Abstract
Inspired by nature, this paper investigates the effect of biomolecules, such as amino acids and proteins, on the nanostructure and mechanical stiffness of calcium-silicate-hydrate (C-S-H). Amino acids with distinct functional groups, and proteins with different structures and compositions were used in the synthesis of the C-S-H nanocomposite. The atomic structure was examined using X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). The morphology was investigated using scanning electron microscopy (SEM) and atomic force microscopy (AFM). AFM nanoindentation was used to evaluate the Young’s modulus of the modified C-S-H. Positively charged, H-bond forming and hydrophobic amino acids were shown to influence the atomic structure of C-S-H. The effect of negatively charged amino acid on atomic structure was more pronounced at higher C/S ratio. A noticeable increase in silicate polymerization of C-S-H modified with proteins at high C/S ratio was observed. The microscopic examination demonstrated a globular morphology for all samples except for C-S-H modified with hemoglobin, which showed a platelet morphology. The Young’s modulus of C-S-H with amino acids and proteins showed a general reduction compared to that of the control C-S-H.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Certain biological composites, such as bones, teeth, and nacre of abalone shells, exhibit superior mechanical and physical performance unmatched by engineering materials1,2,3. This is attributed to the interaction between organic and inorganic materials governing the microstructure of these materials. Inspired by nature, there have been intense research efforts to understand the underlying mechanisms for superior mechanical and physical properties of biological nanocomposites1,4,5,6. A major goal of these studies is to enable synthesis of materials with improved mechanical and functional properties exceeding those of traditional engineering materials.
Concrete is the most widely used infrastructure material and its production is expected to increase at a rate of 5% annually7. Calcium silicate hydrate (C-S-H) is the primary hydration product of cement and water and thus, is considered the main contributor to the mechanical properties and durability of cementitious materials8,9,10,11. In the cement chemistry nomenclature C=CaO, S=SiO2, and H=H2O.
There is an increasing interest in innovative approaches to manipulate the structure of C-S-H at the nanoscale as a way to improve macroscale properties12,13,14,15,16,17,18,19,20. Inspired by nature, the incorporation of polymers as an organic compound in C-S-H is considered to be promising to achieve enhanced mechanical performance in C-S-H. Matsuyama et al.13,17 were the first to investigate the possibility of intercalation of polymers with different charges into the structure of C-S-H with various calcium to silicate ratios. Although they did not report a successful intercalation of small sized polymer molecules, they claimed that polymers with higher molecular size can intercalate between the C-S-H layers. Based on their findings, the intercalation of cationic polymers between C-S-H layers are more favorable at low C/S values. However, anionic polymers are more likely to intercalate at high C/S. They also reported a possible intercalation of non-ionic poly(vinyl alcohol) which was related to the interaction of the polymer with C-S-H, facilitated through the partial ionization of the polymer molecule at the high pH of the solution. Pelisser et al.18 claimed that a lower molecular weight poly(vinyl alcohol) has the potential to intercalate between the C-S-H layers. In another study, Pelisser et al.19 investigated the interaction of poly(diallyldimethylammonium chloride) with C-S-H. According to their findings, at C/S of 0.8, some poly(diallyldimethylammonium chloride) intercalated between the C-S-H layers. However, the rest of the polymer was adsorbed on the surface of C-S-H and decreased the mechanical properties of the C-S-H complex by decreasing its packing density. Alizadeh et al.15 synthesized C-S-H with aniline monomers and then polymerized the monomers to achieve C-S-H/polyaniline nanostructures. They reported a potential increase in the silicate polymerization at various C/S levels in the polyaniline modified C-S-H. Khoshnazar et al.16 investigated the effect of low molecular size nitrobenzoic acid on the structure of C-S-H and reported a possible intercalation at a low polymer concentration. Minet et al.21 showed that small molecular sized organic molecules are able to intercalate between the C-S-H layers without changing the structural framework of C-S-H. However, phase separation occurred for the C-S-H/polymer complexes when the polymer molecule was large in size or highly hydrophobic. In another study22, they reported a successful synthesis of C-S-H with polymers directly bonded to its structure via covalent bonds.
Although the effect of cationic and anionic polymers on the structure of C-S-H has been studied by researchers, the effect of biomolecules has not been investigated. Biomolecules are known to play a crucial role in the growth and microstructure formation of some biological nanocomposites that exhibit superior mechanical properties1,23,24,25. Thus, biomolecules are considered promising compounds to manipulate the structure of bio-inspired materials26,27,28,29. The complex structure and chemical functionalities of biomolecules can permit a wide range of interactions with C-S-H. The ability to modify the characteristics of C-S-H through a specific combination of interactions with biomolecules provides a pathway to manipulate the structure, and the physical and mechanical properties of C-S-H. In a recent study, Picker et al.30 studied the adsorption of peptides on C-S-H with different calcium to silicate ratios to shed light on the possible interactions occurring between C-S-H and peptides. The outcomes of their study revealed the role of various functional groups of peptides on interaction with C-S-H. They showed that an organic additive should contain all three charged, H-forming and hydrophobic functional groups in order to adsorb strongly on C-S-H. This suggests that biomolecules with an ability to interact with other molecules through different functional groups can be considered a promising organic compound to manipulate the properties of C-S-H/biomolecule nanocomposite systems. Motivated by their promise in controlling the nucleation, growth, and self-assembly of inorganic systems30,31, this paper, for the first time, aims to investigate the effect of biomolecules on the structure and mechanical properties of C-S-H. Amino acids include both amine and carboxyl functional groups, as well as a side chain (except glycine), in their molecular structure32. A chain of amino acids build a peptide, which is the building block of proteins. Amino acids based on the functional group of their side chain are classified into three different categories of charged, polar (hydrogen bonding) and non-polar (hydrophobic)32.
In order to elucidate the effect of biomolecules on C-S-H, four amino acids with different functional groups and three proteins with different compositions are used to synthesize C-S-H/biomolecule nanocomposites. Characterization methods, including XRD and FTIR, were used to study the structure of the nanocomposites. Morphology examination was performed using SEM and AFM, and the Young’s modulus was elucidated using nanoindentation.
In this study, the synthesis of the nanocomposites is through the direct precipitation method as detailed in the next section. In real applications for cementitious materials, we envision use of biomolecules in the form of chemical admixtures. Chemical admixtures are widely used to improve the physical and chemical properties of cementitious materials. It should be noted that use of biomolecules as chemical admixtures in cementitious materials requires further investigations to elucidate the interaction between biomolecules and other phases present in the microstructure of cementitious materials. This study is focused on C-S-H as the main binding phase of cementitious materials and lays the foundation for the future investigations.
Experiments
Materials
Biomolecules used in this study include four amino acids with different functional groups and three proteins. The name and properties of amino acids and proteins used in this study are listed in Table 1. Because of their small size, as well as their simple chemical structure, the possible interactions between amino acids and C-S-H is anticipated to be primarily due to their functional groups. Charged amino acids included arginine and glutamic acid, the H-bonding amino acid was glutamine, and the hydrophobic amino acid was leucine. The three proteins studied were lysozyme, albumin, and hemoglobin. These proteins have been extensively studied for various applications including biomineralization of calcium carbonate33, synthesis of nanoparticles34, and synthesis of metal oxide nanocomposites and inorganic/organic hybrid materials35,36,37,38,39. The specifications of the proteins are given in Table 2. The isoelectric point (pI) value is estimated using H++ 3.0, an automated system that computes pI values of ionizable groups in biomolecules at the specified pH40,41,42,43. Albumin has the largest size among the proteins studied here. The percentage of amino acid residues with different pI values present in the structure of the proteins is shown in Fig. 1. It is evident that a higher number of amino acid residues with higher pI values are present in the structure of lysozyme, resulting in a higher pI value for this protein as seen in Table 2.
Sample preparation
C-S-H in this study was synthesized in the form of powder using the direct precipitation method by the reaction of calcium and silicate ions in an aqueous solution44. C-S-H with varied initial C/S of 0.7 and 1.5 were prepared by mixing various amounts of CaCl2 and Na2SiO3 solutions. It should be noted that the C/S of the final products can slightly differ from that of the initial reactants44. Nonetheless, nominal C/S of 0.7 and 1.5 is used in this paper to refer to two C-S-H samples with distinct compositions. Amino acids with concentrations corresponding to 0.025 g of amino acid to 1 g of calcium salt, and proteins with a concentration corresponding to 0.3 g of protein to 1 g of calcium salt were added to the Na2SiO3 solution. The higher mass of proteins compared to amino acids was chosen because of the higher molar mass of the proteins compared to the amino acids. The 1 M CaCl2 solution was gradually added to the 0.22 M Na2SiO3 solution and stirred for seven days in a CO2 free glovebox to prevent carbonation. The solutions were filtered and washed with deionized water and acetone and then dried under vacuum for 3 days and then passed through a #60 sieve to obtain a fine powder. The fine powders were stored in the CO2 free glovebox and were only taken out when performing experiments to minimize the amount of exposure to air and carbonation. For nanoindentation testing, the powder was poured into a stainless steel mold and compacted using a loading machine to a pressure of 30 ksi to obtain a pellet with a diameter of 0.5 in. The pellets were cast in epoxy and then the surface of the samples was polished using SiC sand papers with grit numbers of 80, 180, 320, 600 and 1200, respectively. Isopropyl alcohol was used as a lubricating medium instead of water. Final polishing was performed using a diamond paste containing abrasive particles with a size of 1 μm. Samples were ultrasonically cleaned in isopropyl alcohol for 30 min to remove the polishing residues. The polished samples were used in performing nanoindentation. The sample powders for SEM, XRD, and FTIR were transferred in sealed glass vials.
XRD analysis
The change in the interlayer distance of the control and modified C-S-H was examined using XRD. XRD is particularly effective in characterizing materials with layered structure and has been successfully utilized in studying cement-based materials11,15,45. The change in the interlayer distance of C-S-H was evaluated by measuring the change in the reflection peak corresponding to 002 basal spacing. The XRD scans were conducted using a Siemens X-ray diffractometer with the Cu Kα radiation at a scan rate of 0.3 degrees/min and 0.02 degrees/step.
FTIR analysis
FTIR was used to study the polymerization of silicate chains in C-S-H nanocomposites. In this method, the characteristic stretching vibrations of (Si-O) bonds was used to identify different silicate bonds present in C-S-H15,18,19. The presence and intensity of the bridging silicate tetrahedra (Q2) and end silicate tetrahedra (Q1) can be detected using the FTIR spectra. The FTIR analysis was conducted using a Perkin Elmer Paragon 1000 FTIR equipped with an ATR accessory with a scan rate of 4 cm−1 in the range of 650 cm−1 to 4000 cm−1.
Microscopy examination
Scanning electron microscopy (SEM) was utilized to investigate the effect of amino acids and proteins on the morphology of C-S-H nanocomposites. Powder samples were passed through the #200 sieve and placed on a carbon tape attached to a carbon stub. The surface of the samples was coated with a thin layer of gold or palladium to reduce the effect of charging for high magnification imaging. The SEM images were taken at an accelerating voltage of 20 KV using a PHILIPS XL30 ESEM-FEG device.
AFM imaging was conducted using a TT-AFM from AFMWorkshop. A silicon probe from AppNano with a cantilever length and width of 225 μm and 40 μm, a tip radius of less than 10 nm and spring constant of 36–90 N/m was used for imaging. Images of each sample were taken in the non-contact mode.
Nanoindentation measurement
The Young’s modulus of the C-S-H samples was measured using AFM-based nanoindentation. AFM is suited to determine the Young’s modulus of materials with mechanical properties changing over nanoscales10,46 making it a promising method for the mechanical characterization of cementitious materials10. In an AFM-based indentation test, a probe with a known cantilever stiffness comes into contact with the material, indents up to a certain depth and then retracts from the surface. The deflection of the beam versus vertical position of the tip is recorded by the instrument. Deflection data is logged as an electrical signal in volts units that needs to be converted to distance units using a sensitivity factor. Sensitivity is calculated as the slope of a linear fit to voltage-distance curve when the same probe is pushed against a relatively hard surface compared to the tested material so that the indentation depth can be assumed to be negligible. Deflection is converted to force knowing the spring constant of the cantilever using Hooke’s law to obtain the force-distance curves. The amount of deflection corresponding to the cantilever response obtained from the test on a hard surface with no penetration is subtracted from the total deflection to generate the force-indentation distance curves.
The unloading portion of the load-indentation distance curve was fitted to the Hertz model using the following formula47 in a Matlab code:
where F is the force in nN, δ is the indentation distance in nm, R is the tip radius in nm and M is calculated with the following expression:
where ν1 and E1 are the Poisson’s ratio and Young’s modulus (GPa) of the material and ν2 and E2 are the Poisson’s ratio and Young’s modulus (GPa) of the AFM tip. Since a diamond probe was used in this study and its Young’s modulus is much higher than that of the tested material, the above-mentioned expression was simplified as follows:
In this study a cube corner diamond probe (DNISP from Bruker) with a spring constant of 291 N/m and tip radius of 40 nm based on the specification provided by the manufacturer was used for nanoindentation. Nanoindentation tests were performed on about 48 points located in three random meshes of 5 µm spacing for each of the polished samples. The deflection sensitivity was calibrated using a sapphire substrate purchased from Bruker.
Results and Discussion
XRD results
There are several studies on the stoichiometry of C-S-H, suggesting various models to describe its chemical structure11,48,49. It is generally acknowledged that C-S-H does not have a specific chemical formula and stoichiometry13,17,20,50. However, C-S-H stacks, with their limited lateral extension, follow an ordered structure in localized regions. In this type of structure, the volume fraction of interlayer distance is significantly lower than that of the pores between the C-S-H stacks referred to as gel pores20. The XRD spectra for the control C-S-H and C-S-H samples modified with amino acids at a C/S of 0.7 and 1.5 are shown in Fig. 2a,b, respectively. The 2θ range of 3° to 10° corresponds to the peak of the d002 basal spacing reflection. The interlayer distance for all the samples is calculated using Bragg’s equation51:
where d is the interlayer distance (Å), θ is the peak angle (degrees), n is 2 and λ is 1.5418 (Å). The calculated interlayer distance for different C-S-H samples is shown in Table 3. At C/S of 0.7, C-S-H samples modified with arginine (positively charged), leucine (non-polar) and glutamine (H-bond forming) show a broader and less intense peak compared to that of the control sample. In the spectra of arginine and leucine, multiple peaks (marked with * in Fig. 2a) are observed. There is no change in the intensity of the peak in the C-S-H sample modified with glutamic acid. The presence of other peaks at lower angles in addition to the main peak in the spectra of C-S-H samples modified with leucine and arginine can be attributed to a partial intercalation of amino acids between the C-S-H layers increasing the interlayer distance in some of the C-S-H stacks. It is noted that the interlayer distance has slightly increased in the C-S-H samples modified with glutamine which could be attributed to possible adsorption of glutamine in between C-S-H layers. It is seen that there is no indication of intercalation in the C-S-H samples modified with glutamic acid (negatively charged) as the interlayer distance has not increased compared to the control sample. This is in general agreement with the results of adsorption using phage display of peptides performed by Picker et al.30 on C-S-H sample with C/S of 0.66. Based on their results at low C/S, positively charged, polar (H-bond forming) and hydrophobic amino acids adsorb onto the C-S-H.
Their study showed that negatively charged amino acids have the lowest adsorption at this C/S ratio. The deprotonated silanol groups of C-S-H with negative surface charges favor the electrostatic interactions with the positively charged amino acid arginine, H-bond formation with the polar amino acid glutamine and van der Waals interaction with hydrophobic amino acids30.
The interlayer distance of the control C-S-H sample with C/S of 1.5 is lower than that of the control sample with C/S of 0.7. This increase in crystalline size along the c axis with decreasing C/S ratios is in agreement with previous studies17,51. At C/S of 1.5, the C-S-H samples modified with glutamine (H-bond forming) and glutamic acid (negatively charged) show broader peaks compared to that of the control sample. It is seen that the interlayer distance increased in the samples modified with arginine and leucine indicating the intercalation of amino acids in C-S-H. In the C-S-H sample modified with glutamine the interlayer distance has slightly increased compared to the control sample, indicating the potential intercalation of glutamine in the interlayer space of C-S-H. In the sample modified with glutamic acid another peak in addition to the main peak appeared at a lower angle. This could imply the intercalation of glutamic acid at this C/S ratio, compared to C/S of 0.7, where no such adsorption was observed. An explanation for the increased influence of negatively charged glutamic acid on the C-S-H structure can be sought in the structure of C-S-H. As mentioned previously at low C/S ratio of 0.7, the surface of C-S-H carried negative charges due to the deprotonation of silicate groups; the negatively charged glutamic acid is less likely to interact with C-S-H. With increasing C/S ratio to 1.5, the concentration of Ca2+ is increased and as a result, Ca2+ bonds to negatively charge surface of C-S-H and shields the surface against positively charged amino acids. In this case, the adsorption of negatively charged amino acid, glutamic acid, onto C-S-H surface is facilitated through bridging with Ca2+ 30,31.
The XRD spectra of the control C-S-H and C-S-H samples modified with different proteins are shown in Fig. 3a,b. There is no significant change in the interlayer distance of the samples modified with proteins at C/S of 0.7. However, at C/S of 1.5, the peak corresponding to the C-S-H sample modified with lysozyme has broadened and shifted toward lower angles. As shown in Table 3, the interlayer distance of the C-S-H samples modified with lysozyme has increased compared to the control sample. There is not a significant change in intensity of the basal reflection peak and interlayer distance of the samples modified with albumin and hemoglobin. The larger size of proteins compared to amino acids could be a factor in the lower likelihood of intercalation of proteins compared to amino acids in C-S-H.
The observed influence of lysozyme can be attributed to the specific conformation and composition of this protein. The pH value of the C-S-H solutions right after mixing was measured to be 11.0 and 10.0 at C/S of 0.7 and 1.5, respectively. The proteins at their stable and active state (called the native state) fold into the most thermodynamically favorable structure and tend to take a globular shape52. In this state, the hydrophobic residues are located in the interior of the protein molecules and the hydrophilic residues are exposed at the exterior of the protein molecule. The hydrophobic interaction at the interior and hydrophilic interaction at the exterior are both responsible for stabilizing the protein molecules at their native stage. The change in the pH interferes with the stabilizing interactions and forces the protein molecules to unfold53,54,55,56,57. A schematic of how the proteins unfold at high pH is shown in Fig. 4. This exposes various residues with different functionalities providing additional pathways for the interaction between the protein and C-S-H. The observed influence of lysozyme on the interlayer distance of C-S-H at C/S of 1.5 could be related to the specificity of this biomolecule favoring such effect on C-S-H. The specificity of biomolecules in their interaction with inorganic surfaces has been observed and studied in prior investigations58,59. Further investigations based on computational approaches can provide valuable insights into the effect of protein conformation on the atomic structure of C-S-H.
It should be emphasized here that some biomolecules could physically adsorb onto the starting inorganic chemicals used to synthesize C-S-H, and this results in a reduction in the target C/S of the produced C-S-H and consequently an increase in the interlayer distance. Further investigations are necessary to decouple such potential effect of biomolecules on the final C/S from the effect of biomolecules on the nanostructure of C-S-H.
FTIR Analysis
The FTIR spectra for the control C-S-H and C-S-H samples modified with amino acids and proteins at C/S of 0.7 and 1.5 are shown in Figs 5 and 6, respectively. The frequencies of the Si-O stretching vibrations of the Q1 and Q2 tetrahedra for different C-S-H samples are listed in Table 4. Q1 represents the end silicate tetrahedra and Q2 corresponds to the bridging silicate tetrahedra. The intensity ratio of Q2 to Q1 is a measure of polymerization of silicate chains in C-S-H and is shown in Table 4.
It is observed that the location of the Q2 band is shifted towards higher frequencies in the control sample with a reduction in C/S ratio. This is an indication of increased polymerization in the control sample with a C/S of 0.7 compared to the sample with C/S of 1.5 as it is also evident from the higher intensity ratio of Q2 to Q1 at the lower C/S15,60. It is seen that the location of the Q2 band in arginine sample at C/S of 0.7 is lower than that of the control C-S-H, suggesting a reduction in polymerization as a result of interaction between arginine and C-S-H at this C/S ratio. The intensity ratio of Q2/Q1 in the sample modified with arginine is also lower than that of the control C-S-H. The Q2 peak frequency of the C-S-H with other amino acids except arginine is seen to be unchanged compared to the control C-S-H at C/S of 0.7. At C/S of 1.5, the Q2 peak of arginine shows a similar frequency to the control C-S-H. It is interesting to note the shift to higher frequencies of Q2 in the C-S-H modified with glutamic acid at this C/S ratio, indicating the interaction of glutamic acid with C-S-H and maybe an indication of increased polymerization in C-S-H modified with glutamic acid; however, the intensity ratio Q2/Q1 appears to remain unchanged in this sample. The reduction in the influence of arginine and an increase in influence of glutamic acid with increasing C/S ratio is consistent with the XRD results discussed earlier.
In the samples modified with proteins, at C/S of 0.7 there is a shift to lower frequencies in the Q2 peak of the C-S-H modified with hemoglobin. The corresponding Q2 peak frequency of the C-S-H modified with albumin and lysozyme is unchanged. With increasing C/S ratio from 0.7 to 1.5 the Si-O stretching band corresponding to Q2 shifted to higher frequencies in C-S-H samples modified with proteins. This trend is not similar to that of the control C-S-H sample and C-S-H modified with amino acids. One explanation would be the calcium binding effect of proteins. The proteins can bind the added calcium ions so the actual C/S ratio is lower than what is expected61. To investigate the calcium binding effect of proteins, conductivity measurement was utilized. The binding between proteins and Ca2+ reduces the concentration of free Ca2+ in the solution, which results in a reduction in the conductivity of the solutions. About 100 mL of 0.002 M Ca(OH)2 solutions without proteins and with 0.12 g of proteins were prepared and their conductivity was measured. Two electrodes consisting of stainless steel rods with a diameter of 6 mm were inserted inside a glass beaker with a dimeter of 70 mm. The conductivity of the solutions was measured using a Reference Gamry 600 potentiostat/galvanostat with a 20 mV AC signal and a frequency range of 106 to 10 Hz. The normalized conductivity of the solutions with proteins per the conductivity of the solution without proteins after one hour and after 48 hours of mixing is shown in Table 5. It is seen that the solutions with proteins showed a lower conductivity compared to the solution without proteins, indicating possible binding of proteins to Ca2+.
The second explanation for the notable shift in the Q2 frequencies of C-S-H with all proteins at C/S of 1.5 could be the incomplete nucleation of C-S-H particles at C/S of 1.5 due to the presence of proteins. Consequently, the solution has a high content of unreacted silicate gel and surface adsorbed proteins31. The presence of the bands corresponding to amide I and amide II at around 1640 cm−1 and 1530 cm−1, respectively, indicates the high content of proteins in the C-S-H samples modified with the proteins at C/S ratio of 1.562,63.
The shift in the Q2 frequencies of C-S-H with all proteins can also be viewed as an indication of increased polymerization in the C-S-H samples and suggests the influence of the proteins on silicate polymerization of C-S-H. While the influence of lysozyme on C-S-H is also observed from the XRD results, such an influence of albumin and hemoglobin on C-S-H structure is not evident from the XRD analysis.
Morphology examination
The SEM images of the control C-S-H and C-S-H samples modified with arginine, glutamine, leucine and glutamic acid at C/S of 0.7 are shown in Fig. 7. There is no noticeable difference in the morphology of the control sample and the C-S-H samples modified with amino acids as seen from SEM images. The globular morphology with a size of 20 nm to 100 nm can be observed in all C-S-H samples, which is in agreement with the previous studies11,64.
The SEM images of the C-S-H samples modified with albumin, lysozyme and hemoglobin at C/S of 0.7 and 1.5 are shown in Fig. 8. The morphology of the albumin and lysozyme modified C-S-H is comparable to the control sample. The C-S-H sample modified with hemoglobin at both C/S ratios showed a slightly different morphology. The C-S-H particles in these samples are observed to exhibit a platelet morphology and are less round compared to other C-S-H samples. In this structure, the network is built of pores and building blocks of nano-platelets. This type of structure has been previously observed by researchers in hierarchically nanostructured mesoporous spheres of C-S-H65.
AFM imaging was also utilized to provide more detail regarding the morphological attributes of the C-S-H microstructure. The amplitude error AFM images of the control C-S-H and the C-S-H samples modified with albumin, lysozyme and hemoglobin at C/S of 1.5 are shown in Fig. 9. The amplitude error images were chosen because the boundaries of the nanoparticles can be more readily distinguished in this type of image. The cumulative size distribution of the nanoparticles was measured using the ImageJ software and is shown in Fig. 9e. The size of a nanoparticle is assumed to be equal to the diameter of a circle with the equal area as the nanoparticle. It is seen that the nanoparticles seem to be larger in C-S-H modified with proteins compared to the control C-S-H. The increase in the size of C-S-H nanoparticles modified with proteins can be related to the templating effect of proteins directing the aggregation of C-S-H after nucleation and during growth leading to an increase in the size of the nanoparticles. It is interesting to note the increase in the size of the C-S-H nanoparticles modified with the proteins in light of increase in silicate polymerization at C/S ratio of 1.5 as seen from Table 4. More detailed studies are needed to fully elucidate the relation between morphology and silicate polymerization in the modified C-S-H.
Mechanical property
The Elastic modulus measurements of the control C-S-H and C-S-H samples modified with amino acids at C/S of 0.7 and 1.5 are shown in Fig. 10. Comparing the elastic modulus value of the control samples with C/S of 0.7 and 1.5, it is noted that no significant difference can be observed. Excluding the values more than 45 GPa, which could be attributed to calcium hydroxide66, an average Young’s modulus of 24.9 ± 1.0 GPa for the control C-S-H with C/S of 0.7 and 25.2 ± 1.0 GPa for the control C-S-H samples with C/S of 1.5 was obtained. These values are consistent with the values obtained in previous studies66,67,68. It was shown by Beaudoin and Feldman69 that the intrinsic elastic properties of C-S-H are not dependent on the C/S ratio. This indicates that the decrease in the Young’s modulus of C-S-H, observed in nanoindentation test results, could be because of a decrease in the packing density of C-S-H67.
At C/S of 0.7, the C-S-H modified with arginine, leucine and glutamic acid showed lower values of Young’s modulus compared to that of the control sample. The decrease in the value of Young’s modulus may be due to the presence of these amino acids adsorbed on the surface or in the voids between the C-S-H particles resulting in a lower packing of C-S-H sample compared to the control C-S-H sample18,19. However, no noticeable change was observed in the sample modified with glutamine. At C/S of 1.5, all the samples modified with amino acids have average values comparable to that of the control sample. However, the arginine sample has its higher intensity peak at lower values compared to the other samples potentially related to a reduction in the packing density in C-S-H modified with arginine.
The elastic modulus values of the control C-S-H and C-S-H samples modified with proteins at C/S of 0.7 and 1.5 are shown in Fig. 11. At C/S of 0.7, the C-S-H modified with lysozyme is comparable to the control sample. However, albumin and hemoglobin showed lower values of Young’s modulus compared to that of the control sample.
At C/S of 1.5, all the C-S-H samples modified with proteins had lower values of Young’s modulus compared to that of the control sample. In addition, the Young’s modulus of C-S-H with proteins seems to be slightly lower at C/S = 1.5 than at C/S = 0.7. This can be related to a change in silicate polymerization of C-S-H, as seen from the FTIR results shown in Fig. 6, as well as a change at the mesoscale in terms of increased occupation of gel pores by the proteins thereby reducing packing density of C-S-H. It is noted that the sample modified with lysozyme has higher values of Young’s modulus compared to samples modified with albumin and hemoglobin at C/S = 1.5.
Conclusions
In this study the effect of biomolecules with distinct functional groups and various molecular sizes on the atomic structure, morphology and Young’s modulus of C-S-H was investigated. The findings of this study are as follows:
-
The XRD analysis showed a change in the atomic structure, in the form of intercalation or surface adsorption, of C-S-H modified with the H-bond forming, hydrophobic and positively charged amino acids at both C/S = 0.7 and 1.5. With an increase in C/S ratio, the influence of negatively charged amino acid became more pronounced. Among the proteins studied here, lysozyme appeared to show intercalation in C-S-H only at high C/S = 1.5. This could be related to the composition and conformation of this protein facilitating intercalation of this protein in C-S-H at this C/S.
-
The FTIR results indicated the effect of arginine on the silicate polymerization of C-S-H at low C/S ratio and increased influence of glutamic acid at higher C/S = 1.5. A noticeable increase in the silicate polymerization of samples modified with proteins at C/S = 1.5 was observed.
-
The control C-S-H and the C-S-H modified with amino acids used in this study demonstrated a globular morphology of C-S-H nanoparticles. C-S-H modified with lysozyme and albumin also showed a globular morphology. The C-S-H samples modified with hemoglobin showed a platelet morphology in contrast to a globular morphology of the C-S-H modified with other proteins.
-
A decrease in the Young’s modulus of the C-S-H samples modified with amino acid was observed at lower C/S. However, the effect of amino acids in altering the Young’s modulus of C-S-H system was not significant at high C/S.
-
The Young’s modulus of C-S-H with proteins was lower than that of the control C-S-H at both C/S values. The reduction in the Young’s modulus was slightly increased at high C/S ratio. C-S-H modified with lysozyme was shown to exhibit a higher Young’s modulus than C-S-H modified with albumin and hemoglobin.
References
Das, P. & Walther, A. Ionic supramolecular bonds preserve mechanical properties and enable synergetic performance at high humidity in water-borne, self-assembled nacre-mimetics. Nanoscale 5, 9348 (2013).
Arakaki, A. et al. Biomineralization-inspired synthesis of functional organic/inorganic hybrid materials: organic molecular control of self-organization of hybrids. Org. Biomol. Chem. 13, 974–989 (2015).
Meyers, M. A., McKittrick, J. & Chen, P. Y. Structural biological materials: Critical mechanics-materials connections. Science 339, 773–779 (2013).
Razvag, Y., Gutkin, V. & Reches, M. Probing the interaction of individual amino acids with inorganic surfaces using atomic force spectroscopy. Langmuir 29, 10102–10109 (2013).
Verho, T. et al. Hydration and dynamic state of nanoconfined polymer layers govern toughness in nacre-mimetic nanocomposites. Adv. Mater. 25, 5055–5059 (2013).
Juhl, K. M. S. et al. Change in organic molecule adhesion on α-alumina (Sapphire) with change in NaCl and CaCl2 solution salinity. Langmuir 30, 8741–8750 (2014).
Vandamme, M. & Ulm, F. J. Nanogranular origin of concrete creep. Proc. Natl. Acad. Sci. USA 106, 10552–10557 (2009).
Alizadeh, R., Beaudoin, J. J. & Raki, L. Mechanical properties of calcium silicate hydrates. Mater. Struct. Constr. 44, 13–28 (2011).
Pellenq, R. J. M., Lequeux, N. & van Damme, H. Engineering the bonding scheme in C-S-H: The iono-covalent framework. Cem. Concr. Res. 38, 159–174 (2008).
Jones, C. A., Grasley, Z. C. & Ohlhausen, J. A. Measurement of elastic properties of calcium silicate hydrate with atomic force microscopy. Cem. Concr. Compos. 34, 468–477 (2012).
Nonat, A. The structure and stoichiometry of C-S-H. Cem. Concr. Res. 34, 1521–1528 (2004).
Pelisser, F., Gleize, P. J. P. & Peterson, M. Synthesis of calcium silicate hydrate/polymer complexes: Part I. Anionic and nonanionic polymers. J. Mater. Res. 14, 3379–3388 (1999).
Matsuyama, H. & Young, J. F. Synthesis of calcium silicate hydrate/polymer complexes: Part II. Cationic polymers and complex formation with different polymers. J. Mater. Res. 14, 3389–3396 (1999).
Mojumdar, S. C. & Raki, L. Preparation and properties of calcium silicate hydrate-poly(vinyl alcohol) nanocomposite materials. in. Journal of Thermal Analysis and Calorimetry 82, 89–95 (2005).
Alizadeh, R., Beaudoin, J. J., Raki, L. & Terskikh, V. C–S–H/polyaniline nanocomposites prepared by in situ polymerization. J. Mater. Sci. 46, 460–467 (2010).
Khoshnazar, R., Beaudoin, J. J., Raki, L. & Alizadeh, R. Interaction of 2-, 3- and 4-nitrobenzoic acid with the structure of calcium-silicate-hydrate. Mater. Struct. 49, 499–506 (2016).
Matsuyama, H. & Young, J. F. Intercalation of polymers in calcium silicate hydrate: a new synthetic approach to biocomposites? Chem. Mater. 11, 16–19 (1999).
Pelisser, F., Gleize, P. J. P. & Mikowski, A. Structure and micro-nanomechanical characterization of synthetic calcium-silicate-hydrate with Poly(VinylAlcohol). Cem. Concr. Compos. 48, 1–8 (2014).
Pelisser, F., Gleize, P. J. P. & Mikowski, A. Effect of poly(diallyldimethylammonium chloride) on nanostructure and mechanical properties of calcium silicate hydrate. Mater. Sci. Eng. A 527, 7045–7049 (2010).
Merlin, F. et al. Cement-polymer and clay-polymer nano- and meso-composites: spotting the difference. J. Mater. Chem. 12, 3308–3315 (2002).
Minet, J. et al. Organic calcium silicate hydrate hybrids: a new approach to cement based nanocomposites. J. Mater. Chem. 16, 1379 (2006).
Minet, J. et al. New layered calcium organosilicate hybrids with covalently linked organic functionalities. Chem. Mater. 16, 3955–3962 (2004).
Tang, Z., Kotov, N. A., Magonov, S. & Ozturk, B. Nanostructured artificial nacre. Nat. Mater. 2, 413–8 (2003).
Sun, J. & Bhushan, B. Hierarchical structure and mechanical properties of nacre: a review. RSC Adv. 2, 7617 (2012).
Podsiadlo, P., Liu, Z., Paterson, D., Messersmith, P. B. & Kotov, N. A. Fusion of seashell nacre and marine bioadhesive analogs: High-strength nanocomposite by layer-by-layer assembly of clay and L-3,4-dihydroxyphenylalanine polymer. Adv. Mater. 19, 949–955 (2007).
Sugawara, A., Ishii, T. & Kato, T. Self-organized calcium carbonate with regular surface-relief structures. Angew. Chemie - Int. Ed. 42, (5299–5303 (2003).
Zhu, F. et al. Tuning the stability of CaCO3 crystals with magnesium ions for the formation of aragonite thin films on organic polymer templates. Chem. - An Asian J. 8, 3002–3009 (2013).
Nakamura, S. & Naka, K. Bendable, free-standing calcite thin films. Langmuir 31, 2014–2018 (2015).
Sakamoto, T., Oichi, A., Nishimura, T., Sugawara, A. & Kato, T. Calcium carbonate/polymer thin-film hybrids: induction of the formation of patterned aragonite crystals by thermal treatment of a polymer matrix. Polym. J. 41, 522–523 (2009).
Picker, A., Nicoleau, L., Nonat, A., Labbez, C. & Cölfen, H. Identification of binding peptides on calcium silicate hydrate: a novel view on cement additives. 26, 1135–1140 (2014).
Picker, A. Influence of Polymers on Nucleation and Assembly of Calcium Silicate Hydrates Dissertation. (2013).
Ellington, A. & Cherry, J. M. Characteristics of amino acids. Current Protocols in Molecular Biology 2, suppl. 12, appendixes 1.8–1.9. Edited by F. M. Ausubel, R. Brent, D. D. Moore, J. G. Seidman, J. A. Smith & K. Struh. Chichester: John Wiley. (1994).
Song, S. M. & Kim, I. H. Biomineralization of calcium carbonate by adding aspartic acid and lysozyme. Korean J. Chem. Eng. 28, 1749–1753 (2011).
Bakshi, M. S., Kaur, H., Banipal, T. S., Singh, N. & Kaur, G. Biomineralization of gold nanoparticles by lysozyme and cytochrome c and their applications in protein film formation. Langmuir 26, 13535–13544 (2010).
Kim, J. K. et al. Lysozyme-mediated biomineralization of titanium–tungsten oxide hybrid nanoparticles with high photocatalytic activity. Chem. Commun. 50, 12392–12395 (2014).
Li, P., Tong, Z., Jia, Z. & Su, W. Preparation and characterization of hemoglobin-silver composites as biocompatible antiseptics. J. Biomater. Appl. 31, 773–783 (2016).
Lu, X., Zou, G. & Li, J. Hemoglobin entrapped within a layered spongy Co3O4 based nanocomposite featuring direct electron transfer and peroxidase activity. J. Mater. Chem. 17, 1427–1432 (2007).
Ageeva, S. A. et al. Nanotube-based three-dimensional albumin composite obtained using continuous laser radiation. Semiconductors 43, 1714–1718 (2009).
Zhao, J. et al. Cross-linked bovine serum albumin composite membranes prepared by interfacial polymerization with stimuli-response properties. J. Memb. Sci. 445, 1–7 (2013).
Anandakrishnan, R. An automated system that computes pK values of ionizable groups in macromolecules and adds missing hydrogen atoms according to the specified pH of the environment, Virginia Tech., Blacksburg, VA, USA. http://biophysics.cs.vt.edu/ H++ (2017).
Anandakrishnan, R., Aguilar, B. & Onufriev, A. V. H++ 3.0: Automating pK prediction and the preparation of biomolecular structures for atomistic molecular modeling and simulations. Nucleic Acids Res. 40, 537–541 (2012).
Rezácová, P., Borek, D., Moy, S. F., Joachimiak, A. & Otwinowski, Z. Crystal structure and putative function of small Toprim domain-containing protein from Bacillus stearothermophilus. Proteins 70, 311–319 (2008).
Gordon, J. C. et al. H++: A server for estimating pKas and adding missing hydrogens to macromolecules. Nucleic Acids Res. 33, 368–371 (2005).
Matsuyama, H. & Young, J. F. Synthesis of calcium silicate hydrate/polymer complexes: Part I. Anionic and nonanionic polymers. J. Mater. Res. 14, 3379–3388 (1999).
Němeček, J. Creep effects in nanoindentation of hydrated phases of cement pastes. Mater. Charact. 60, 1028–1034 (2009).
Monclus, M. A., Young, T. J. & Di Maio, D. AFM indentation method used for elastic modulus characterization of interfaces and thin layers. J. Mater. Sci. 45, 3190–3197 (2010).
Hertz, H. On the contact of elastic solids. J Reine Angew Math 92, 156–171 (1881).
Taylor, H. F. W. Nanostructure of C-S-H: Current status. Adv. Cem. Based Mater. 1, 38–46 (1993).
Xiandong, C. & Kirkpatrick, R. J. 29Si MAS NMR study of the structure of calcium silicate hydrate. Adv. Cem. Based Mater. 3, 144–156 (1996).
Popova, A., Geoffroy, G., Renou-Gonnord, M. F., Faucon, P. & Gartner, E. Interactions between polymeric dispersants and calcium silicate hydrates. J. Am. Ceram. Soc. 83, 2556–2560 (2000).
Grangeon, S., Claret, F., Linard, Y. & Chiaberge, C. X-ray diffraction: A powerful tool to probe and understand the structure of nanocrystalline calcium silicate hydrates. Acta Crystallogr. Sect. B Struct. Sci. Cryst. Eng. Mater. 69, 465–473 (2013).
Dill, K. A., Ozkan, S. B., Shell, M. S. & Weikl, T. R. The protein folding problem. Annu. Rev. Biophys. 37, 289–316 (2008).
Brüning, A. & Jückstock, J. Misfolded proteins: from little villains to little helpers in the fight against cancer. Front. Oncol. 5, 47 (2015).
Nick Pace, C., Martin Scholtz, J. & Grimsley, G. R. Forces stabilizing proteins. FEBS Letters 588, 2177–2184 (2014).
Lesser, G. J. & Rose, G. D. Hydrophobicity of amino acid subgroups in proteins. Proteins Struct. Funct. Bioinforma. 8, 6–13 (1990).
Yan, Y. et al. pH-dependent aggregation and disaggregation of native β-lactoglobulin in low salt. Langmuir 29, 4584–4593 (2013).
Pinho Melo, E., Aires-Barros, M. R., Costa, S. M. B. & Cabral, J. M. S. Thermal unfolding of proteins at high pH range studied by UV absorbance. J. Biochem. Biophys. Methods 34, 45–59 (1997).
Patwardhan, S. V., Patwardhan, G. & Perry, C. C. Interactions of biomolecules with inorganic materials: principles, applications and future prospects. J. Mater. Chem. 17, 2875–2884 (2007).
Ramakrishnan, S. K., Zhu, J. & Gergely, C. Organic-inorganic interface simulation for new material discoveries. WIREs Computational Molecular Science 7, 1277 (2017).
Yu, P., Kirkpatrick, R. J., Poe, B., McMillan, P. F. & Cong, X. Structure of calcium silicate hydrate (C-S-H): Near-, mid-, and far-infrared spectroscopy. J. Am. Ceram. Soc. 82, 742–748 (1999).
Yáñez, M., Gil-Longo, J. & Campos-Toimil, M. Calcium binding proteins. Adv. Exp. Med. Biol. 740, 461–482 (2012).
Venkataramani, S., Truntzer, J. & Coleman, D. R. Thermal stability of high concentration lysozyme across varying pH: A Fourier Transform Infrared study. J. Pharm. BioAllied Sci. 5.2, 148–153 (2013).
Calabrò, E. & Magazù, S. Unfolding-induced in haemoglobin by exposure to electromagnetic fields: A FTIR spectroscopy study. Orient. J. Chem. 30, 31–35 (2014).
Mondai, P., Shah, S. R. & Marks, L. D. Nanoscale characterization of cementitious materials. ACI Mater. J. 105, 174–179 (2008).
Wu, J., Zhu, Y. J., Cao, S. W. & Chen, F. Hierachically nanostructured mesoporous spheres of calcium silicate hydrate: Surfactant-free sonochemical synthesis and drug-delivery system with ultrahigh drug-loading capacity. Adv. Mater. 22, 749–753 (2010).
Kim, J. J., Foley, E. M. & Reda Taha, M. M. Nano-mechanical characterization of synthetic calcium-silicate-hydrate (C-S-H) with varying CaO/SiO2 mixture ratios. in Cement and Concrete Composites 36, 65–70 (2013).
Constantinides, G. & Ulm, F. J. The effect of two types of C-S-H on the elasticity of cement-based materials: Results from nanoindentation and micromechanical modeling. Cem. Concr. Res. 34, 67–80 (2004).
Foley, E. M., Kim, J. J. & Reda Taha, M. M. Synthesis and nano-mechanical characterization of calcium-silicate-hydrate (C-S-H) made with 1.5 CaO/SiO2 mixture. Cem. Concr. Res. 42, 1225–1232 (2012).
Beaudoin, J. J. & Feldman, R. Dependence of degree of silica polymerization and intrinsic mechanical properties of C-S-H on C/S. in 8th International Congress on the Chemistry of Cement (1986).
Acknowledgements
This study was partially supported by the NASA Florida Space Research Grant and University of Miami’s Provost Research Award.
Author information
Authors and Affiliations
Contributions
A.G. was involved in work conception, experimental design, data analysis, and manuscript writing. M.K. provided work conception, performed experiments and data analysis, and was involved in manuscript writing. All authors agree for work accountability.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Kamali, M., Ghahremaninezhad, A. Effect of Biomolecules on the Nanostructure and Nanomechanical Property of Calcium-Silicate-Hydrate. Sci Rep 8, 9491 (2018). https://doi.org/10.1038/s41598-018-27746-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-27746-x
- Springer Nature Limited