by a liquid-nitrogen cooled NIR-CCD with a linear InGaAs photodiode array (Princeton Instruments OMA-V/LN 1024) with a cut-off wavelength of 1.7 μm. The grating (1200 grooves/mm) and entrance slit width (25 μm) combined with the CCD dispersion (25 pm/pixel) provided a spectral resolution of 45 pm.
TRμPL was excited by a 775-nm fundamental emission line from a mode-locked Ti:Sapphire laser (Spectra-Physics “Tsunami”, repetition rate 80 MHz, pulse width 100 fs). The resulting PL was dispersed by a 0.3-m grating monochromator (Acton Research SP-2300) and recorded by a synchroscan streak-camera (Hamamatsu C5680) with NIR-enhanced S1 photocathode. The cathode’s spectral response in the NIR range from 1000 to 1300 nm is characterized by a drop in sensitivity by two orders of magnitude. The spectral resolution is about 1 nm at the central wavelength (1.15 μm). The temporal resolution is better than 10 ps. An acceptable signal-to-noise ratio of the PL signal was achieved at the time-averaged light-in power of 50 μW in the analog integration acquisition mode of the streak camera. This corresponds to 0.6 pJ per pulse, which creates about 2 × 106 electron-hole pairs. The 100× objective focuses the excitation light on a spot of ∼1 μm diameter on the sample. The penetration depth of the excitation pulse (780 nm) in the GaAs is ∼1 μm. As the diffusion length of electrons in lightly doped GaAs (up to 20 μm15) exceeds the disk size, a quasi-homogeneous non-equilibrium carrier concentration 2 × 1017 cm−3 in the microdisk can be assumed, which amounts to about 106 electron-hole pairs in the active area. This is equivalent to 20 electron-hole pairs per QD.
WGM modeling
Microdisk WGMs were modeled using the finite-element method by solver COMSOL multiphysics (eigenfrequency analysis) utilizing azimuthal symmetry16. The active area was set as a homogeneous GaAs medium with optical constants taken from ref.17. The (AlGa)xOy pedestal was modeled as a lossless homogeneous medium with the refractive index of 1.6. The microdisk and the pedestal were surrounded by air.
Results and Discussion
PL from as-grown DWELL sample
Since there is no cavity present in the unstructured DWELL sample, lasing does not yet occur and the PL signal discussed in this section corresponds to the spontaneous emission from the QDs. CWμPL spectra of the as-grown InGaAs DWELL structure for various light-in power on the disk are shown in Fig. 2a. One can see the broadening of the PL signal with the increase of the excitation power, and the presence of several maxima, which reflect quantum energy-levels of different states in the epitaxial structure (a schematic of the QD optical transitions is shown in Fig. 2c). For low power (P = 1 μW), the PL response occurs close to 1.3 μm corresponding to optical transitions between electron-hole ground states (GSs) of the QDs. The luminescence profile is related to the size distribution of the QDs and characterized by the full width at half maximum (FWHM) of 40 nm (30 meV). Increasing light-in power leads to the sequential filling of excited states ES1, ES2, and ES3 up to QW states.
Due to the inhomogeneous broadening of the levels, PL bands overlap and the total signal is spectrally “blurred”. In order to analyze the population of QD electron levels, measured PL spectra were deconvoluted by four Gaussians corresponding to optical transitions from different QD states. The capacity of QD electron states according to the simplified atomic model grows as 2(s)/6(p)/10(d)/14(f). In comparison, the integrated PL intensity ratio of Gaussians for 250 μW light-in CW-power (Fig. 2a) is 2(GS)/2(ES1)/1(ES2)/0.2(ES3), while an analogous deconvolution for the 1750 μW CW-power gives the intensity ratio 2/2.5/2/1.5. For the pulsed power, the ratio is 2/3/6/4. These ratios imply that even for the highest pump power the excited states are not completely filled, which agrees with the 20 electron-hole pairs per QD estimation made in Methods section.
We characterize the temporal behavior of the luminescence by PL decay time τD and PL delay time Δt obtained from high-excitation TRμPL and shown in Fig. 2b. Under high-excitation conditions, the channels of non-radiative defect-assisted recombination are saturated and, therefore, can be neglected. In this case, the temporal profile can be fitted by one exponent, and the PL decay time will be mainly governed by the radiative lifetime of the as-grown DWELL structure. Such fit was done for each 10-nm spectral region of interest. With the same step, the PL delay time Δt was determined from the temporal profiles as an interval between the excitation peak (t = 0) and the maximum of the PL signal. Both characteristics show the slowing of the PL response for transitions between deeper QD levels. The radiative lifetime τD increases from 210 ps for ES3 to 1800 ps for GS transitions, and the delay time Δt also grows from 20 ps to 130 ps. These observations can be explained with the help of the transition cascade in Fig. 2c. After excitation, a large part of the excited electron-hole pairs occupy conduction and valence band levels in the GaAs waveguide and the QW-region of the microdisk. They relax first into the highest QD-levels (e.g. the f-level in Fig. 2c), so that the occupation of these excited QD-levels rises first resulting in the quick onset of the observed high energy (short wavelength) ES3 radiative transition. However, this transition is relatively short-lived since the carriers can relax further to several lower lying QD-levels emptying the highest QD-level. The strong competition of these intersubband relaxation channels with the radiative ES3 transition results in the short ES3-decay time of (τD = 210 ps). Next the slightly lower lying QD-d-level is filled giving rise to the radiative ES2-transition, which noticeably starts after the onset of the ES3-transition. However, also for this level, the intersubband relaxation to the lower p- and s- QD-levels competes with the radiative ES2-transition leading to a further trickling down of the excited carriers. This cascade of intersubband transitions - subsequently filling and emptying the different QD-levels - results in the stepwise increase of the delay times for the transitions ES3, ES2, ES1, and GS. When the remaining carriers reach the GS the cascade comes to an end and only the low energy radiative GS-transition occurs. Since this does not compete anymore with intersubband relaxation channels the GS- level exhibits the largest lifetime (τD = 1800 ps).
PL from a microdisk with embedded DWELL structure
A typical time-integrated μPL spectrum of a disk fabricated on the DWELL structure is shown in Fig. 3a. The transformation of the DWELL PL is evident: the broad bands turn into narrow lines due to the coupling of the QD emission to WGMs. Their spectral positions correspond to the wavelengths for which the resonance condition is satisfied, and a standing wave is formed by a defined number of internal reflections on the side wall of the microdisk. In order to identify dominant resonances in the PL spectrum, Fig. 3a also shows TE WGMs simulated by a finite-element method (vertical lines). Additional peaks correspond to higher order TE- or TM-modes. The mode profiles (normalized electric field) for TE and TM WGMs are shown in Fig. 3b,c and demonstrate the concentration of the WGM mode fields near the rim of the microdisks.
The far-field PL of microdisks exhibits the directional character of WGM emission2,18. Due to the radiation leakage through the side walls of the disk, the emission pattern of WGMs has a sharp maximum in the disk plane and no oblique components. This means, that in the back-scattering geometry used here, we should not detect WGM emission. However, Fig. 3 clearly shows the presence of the WGM-related peaks. We attribute this to the light scattering in a “non-ideal” microdisk, which enables emission along the oblique directions that can be collected by the high NA microscope objective. We performed PL measurements in two geometries: excitation at the 90°-angle (along the normal), collection at the same 90°-angle (back-scattering geometry); excitation like the previous one (90°), collection at the 7°-angle (with respect to the disk plane), and compared WGM intensities. It turned out that up to one-quarter of the maximum possible PL signal was collected in the case of back-scattering geometry. This confirms the presence of strong scattering and agrees with the data obtained in ref.18, where the angular dependence of WGM emission from the microdisks with GaAs QWs was measured.
The scattering was attributed to side-wall and surface roughness of the fabricated microdisks. Moreover, in our samples, the emitting medium consists of InAs QDs embedded in the GaAs-based waveguide. The QDs act as scattering centers due to the different refractive indices. The presence of scattering centers is disadvantageous for resonant characteristics, namely, it can lead to the decrease of a quality factor (Q-factor) and, hence, broadening of WGM lines19. For embedded nanoparticles (QDs), scattering also results in a splitting of WGM lines into doublets20,21. This splitting is caused by the lifting of the two-fold degeneracy of clockwise and counter-clockwise WGM waves22,23. The splitting of the TM38.1 WGM (1296 nm) into a doublet is demonstrated in Fig. 3d for CW-excitation. The doublet was deconvoluted into two Lorentzians exhibiting a spectral splitting of 130 pm and a FWHM of 90 pm for both components.
Besides the splitting of the WGM modes, we have checked the spatial localization of the WGM modes by varying the position of the excitation/collection spot. The change of the TRμPL spectrum by moving the 1 μm wide excitation spot from the center to the periphery of the disk (Fig. 4a,b) is shown in Fig. 4c,d. When the excitation spot is placed at the disk center (4a), only Fabry-Perot modes (FPMs) are detected as broad and long oscillatory traces in the emission spectrum. The FPMs are formed by the radial propagation of the light between the disk center and the reflecting rim of the microdisk. For an excitation near the rim of the microdisks (4b) mainly the WGMs are excited (narrow short spots on the detection panel d) and the FPMs give only a minor contribution to the emission field at the periphery of the disks.
The resonances exhibit a “red” shift during the emission process, which appears in TRμPL spectra as inclined traces (Fig. 4c,d). This behavior is attributed to the increase of refractive index Δn of the microdisk during the emission process. This can be explained by the decay of the non-equilibrium carrier concentration ΔN due to the recombination after the excitation pulse. The carrier-induced change of n is characterized by the Δn/ΔN ratio, which varies from −7 × 10−21 to −3 × 10−22 cm3 in literature24. As it follows from the WGM modeling, the overall shift of ∼1 nm measured for WGMs in Fig. 4d corresponds to the change of the refractive index of Δn ∼0.0015. This allows us to estimate the pulse-induced concentration of nonequilibrium carriers in the microdisk cavity ΔN = (2–50) × 1017 cm−3, which agrees with the value of 2 × 1017 cm−3 obtained from the absorbed power (see Methods section).
CW lasing in DWELL microdisk
WGM cw lasing was investigated by measuring CWμPL light-in/light-out power dependence of the PL. Inset in Fig. 5a shows such dependence for TE41,1 WGM. It exhibits a sudden increase in the peak intensity that indicates the achievement of the lasing threshold. Similar threshold behavior was also observed for other resonances. The following dominant WGMs were chosen to characterize the lasing from the different states of QDs: TE41,1 (1278 nm) for GS, TE44,1 (1207 nm) for ES1, TE49,1 (1108 nm) for ES2, and TE55;1 (1001 nm) for ES3. The WGM peaks were fitted by Lorentzians, and their integrated intensity is shown in Fig. 5a. The threshold power (Pth) was determined as a kink in the integrated intensity and is indicated with yellow arrows. One can see that excited states require higher excitation power to achieve lasing. The cascade development of lasing originates from the ladder of QD states. A comparison of the threshold values (Fig. 5a) with the power dependence of as-grown DWELL PL (see the last section) leads us to a conclusion that the lasing on the ES transitions does not require the complete filling of the corresponding QD states.
Along with the nonlinear increase in the emission intensity, a narrowing of the emission peaks occurs (Fig. 5b). The FWHM at the “empty cavity” limit was determined for peaks at an excitation intensity just one filter step (optical density = 0.1) below the lasing threshold. The FWHM-values, in this case, are used to determine the Q-factor of the cavity before the emission is governed by stimulated emission. Using the obtained Q-factors, Purcell factor was calculated as \({F}_{{\rm{p}}}=\frac{3}{4{\pi }^{2}}\frac{Q}{{V}_{{\rm{m}}}}{(\frac{\lambda }{{n}_{{\rm{eff}}}})}^{3}\), where neff is the effective refractive index (we took the constant value neff = 3.5 for GaAs). The mode Volume Vm was obtained from numerical modeling as the ratio of the total electric energy in the microdisk and the maximum value of the electric energy density \({V}_{m}=\frac{{\int }_{V}\varepsilon (\overrightarrow{r}){|\overrightarrow{E}(\overrightarrow{r})|}^{2}{d}^{3}r}{{\rm{\max }}(\varepsilon (\overrightarrow{r}){|\overrightarrow{E}(\overrightarrow{r})|}^{2})}\). The lasing characteristics of WGMs for different QD states are summarized in Table 1; the transient behavior of the luminescence is described below.
Lasing dynamics of WGMs
For TRμPL measurements of microdisks, a 50 μW (time-averaged) power pulsed excitation was used corresponding to 0.6 pJ; the temporal and spectral resolutions were 10 ps and 1 nm, respectively. A comparison with the CW spectra in Fig. 5a clarifies that these TRμPL measurements were made above the lasing threshold.
WGM lifetime
Figure 4e compares the transient behavior of the PL from an as-grown DWELL structure and from the microdisk. The ES2 QD transition (λ = 1088 nm) in an as-grown DWELL-structure has a long lifetime of \({\tau }_{{\rm{D}}}^{{\rm{sp}}}\) = 600 ps (shown with gray circles). When the microdisk is excited at the center the luminescence curve at the same wavelength of 1088 nm exhibits a shorter spontaneous emission lifetime of \({\tau }_{{\rm{D}}}^{{\rm{FPM}}}\) = 150 ps (solid orange line). This is connected with the excitation of the FPM as discussed before. The PL decay profile of the TE50,1 WGM (blue solid line) is obtained when the excitation spot is moved to the rim of the disk. It shows a more complex profile which consists of the peaked WGM emission with \({\tau }_{{\rm{D}}}^{{\rm{st}}}\) = 30 ps, and the underlying rather flat FPM emission (blue dotted line). The onset of the WGM lasing is delayed relative to underlying the spontaneous FPM emission and appears 100 ps after the excitation pulse forming the steep peak on top of the FPM emission. Summarized TRμPL data for WGMs corresponding to different QD optical transitions are collected in Table 1 and in Fig. 6c. The radiative lifetime \({\tau }_{{\rm{D}}}^{{\rm{st}}}\) for the WGM lasing emission (Fig. 6c) shows the same trend as the radiative lifetime \({\tau }_{{\rm{D}}}^{{\rm{sp}}}\) of the as-grown, unstructured DWELL-structures (Fig. 2b): the shortest lifetime for the highest excited state, and the longest lifetime for the ground state.
WGM delay time
The appearance of emission in the WGM as a response to the pulsed excitation arises after a delay time Δtst (see Fig. 6b,c). For selected modes, Δtst are listed in Table 1 . Often the lasing delay is related to the time that photons stay inside the cavity, which is known as photon lifetime within cavity τph. Using the second definition of Q-factor as the ratio of the stored photon energy in the cavity to the energy loss per photon cycle25, τph can be expressed as \({\tau }_{{\rm{ph}}}=\frac{Q}{\omega }=\frac{1}{2\pi cn}\frac{{\lambda }^{2}}{{\rm{\Delta }}\lambda }\), where ω is the cyclic photon frequency, c is the speed of light. For all investigated wavelengths, τph is about 2 ps, which agrees with the value reported in ref. 26 but does not differ much for the considered wavelengths. Since in our case the observed delay times are one or two orders of magnitude larger and also show a clear wavelength dependence, they have to be governed by another process. We attributed the observed Δtst to the time that the population inversion takes to build up to satisfy the lasing conditions. This can be understood with the help of the relaxation cascade from Fig. 2b. After the excitation, electrons relax from the continuum to the nearest (highest) QD level within 1–10 ps27, so that the population inversion can build up in this level and lasing starts at the ES3-transition having only a very short turn-on delay of Δtst = 20 ps. After further relaxation of the carriers down, the cascade population inversion is next reached for the ES2-transition whose turn-on delay is already 100 ps relative to the excitation time. After population inversion for the ES1-transition is reached, finally also population inversion and lasing occurs at the GS. Since this is the final state of the relaxation cascade all remaining carriers will finally end up there and the GS, therefore, offers the longest lasing pulse (\({\tau }_{{\rm{D}}}^{{\rm{st}}}\) = 125 ps). The turn-on dynamics of QD lasers is important for fast data transmission systems. These results demonstrate that a fast dynamical response should rely on the emission from excited states (ES1–3). Charge carriers are collected first in these excited states leading to short turn-dynamics. Furthermore, their emission is quenched effectively by the carrier relaxation to lower lying QD-states resulting in a potentially high modulation speed. The drawback is the higher threshold power necessary to obtain population inversion and lasing in these states.
Damped relaxation oscillations of ES3 WGMs
In the case of a slightly defocused excitation laser beam, we observed the oscillation of ES3-WGM-intensity in TRμPL measurements, which is shown in Fig. 7. The damped relaxation oscillations are well known for electrically driven semiconductor lasers28,29 and occur due to the dynamic interaction between the photons and the carriers.
This modulation of the emission intensity can be explained by the out-of-phase correlation between the evolving photon and carrier densities30. An increasing number of photons in the cavity leads to the fast depletion of excited carriers by stimulated emission. When the population inversion is then run down, lasing stops and the number of photons decreases. However, subsequently the carrier density inside the QD can recover if there are enough carriers in the surrounding of the QDs leading to a new population inversion, and the cycle repeats resulting in an oscillation of the luminescence intensity. However, on average, emission intensity decays in an asymptotic manner as the number of charge carriers once excited is limited. These oscillations are important features of laser dynamics and limit the frequency with which a laser can be modulated; for high-frequency lasers, it is desired to have no damped relaxation oscillations.
We observed such damped relaxation oscillations with a period of 75 ps, i.e. relaxation frequency fR = 13 GHz. A damping time of 40 ps was determined from the exponential fit of the intensity decay (dotted line in Fig. 7b). Following the formalism for the electrically driven lasers28,31,32,33, we introduce the following parameters: damping factor γ = 25 GHz (reciprocal of the decay period), modulation factor K, and maximal modulation bandwidth fM. These quantities relate to each other through equations \(\gamma =K{f}_{{\rm{R}}}^{2}\) and \({f}_{{\rm{M}}}=\sqrt{1+\sqrt{2}}\cdot {f}_{{\rm{R}}}\). Substituting experimental values of fR and γ in the equations above, we find K-factor and maximal modulation frequency: K = 150 ps and fM = 20 GHz.
Conclusion
A comparison of the lasing behavior of the whispering gallery modes on the ground and excited states of quantum dots in dot-in-well (DWELL) structure covering a spectral range of 1.0–1.3 μm was carried out. Optically pumped single microdisks with a diameter of 6 μm were measured at room temperature by steady-state and time-resolved micro-photoluminescence. Due to the large sizes of the investigated QDs, several higher QD-states exist. This has a crucial impact on the observed emission spectra and dynamics. Investigating the static and dynamic behavior of the lasing from GS and three ESs, we demonstrated a cascade nature of the excitation relaxation. We show that more power is required to reach the lasing threshold for the higher QD states deteriorating the cw characteristics of the lasing from these excited states. In contrast, the dynamic behavior is improved from GS towards ES3: turn-on times and lifetimes of WGMs become shorter resulting in accelerated lasing dynamics from QD excited states.
Data Availability
All data generated or analyzed during this study are available upon a request.
References
He, L., Özdemir, Ş. K. & Yang, L. Whispering gallery microcavity lasers. Laser & Photonics Rev. 7, 60–82 (2012).
McCall, S. L., Levi, A. F. J., Slusher, R. E., Pearton, S. J. & Logan, R. A. Whispering-allery mode microdisk lasers. Applied Physics Lett. 60, 289–291, https://doi.org/10.1063/1.106688 (1992).
Slusher, R. E. et al. Threshold characteristics of semiconductor microdisk lasers. Applied Physics Lett. 63, 1310–1312, https://doi.org/10.1063/1.109714 (1993).
Cao, H. et al. Optically pumped InAs quantum dot microdisk lasers. Applied Physics Lett. 76, 3519–3521, https://doi.org/10.1063/1.126693 (2000).
Maximov, M. V. et al. Ultrasmall microdisk and microring lasers based on InAs/InGaAs/GaAs quantum dots. Nanoscale Research Letters 9, 657, https://doi.org/10.1186/1556-276X-9-657 (2014).
Ngo, C. Y., Yoon, S. F., Lim, C. S., Wong, V. & Chua, S. J. Effect of growth temperature on the thermal stability of 1.3μm InAs/InGaAs/GaAs quantum dot structures. In 20th International Conference on Indium Phosphide and Related Materials, 1–3, http://ieeexplore.ieee.org/document/4702946/ (IEEE, 2008).
Michler, P. et al. Laser emission from quantum dots in microdisk structures. Applied Physics Lett. 77, 184–186, https://doi.org/10.1063/1.126918 (2000).
Kryzhanovskaya, N. V. et al. Room Temperature Lasing in 1-μm Microdisk Quantum Dot Lasers. IEEE J of Sel Top in Quantum Electron 21, 709–713, http://ieeexplore.ieee.org/document/7115038/ (2015).
Srinivasan, K. & Painter, O. Linear and nonlinear optical spectroscopy of a strongly coupled microdisk-quantum dot system. Nature 450, 862–865, http://www.nature.com/articles/nature06274 (2007).
Srinivasan, K. et al. Optical loss and lasing characteristics of high-quality-factor AlGaAs microdisk resonators with embedded quantum dots. Applied Physics Letters 86, 151106, https://doi.org/10.1063/1.1901810 (2005).
Zhang, L. & Hu, E. Lasing from InGaAs quantum dots in an injection microdisk. Appl. Phys. Lett. 82, 319–321, https://doi.org/10.1063/1.1538312. (2003).
Li, Q. et al. 13-μm InAs quantum-dot micro-disk lasers on V-groove patterned and unpatterned (001) silicon. Opt. Express 24, 21038, https://doi.org/10.1364/OE.24.021038 (2016).
Lüdge, K. et al. Turn-on dynamics and modulation response in semiconductor quantum dot lasers. Physical Review B 78, 035316, https://doi.org/10.1103/PhysRevB.78.035316. (2008).
Olshansky, R., Lanzisera, V., Su, C. B., Powazinik, W. & Lauer, R. B. Frequency response of an InGaAsP vapor phase regrown buried heterostructure laser with 18 GHz bandwidth. Appl. Phys. Lett. 49, 128–130, https://doi.org/10.1063/1.97620 (1986).
Aukerman, L. W., Millea, M. F. & McColl, M. Diffusion lengths of electrons and holes in gaas. J. of Appl. Phys. 38, 685–690, https://doi.org/10.1063/1.1709396 (1967).
Oxborrow, M. How to simulate the whispering-gallery modes of dielectric microresonators in FEMLAB/COMSOL. 64520J, https://doi.org/10.1117/12.714954. (2007).
Skauli, T. et al. Improved dispersion relations for GaAs and applications to nonlinear optics. J. of Appl. Phys. 94, 6447–6455, https://doi.org/10.1063/1.1621740 (2003).
Peter, E. et al. Highly directional radiation pattern of microdisk cavities. Appl. Phys. Lett. 91, 151103, https://doi.org/10.1063/1.2789956 (2007).
Zhu, J. et al. On-chip single nanoparticle detection and sizing by mode splitting in an ultrahigh-Q microresonator. Nat. Photonics 4, 46–49, http://www.nature.com/articles/nphoton.2009.237 (2010).
Hiremath, K. R. & Astratov, V. N. Perturbations of whispering gallery modes by nanoparticles embedded in microcavities. Opt. Express 16, 5421 https://www.osapublishing.org/oe/abstract.cfm?uri=oe-16-8-5421 (2008).
Jones, B. D. et al. Splitting and lasing of whispering gallery modes in quantum dot micropillars. Optics Express 18, 22578 https://www.osapublishing.org/oe/abstract.cfm?uri=oe-18-21-22578 (2010).
Kippenberg, T. J. Particle sizing by mode splitting. Nat. Photonics 4, 9–10, http://www.nature.com/articles/nphoton.2009.246 (2010).
Jaffrennou, P. et al. Whispering gallery mode lasing in high quality GaAs/AlAs pillar microcavities. Appl. Phys. Lett. 96, 071103, https://doi.org/10.1063/1.3315869 (2010).
Dutta, N. K., Olsson, N. A. & Tsang, W. T. Carrier induced refractive index change in AlGaAs quantum well lasers. Appl. Phys. Lett. 45, 836–837, https://doi.org/10.1063/1.95418 (1984).
Band, Y. Light and Matter, Volume 1, Electromagnetism, Optics, Spectroscopy and Lasers (2006).
Luo, K. J. et al. Ultrafast dynamics of InAs/GaAs quantum-dot microdisk lasers. Appl. Phys. Lett. 78, 3397–3399, https://doi.org/10.1063/1.1376437 (2001).
Yuan, Z. Many-body effects in carrier capture and energy relaxation in self-organized InAs/GaAs quantum dots. Phys. B: Condens. Matter 272, 12–14, http://linkinghub.elsevier.com/retrieve/pii/S0921452699002343 (1999).
Petermann, K. Laser Diode Modulation and Noise, https://doi.org/10.1007/978-94-009-2907-4. (Springer Netherlands, Dordrecht, 1988).
In Kapon, E. (ed.) Semiconductor Lasers I, Optics and Photonics, http://www.sciencedirect.com/science/article/pii/B978012397630750007X (Academic Press, San Diego, 1999).
Coldren, L. A., Corzine, S. W. & Mašanović, M. L. Diode Lasers and Photonic Integrated Circuits, https://doi.org/10.1002/9781118148167 (John Wiley & Sons, Inc., Hoboken, NJ, USA, 2012).
Uomi, K., Aoki, M., Tsuchiya, T., Suzuki, M. & Chinone, N. Dependence of relaxation oscillation frequency and damping k factor on the number of quantum wells in 1.55 mu m ingaasp dfb lasers. IEEE Photonics Technol. Lett. 3, 493–495 (1991).
Olshansky, R., Hill, P., Lanzisera, V. & Powazinik, W. Frequency response of 1.3μm ingaasp high speed semiconductor lasers. IEEE J of Quantum Electron. 23, 1410–1418 (1987).
Kuntz, M. et al. Spectrotemporal response of 1.3 μm quantum-dot lasers. Applied Physics Letters 81, 3846–3848, https://doi.org/10.1063/1.1521572 (2002).
Acknowledgements
V.R. and J.S. thank the Federal Ministry for Education and Research (“Bundesministerium für Bildung und Forschung”, Project N. 03Z2HN12) for their financial support within the Centre for Innovation Competence SiLi-Nano. V.R. acknowledges Prof. Eli Kapon, Prof. Frank Jahnke, and Dr. Christopher Gies for the fruitful discussions. This work was supported by the Russian Science Foundation (“Epitaxial growth, MD process and characterization”, grant N. 18-12-00287).
Author information
Authors and Affiliations
Contributions
J.W.T., J.S. and A.Z. supervised the project, V.T., V.R. and J.S. wrote the manuscript, V.T. and N.K. measured the PL spectra, V.R. performed the WGM modeling. All authors contributed equally to the manuscript preparation. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Talalaev, V., Kryzhanovskaya, N., Tomm, J.W. et al. Dynamics of Broadband Lasing Cascade from a Single Dot-in-well InGaAs Microdisk. Sci Rep 9, 5635 (2019). https://doi.org/10.1038/s41598-019-41307-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-41307-w
- Springer Nature Limited
This article is cited by
-
Quantum-dot microlasers based on whispering gallery mode resonators
Light: Science & Applications (2021)